• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.6
• /
• pp.1775-1781
• /
• 2008

The effects of the type of curing agent on the swelling of the natural rubber(NR) sponge applicable to the self-sealing layer of a helicopter fuel tank were investigated. The curing systems employed were peroxide and mixed ones of sulfur and peroxide. The NR compounds were prepared in a kneader and a roll-mill. The compounds were partially cured in a press at high pressure and subsequently cured fully with expansion in another press at atmospheric pressure. The apparent density of the NR sponge was measured and the cell structure was observed with scanning electron microscopy. The swelling experiments were performed at room temperature using toluene, iso-octane, and an aircraft fuel as a solvent. More rapid volume swelling of the NR sponge cured by peroxide was achieved than cured by sulfur and peroxide with similar amount of curing agent added in rubber compounds. The apparent density and cell structure of the sponge were extremely sensitive to the amount of peroxide, which influences again the swelling behavior of the NR sponge. It is important to control properly two reactions of decomposition of foaming agent and crosslinking of NR in the mold to obtain rapid swelling of the NR sponge on contact of the fuel.

• Journal of the Korean Chemical Society
• /
• v.46 no.3
• /
• pp.233-240
• /
• 2002

In this work, the cure kinetics and rheological and mechanical properties of diglycidylether of bispheonol A (DGEBA, EP)/polyurethane (PU) blends were investigated. The 1 wt% N-benzylpyrazinium hexafluoroantiminate (BPH) was used as a latent thermal catalyst. Latent properties were performed by measurement of the conversion as a function of reaction temperature using DSC. And the rheological properties of the blend systems were investigated under isothermal conditions using a rheometer. Crosslinking activating energies (Ec) were also determined from the Arrhenius equation based on gel time and curing temperature. The impact strengths were measured as mechanical properties of the casting specimens. The BPH in the blend systems could be an excellent latent thermal catalyst without any co-initiator. The rheological results showed that Ec was highest when PU content was 30 wt% which was in good agreement with the impact strengths. This was probably due to the intermolecular hydrogen bonding between the hydroxyl group in PU and EP, resulting in increasing the crosslinking density.

• Polymer(Korea)
• /
• v.28 no.1
• /
• pp.18-23
• /
• 2004

Superabsorbent poly(potassium acrylate-co-acrylamide)s were synthesized in particle form using inverse suspension polymerization technique. Mean diameter of the prepared polymer particles decreased from 300 to 50 $\mu\textrm{m}$ with increasing surfactant concentration. The dynamic and equilibrium swelling behaviors during water absorption and drying process were investigated by weight measurement. The swelling ratio of polymer particles in water changed according to not only polymer crosslinking density, but particle size, saline concentration of aqueous medium, and copolymer compositions. Water sorption amount was increased with decreasing particle size, crosslinking agent concentration, and ion concentration in bulk solution. Being different from the water sorption process, the drying process was not significantly affected by particle size, polymer composition, or crosslinking amount.

• Proceedings of the Korean Fiber Society Conference
• /
• 2003.04a
• /
• pp.347-347
• /
• 2003

폴리아크릴로니트릴을 NaOH로 가수분해시키면 carboxylate anion과 carboxanlide기가 생성되며, 물을 흡수할 경우 sodium carboxylate기의 해리로 팽윤이 크게 일어나므로 고흡수성을 지니게 된다. 일찍이 flory[1]는 가교된 고분자 전해질이 고흡수성을 나타내는 겔을 형성할 것으로 예측한 바 있다. 이 가교 결합이 아크릴 섬유의 부분 가수분해에 대한 자료는 새로운 기능을 부여하면서 섬유의 물성을 어느 정도 유지하는데 요구되는 조건을 제시하게되므로 향후 아크릴 섬유의 개질에 활용될 수 있다. (중략)

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.23 no.3
• /
• pp.247-254
• /
• 2010

Due to lightweight and high durability of glass-fiber reinforced polyester (GFRP) materials, they are promising alternatives to conventional construction materials such as steel, concrete and wood. As good application examples of GFRP materials, several types of temporary arch bridges were suggested and verified by finite element analyses in our previous study where snap-fit GFRP decks were applied. In this paper, we conduct a structural performance test to verify safety and serviceability of the temporary arch bridge, where snap-fit GFRP decks are assembled by bolts. The structural problems occurred in this test are also discussed and improvement of temporary arch bridges is suggested to resolve the occurred structural problems.

• Elastomers and Composites
• /
• v.45 no.3
• /
• pp.165-169
• /
• 2010

Recently supramolecular network thermo-reversible crosslinking elastomer having flexibility, various functionality, and advantages of thermoplastic elastomer (TPE) such as recycle and easy processbility is introduced. Although thermo-reversible bonds such as hydrogen bond and ionic cluster is recognized as a common technology since 1990, control technology of bonding and dissociation of crosslink in supramolecular network is a recent technology. In this review, characteristics of thermo-reversible crosslinking elastomer having rheological properties of TPE and reinforcing behaviors of thermoset elastomer are summarized.

• Applied Chemistry for Engineering
• /
• v.32 no.4
• /
• pp.472-477
• /
• 2021

The crosslinking behavior of polyhedral oligomeric silsesquioxane (POSS) containing eight acrylate groups in a cage form in ethylene-propylene-diene rubber (EPDM) peroxide crosslinking, the effect on mechanical properties, and the thermal stability were investigated. An EPDM/POSS composite material was prepared by mixing 0 to 12 parts per hundreds of rubber (phr) of POSS per 100 phr of rubber by content and adding a peroxide crosslinking agent. As a result of crosslinking properties, it was found that the acrylate group of POSS was activated by peroxide and improved the peroxide crosslinking efficiency. Although the dispersion stability of POSS in EPDM/POSS composites was poor, the fracture strength, elongation and thermal stability were improved.

• Polymer(Korea)
• /
• v.28 no.1
• /
• pp.92-102
• /
• 2004

(6-Cholesteryloxycarbonylpentoxypropyl)celluloses (CHPCs) with degree of esterification (DE) ranging from 2.25 to 2.91 were synthesized by reacting hydroxypropyl cellulose with 6-cholesteryloxycarbonylpentanoyl chloride. The acrylic esters of CHPCs (CHPCEs) and their photocrosslinked films with liquidcrystalline order were also synthesized. The thermotropic properties of mesophase for both uncrosslinked and crosslinked samples and the swelling behavior of the crosslinked samples in acetone were investigated. The hydroxypropyl cellulose exhibited an enantiotropic cholesteric phas, while all the uncrosslinked cholesterylbearing samples exhibited a monotropic cholesteric phases; the 6-cholesteryloxycarbonylpentanoyl chloride also showed a monotropic smectic phase. The hydroxypropyl cellulose formed a right-handed helix whose optical pitch (λ$\sub$m/) increases with temperature, whereas all the uncrosslinked derivatives farmed left-handed helices whose λ$\sub$m/'s decreased with temperature. The thermal stability of the mesophase and the magnitude of λ$\sub$m/ at the same temperature for both CHPCs and CHPCEs decreased with increasing DE. All the crosslinked samples, in constrast with CHPCEs, did not display reflection colors but exhibited an anisotropic swelling characteristic of crosslinked gel retaining liquid-crystalline order.

• Journal of Adhesion and Interface
• /
• v.9 no.2
• /
• pp.24-31
• /
• 2008

In this work, calcium hydroxide and magnesium carbonate as metal ionic crosslinking agents were used to introduce ionic crosslinking points to the ethylene vinylacetate (EVA) emulsions for the enhancement of water resistance and mechanical properties of emulsion films. The properties of EVA emulsion film were investigated in crosslinking density, thermal features, surface energy, and mechanical properties, such as tensile strength, elongation at break and tear strength. With the increasing content of metal ionic crosslinking agent, the crosslinking density of the EVA emulsion film increases, resulting into the improvement of water resistance. The surface energy and mechanical properties of the EVA emulsion film, however, showed somewhat different behaviors. The highest surface energy, tensile strength, and tear strength were observed when 0.4% for calcium hydroxide and 0.5% for magnesium carbonate was added respectively, because the EVA emulsion containing carboxylic acid forms strong carboxylate-metal bond of ionically-crosslinked system. Therefore, it can be concluded that metal ionic crosslinking agents, such as magnesium carbonate and calcium hydroxide are considered to improve water resistance and mechanical properties of the EVA emulsion.

• Polymer(Korea)
• /
• v.28 no.1
• /
• pp.41-50
• /
• 2004

A new hydroxypropyl chitosan capable of forming a thermotropic liquid crystalline phase and two kinds of derivatives based on the hydroxypropyl chitosan (6-cholesteryloxycarbonylpentoxypropyl) chitosans (CHPCTs) and acrylic acid esters of CHPCT (CHPCTEs) were synthesized. The crosslinked films with liquid crystalline order were also prepared by photocrosslinking CHPCTE in mesophase. The liquid crystalline properties for all the samples and the swelling behavior of the crosslinked samples in acetone were investigated. In contrast with the hydroxypropyl chitosan, all the uncrosslinked cholesteryl-bearing samples farmed monotropic cholesteric phases with left-handed helicoidal structures and exhibited reflection colors over the full cholesteric range. This is the first report of a thermotropic cholesteric liquid crystalline chitosan derivative with reflection bands in the visible region. Both the optical pitches (λ$\_$m/'S) of CHPCT and CHPCTE decrease with temperature or with cholesteryl content at a given temperature. However, the λ$\_$m/ of CHPCT was larger than that of CHPCTE at the same temperature and at the same cholesteryl content. All the crosslinked samples did not display reflection colors, indicating that the cholesteric structure of CHPCTE significantly changes upon crosslinking. The two-dimentional anisotropic swelling characteristic of liquid crystalline networks was observed for all the crosslinked samples.