• Journal of the Korean Vacuum Society
• /
• v.4 no.2
• /
• pp.172-176
• /
• 1995

$YBa_2Cu_3O_{7-y}$ thin films have been prepared on MgO(100)substrates placed on-axis to the target by dc magnetron sputtering in a variety of oxygen/argon gas pressures with different substrate-target distances. We found that films with the c-axis perpendicular to the substrate deposited in an optimally high gas pressure with on-axis substrate-target configuration do. Increasing the substrate-target distance was found to be effetive in reducing the resputtering effect and enhancing superconductivity of films, but not so much $\alpha$-and c-axis growth of YMCO films on MgO substrates. Dependences of the Tc, the rationj of resistances at 300K and 100K, and the X-ray diffraction pattern on the gas pressure and the substrate target distance are described.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1995.05a
• /
• pp.26-30
• /
• 1995

We describe the preparation and characterization of epitaxial thin films made with high temperature superconductor, $YBa_2Cu_3O_{7-\delta}$. The influence of processing parameters for YBCO thin films on MgO substrates in-situ grown by the pulsed laser deposition, including parameters of a laser beam energy, oxygen pressure, substrate temperature, target-substrate dis-tance is discussed. The characteristics of YBCO thin films were analyzed by using XRD, R-T measurement, AFM, crosssectional TEM, and RBS. For examples of microwave device applications, The fabrication and characterization of the microstrip lowpass filter and bandpass filter are also presented.

• Bulletin of the Korean Chemical Society
• /
• v.15 no.7
• /
• pp.545-549
• /
• 1994

Using the extended Hackel molecular orbital method in connection with the tight binding model, we have studied electronic structure and related properties of the charged cluster models relating to superconducting $YBa_{2}Cu_{3}O_{7-x}$, crystals in which O-atoms in regular sites were selectively replaced with Se atoms. In analogy to the isomorphism problem with molecules, we discuss all possible combinations of Se-substitutions in O-sites with one, two, and four Se atoms. The calculations are carried out within charged cluster models for analogues of YBa-copper oxide. Our results suggest that the electronic structure of the symmetrically Se-substituted or Se-added compound is closer to that of the YBCO superconducting compound than that obtained from the unsymmetrical substitution. This applies in particular if O is replaced with Se around the Cu(1) site. Symmetrical substitutions in the $CuO_2$ layers give rise to large variations in the electronic structure of $YBa_{2}Cu_{3}O_{7}$. This is consistent with the fact that superconductivity is very sensitive to the electronic population of the $CuO_2$ layers.

• Journal of the Korean Chemical Society
• /
• v.34 no.6
• /
• pp.555-560
• /
• 1990

High temperature superconducting films of $YBa_2Cu_3O_{7-x}$ were fabricated on the (100) single crystal faces of YSZ (yttria stabilized zirconia) and SrTi$O_3$ by aerosol spray using ultrasonic atomization. The superconducting phase was formed by a three-step process: (a) spraying of a stoichiometric solution of nitrates of yttrium, barium, and copper on heated substrates kept at 250$^{\circ}C$, (b) preheating of the sprayed films in air at 550$^{\circ}C$, and (e) sintering of the films in flowing oxygen at 950$^{\circ}C$, followed by furnace cooling. Resistances of the films were measured by the dc four-probe method and superconductivity was confirmed above the liquid nitrogen temperature.

• Journal of the Korean Ceramic Society
• /
• v.25 no.2
• /
• pp.154-160
• /
• 1988

Almost single phase of Y1Ba2Cu3Ox, which exhibits the onset of superconducting transition at 90K, has been prepared via a conventional ceramic processing route followed by an anneal for a period of 10 hours at 45$0^{\circ}C$ in an atmosphere of 100% O2. The mean value for the oxygen content has been determined as x=6.85$\pm$0.02 by an iodometric titration technique. X-ray photoemission spectra are found to be consistent with a mixture of the d8(Cu3+) and d9(Cu2+) as the ground state and reveals that the local concentration of Cu3+ decreases with depth from the surface where x corresponds to 7.0. This is explained as being associated with the intercalation of oxygen during cooling from the annealing temperature.

• Proceedings of the KIEE Conference
• /
• 1989.07a
• /
• pp.299-301
• /
• 1989

This study presents a method of preparing $YBa_2Cu_3O_{7-x}$ ceramic and chlorine doping in it for the purpose of Jc enhancement us ins sol-gel process.Tetramethylammonium-hydroxide and pottasium carbonate solution were added to the aqueous solution of Yttrium nitrate, Barium chloride and Copper nitrate for pH control as well as forming hydroxy-carbonate precipitation. Instead of Barium nitrate, Barium chloride was used for doping chloride impurities in the specimen. The resulted materal showed good high Tc-superconductivity after calcination. Tc and Jc value are 92 K and 120.8 $A/cm^2$ respectively.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.37-45
• /
• 1991

The critical current density, electrical conductivity, critical magnetic field, Meissner effect, apparent density, and microstructure of YBa2Cu3O7-x ceramic superconductor prepared by polymeric precursor, while varing calcining and sintering conditions, were investigated. The best superconducting properties could be obtained from the body sintered at 93$0^{\circ}C$ for 10h after calcining at 90$0^{\circ}C$ for 10h, which gave 383A/$\textrm{cm}^2$ of critical current density(Jc), 96K of onset temperature(Tonset), 94. 8K of zero temperature (Tzero) 225 Oe of critical magnetic field (Hc1), 72.8% of superconducting volume fraction measured by Meissner effect and 6.28g/㎤ of apparent density.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.85-88
• /
• 1999

We fabricated resistive superconducting fault current lmiters based on YBa$_2$Cu$_3$O$_{7}$ thin films and investigated their quench propagation characteristics. The YBa$_2$Cu$_3$O$_{7}$ film was coated with a gold layer and patterned into 1 mm wide meander lines by photolithography. The limiters were tested with simulated fault currents of various fault angles and amplitudes. The quench propagation characteristics were explained based on the heat transfer within the film as well as between the film and the surrounding liquid nitrogen. The quench completion time strongly depended on the potential fault current. It was 1 msec at the peak fault current of 76 A/peak/ and corresponding quench propagation speed was 43 m/sec (film cross section: 4 x 10$^{-6}$ $\textrm{cm}^2$).

• Progress in Superconductivity and Cryogenics
• /
• v.1 no.1
• /
• pp.1-6
• /
• 1999

The microstructures of top seed mult processde $\textrm{YBa}_2\textrm{Cu}_3\textrm{O}_7$.$\delta$ single crystal were studied. Although shape of the seed was not faceted. the growth shape of Y123 single crystal was faceted. It was observed that Y211 phases were trapped in specific spaces of the faceted region. From the microstructural investigation. it was suggested that the segregation of Y211 is due to the difference of growth rates in crystal direction. When a single crystal was grown by the single seed with stepped multi surfaces. a microstrue was grown from multi-seed. The microstructure show the possibility of multi-seed growth. Corn kernel like structure without Y211 phase was observed and seemed to be formed by the diffusion reaction between Y211 phase in crystal and liquid wetted on the crystal. the diagonal line on Y123 crystal was observed that it was formed by the corn kernel like structure.

• Progress in Superconductivity and Cryogenics
• /
• v.10 no.1
• /
• pp.1-5
• /
• 2008

The effect of $BaCeO_3$ doping on the critical current density of YBCO film by TFA-MOD method was studied. $BaCeO_3$ doping was made by two method; one is direct addition of $BaCeO_3$ nano-sized powder prepared by citrate process followed by grinding with planetary ball mill for 10 hours. Another is addition of Ba-Ce precursor solution prepared with Ba-acetate and Ce acetate dissolved in TFA to the YBCO-TFA precursor solution. The film was made by standard dip coating and heat treatment process with conversion temperature of $790^{\circ}C$ in 1000 ppm oxygen containing moisturized Ar gas atmosphere. The direct addition of $BaCeO_3$ powder resulted in YBCO film with good epitaxial growth and no evidence of second phase formation. The addition through precursor solution resulted in the increase of critical current density upto 30 at% doping and uniform dispersion of $BaCeO_3$ fine inclusion was confirmed by SEM-EDX.