• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집
• /
• pp.50-53
• /
• 2002

YMnO$_3$ thin films were spun-coated on the Pt/Ti/SiO$_2$/Si substrates by sol-gel process using alkoxides, and then dried on hot plates from 300 to 450 $^{\circ}C$. The prepared YMnO$_3$ thin films were annealed at 850 $^{\circ}C$ in O$_2$ atmosphere for 1 h. The crystallization of YMnO$_3$ thin films were improved to preferred c-axis orientation and the dielectric characteristics were progressed by increasing the drying temperature. The range of dielectric constant of thin film dried at 450 $^{\circ}C$ is 12.9-22.3 and close to that of YMnO$_3$ single crystal. The ferroelecrtic property of YMnO$_3$ thin film was observed on the YMnO$_3$ films. The maximum remnant polarization (2Pr) of YMnO$_3$ thin films dried at 450 $^{\circ}C$ was about 2.91 ${\mu}$ C/cm2. It was suggested that the drying temperature affect to the initial stage of thin film growth of preferred c-axis orientation.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집
• /
• pp.213-216
• /
• 2001

Etching behaviors of ferroelectric YMn $O_3$ thin films were studied by an inductively coupled plasma (ICP). Etch characteristic on ferroelectric YMn $O_3$ thin film have been investigated in terms of etch rate, selectivity and etch profile. The maximum etch rate of YMn $O_3$ thin film is 300 $\AA$/min at Ar/C $l_2$ of 2/8, RF power of 800W, dc bias voltage of 200V, chamber pressure of 15mTorr and substrate temperature of 3$0^{\circ}C$. Addition of C $F_4$ gas decrease the etch rate of YMn $O_3$ thin film. From the results of XPS analysis, Y $F_{X}$ compunds were found on the surface of YMn $O_3$ thin film which is etched in Ar/C1/C $F_4$ plasma. The etch profile of YMn $O_3$ film is improved by addition of C $F_4$ gas into the Ar/C $l_2$ plasma. These results suggest that fluoride yttrium acts as a sidewall passivants which reduce the sticking coefficient of chlorine on YMn $O_3$.>.

• 한국전기전자재료학회논문지
• /
• 제15권4호
• /
• pp.314-318
• /
• 2002

The etching behaviors of the ferroelectric $YMnO_3$ thin films were studied by an inductively coupled plasma (ICP). The maximum etch rate of $YMnO_3$ thin film is 300 ${\AA}/min$ at Ar/$Cl_2$of 2/8, RF power of 800W, dc bias voltage of 200V, chamber pressure of 15mTorr and substrate temperature of $30^{\circ}C$. Addition of $CF_4$ gas decrease the etch rate of $YMnO_3$ thin film. From the results of XPS analysis, nonvolatile $YF_x$ compounds were found on the surface of $YMnO_3$ thin film which is etched in Ar/$Cl_2$/CF$_4$plasma. The etch profile of YMnO$_3$film is improved by addition of $CF_4$ gas into the Ar/$Cl_2$ plasma. These results suggest that YF$_{x}$ compound acts as a sidewall passivants which reduce the sticking coefficient of chlorine on $YMnO_3$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.213-216
• /
• 2001

Etching behaviors of ferroelectric $YMnO_3$ thin films were studied by an inductively coupled plasma (ICP). Etch characteristic on ferroelectric $YMnO_3$ thin film have been investigated in terms of etch rate, selectivity and etch profile. The maximum etch rate of $YMnO_3$ thin film is $300{\AA}/min$ at $Ar/Cl_2$ of 2/8, RF power of 800W, dc bias voltage of 200V, chamber pressure of 15mTorr and substrate temperature of $30^{\circ}C$. Addition of $CF_4$ gas decrease the etch rate of $YMnO_3$ thin film. From the results of XPS analysis, YFx compounds were found on the surface of $YMnO_3$ thin film which is etched in $Ar/Cl/CF_{4}$ plasma. The etch profile of $YMnO_3$ film is improved by addition of $CF_4$ gas into the $Ar/Cl_2$ plasma. These results suggest that fluoride yttrium acts as a sidewall passivants which reduce the sticking coefficient of chlorine on $YMnO_3$.

• 한국세라믹학회지
• /
• 제39권5호
• /
• pp.511-516
• /
• 2002

$Y(NO_3)_3{\cdot}5H_2O$ 과 $Mn(CH_3CO_2)_2{\cdot}4H_2O$를 출발물질로 하여 졸-겔(sol-gel)법으로 Si(100) 기판위에 육방정계의 $YMnO_3$ 박막을 제조하였다. $YMnO_3$ 박막의 열처리 온도변화, 가수분해시 가수의 양(Rw)과 촉매제의 첨가에 따른 결정 구조 및 전기적 특성을 조사하였다. $YMnO_3$ 박막의 결정화는 700${\circ}C$부터 시작되었고 완전한 결정화는 800${\circ}C$-1시간 열처리하여 이루어 졌으며, $YMnO_3$ 박막의 가수의 양 Rw=6일때 육방정계 $YMnO_3$상의 c-축 (0001) 우선 배향성을 나타내었고, Rw=1 과 Rw=12인 경우에는 Rw=6인 경우보다 c-축 배향성은 감소하였다. 산성이나 염기성 촉매제 첨가에 따라 $YMnO_3$ 박막의 결정성 및 우선 배향성은 영향을 받아 c-축 우선 배향성은 감소하고 사방정계의 $YMnO_3$ 상을 형성하였다. Rw=6일 때 $YMnO_3$박막은 0.2V인가 전압에서 $1.2{\times}10-8 A/cm^2$으로 우수한 누설 전류 밀도를 나타내었고 누설 전류 밀도는 인가 전압에 따라 크게 변하지 않았다.

• 한국세라믹학회지
• /
• 제40권4호
• /
• pp.398-400
• /
• 2003

The YMnO$_3$ thin films were prepared on platinized-silicon substrates by chemical solution deposition and annealed at 750 to 85$0^{\circ}C$ for 1 h under various oxygen pressures, from 2 mTorr to 760 Torr. Effects of annealing oxygen pressures on the crystallization behavior and electrical properties of YMnO$_3$ thin films were investigated. Crystallinity and c-axis preferred orientation of YMnO$_3$ thin film were improved by decreasing the oxygen pressure but were deteriorated at extremely low oxygen pressure, 2 mTorr. Leakage current density of the YMn03 thin film decreased as the oxygen pressure decreased. The film annealed at 80$0^{\circ}C$ under 2 Torr, which had the best crystallinity and the highest c-axis preferred orientation. showed the best-developed ferroelectric C-V hysteresis.

• 한국세라믹학회지
• /
• 제37권2호
• /
• pp.168-173
• /
• 2000

YMnO3 thin films were prepared on Pt/Ti/SiO2/Si substrate by chemical solution deposition method. The films were crystallized by heat-treatment at 85$0^{\circ}C$ for 1 hour. Effects of an annealing atmosphere(O2, Ar, vacuum) on the crystallization behavior and electridcal properties were investigated. YMnO3 thin films annealed under Ar atmosphere showed a superior crystallinity and a very strong c-aix preferred-orientation which was a polar axis. Leakage current density of the films decreased with lowering oxygen partial pressure of the annealing atmosphere. C-V and P-E ferroelectric hysteresis were observed only in the thin film heat-treated under Ar atmosphere.In order to prepare YMnO3 thin films having both low leakage current and ferroelectricity, the annealing atmsphere should be kept under a proper oxygen partial pressure which was about 1 Pa in this work. Leakage current density at 1 volt, dielectric constant($\varepsilon$r), remanent polarization(Pr), and coercive field(Ec) were 1.7$\times$10-8 A/$\textrm{cm}^2$, 25, 1.08$\mu$C/$\textrm{cm}^2$, and 100 kV/cm, respectively.

• 한국세라믹학회지
• /
• 제37권7호
• /
• pp.665-672
• /
• 2000

The ferroelectric YMnO3 thin films were prepared by MOD(metal-organic decomposition) method with Y- and Mn-acetylacetonate as starting materials. Thin films were grown on various substrates by spin-coating technique. The crystalline phases of the thin films were identified by X-ray diffractometer as a function of heat-treatment temperature, pH of coating solution and substrate. In addition, the effect of Mn/Y molar ratio(0.8~1.2) on the formation of hexagonal-YMnO3 phase was investigated. In forming highly c-axisoriented hexagonal-YMnO3 single phase, the Pt coated Si substrate was more effective than the bare Si substrate, and the optimum heat-treatment condition was at 82$0^{\circ}C$ for 30 min. Higher Mn/Y molar ratio within 0.8~1.2 and pH of YMnO3 precursor solution within 0.5~2.5 favored formation of ferroelectric hexagonal phase rather than orthorhombic phase. Leakage current density of the hexagonal-YMnO3 thin film formed on Pt(111)/TiO2/SiO2/Si substrate was low enough as 0.4~4.0$\times$10-8(A/$\textrm{cm}^2$) at 5 V and its remanent polarization(Pr), calculated from the P-E hysteresis loop, was 3 nC/$\textrm{cm}^2$.

• 한국전기전자재료학회논문지
• /
• 제16권6호
• /
• pp.449-453
• /
• 2003

Ferroelectric YMnO$_3$ thin films were etched with Ar/Cl$_2$ and CF$_4$/Cl$_2$ inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$ thin film was 300 $\AA$/min at a Ar/Cl$_2$ gas mixing ratio of 2/8, a RF power of 800 W, a DE bias of 200 V, a chamber pressure of 15 mTorr, and a substrate temperature of 30 $^{\circ}C$. From the X-ray photoelectron spectroscopy (XPS) analysis, yttrium etched by chemical reactions with Cl radicals assisted by Ar ion bombardments in Ar/Cl$_2$ plasma. In CF$_4$/Cl$_2$ plasma, yttrium are remained on the etched surface of YMnO$_3$ and formed of nonvolatile YF$_{x}$ compounds manganese etched effectively by chemical reactions with Cl and F radicals. From the X-ray diffraction (XRD) analysis, the (0004) diffraction peak intensity of the YMnO$_3$ thin film etched in Ar/Cl$_2$ plasma shows lower value than that in CF$_4$/Cl$_2$ plasma. It indicates that the crystallinty of YMnO$_3$ thin film is more easily damaged by the Ar ion bombardment than the changes of stoichiometry due to nonvolatile etch by-products.s.

• 한국전기전자재료학회논문지
• /
• 제14권2호
• /
• pp.93-98
• /
• 2001

YMnO$_3$ films are excellent gate dielectric materials of ferroelectric random access memories (FRAMs) with MFSFET (metal -ferroelectric-semiconductor field effect transistor) structure because YMnO$_3$ films can be deposited directly on Si substrate and have a relatively low permittivity. Although the patterning of YMnO$_3$ thin films is the requisite for the fabrication of FRAMs, the etch mechanism of YMnO$_3$ thin films has not been reported. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$ film is 285$\AA$/min under Cl$_2$/(Cl$_2$+Ar) of 1.0, RF power of 600 W, dc-bias voltage of -200V, chamber pressure of 15 mTorr and substrate temperature of $25^{\circ}C$. The selectivities of YMnO$_3$ over CeO$_2$ and $Y_2$O$_3$ are 2.85, 1.72, respectively. The selectivities of YMnO$_3$ over PR and Pt are quite low. Chemical reaction in surface of the etched YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy (XPS) surface of the selected YMnO$_3$ thin films was investigated with X-ray photoelectron spectroscopy(XPS) and secondary ion mass spectrometry (SIMS). The etch profile was also investigated by scaning electron microscopy(SEM)