• Journal of the Korean Ceramic Society
• /
• v.36 no.5
• /
• pp.478-482
• /
• 1999

SrTiO3 :Al, Pr phosphor as an oxide compound phosphor is expect to be applied for a field emission display(FED). In this phosphor the excitation spectrum shows a different tendency according to an addition Al3+ and Pr3+ In this excitation spectrum the main peak at 359 nm represent excitation level of Pr3+(1S0longrightarrow1D2 transition) and the absorption characteristic according to Ti/Sr molar ratio is influenced by the structure symmetry. The emission spectrum exhibits the red luminescence with the radiative decay of the 1D2 states(1D2 longrightarrow3H4 transition) The concentration quenching phenomena at 1D2 state shows up as Al3+ and Pr3+ ion concentration increases.

• Journal of the Korean Ceramic Society
• /
• v.47 no.6
• /
• pp.498-502
• /
• 2010

Aluminium titanate($Al_2TiO_5$) has extremely anisotropic thermal expansion properties in single crystals, and polycrystalline material spontaneously microcracks in the cooling step after sintering process. These fine intergranular cracks limit the strength of the material, but provide an effective mechanism for absorbing strain energy during thermal shock and preventing catastrophic crack propagation. Furthermore, since machinable BN-ceramics used as an insulating substrate in current micro-electronic industry are very expensive, the development of new low-cost machinable substrate ceramics are consistently required. Therefore, cheap $Al_2TiO_5$-machinable ceramics was studied for the replacement of BN ceramics. $Al_2O_3-Al_2TiO_5$ ceramic composite was fabricated via in-situ reaction sintering. $Al_2O_3$ and $TiO_2$ powders were mixed with various mol-ratio and sintered at 1400 to $1600^{\circ}C$ for 1 h. Density, hardness and strength of sintered ceramics were systematically measured. Phase analysis and microstructures were observed by XRD and SEM, respectively. Machinability of each specimens was tested by micro-hole machining. The results of research showed that the $Al_2TiO_5$-composites could be used for low-cost machinable ceramics.

• Korean Journal of Materials Research
• /
• v.14 no.3
• /
• pp.163-167
• /
• 2004

TiAl(La)N thin films were oxidized in vacuum of about 7 Pa to reduce the oxidation of WC-Co as a substrate. The oxidation rate constants of the thin films were quantified by an assumption of parabolic oxidation. Increasing AI content significantly decreased the parabolic oxidation rate constant. A simultaneous addition of AI and La was more effective to reduce the oxidation rate. The parabolic oxidation rate constant of $Ti_{0.66}$ $Al_{0.32}$ $La_{ 0.02}$N thin film at 1273 K showed about ten times lower than that of TiN. The addition of a small amount of La with Al induced the preferential formation of dense $\alpha$ $-Al_2$$O_3$ film in oxide film, leading to the abrupt reduction of oxidation rate.

• Journal of the Korean institute of surface engineering
• /
• v.26 no.5
• /
• pp.235-244
• /
• 1993

The oxidation behavior of a two-phase(Ti3Al+TiAl) intermetallic compound, Ti-33.8wt%Al, has been in-vestigated in air at 800, 900 and $^1000{\circ}C$. Though the isothermal oxidation behavior followed a parabolic law up to 100$0^{\circ}C$ indicating that protective oxide scales were formed, the cyclic oxidation behavior followed a lin-ear law in the entire temperature range tested because flaky or stratified scales were usually spalled from the surface during cooling. During oxidation at 80$0^{\circ}C$, the alloy showed excellent oxidation resistance because continuous protective Al2O3 films were formed on the outermost surface of the alloy. However, above $900^{\circ}C$, the oxidation resistance of the alloy was decreased gradually because relatively non-protective TiO2 scales as well as some of Al2O3 scales were formed on the outer oxide scale. The oxidation mechanism of the alloy at different temperature was proposed.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.2
• /
• pp.49-55
• /
• 2018

A T-shape structure was manufactured by the superplastic forming and diffusion bonding process using two Ti-3Al-2.5V alloy tubes. A Ti-3Al-2.5V tube was prepared for the hydroforming in the superplastic condition until it reaches a surface area such as a roof welded in the hole of another Ti-3Al-2.5V tube. Afterward, the superplastic forming process and the diffusion bonding process were carried out simultaneously until the appropriate bonding along the interface area of two Ti-3Al-2.5V tubes was obtained. The bonding qualities were different at each location of the entire interface according to the applied process conditions such as strain, pressure, temperature, holding time, geometries, etc. The microstructures of bonding interface have been observed to understand the characteristics of the applied processes in this study.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2001.11a
• /
• pp.133-133
• /
• 2001

• Journal of Powder Materials
• /
• v.28 no.1
• /
• pp.31-37
• /
• 2021

This study explores reducing the oxygen content of a commercial Ti-48Al-2Cr-2Nb powder to less than 400 ppm by deoxidation in the solid state (DOSS) using Ca vapor, and investigates the effect of Ca vapor on the surface chemical state. As the deoxidation temperature increases, the oxygen concentration of the Ti-48Al-2Cr-2Nb powder decreases, achieving a low value of 745 ppm at 1100℃. When the deoxidation time is increased to 2 h, the oxygen concentration decreases to 320ppm at 1100℃, and the oxygen reduction rate is approximately 78% compared to that of the raw material. The deoxidized Ti-48Al-2Cr-2nb powder maintains a spherical shape, but the surface shape changes slightly owing to the reaction of Ca and Al. The oxidation state of Ti and Al on the surface of the Ti-48Al-2Cr-2Nb powder corresponds to a mixture of TiO2 and Al2O3. As a result, the peaks of metallic Ti and Ti suboxide intensify as TiO2 and Al2O3 in the surface oxide layer are reduced by Ca vapor deposition.

• Journal of the Korean Society for Heat Treatment
• /
• v.8 no.1
• /
• pp.84-88
• /
• 1995

Various heat-treatments were conducted to Ti-48.1at%Al and Ti-48.3at%Al-1.2at%Mn alloys casted by plasma arc melting system. Mechanical properties, microstructure and high temperature oxidizing behaviors of as-casted and heat-treatment alloys were investigated. Ti-48.1Al and Ti-48.3Al-1.2Mn alloys were decreased in strength according to increased of heattreatment temperature. Oxidizing weight gain of Ti-48.1Al alloy which conducted at $1273^{\circ}K$ was linearly increased. In case of adding Mn to alloy, there was no rapid increase of oxidizing weight gain during early time.

• Journal of the Korean institute of surface engineering
• /
• v.31 no.5
• /
• pp.278-285
• /
• 1998

Alloys of Ti-15Mo-5Zr-3Al(wt%) were oxidized in air between 700 and $900^{\circ}C$. It was found that the oxidation resistance is much better than that of either commercially available pure Ti-6Al-4V(wt%) alloys. The oxide scales were primarily composed of thick Ti-ox-ides which were formed by the inward diffusion of oxygen from the atmosphere. At higher temperatures a thin $\alpha$-$Al_2O_3$ layer was formed on Ti-oxides owing to the outward diffusion of Al from the base alloys. Molybdenum, the noblest metal among the alloy components, was predominantly present behind the oxide-substrate interface. Zirconium, an oxygen active metal, was present at both the oxide layer and the substrate.

• Journal of the Korean Ceramic Society
• /
• v.34 no.4
• /
• pp.368-372
• /
• 1997

The microwave dielectric properties of (1-x)La2/3TiO3-xLaAlO3 system in which LaAlO3 having $\varepsilon$r$\geq$90 and positive $\tau$f was investigated. The crystal system of (1-x)La2/3TiO3-xLaAlO3 was pseudo-cubic in the range of 0.1$\leq$x$\leq$0.07. Its lattice constant increased with increasing x in spite that the amount of LaAlO3 containing of smaller Al(0.57 $\AA$) ion than Ti(0.64 $\AA$) increased. As the amount of LaAlO3 increased from x=0.1 to 0.9, the relative dielectric constant ($\varepsilon$r) decreased from 50 to 23 and the temperature coefficient of resonant frequency($\tau$f) decreased from +84 to -50. On the other hand, the value of Q.f0 reached a maximum (148,000 at 7 GHz) at x=0.7, where a rapid increase in the peak intensity of XRD occured, and further increased after prolonged sintering. The microwave dielectric properties of $\varepsilon$r=37, Q.f0=47,000 (at 7 GHz), and $\tau$f=-2 ppm/$^{\circ}C$ were obtained near 0.6La2/3TiO3-0.4LaAlO3 (x=0.4) composition.