• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05d
• /
• pp.72-76
• /
• 2003

The $Sr_{0.7}Bi_{2.6}Ta_2O_9$(SBT) thin films are deposited on Pt-coated electrode(Pt/$TiO_2/SiO_2$/Si) using RF magnetron sputtering method. The structural and electrical properties of SBT capacitors were influenced with annealing atmosphere. In the XRD pattern, the SBT thin films in all annealed atmosphere had (105) orientation. In the SEM images, Bi-layered perovskite phase was crystallized in all annealing atmosphere and grains largely grew in oxygen annealing atmosphere. The maximum remanent polarization and the coercive electric field in oxygen annealing atmosphere are $12.40[{\mu}C/cm^2]$ and 30[kV/cm] respectively. The fatigue characteristics of SBT capacitors did not change up to $10^{10}$ switching cycles.

• Journal of the Korean Vacuum Society
• /
• v.7 no.3
• /
• pp.195-200
• /
• 1998

We have investigated the crystal structure and electrical properties of Pt/SBT/$CeO_2$/Si(MFIS) and Pt/SBT/Si(MFS) structures for the gate oxide of ferroelectric memory. XRD spectra and SEM showed that the SBT film of SBT/$CeO_2$/Si structure had larger grain than that of SBT/Si structure. Furthermore HRTEM showed that SBT/$CeO_2$/Si had 5 nm thick $SiO_2$layer and very smooth interface but SBT/Si had 6nm thick $SiO_2$layer and 7nm thick amorphous intermediate interface. Therefore, $CeO_2$film between SBT film and Si substrate is confirmed as a good candidate for a diffusion barrier. The remanent polarization decreased and coercive voltage increased in Pt/SBT/$CeO_2/Pt/SiO_2$/Si structure. This effect may increase memory window of MFIS structure directly related to the coercive voltage. From the capacitance-voltage characteristics, the memory of Pt/SBT(140 nm)/$CeO_2$(25 nm)/Si structure were in the range of 1~2 V at the applied voltage of 4~6 V. The memory window increased with the thickness of SBT film. These results may be due to voltage applied at SBT films. The leakage currents of Pt/SBT/$CeO_2$/Si and Pt/SBT/Si were $ 10^8A/\textrm{cm}^2$ and $ 10^6 A/\textrm{cm}^2$, respectively.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.945-952
• /
• 1998

Ferroelectric Sr0.8Bi2.4Ta2O9 stock solutions were prepared by MOD(Metaloganic Decompostion) process. The phase transformation for the layered perovskite of the SBT thin films by changing RTA(Rapid her-mal Annealing) temperatuer from 700$^{\circ}C$to 780$^{\circ}C$ were observed using XRD and SEM. Layered perovskite phase began to appear above 740$^{\circ}C$ and then SBT thin films were annealed at 800$^{\circ}C$ for 1hr for its com-plete crystallization. The specimens showed well shaped hysteresis curves without post annealing that car-ried out after deposition of Pt top electrode. The SBT thin films showed the asymmetric ferroelectric pro-perties. It was confirmed that the properties were caused by interface effect to SBT and electrode by leak-age current density measurement and asymmetric properties reduced by post annealing. At post annealing temperature of 800$^{\circ}C$ remanant polarization values (2Pr) were 6.7 9 ${\mu}$C/cm2 and those of leakage current densities were 3.73${\times}$10-7 1.32${\times}$10-6 A/cm2 at 3, 5V respectively. Also bismuth bonding types of SBT thin film surface were observed by XPS.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.73-74
• /
• 2006

Ferroelectric thin films have been widely investigated for future nonvolatile memory application. We fabricated the BLT ($(Bi,La)_4Ti_3O_{12}$) films on Si using a STA ($SrTa_2O_6$) buffer layer BLT and STA film were prepared by sol-gel method. Measurement data by XRD and AFM, showed that BLT film and STA films were well crystallized and a good surface morphology. From C-V measurement reward that the Au/BLT/STA/Si structure showed a clockwise hysteresis loop with a memory window of 1.5 V for the bias voltage sweep of ${\pm}5$ V. From results, the Au/BLT/STA/Si structure is useful for FeFETs.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.817-820
• /
• 2004

The $Sr_{0.7}Bi_{2.6}Ta_2O_9$(SBT) thin films are deposited on Pt-coated electrode($Pt/TiO_2/SiO_2/Si$) using a RF magnetron sputtering method. The ferroelectric properties of SBT capacitors with annealing time were studied. In the SEM images, Bi-layered perovskite phase was crystallized at 10min and grains largely grew with annealing tune. SBT thin films are transformed from initial amorphous phase to the fully formed layer-structured perovskite. During the annealing process at $750^{\circ}C$, we found that an fluorite-like stage is formed after 3min. In the XRD pattern, the SBT thin films after 3min annealing time had (105) orientation. The ferroelectric properties of SBT capacitor with annealing time represent a favorable properties at 60 min. The maximum remanent polarization and the coercive electric field with 60 min are $12.40C/cm^2$ and 30kV/cm, respectively. The leakage current density with 60min is $6.81{\times}10^{-10}A/cm^2$.

• Journal of the Korean Vacuum Society
• /
• v.8 no.3A
• /
• pp.238-244
• /
• 1999

Pt/SBT/Pt capacitors were fabricated using the MOD-derived $SrBi_{2x}Ta_2O_9$ (SBT) films and their ferroelectic and leakage current characteristics were investigated with post annealing at 400~$800^{\circ}C$. Although the MOD-derived SBT film exhibited the hysteresis loop typical for the leaky film, the well-saturated ferroelectric hysteresis loop could be obtained by post annealing the Pt/SBT/Pt capacitors at $550^{\circ}C$~$800^{\circ}C$. The remanent polarization $2P_r$ of the SBT film exhibited a maximum value of 9.72$\mu\textrm{cm}^2$ with post annealing at $600^{\circ}C$, and then decreased with increasing the post annealing temperature above $600^{\circ}C$. The MOD-derived SBT films exhibited the high leakage current density of ~$10^{-3} \textrm{A/cm}^2$ at 75kV/cm. With post annealing the Pt/SBT/Pt capacitor at 600~$800^{\circ}C$, however, the leakage current density decreased remarkably to less than $10^{-6}\textrm{A/cm}^2$ at 75kV/cm.

• Proceedings of the Mineralogical Society of Korea Conference
• /
• 2001.06a
• /
• pp.95-95
• /
• 2001

The Yeongdong basin is one of the pull-apart basins in the southwestern part of the Korean Peninsula that has developed during Cretaceous sinistal fault movement. The bimodal igneous activities (basalts and rhyolites) in the basin appear to be closely associated with the basin development. Here, we discuss the origin of the igneous rocks using chemical and radiogenic isotope data. Basaltic (48.4-52.7 wt% SiO$_2$) and rhyolitic (70.3-70.8 wt% SiO$_2$) rocks are slightly alkalic in a total alkali-silica diagram. The rhyolitic rocks with have unusually high K$_2$O contents (5.2-6.0 wt%). The basaltic rocks show an overall pattern of within-plate basalt in a MORB-normalized spider diagram, but have distinct negative anomaly of Nb, which indicates a significant amount of crustal component in the magma. The basaltic rocks plot within the calc-alkaline basalt field in the Hf/3-Th-Ta and Y/l5-La/10-Nb/8 discrimination diagrams. The eNd(T) values of the basaltic rocks (-13.6 to 14.3) are slightly higher than those of the rhyolitic rocks (-14.1 to 15.2), and the initial Sr isotopic ratios of the former (0.7085-0.7093) are much lower than those of the latter (0.7140-0.7149). However, the initial Nd and Sr isotope ratios of the igneous rocks in the Yeongdong basin are similar to those of the nearby Cretaceous igneous rocks in the Okcheon belt. The Pb isotope ratios plot within the field of Mesozoic granitoids outside of the Gyeongsang basin in Pb-Pb correlation diagrams. Since a basaltic magma requires the mantle source, the enriched isotopic signatures and negative Nb anomaly of the basaltic rocks suggest two possibilities for their origin: enriched mantle lithospheric source, or depleted mantle source with significant amount of crustal contamination. However, we prefer the first possibility since it would be difficult for a basaltic magma to maintain its bulk composition when it is significantly contaminated with granitic crustal material. The slightly more enriched isotopic signatures of rhyolitic rocks also suggest two possibilities: differentiate of the basaltlc magma with some crustal contamination, or direct partial melting of the lower crust. Much larger exposed volume of the rhyolitic rocks, compared with the basaltic rocks, indicates the latter possibility more favorable.

• Proceedings of the KIEE Conference
• /
• 1999.07d
• /
• pp.1553-1555
• /
• 1999

Recently, $SrBi_2Ta_2O_9$(SBT) and $Pb(ZrTi)O_3$(PZT) were much attracted as materials of capacitor for ferroelectric random access memory(FRAM) showing higher read/write speed, lower power consumption and nonvolartility. Bi-layered SBT thin film has appeared as the most prominent fatigue free and low operation voltage for use in nonvolatile memory. To highly integrate FRAM, SBT thin film should be etched. A lot of papers on SBT thin film and its characteristics have been studied. However, there are few reports about SBT thin film due to difficulty of etching. In order to investigate properties of etching of SBT thin film, SBT thin film was etched in $CF_4$/Ar gas plasma using magnetically enhanced inductively coupled plasma (MEICP) system. When $CF_4/(CF_4+Ar)$ is 0.1, etch rate of SBT thin film was $3300{\AA}/min$, and etch rate of Pt was $2495{\AA}/min$. Selectivities of SBT to Pt. $SiO_2$ and photoresist(PR) were 1.35, 0.6 and 0.89, respectively. With increasing $CF_4$ gas, etch rate of SBT thin film and $P_t$ decreased.