• Journal of IKEEE
• /
• v.25 no.1
• /
• pp.128-132
• /
• 2021

In this paper, the surface of electrodes used in solar cells was roughened using wet etching method among surface texturing method, and after surface treatment, dye sensitive solar cell using TiO2 oxide semiconductor was produced. The surface spectroscopic properties of surface treated electrodes were analyzed according to etching time, and by evaluating the electrical properties of TiO2 dye-sensitized solar cells produced according to etching time, the study on improving the efficiency of solar cells according to surface treatment was conducted. As a result, solar cells that etched the electrode surface for 10 minutes could see an improvement of about 27.46[%] over their existing efficiency.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.06a
• /
• pp.320-322
• /
• 2007

A new binder-free $TiO_{2}$ paste was prepared by common ion applying effect, enabling low temperature fabrication required for flexible solar cells. The binder-free and high viscosity $TiO_{2}$ coating solution was produced by adding 7.5% aniline in $TiO_{2}$ colloid solution obtained from the high pressure water-heat response method. The resulting pastes had high level of viscosities proper for optimal coating and thus revealed excellent performances in terms of thickness uniformity and I-V characteristics.

• Advances in concrete construction
• /
• v.3 no.2
• /
• pp.145-159
• /
• 2015

The evolution of nanotechnology provides materials with advance properties. It's a fast growing area of research to introduce the oxide nanoparticles into the cement pastes to improve their performance. The purpose of this paper is to review the effects of oxide nanoparticles (such as $SiO_2$, $TiO_2$, $Fe_2O_3$, $ZnO_2$, $Cr_2O_3$ and $Al_2O_3$) on both of hardened concrete properties (i.e., compressive strength, split tensile strength and flexural strength, water permeability, Abrasion resistance and pore structure of concrete) and fresh concrete properties (i.e., workability and setting time). Graphical representations of all these parameters were presented to facilitate the comparison of the effect of oxide nanoparticles on concrete processing. The paper also introduces some discussion about future work in this direction by identifying some open research area.

• Journal of IKEEE
• /
• v.23 no.1
• /
• pp.330-333
• /
• 2019

Various studies on dye-sensitized solar cells, which are cheaper to manufacture and have superior stability than silicon solar cells, are continuously conducted. In this study, the properties of dye-sensitized solar cells were studied using semiconductor oxides made by mixing $TiO_2$ and $Nb_2O_5$. By adding $Nb_2O_5$ in different proportions, the solar cell was made, and the surface area and electrical characteristics of this cell were measured. As $Nb_2O_5$ was added, the contact area of dye and electrolyte increased and the short-circuit current, open voltage, fill factor and conversion efficiency of dye-sensitized solar cells were confirmed to be improved.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2005.09a
• /
• pp.201-212
• /
• 2005

[ $Epoxy/BaTiO_3$ ] composite embedded capacitor films (ECFs) were newly designed fur high dielectric constant and low tolerance (less than ${\pm}15\%$) embedded capacitor fabrication for organic substrates. In terms of material formulation, ECFs are composed of specially formulated epoxy resin and latent curing agent, and in terms of coating process, a comma roll coating method is used for uniform film thickness in large area. Dielectric constant of $BaTiO_3\;&\;SrTiO_3$ composite ECF is measured with MIM capacitor at 100 kHz using LCR meter. Dielectric constant of $BaTiO_3$ ECF is bigger than that of $SrTiO_3$ ECF, and it is due to difference of permittivity of $BaTiO_3\;and\;SrTiO_3$ particles. Dielectric constant of $BaTiO_3\;&\;SrTiO_3$ ECF in high frequency range $(0.5\~10GHz)$ is measured using cavity resonance method. In order to estimate dielectric constant, the reflection coefficient is measured with a network analyzer. Dielectric constant is calculated by observing the frequencies of the resonant cavity modes. About both powders, calculated dielectric constants in this frequency range are about 3/4 of the dielectric constants at 1 MHz. This difference is due to the decrease of the dielectric constant of epoxy matrix. For $BaTiO_3$ ECF, there is the dielectric relaxation at $5\~9GHz$. It is due to changing of polarization mode of $BaTiO_3$ powder. In the case of $SrTiO_3$ ECF, there is no relaxation up to 10GHz. Alternative material for embedded capacitor fabrication is $epoxy/BaTiO_3$ composite embedded capacitor paste (ECP). It uses similar materials formulation like ECF and a screen printing method for film coating. The screen printing method has the advantage of forming capacitor partially in desired part. But the screen printing makes surface irregularity during mask peel-off, Surface flatness is significantly improved by adding some additives and by applying pressure during curing. As a result, dielectric layer with improved thickness uniformity is successfully demonstrated. Using $epoxy/BaTiO_3$ composite ECP, dielectric constant of 63 and specific capacitance of 5.1nF/cm2 were achieved.

• Korean Journal of Materials Research
• /
• v.25 no.12
• /
• pp.683-689
• /
• 2015

In this study, the properties of Ag-coated $TiO_2$ nanoparticles were observed, while varying the molar ratio of water and $Ag^+$ for the surfactant and $TiO_2$. According to the XRD results, each nanoparticle showed a distinctive diffraction pattern. The intensity of the respective peaks and the sizes of the nanoparticles increased in the order of AT1($R_1=5$)(33.3 nm), AT2($R_1=10$)(38.1 nm), AT3($R_1=20$)(45.7 nm), AT4($R_1=40$)(48.6 nm) as well as AT5($R_2=0.2$, $R_3=0.5$)(41.4 nm), AT6($R_2=0.3$, $R_3=1$)(45.1 nm), AT7($R_2=0.5$, $R_3=1.5$)(49.3 nm), AT8($R_2=0.7$, $R_3=2$)(57.2 nm), which values were consistent with the results of the UV-Vis. spectrum. The surface resistance of the conductive pastes fabricated using the prepared Ag-coated $TiO_2$ nanoparticles exhibited a range 7.0~9.0($274{\sim}328{\mu}{\Omega}/cm^2$) times that of pure silver paste(ATP)($52{\mu}{\Omega}/cm^2$).

• Proceedings of the KIEE Conference
• /
• 2003.07c
• /
• pp.1529-1531
• /
• 2003

Thick film mechanical sensors can be categorized into four main areas piezoresistive, piezoelectric, piezocapastive and mechanic tube. In this areas, the thick film strain gage is the earliest example of a primary sensing element based on the substrates. The latest thick film sensor is used various pastes that have been specifically developed for pressure sensor application. The screen printing technique has been used to fabricate the pressure sensors on alumina substrate($Al_2O_3$). Thick film capacitive of strain sensing characteristics are reported and dielectric paste based on (Ti+Ba) materials. The electric property of dielectric paste has been studied and exhibit good properly with good gage factor comparable to piezoresistive strain gage. New piezocapacitive strain sensor was designed and tested. The output of capacitive value was good characteristics.