• Korean Journal of Materials Research
• /
• v.17 no.3
• /
• pp.125-131
• /
• 2007

[ $TiO_{2}-solution$ ] was aaded in $SiO_{2}-solution$ by various composition. $SiO_{2}-TiO_{2}$ thin films were obtained by the dip-coating method on the $SiO_{2}$ glass substrates, and then heat-treated at various temperature. Nano-size $TiO_{2}$ particles dispersed $SiO_{2}-TiO_{2}$ films showed absorption peak by quantum size effect at short wavelength region $350{\sim}400nm$, which made them good candidates for non-linear optical materials and photo-catalytic materials. The thickness of $SiO_{2}-TiO_{2}$ films were $300{\sim}430nm$. The contact angle of $SiO_{2}-TiO_{2}$ films for water was $5.3{\sim}47.9^{\circ}$, and therefore it is clear that $SiO_{2}-TiO_{2}$ films have super hydrophilic properties and the self-cleaning effects.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.373-373
• /
• 2010

광촉매능을 갖는 $TiO_2$는 국내외적으로 많은 연구가 진행되고 있다. 빛의 조사로 발생하는 다양한 물리 화학적 촉매특성이 환경정화 뿐만 아니라 및 에너지 흡수차단 기능도 갖고 있어 최근 주목을 받고 있다. 응용분야로 초친수성 유리제품, 필터, 살균기능의 의료용 부품소재, 고효율 수소생산 및 태양전지 등에 활용성이 커서 친환경에너지 소재로 각광을 받고 있다. 본 연구에서는 초친수성 자동차의 사이드미러 개발을 위해 유리표면에 초친수성 $TiO_2$를 코팅하 고 그의 특성을 평가하였다. 특히, 이종밴드갭을 갖는 복합구조 $TiO_2/Cr_2O_3$/Cr 박막을 스퍼터링법으로 증착하여 중간층인 $Cr_2O_3$의 역할을 고찰하였다. 제조된 박막의 결정구조는 thin film형 X-선회절기(XRD)를 사용하여 분석하였으며, 박막의 표면 미세구조는 FE-SEM(Field Emission Scanning Electron Microscope)와 AFM(Atomic Force Microscope)으로, 화학구조는 XPS(X-ray Photoelectron Spectroscope)로 분석하였다. 친수성 평가는 실온 분위기에서 접촉각 측정기(Topcon-UVR2)를 사용하여 평가 하였으며 이때 조사되는 UV는 파장이 365nm이다. $Cr_2O_3$(비정질)/Cr박막위에 제조된 $TiO_2$ 박막은 균일한 anatase-$TiO_2$가 성장했으나, Cr, $Cr_2O_3$(결정질)박막위에 제조 된 $TiO_2$ 박막은 anatase상과 rulile상이 혼합된 형태로 성장하였다. $TiO_2$/Cr, $TiO_2/Cr_2O_3$(비정질)/Cr, $TiO_2/Cr_2O_3$(결정질)/Cr박막은 UV조사 1시간 만에 $10^{\circ}$ 이하의 초친수성을 나타내었다. 이종 밴드갭을 갖는 $TiO_2/Cr_2O_3$(비정질)/Cr박막은 40시간까지 친수성을 유지하는 결과를 나타냈다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.682-685
• /
• 2002

The $0.96MgTiO_3-0.04SrTiO_3$ ceramics with $B_2O_3$(10wt%) were prepared by the conventional mixed oxide method. The structural properties were investigated with sintering temperature by XRD. According to the X-ray diffraction pattern of the $0.96MgTiO_3-0.04SrTiO_3$ ceramics with $B_2O_3$(10wt%), the ilmenite $MgTiO_3$ and perovskite $SrTiO_3$ structures were coexisted and secondary phase of the $MgTi_2O_5$ were appeared. In the case of $0.96MgTiO_3-0.04SrTiO_3+B_2O_3$(10wt%) ceramics sintered $1225^{\circ}C$, dielectric constant, quality factor and temperature coefficient of resonant frequency were 19.82, 62,735GHz, $-2.983ppm/^{\circ}C$, respectively.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.54 no.12
• /
• pp.573-577
• /
• 2005

[$TiO_2$] sol and $SiO_2$ sol were prepared using sol-gel method. As $H_{2}O$/Alkoxide ratios increased, sol had cluster structure and as $H_{2}O$/Alkoxide ratios decreased, sol had linear structure. Gelation time of $TiO_2$ sol was faster than that of $SiO_2$ sol according to the time. In comparison with initial viscosity between $TiO_2$ sol and $SiO_2$ sol, $TiO_2$ sol was highest at $H_{2}O/Ti(OC_{3}H_{7})_{4}=5$, $SiO_2$ sol was almost constant according to $H_{2}O/Si(OC_{2}H_{5})_{4}$ ratios.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.4
• /
• pp.925-928
• /
• 2010

Nitrogen-doped $TiO_2$ ($TiO_2$:N) nano-particles with a pure anatase crystalline structure were successfully synthesized through the hydrolysis of $TiCl_4$ in an ammonia aqueous solution. The samples were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), $N_2$-sorption, and UV-vis diffuse reflectance spectra (UV-vis DRS) techniques. The absorption edge of nitrogen-doped $TiO_2$ shifted into the visible wavelength region. The photoelectrochemical (PEC) performances were investigated for the $TiO_2$ mesoporous electrodes doped with different nitrogen concentrations. The $TiO_2$:N electrodes exhibited much higher PEC responses compared to the pure $TiO_2$ electrode because of the significantly enhanced visible-photoresponsibility of the $TiO_2$:N electrodes.

• Applied Chemistry for Engineering
• /
• v.32 no.6
• /
• pp.599-606
• /
• 2021

In this study, an experiment and a reaction characteristic study were conducted to enhance the reaction activity of V₂O₅/WO₃/TiO₂ at 300 ℃ or less by adding selenium to the support, in a selective catalytic reduction method using ammonia as a reducing agent to remove nitrogen oxides. Se-TiO₂ and TiO₂ were synthesized using the sol-gel method, and used as a support when preparing V₂O₅/WO₃/TiO₂ and V₂O₅/WO₃/Se-TiO₂ catalysts. The reaction activity of our catalyst was compared with that of a commercial catalyst. The denitration efficiency of the catalyst using TiO₂ prepared by the sol-gel method was lower than that of the catalyst prepared using commercial TiO₂, but was improved by the addition of selenium. Thus, the effect of selenium addition on the catalyst structure was analyzed using BET, XRD, Raman, H₂-TPR, and FT-IR measurements and the effect of the increase in specific surface area by selenium addition and the formation of monomer and complex vanadium species on reaction characteristics were confirmed.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.14 no.1
• /
• pp.5-14
• /
• 1977

"Electrical Properties of Barium Titanates with Addition Sb2O3." PTC BaTiO3 in low resistance at room temperature was prepatred. Al2O3, SiO2 and TiO2 were doped with a view to improving reproduction. Sb2O3 was doped as impurity in order to control of resistivity of the specimens. The relations between the amount of Sb3O3 and electrical properties wereinvestigated. Of the compositions studied, additions of 3.75mole% Al2O3, 1.25mole% SiO2, 2.25mole% TiO2 and 0.16~0.25wt% Sb2O3 to BaTiC3 was low resistivity in 14-300 ohm-cm.00 ohm-cm.

• Journal of the Korean Ceramic Society
• /
• v.19 no.4
• /
• pp.287-292
• /
• 1982

Nonohmic properties of ZnO ceramics with various small amounts of additives were studied in relation to experimental methods, additive contant and sintaring temperature. The kinds of additives used to following chemicals were basic additives ($0.5Bi_2O_3$, $0.3BaCO_3$, $0.5MnCO_3$, $0.5Cr_2O_3$, $0.1KNO_3$), $TiO_2$ and $Al(OH)_3$. Expecially, this study has focused on the effectsof $TiO_2$ and $Al(OH)_3$ in ZnO ceramics with the basic additives. SEM studies indicated that the addition of TiO2 promoted grain growth but retarded grain growth with the addition of $Al(OH)_3$. Also, in the case of calcination of ZnO with $TiO_2$ and ZnO with $Al(OH)_3$ previously, grain size of ZnO with $TiO_2$ was larger and that of ZnO with Al(OH)3 was smaller in comparison to the case with out calcination. From the viewpoint of nonohmic exponent and nonohimic resistance, electrical characteristics of ZnO, $TiO_2$ and the basic additives was more effective than that of ZnO, $Al(OH)_3$ and the basic additives. Nonohmic exponent and nonohmic resistance of ZnO, $TiO_2$ and the basic additives was 11-13 and 40-65 respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.37-42
• /
• 2000

The comparative study of texture of Al/Ti thin films deposited on low-dielectric polymer and $SiO_2$substrates has been investigated. Fifty-nm-thick Ti films and 500-nm-thick Al-1%Si-0.5%Cu (wt%) films were deposited sequentially onto low-k polymers and $SiO_2$by using a DC magnetron sputtering system. The texture of Al thin film was determined using X-ray diffraction (XRD) theta-2theta ($\theta$-2$\theta$) and rocking curve and the microstructure of Al/Ti films on low-k polymer and $SiO_2$substrates was characterized by cross-sectional transmission electron microscopy (TEM). Both the $\theta$-2$\theta$ method and rocking curve measurement suggest that Al/Ti thin films deposited on $SiO_2$have stronger texture than those deposited on low-k polymer. The texture of Al thin films strongly depended on that of Ti films. Cross-sectional TEM revealed that grains of Ti films on $SiO_2$substrates had grown perpendicular to the substrate, while the grains of Ti alms on SiLK substrates were formed randomly. The lower degree of (111) texture of Al thin films on low-k polymer was due to Ti underlayer.

• Journal of Environmental Science International
• /
• v.16 no.6
• /
• pp.683-688
• /
• 2007

In this study, N doped $TiO_2$ (TiO-N) thin film was prepared by DC magnetron sputtering method to show the photocatalytic activity in a visible range. Various gases (Ar, $O_2\;and\;N_2$) were used and Ti target was impressed by 1.2 kW -5.8 kW power range. The hysteresis of TiO-N thin film as a function of discharge voltage wasn't observed in 1.2 and 2.9kW of applied power. Cross sections and surfaces of thin films by FE-SEM were tiny and dense particle sizes of both films with normal cylindrical structures. XRD pattern of $TiO_2$ and TiO-N thin films was appeared by only anatase peak. Red shift in UV-Vis adsorption spectra was investigated TiO-N thin film. Photoactivity was evaluated by removal rate measurement of suncion yellow among reactive dyes. The photodegradation rate of $TiO_2$ thin film on visible radiation was shown little efficiency but TiO-N was about 18%.