• 한국세라믹학회지
• /
• 제24권2호
• /
• pp.111-116
• /
• 1987

By the method of direct wet process which has been developed in our laboratory, the high purity BaTiO3 powders could be synthesized from the room temperature to 90$^{\circ}C$ according to particle sizes. For to detect the PTCR effects, Sb2O3 wasdoped in the BaTiO3 powders which had been prepared on above method. As the results, the PTCR effects were in creased with the decreasing grain size of BaTiO3 powders.

• 한국지반환경공학회 논문집
• /
• 제20권11호
• /
• pp.5-10
• /
• 2019

본 연구에서는 장파장에서 감응하는 광촉매를 개발하기 위하여 상용화된 $TiO_2$에 Ag를 도핑하여 제조하였으며 광촉매 효율을 향상시키기 위하여 귀금속의 분산을 증대시키는 마이크로에멀젼 방법을 이용하였다. 제조된 $Ag/TiO_2$의 물리적 특성은 SEM(Scanning Electron Microscopy), FE-TEM(Field Emission Transmission Electron Microscopy), DRS(Diffuse Reflectance Spectroscopy)를 통해 분석하였다. RO 16(Reactive Orange 16)에 대한 광촉매의 제거 효율은 25ppm의 RO 16을 대상으로 UV-A 영역(365nm)에서 수행하였다. Ag의 도핑방법에 의한 광촉매 효율을 비교하기 위해 볼밀링 및 딥코팅 방법으로 제조하여 광촉매 효율을 분석하였으며 광촉매 효율에 대한 Ag 및 계면활성제 함량에 대한 최적화를 진행하였다. 도핑방법에 따른 RO 16 제거효율 분석 결과, 마이크로에멀젼 방법으로 제조한 $Ag/TiO_2$의 RO 16 제거효율이 가장 높았으며 Ag 함량 2wt%, 계면활성제 0.5g에서 가장 높은 제거효율을 보였다.

• 한국분말재료학회지
• /
• 제12권4호
• /
• pp.249-254
• /
• 2005

Titanium dioxide was prepared by Polymer Complex Solution Method(PCSM) according to the mole ratio of Titanium (IV) isopropoxide(TTIP)/solvent and polymer(Poly Ethylene Glycol). Polymer electrolytes were usually made by dispersing preproduced ceramic nanoparticles in a polymer matrix. Using this method, pure and nano-sized $TiO_2$ powder was synthesized through a simple procedure and polymer entrapment route. At the optimum amount of the polymer, the titanium ions are dispersed in solution and a homogeneous polymeric network is formed. The maximum intensity of anatase phase of $TiO_2$ was achieved by calcining at $500^{\circ}C$ for 2h. The synthesized $TiO_2$ powders were nano-sized and the average size was about 50nm. Anatase/Rutile ratio of the synthesized $TiO_2$ was 70%/30%.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 Techno-Fair 및 합동춘계학술대회 논문집 전기물성,응용부문
• /
• pp.161-163
• /
• 2008

$TiO_2-V_2O_5$ sol was fabricated using sol-gel method and $TiO_2-V_2O_5$, thin films were fabricated using dip-coating method. $V_2O_5$ sol was added 0.01mole, 0.03mole, 0.05mole into $TiO_2$ sol. Capacitance of thin films decreased with increasing $V_2O_5$ additive and it increased largest at 0.01mole. Because adsorption time and desorption time of thin films was about 2 minutes 40 seconds and about 3 minutes 40 seconds respectively, adsorption time was faster about 1 minutes than desorption time.

• Korean Chemical Engineering Research
• /
• 제51권2호
• /
• pp.195-202
• /
• 2013

본 연구에서는 Titanium(IV) sulfate($Ti(SO_4)_2$)와 암모니아수로부터 수열합성법을 이용하여 비교적 낮은 합성온도($80{\sim}100^{\circ}C$)와 상압에서 소성과정을 거치지 않고 $TiO_2$ 분말을 제조하였고, $TiO_2$ 제조 시 반응온도, 반응물의 초기농도, 혼합용액의 pH와 같은 반응조건에 따른 $TiO_2$ 입자의 결정구조와 입자분포, 형상 등과 같은 물리적 특성을 고찰하였다. 제조한 시료는 UV 조사 하에 Brilliant Blue FCF(BB-FCF)의 광분해 실험을 실시하여 광분해 성능과 DRS 분석을 통해 광촉매 활성을 비교하였다. 제조한 시료의 물성은 XRD, SEM, PL, 입도분포 측정을 통하여 확인하였다. Titanium(IV) sulfate($Ti(SO_4)_2$)의 초기농도가 증가할수록 $TiO_2$의 평균 입자크기와 결정화도는 증가하였고 광촉매 활성은 감소하였다. 혼합용액의 pH가 높을수록 평균 입자크기는 감소하였고 광촉매 활성은 증가하였다. 반응온도가 높을수록 결정화도와 광촉매 활성은 증가하였다. 이상의 결과들로부터 $Ti(SO_4)_2$와 암모니아수를 이용한 비교적 낮은 합성온도와 상압에서의 수열합성법으로도 순수한 anatase 결정구조의 $TiO_2$가 제조됨을 확인할 수 있었다.

• 한국대기환경학회지
• /
• 제8권1호
• /
• pp.58-67
• /
• 1992

For removing $NO_x$ and $SO_x$ from the flue gases emitted from stationary sources, $V_2O_5-MoO_3/TiO_2$ catalysts were prepared by the conventional impregnation method (aqueous solution) and a sort of surface fixation method(nonaqueous solution) as reported excellent reproducibility catalysts. And these catalysts observed their catalytic activities as well as their surface properties. V-Mo-O oxide, prepared from nonaqueous solution of $VOCl_3$ and $Mo(CO)_6$ and aqeous solution method, was supported as amorphous state by XRD and SEM measurements. The infrared spectra of fresh and used catalysts showed that in used catalysts, V=O bands decreased and new bands of vanadium oxysulfate bands were very sensitive. So the catalysts prepared from nonaqueous solution may bring about the high activity. Results from catalytic activity measurements at 350$^\circ$C, in the presence of $SO_2, NO$ conversion was more increased than in absence of $SO_2$. As the $MoO_3$ was added to $V_2O_5/TiO_2 system, SO_2$ conversion increased. It found that from the results, $V_2O-5-MoO_3/TiO_2$ catalysts prepared from an nonaqueous solution may bring about the high activity for both the reaction of NO and $SO_2$ removal.

• 한국결정성장학회지
• /
• 제23권6호
• /
• pp.320-324
• /
• 2013

$CeO_2$의 첨가가 $CeO_2-TiO_2$계 SCR촉매 활성에 미치는 영향을 구조적, 형상학적, 물리화학적 분석을 통해 규명하였다. 순수한 $TiO_2$ 분말과 10, 20, 30 wt%의 $CeO_2$를 첨가한 $CeO_2-TiO_2$ 분말을 졸겔법으로 합성한 결과, 분말 모두 $TiO_2$의 아나타제 (anatase)상을 나타내었고 $CeO_2$를 첨가할수록 $TiO_2$ 표면에 결정성이 낮은 $CeO_2$가 분산되어 피크강도가 낮아짐을 확인하였다. 순수한 $TiO_2$의 비표면적이 $60.6306m^2/g$인데 반해 $CeO_2-TiO_2$의 비표면적은 30 wt%의 $CeO_2$를 첨가한 경우 $116.2791m^2/g$으로 비표면적이 증가하였고 따라서 첨가된 $CeO_2$가 $TiO_2$의 응집을 억제한 것으로 예상된다. $NO_x$ 제거효율은 30 wt% $CeO_2-TiO_2$ 촉매가 $300^{\circ}C$에서 98 %로 다른 분말보다 높은 효율을 나타내는데 이는 FT-IR을 이용하여 촉매의 산점 변화를 확인한 결과 30 wt% $CeO_2-TiO_2$ 분말의 경우가 다른 분말들에 비해 산점이 상대적으로 많았기 때문이다. 따라서 졸겔법으로 합성한 SCR용 $CeO_2-TiO_2$계 촉매에서 $CeO_2$의 첨가는 $TiO_2$의 입성장을 억제하여 비표면적을 증가시키고 $Br{\Phi}nsted$ 및 Lewis 산점을 증가시킴으로써 촉매 효율을 향상시켰다고 판단된다.

• 한국세라믹학회지
• /
• 제33권10호
• /
• pp.1147-1155
• /
• 1996

• 한국전기전자재료학회논문지
• /
• 제28권9호
• /
• pp.561-564
• /
• 2015

Nano-size $BaTiO_3$ powder was synthesized by relatively simple hydrothermal reaction method. Finely dispersed Ti hydroxide precursor was first precipitated using $Ti(SO_4)_2$ and NaOH solution by applying ultrasonic power and washed thoroughly to remove $SO_4{^{2-}}$ and $Na^+$ ion. Then hydrothermal reaction was done at $160^{\circ}C$ for 6 hrs using solution prepared by washed Ti hydroxide precursor slurry and $Ba(OH)_2{\cdot}8H_2O$ with Ti:Ba mole ratio of 1:1. 200 ~ 500 nm size and uniform size distributed $BaTiO_3$ powder was synthesized by relatively low temperature and simple process.

• 한국세라믹학회지
• /
• 제46권6호
• /
• pp.554-560
• /
• 2009

We investigate a method for the electrochemical preparation of titanium dioxide/carbon nanotube ($TiO_2$/CNT) composites involving the electroplating of Ti in a titanium n-butoxide (TNB) electrolyte into a CNT matrix. The Brunauer-Emmett-Teller (BET) surface areas of $TiO_2$/CNT composites decrease as the electrochemical operating time increases. Changes in XRD patterns show a typical anatase type on the $TiO_2$/CNT composite prepared with a CNT matrix by the electroplating method in a TNB solution. In SEM micrographs, the titanium complex particles are uniformly distributed on the CNT surface. The results of chemical elemental analysis for the $TiO_2$/CNT composites show that most of the spectra for these samples produce stronger peaks for carbon and Ti metal than for any other element. Finally, the prominent photoelectrocatalytic activities of the $TiO_2$/CNT composites can be attributed to the combined effects of photodegradation of $TiO_2$, electron assistance of CNT, and the application of a sufficient voltage.