Abstract
The effect of sputtering conditions on magnetic properties of CoCrMo/Cr magnetic thin film was investigated. Substrate temperature were controlled from R. T to $250^{\circ}C$. The thickness changes of Cr underlayer and CoCrMo magnetic layer were in the range of $1000-2500\AA$ and $300-800\AA$, respectively. Grain size was found to be decreased with increasing magnetic layer thickness(from $500\AA$ to $800\AA$). CoCrMo magnetic layer microstructure showed relatively small dependence on Cr underlayer thickness, substrate temperature. Coercivity increased with increasing Cr underlayer, magnetic layer thickness and substrate temperature. CoCrMo/Cr thin film showed a coercivity of 880 Oe in $700\AA$ magnetic layer thickness and $1000\AA$ Cr underalyer thickness.
스퍼터된 자기기록매체 Co-10at%Cr-2at%Mo/Cr 자성박막의 제조조건이 미세구조와 자기적특성에 미치는 영향을 조사하였다. 기판의 온도는 상온-$250^{\circ}C$로 하였으며 Cr하지층과 CoCrMo층의 두께는 각각 $1000-2500\AA$, $300-800\AA$이었다. CoCrMo층의 두께가 $500{\AA}-800{\AA}$ 증가함에 따라 결정립은 미세화 되었으며 균일한 조직을 나타냈다. 보자력은 기판의 온도, CoCrMo자성층, Cr하지층의 두께 를 증가시켰을때 향상되었다. 기판온도가 $250^{\circ}C$, 자성층의 두께가 $700\AA$, Cr 하지층의 두께가 $1000\AA$일때 880 Oe의 보자력을 나타냈다.