• Journal of the Korean Ceramic Society
• /
• v.31 no.11
• /
• pp.1378-1386
• /
• 1994

The characteristic of calcined BaTiO3 powder and sintered PTC ceramics was investigated varing with calcination temperature and time of BaTiO(C2O4)2.4H2O synthesized from BaCl2.2H2O, TiCl4, oxalic acid and ethanol by oxalic acid method. When the particle size was less than 0.1 ${\mu}{\textrm}{m}$ by controlling calcination temperature and time, the resistance at room temperature was measured very high (above M{{{{ OMEGA }}). However, when the calcined particle sizes ranged from 0.2 to 0.3 ${\mu}{\textrm}{m}$, the resistance was 100 {{{{ OMEGA }} (After sintering, the grain size was 10~30 ${\mu}{\textrm}{m}$ homogeneously with the addition of dopant in sintering, the resistivity, resistance, $\alpha$ value and jumped to were 110{{{{ OMEGA }}.cm, 24$^{\circ}C$/% and 106{{{{ OMEGA }}, respectively.

• Bulletin of the Korean Chemical Society
• /
• v.22 no.11
• /
• pp.1183-1191
• /
• 2001

The metallorganic chemical vapor deposition (MOCVD) method has been used to prepare TiO2 thin films for the degradation of hazardous organic compounds, such as 2-chlorophenol (2-CP). The effect of supporting materials and metal doping on the photocatalytic activity of TiO2 thin films also has been studied. TiO2 thin films were coated onto various supporting materials, including stainless steel cloth(SS), quartz glass tube (QGT), and silica gel (SG). Transition metals, such as Pd(II), Pt(IV), Nd(III) and Fe(III), were doped onto TiO2 thin film. The results indicate that Nd(Ⅲ) doping improves the photodegradation of 2-CP. Among all supporting materials studied, SS(37 ${\mu}m)$ appears to be the best support. An optimal amount of doping material at 1.0 percent (w/w) of TiO2-substrate thin film gives the best photodegration of 2-CP.

• Proceedings of the Optical Society of Korea Conference
• /
• 2009.02a
• /
• pp.227-228
• /
• 2009

• Applied Chemistry for Engineering
• /
• v.34 no.1
• /
• pp.36-44
• /
• 2023

Core-shell TiO₂/Ag nanoparticles were synthesized by a modified sol-gel process and the reverse micelle method using acetoxime as a reducing agent in water/dodecylbenzenesulfonic acid (DDBA)/cyclohexane. The structure, shape, and size of the TiO₂/Ag nanoparticles were investigated using X-ray diffraction (XRD), UV-visible spectroscopy, scanning electron microscope (SEM), transmission electron microscope (TEM), and thermogravimetric analysis (TGA). The size of TiO₂/Ag nanoparticles could be controlled by changing the [water]/[DDBA] molar ratio values. The size and the polydispersity of TiO₂/Ag nanoparticles increased when the [water]/[DDBA] molar ratio rose. The resultant Ag nanoparticles over the anatase crystal TiO₂ nanoparticles exhibited a strong surface plasmon resonance (SPR) peak at about 430 nm. The SPR peak shifted to the red side with the increase in nanoparticle size. Conductive pastes with 70 wt% TiO₂/Ag nanoparticles were prepared, and the pastes were coated on the PET films using a screen-printing method. The printed paste films of the TiO₂/Ag nanoparticles demonstrated greater surface resistance than conventional Ag paste in the range of 405~630 μΩ/sq.

• Proceedings of the KIEE Conference
• /
• 2003.07c
• /
• pp.1586-1588
• /
• 2003

The Pb$(Zr{_{0.7}}Ti_{0.3})O_3$[PZT(70/30)] thin films were fabricated on Pt/$TiO_2/SiO_2$/Si substrate by RF sputtering method. The effects of Ar/$O_2$ ratio on the structural and dielectric properties of PZT thin fillms were investigated. In the case of the PZT thin films deposited with condition of 50/50$(Ar/O_2) $ ratio, the grain of the PZT thin films were fine and uniform. Increasing of $O_2$ ratio, the dielectric constant was increased. In this case the dielectirc constant and dielectric loss of PZT thin fims were about 627 and 0.010, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.682-685
• /
• 2002

The $0.96MgTiO_3-0.04SrTiO_3$ ceramics with $B_2O_3$(10wt%) were prepared by the conventional mixed oxide method. The structural properties were investigated with sintering temperature by XRD. According to the X-ray diffraction pattern of the $0.96MgTiO_3-0.04SrTiO_3$ ceramics with $B_2O_3$(10wt%), the ilmenite $MgTiO_3$ and perovskite $SrTiO_3$ structures were coexisted and secondary phase of the $MgTi_2O_5$ were appeared. In the case of $0.96MgTiO_3-0.04SrTiO_3+B_2O_3$(10wt%) ceramics sintered $1225^{\circ}C$, dielectric constant, quality factor and temperature coefficient of resonant frequency were 19.82, 62,735GHz, $-2.983ppm/^{\circ}C$, respectively.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.42 no.2
• /
• pp.163-170
• /
• 2022

The present study investigates NO_x-removal and sound-absorption performances of photocatalytic porous concrete prepared by various TiO₂ application methods. Photocatalytic porous concrete samples were prepared by one of the following: 1) mechanically mixing TiO₂ during casting; 2) mixing bottom ash aggregate pretreated with TiO₂ during casting; and 3) spraying TiO₂ solution to the normally fabricated porous concrete. The test results indicated that the mechanical mixing of TiO₂ decreased the compressive strength as the added TiO₂ content increased. The use of pretreated bottom ash aggregate reduced the porosity, yet the compressive strength of the concrete was similar to that measured from the former method. Porous concrete samples sprayed with the TiO₂ solution exhibited enhanced compressive strength, while the porosity was analogous to those measured from other methods. The NO_x-removal performance was the highest in the samples sprayed with the TiO₂ solution, followed by the samples using pretreated bottom ash aggregate and mechanically mixed TiO₂. The samples with mechanically mixed TiO₂ identified a relationship between soundabsorption performance and porosity. However, no particular tendency was observable in the samples with other TiO₂ application methods.

• Korean Journal of Optics and Photonics
• /
• v.17 no.3
• /
• pp.296-302
• /
• 2006

ILow-temperature $TiO_2$ sol was synthesized with various catalyst contents by using a sol-gel method. $TiO_2$ thin films were produced by a dip-coating method and their optical, structural and photocatalytic properties were examined. Transmittance of $TiO_2$ thin films with 0.10 mol, 0.25 mol, 0.50 mol and 0.75 mol catalyst content showed high transmittance in the visible range. XRD results showed the anatase-to-rutile phase transition was accelerated with increasing catalyst content and the crystallinity size of the $TiO_2$ thin films increased with increasing catalyst content. SEM results indicated that the particle size of the $TiO_2$ thin films was the smallest with catalyst content of 0.25 mol. Photocatalytic results showed that methylene blue was completely decomposed in the presence of anatase film prepared with 0.10 mol, 0.25 mol and 0.50 mol catalyst content.

• Journal of the Korean Ceramic Society
• /
• v.44 no.3 s.298
• /
• pp.137-141
• /
• 2007

$La_{2}O_{3}-TiO_{2}-SiO_{2}$ glass, a type that could not obtained so far by the conventional melting method, was prepared successfully using a sol gel process. Glass derived with the sol-gel process has compositions of $5La_{2}O_{3}-5TiO_{2}-90SiO_{2},\;5La_{2}O_{3}-10TiO_{2}-85SiO_{2}$, and $5La_{2}O_{3}-20TiO_{2}75SiO_{2}$. The UV-visible absorption edge of all glass compositions was below 400 nm. The measured density is in the range of 2.55-2.89, and was nearly identical to the calculated density and the refractive index of the glasses derived from the sol-gel ranges from 1.545 to 1.645. The molar additive coefficient of $TiO_{2}$ measured in this ternary system is lower than the calculated value, while the value of $La_{2}O_{3}$ is higher.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.37-42
• /
• 2000

The comparative study of texture of Al/Ti thin films deposited on low-dielectric polymer and $SiO_2$substrates has been investigated. Fifty-nm-thick Ti films and 500-nm-thick Al-1%Si-0.5%Cu (wt%) films were deposited sequentially onto low-k polymers and $SiO_2$by using a DC magnetron sputtering system. The texture of Al thin film was determined using X-ray diffraction (XRD) theta-2theta ($\theta$-2$\theta$) and rocking curve and the microstructure of Al/Ti films on low-k polymer and $SiO_2$substrates was characterized by cross-sectional transmission electron microscopy (TEM). Both the $\theta$-2$\theta$ method and rocking curve measurement suggest that Al/Ti thin films deposited on $SiO_2$have stronger texture than those deposited on low-k polymer. The texture of Al thin films strongly depended on that of Ti films. Cross-sectional TEM revealed that grains of Ti films on $SiO_2$substrates had grown perpendicular to the substrate, while the grains of Ti alms on SiLK substrates were formed randomly. The lower degree of (111) texture of Al thin films on low-k polymer was due to Ti underlayer.