• Journal of the Korean Chemical Society
• /
• v.54 no.1
• /
• pp.99-104
• /
• 2010

Platinum nanoparticles were added to a mixture of HEMA (2-hydroxyethyl methacrylate), NVP (N-vinyl pyrrolidone) and MMA (methyl methacrylate) in a mould at various concentrations. The resulting mixture was copolymerized by heating at $70^{\circ}C$ for 40 min, $80^{\circ}C$ for 40 min, and $100^{\circ}C$ for 40 min, respectively. The physical properties of contact lens were then measured. The oxygen transmissibility of $9{\sim}15{\times}10^{-9}$ cm/s mL $O_2$/mL ${\times}$ mmHg, water content of 34.22~35.52%, refractive index of 1.432~1.435, visible transmittance of 88.3~91.2% and tensile strength of 0.141~0.152 kgf were obtained. The addition of platinum nanoparticles to the polymer allowed the contact lens to have various colors without artificial coloring agents. The polymer materials satisfied the physical properties required to produce contact lenses, making the material suitable to be applied as a functional material for ophthalmological purposes.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.299-299
• /
• 2012

투명전도산화물 박막은 디스플레이, 태양전지, 압전소자 등 다양한 응용분야에 많이 이용되고 있는 소재이다. 그 중에서 현재 산업에서 활용 빈도가 높은 투명전도막의 재료는 ITO를 기반으로 하는 물질이다. 하지만 인듐의 높은 생산단가와 플라즈마 노출시 열화로 인한 문제점 때문에 기존의 ITO를 대체하기 위한 새로운 재료에 관심이 증대되고 있다. 본 연구에서는 대표적인 ITO 대체 물질 중의 하나인 ZnO 박막에 대해서 증착환경변화에 따른 물성변화를 조사하였다. 먼저 대기중에서 안정화된 ZnO 박막을 얻기 위해서 인(P) 2% 첨가된 ZnO 세라믹을 고상반응법으로 제작하고, 펄스레이저 증착법을 이용하여 Al2O3(0001)기판에 산소분압을 30~150 mTorr로 변화를 주어 P-ZnO 박막을 제작하였다. 이 때 증착온도는 $400^{\circ}C$로 고정하였다. X선 회절 결과로부터 산소분압에 상관없이 ZnO (002)방향으로 증착되었다. 하지만 결정립의 크기는 산소분압이 증가하면서 줄어들고, ZnO (002)피크로부터 얻어진 격자상수(c-축)는 벌크 값에 가까워짐을 알 수 있었다. 하지만 P첨가로 인해서 박막의 격자상수는 순수한 ZnO 벌크 값 보다 큰 것으로 알 수 있다. 산소분압 변화에 따른 P-ZnO 박막의 산화 상태는 X-선 광전자 분광기를 이용하여 측정하였다. 그 결과 산소 core-level의 스펙트럼은 자연산화, 산소 vacancy, Zn-O 결합으로 구성되어짐을 알 수 있었다. 산소분압이 증가하면 Zn-O 결합은 증가하지만 산소 vacancy는 감소함을 알 수 있었다. 전기적 특성 결과 P-ZnO 박막은 30 mTorr에서는 n형 반도체 특성, 100 mtorr에서 p형 반도체의 특성이 나타내었고, 산소분압이 증가하면 다시 n형 반도체 특성을 나타냄을 알 수 있었다. 광학적 특성 결과 P-ZnO 박막은 산소분압에 상관없이 가시광선 영역에서 80%이상의 투과율을 나타내었으며, 산소분압이 증가할수록 에너지 갭이 증가하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.138-139
• /
• 2009

폴리머 기판위에서 ICP-RIE 방법을 이용하여 $O_2$ 플라즈마 전처리효과에 따른 GZO박막의 전기적, 광학적인 특성을 고찰 하였다. ICP-RIE 방법을 이용하여 폴리머 기판 위에 $O_2$ 플라즈마 전처리의 공정 값은 공정압력은 20 mTorr, 파워는 100 W로 하고 변수로는 시간을 60초 ~ 600초로 하였다. $O_2$ 플라즈마 전처리한 기판위에 RF Sputtering 방법을 이용하여 4인치의 GZO(ZnO: 95 wt%, $Ga_2O_3$: 5 wt%) 타겟을 사용하여 공정압력은 5 mTorr, 파워는 150 W, 박막의 두께는 500 nm의 조건으로 박막을 증착하였다. PET 기판의 600초의 $O_2$ 플라즈마 처리 후 증착한 GZO 박막의 비저항이 $6.2\times10^{-3}\;{\Omega}$-cm이었고, PEN 기판의 120초의 $O_2$ 플라즈마 처리 후 증착한 GZO 박막의 비저항이 $1.1\;{\times}\;10^{-3}\;{\Omega}$-cm이었다. 또한 300 nm 이하의 자외선 영역에서는 뛰어난 광 차단 효과를 가지고 있었으며, 가시광선 영역 (400 nm ~ 700 nm)에서 증착 된 시편들이 80 % 광 투과율을 나타내었다.

• Journal of the HCI Society of Korea
• /
• v.2 no.1
• /
• pp.57-63
• /
• 2007

Our research was performed in order to implement a new pointing device for human-computer interactions in a collaborative environments based on Tiled Display system. We mainly focused on tracking the position of an infrared light source and applying our system to various areas. More than simple functionality of mouse clicking and pointing, we developed a device that could be used to help people communicate better with the computer. The strong point of our system is that it could be implemented in any place where a camera can be installed. Due to the fact that this system processes only infrared light, computational overhead for LED recognition was very low. Furthermore, by analyzing user's movement, various actions are expected to be performed with more convenience. This system was tested for presentation and game control.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.12 no.5
• /
• pp.234-239
• /
• 2002

The spinel was calcined at temperatures in the range of $1000^{\circ}C$ to $1300^{\circ}C$ with $100^{\circ}C$ interval to evaluate the effect of calcination temperature on mechanical properties of spinel-glass dental composites. Although the average particle size of spinel calcined at temperatures from $1000^{\circ}C$ to $1200^{\circ}C$ was within 2.8~3.0 $\mu\textrm{m}$, the spinel calcined at $1300^{\circ}C$ was 4.66 $\mu\textrm{m}$ due to abnormal grain growth. Shrinkage and pore size of the spinel preform decreased and increased, respectively, as calcination temperature increased, indicating that the calcination temperature was significant to the powder compaction and the densification of the composites as a result of particle size and distribution. The optimum strength and the fracture toughness of the composite calcined at $1200^{\circ}C$ were 284$\pm$40 MPa, 2.5$\pm$0.1 MPaㆍ$m^{1/2}$ respectively. Optical experimental results showed that transmittance of the spinel-glass composite in the visible region was twice higher than that of the alumina-glass composite, suggesting that the spinel-glass composites possessed better aesthetic properties for all-ceramic dental crown application.

• Korean Journal of Materials Research
• /
• v.11 no.7
• /
• pp.550-555
• /
• 2001

A diamond-like carbon(DLC) films were deposited on the borosilicate glass substrate by radio frequency plasma enhanced chemical deposition(rf-PECVD). The $methane(CH_4)-hydrogen(H_2)$ gas mixture was used as precursor gas. The morphologies, the structure and the optical properties of the DLC films were investigated by SEM, Raman and UV spectrometer. The deposition rate was slightly increased with the hydrogen concentration in the gas mixture and it maintained constant at over 25 sccm of the gas flow rate. The optical band gap calculated by UV spectra decreased with increase of deposition time and DC self bias, but that were not effected by hydrogen content. Most effective parameter on the transmittance of film was bias voltage, especially in the range of ultra violet and visible light.

• Journal of Korean Ophthalmic Optics Society
• /
• v.9 no.2
• /
• pp.397-415
• /
• 2004

This study surveyed differences among KS, ISO, JIS and ANSI ophthalmic spectacle lenses standards. These standards applied to several lenses that were in common currency and we checked over problems and improvements in KS. KS corresponded to ISO, for the most part, and ANSI, partly. But terms, definitions, progressive power lenses standards, UV transmittance and base curves clauses did not exist in KS. There was no differences between nominal data and actual data in important clauses estimation-minimum requirements on refractive power, tolerances on the size of lenses, material and surface quality. But tolerances of thickness, base curves, UV and visible transmittance values were not existing, there were differences among several ophthalmic spectacle lenses in the test of these clauses. These requirements will be needed for better and more comfortable vision.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2013.02a
• /
• pp.507-507
• /
• 2013

유리기판으로 투과되는 빛들 중에는 내부 전반사나 wave-guided mode로 인하여 손실이 일어나 일반적으로 20%의 광추출 효율을 가진다. 이러한 문제점을 해결하기 위한 연구에는 Photonic Crystal과 같은 주기적인 나노 구조물이 있는데 이러한 구조물을 제작하기 위한 마스크 공정 과정은 대부분 복잡하거나 비싼 단점이 있다. 이에 본 발표에서는 마스크 없이 비정질소다라임 유리의 구조물 생성으로 광 추출 효율이 상승하는지 보고자 하였다. M-ICP (Magnetized-Induced Coupled Plasma)란 용량 결합형 플라즈마와 유도 결합형 플라즈마 두 가지 방식의 플라즈마를 이용한 것인데 용량 결합형 플라즈마를 이용해 이온이 sheath에 의해 가속되어 유리표면에 부딪히고 그에 따라 유리가 식각되는 물리적 식각을 이용하였다. 또한 이온의 밀도를 조절하기 위해 유도결합형 플라즈마 방식을 이용하여 식각률을 높였다. 화학적 식각을 위해서는 CF4와 O2혼합 가스를 이용해 F가 Si와 결합하여 SiF4가 되어 사라지고 탄소잔여물인 C는 O2와 반응하여 제거하였다. 그 결과, 랜덤한 분포를 가지는 미세한 구조물(stochastic sub-wavelength structure)을 유리 표면에 형성할 수 있었고, 또한 다양한 가스 종류와 압력, source power와 bias power, 그리고 시간을 바꿔가며 미세 구조물들을 관찰하였다. 실험 결과, 가시광선 파장 이하의 높이를 갖고 수 마이크로미터의 너비를 갖는 구조물이 전반사되는 빛을 효율적으로 추출하는 것을 산란되는 빛의 정도인 diffusive transmittance 가 기존 0%에서 15% 정도로 증가하는 것으로 스펙트로포토미터 측정을 통해 확인하였다. 이러한 유리 기판 위 구조물 생성방법을 OLED에 적용한다면 적은 비용으로 소자의 효율을 크게 향상 시킬 수 있을 것이다. 또한 본 처리 과정의 장점은 기존의 방법에 필요한 스퍼터링이나 RTA 처리 과정이 필요 없어 공정 단가 절감과 제조 공정의 단순화로 높은 생산성을 얻을 수 있으며 대면적화에도 유리하다.

• Korean Chemical Engineering Research
• /
• v.53 no.6
• /
• pp.762-769
• /
• 2015

The titania ($TiO_2$) nanoparticles with a diameter 2?3 nm were synthesized by controlling hydrolysis of titanium tetraisopropoxide (TTIP) in acid solution. Organic-inorganic hybrid coating solutions were prepared by reacting the titania nanoparticles with 3-glycidoxypropyl trimethoxysilane (GPTMS) by the sol-gel method. The hard coating films with high refractive index were obtained by curing thermally at $120^{\circ}C$ after spin-coating the coating solutions on the polycarbonate (PC) sheets. The coating films showed high optical transparency of 90% in the visible range and exhibited a pencil hardness of 2H. Also, the refractive index at 633 nm wavelength of coating films enhanced from 1.502 to 1.584 as the weight content of titania nanoparticles in the coating solutions increased from 4% to 25%.

• Journal of the Korean Chemical Society
• /
• v.54 no.3
• /
• pp.317-322
• /
• 2010

This study used 4-fluorostyrene with the cross-linker EGDMA (ethylene glycol dimethacrylate), HEMA (2-hydroxyethyl methacrylate) and the initiator AIBN (azobisisobutyronitrile) for copolymerization. Measurement of the physical properties of the copolymerized polymer showed that the water content was 19.98 ~ 31.08%, refractive index 1.443 ~ 1.475, visible transmittance 87 ~ 93% and tensile strength 0.246 ~ 0.311 kgf while the contact angle showed a distribution between $54.14^{\circ}$ and $66.95^{\circ}$. Therefore, the ophthalmic material produced using 4-fluorostyrene satisfied the basic physical properties required for contact lenses and also showed an increase in wettability and refractive index while having no significant change in water content with relation to styrene. Based on the results of this study, the produced copolymer is suitable for use as a material to high refractive index and wettability contact lenses.