The Creataceous volcanic rocks distributed in the southeastern part (Kyeongsang basin) of Korea peninsula are composed of basalt, basaltic andesite, andesite, dacite and rhyolite. The variation of major elements show that contents of MgO, CaO, $FeO^T$, $Al_2O_3$, $TiO_2$ and $P_2O_5$ decrease with increasing of $SiO_2$, but $K_2O$ contents are increased slightly, $Na_2O$ widely dispersed. We can show slightly inflection point and low frequency of dacites in range between 63-65 wt.% $SiO_2$, while continuous trend exit in variation diagram. Variation trends in Harker diagrams for the major, minor, trace and REEs suggest that the BAV (basaltic to andesitic volcanics) and DRV (dacitic to rhyolitic volcanics) are not related to a simple crystal fractionation process. In the regime of under 65 wt. % in silica content, fractionation of olivine and clinopyroxene is predominant, while that of plagioclase happens strongly higher than 65 wt.% (e.g., $SiO_2$, vs. Eu and Sr, MgO vs. $Al_2O_3$ and CaO). The latter means low-pressure fractional crystallization for DRV. On the discriminant diagram, DRV are located in more mature environment than BAV. The $(Ce/Sm)_N$ vs. CeN digram shows that these two classes cannot be related to crystal fractionation. If they had been produced by fractionation, although they plotted in a slightly elongate cluster along the same horizontal trend, DRV should lie to the right of these primitive compositions. These diagrams clearly rule out a simple fractionation throughout from BAV to DRV. BAV had been influenced greatly subductiong slab as shown by K/Yb vs. Ta/Yb. We suggest that BAV primitive magma generated higher degree of partial melting than DRV primitive magma. LILE (K, Ba, $Rb{\pm}Th$) enriched characteristics as shown in BAV are inherited from subducting slab fluids and/or higher degree of partial melting of mantle material. However, lower degree of partial melting of mantle relative to BA V and contamination at high-level magma reservoir caused LILE enrichment to DRV.

• 한국전기전자재료학회논문지
• /
• 제23권6호
• /
• pp.477-480
• /
• 2010

In this study, we fabricate 3 wt% $Li_2CO_3$ doped $(Ba,Sr)TiO_3$ thick films on the Ag/Pd bottom electrode printed $Al_2O_3$ substrates for the LTCCs (low temperature co-fired ceramics) applications. From the X-ray diffraction analysis, 3 wt% $Li_2CO_3$ doped BST thick films on the Ag/Pd printed $Al_2O_3$ substrates, which sintered at $900^{\circ}C$, showed perovskite structure without any pyro phase. The dielectric properties of 3 wt% $Li_2CO_3$ doped BST thick films are measured from 1 kHz to 1 MHz. To investigate the electrical properties of 3 wt% $Li_2CO_3$ doped BST thick films, we employ the impedance spectroscopy. The complex impedance of 3 wt% $Li_2CO_3$ doped BST thick films are measured from 20 Hz to 1 MHz at the various temperatures.

• 전자공학회논문지D
• /
• 제35D권5호
• /
• pp.33-39
• /
• 1998

The BST (Ba$_{1-x}$ Sr$_{x}$TiO$_{3}$)(50/50) thin film has been grown by RF magnetron reactive sputtering and its characteristics such as crystallization, surface roughness, and electrical properties have been investigated with varying the film thickness. The crystallization and surface roughness of BST thin film are investigated by using XRD and AFM, respectively The BST thin film anealed at 800.deg. C for 2 min has pure perovskite structure and good surface roughness of 16.1.angs.. We estimate that the thickness and dielectric constant of interface layer between BST film and electrode are 3nm and 18.9, respectively, by measuring the capacitance with various film thickness. As the film thickness increases form 80nm to 240nm, the dielectric constant at 10kHz increases from 199 to 265 and the leakage current density at 200kV/cm decreases from 0.682.mu.A/cm$^{2}$ to 0.181 .mu.A/cm$^{2}$. In the case of 240nm-thick BST thin film, the charge storage density and leakage current density at 5V are 50.5fC/.mu.m$^{2}$ and 0.182.mu.A/cm$^{2}$, respectively. The values indicate that the BST thin film is a very useful dielectric material for the DRAM capacitor.or.

• 한국정보통신설비학회:학술대회논문집
• /
• 한국정보통신설비학회 2003년도 하계학술대회
• /
• pp.286-288
• /
• 2003

In this paper, in order to obtain a large differential phase shift with a little change in applied voltage, a ferroelectric reflective load circuit has been designed on top of barium strontium titanate $(Ba,Sr)TiO_3$ [BST] thin film. The design of the ferroelectric reflection-type phase shifter is based on a reflection theory of terminating circuit, which has a reflection-type analogue phase shifter with two ports terminated in symmetric phase-controllable reflective networks. To achieve large amounts of phase shift in low bias-voltage range, the effects of change of capacitance and transmission line connected with two coupled ports of a 3-dB $90^{\circ}$ branch-line hybrid coupler have been investigated. A large phase shift with a small capacitance change in the parallel terminating circuit has been demonstrated in the paper.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2010년도 하계학술대회 논문집
• /
• pp.28-28
• /
• 2010

This study realized low-temperature crystallization process of the $Ba_{0.6}Sr_{0.4}TiO_3$ (BST) thin films without thermal damage of substrate using excimer laser annealing (ELA) and structural and electrical characteristics were investigated. The amorphous BST thin films were prepared on Pt/Ti/$SiO_2$/Si substrate by sol-gel method at $250^{\circ}C$. The ELA was carried out using KrF excimer laser which provided excitation wavelength of 248 nm. The beam homogenizing system was used in order to homogenize beam shape of Gaussian fit. The XRD and SEM were used to analyze structural characteristics and the microwave capacitance, dielectric loss and tunability of the BST films were measured by a symmetrical stripline resonator method with shorted end. Consequently, the crystallinity of BST thin films were improved after ELA process and RF tunable capacitor was demonstrated at low temperature below $300^{\circ}C$.

• Journal of Korean Vacuum Science & Technology
• /
• 제4권4호
• /
• pp.97-101
• /
• 2000

In this study, two kinds of barium strontium titanate (BST) samples were prepared. One is a conventional BST film that is sputtered in a mixture of argon and oxygen. The other is a nitrogen-incorporated BST film that is sputtered in a mixture of oxygen and intentionally added nitrogen instead of argon gas. The structural properties of both of the BST films had not changed significantly with the species of sputtering gas. However, the leakage current of BST films sputtered at ($N_2$+O$_2$) atmosphere was lower than those sputtered at (Ar +O$_2$) atmosphere: 1.9$\times$10$^{-8}$ A/cm$^2$ at 2V for the films prepared at (Ar +O$_2$) atmosphere and 8.6$\times$10$^{-9}$ A/cm$^2$ for the films at ($N_2$+O$_2$) atmosphere. From an XPS analysis, it has been found that nitrogen atoms are incorporated in BST films with a concentration of 1.92 at% and form a certain oxynitride phase. It is proposed that nitrogen atoms are able to fill the oxygen vacancies of BST films during sputtering process, and then the leakage current reduces due to a decrease in the vacancies. The BST films sputtered at ($N_2$+O$_2$) atmosphere have superior electrical properties to the films sputtered at (Ar +O$_2$), without any significant structural changes.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.1
• /
• pp.393-396
• /
• 2004

본 논문에서는 완충층용 MgO 박막을 P-type(100)Si 기판위에 작업가스 $Ar:O_2=80:20$, RF 파워 50W, 기판온도 $400^{\circ}C$, 10mtorr의 작업진공에서 $500{\AA}$ 증착하였다. 제작된 MgO/Si 기판위에 RF Magnetron sputtering법으로 작업가스 $Ar:O_2$의 비율을 90:10, 80:20, 70:30으로 변화하면서 $BST(Ba_{0.5}Sr_{0.5}TiO_3)$ 박막을 약 $2000{\AA}$ 증착하였다. XRD 측정결과 작업가스비의 변화에 관계없이(110)BST와 (111)BST 피크만이 관찰되었으며 작업가스 $Ar:O_2=80:20$에서 가장 양호한 결정성을 나타내었다. I-V 측정결과 인가전계 ${\pm}100kV/cm$에서 $10^{-7}A/cm^2$이하의 양호한 누설전류 특성을 보여주고 있으며 C-V 측정결과 작업가스 $Ar:O_2$의 비율 90:10, 80:20, 70:30에서의 비유전율은 각각 283, 305, 296으로서 작업가스비 80:20에서 제작된 박막의 특성이 가장 우수하였다. 작업가스비 80:20에서 제작된 박막의 SEM 측정결과 결정이 성장되었음을 확인할 수 있었고 그레인의 크기는 약 10nm였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.581-584
• /
• 2002

In this work, a CPW resonator was designed and fabricated to investigate the basic microwave properties, such as effective dielectric constant, of BST thin films. Their properties were used as basic data to simulate and design CPW tunable bandpass filter. We also report on gold/$Ba_{0.5}Sr_{0.5}TiO_3$(BST) ferroelectric thin film C-band tunable bandpass filters(BPFs) designed and fabricated on magnesium oxide substrates using CPW structure. The 2 pole filter was designed for a center frequency of 5.88 GHz with a bandwidth of 9 %. The BST based CPW filter offers a high sensitivity parameter as well as a low loss parameter. The tuning range for the bandpass filter with CPW structure was determined to be 170 MHz.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.167-167
• /
• 2008

The barium strontium calcium titanate powders were prepared by sol-gel method. Ferroelectric $(Ba_{0.54}Sr_{0.36}Ca_{0.1})TiO_3$(BSCT) thick films were fabricated by the screen-printing method on alumina substrate. And we investigated the structural and dielectric properties of BSCT thick films with the variation of sintering temperature. As a result of thermal analysis, BSCT polycrystalline perovskite phase was formed at around $660^{\circ}C$. The results of X-ray diffraction analysis were showed a cubic perovskite structure without presence of the second phase in all BSCT thick films. The average grain size and the thickness of the specimen sintered at $1450^{\circ}C$ were about 1.6 mm and 45 mm, respectively. The relative dielectric constant increased and the dielectric loss decreased with increasing the sintering temperature, the values of the BSCT thick films sintered at $1450^{\circ}C$ were 5641 and 0.4% at 1kHz, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 제5회 영호남 학술대회 논문집
• /
• pp.31-34
• /
• 2003

($Ba_{0.6-x}Sr_{0.4}Ca_x)TiO_3$ (BSCT) (x=0.10, 0.15, 0.20) powder, prepared by the sol-gel method, were mixed with organic vehicle and the BSCT thick films were fabricated by the screen-printing techniques on alumina substrates using the BSCT paste. The structural and the electrical properties were investigated for various composition ratio and sintering temperature. BSCT thick film thickness, obtained by four printings, was approximately 110 ~ 120 ${\mu}m$. The Curie temperature and dielectric constant at room temperature were decreased with increasing Ca content. The relative dielectric constant, dielectric loss and tunability of the BSCT(50/40/10) specimen, which was sintered at $1420^{\circ}C$ and measured at 1MHz, were about 910, 0.46% and 9.28% at 5kV/cm, respectively.