• 한국세라믹학회지
• /
• 제32권12호
• /
• pp.1331-1336
• /
• 1995

The glass-ceramics for ferro-electric were made from compositions of 70PbO.16TiO2.8SiO2.4B2O3.2AlPO4 (wt%) and 67.5PbO.20TiO2.8.5SiO2.2B2O3.2AlPO4 (wt%). The crystallization kinetics for PbTiO3 crystalline phase formation from glass was studied using non-isothermal DSC techniques. The values of activation energy, ΔE using variables of heating rate and temperature were calculated at various reaction fractions obtained from peak area over DSC. The results indicated that activation energy was lowest at 60% reaction fractions and the activation energy of glass containing 20.0 wt% TiO2 is higher than that of glass containing 16.0 wt% TiO2. The crystallization mechanism was three dimensional growth (n=4).

• 한국세라믹학회지
• /
• 제34권7호
• /
• pp.774-780
• /
• 1997

Porous low reflective coating films of SiO2.ZrO2 system were prepared from the mixed alkoxide solutions of Zr(O-nC3H7)4 and partially prehydrolyzed TEOS by the sol-gel method using the dip-coating technique. In the case of 90SiO2.10ZrO2 porous coating films with HCl and H2O content was 0.3 mole and 4 mole, 378 m2/g of the specific surface area, 0.254 cm3/g of total pore volume, 30-50$\AA$ of average pore diameter. The transmittance of 90SiO2.10ZrO2 porous coated films was 95.38% at the wavelength of 550 nm, compared with the parent glass, the transmittance was increased with 4.38%.

• 한국안전학회지
• /
• 제18권3호
• /
• pp.14-21
• /
• 2003

This study deals with the influence of ceramic coating on characteristics of friction and abrasion of aluminum allot(7075 T6) used in mechanical casting. In this research, frictional wear characteristic of ceramic coating materials such as $A1_2O_3$, $Si_3N_4$, SiC was investigated using aluminum alloy(7075 T6) and stainless 403 cast iron under room temperature and normal air pressure. The coating layer was observed using SEM. The conclusions are as follows: 1) Friction coefficients of $A1_2O_3$, SiC and $Si_3N_4$ are obtained 0.63 0.56 and 0.54 respectively. 2) Abrasion resistance of stainless 403 cast iron with $Si_3N_4$ is the best among the ceramic coating materials. 3) Abrasion mechanism of aluminum alloy(7075 T6) coaled with ceramic material and stainless 403 cast iron is caused by brittle fracture. 4) Coating the ceramic material on the aluminum alloy(7075 T6) can effectively increase the antiwear, impact properties, and corrosion resistance.

• 한국생산제조학회지
• /
• 제9권6호
• /
• pp.170-177
• /
• 2000

Dense $Al_2$O$_3$-30%TiC and Si$_3$N$_4$ ceramic tool materials with various grain size were produced by sintering-HIP treatment and by gas-pressure sintering. The fracture toughness was measured by indentation fracture and indentation strength method for both ceramics with various grain size. The effect of the grain size on the fracture toughness was evaluated, and the correlation between fracture toughness and mechanical properties such as hardness, Young\`s modulus and flexural strength of these ceramic were also investigated. The highest fracture toughness of around 6.7 MPa.m(sup)1/2 was obtained in Si$_3$N$_4$ ceramics with grain size of 1.58${\mu}{\textrm}{m}$. With a larger grain size of $Al_2$O$_3$-30%TiC and Si$_3$N$_4$ ceramics, the fracture toughness was generally increased. The increased fracture toughness of these ceramic also improved the flexural strength although the hardness decreased considerably. Similar results were obtained in grain size and mechanical properties on both $Al_2$O$_3$-30%TiC and Si$_3$N$_4$ ceramic tool materials.

• 한국세라믹학회지
• /
• 제33권8호
• /
• pp.871-876
• /
• 1996

It is believed that fly ash could be suitable for preparing the sialon by carbothermal reduction method because the total amount of SiO2 and Al2O3 is above 80% and the unburned residual carbon is above 5% within the fly ash. The effects of reaction temperature (1350, 1400, 145$0^{\circ}C$) reaction time (1, 5, 10 hours) and the amount of carbon additions (C/SiO2=2, 3, 4 mole) on the $\beta$-sialon synthesis were obserbed, It was conformed that $\beta$-sialon (Z=2.15~2.18) was formed as major phase under all of the synthesis conditions and small amount of Si2ON2 SiC, AlN and Si3N4 was formed depending on the synthesis conditions. FeSix intermetal-lic compound was formed above 140$0^{\circ}C$ reaction temperature due to the large amount of iron oxides within the raw fly ash.

• 한국세라믹학회지
• /
• 제21권1호
• /
• pp.11-18
• /
• 1984

$eta$-Sialon synthesis was investigated via the simultaneous reduction and nitridation of Hadong Pink Kaolin using the graphite as a reducing agent at 135$0^{\circ}C$ under 80% $N_2-20%H_2$ atmosphere. When Hadong Pink Kaolin-graphite-silicon nitride seed(molar ratio ; $SiO_2:C:Si_3N_4$=1;3.5:0.05) mixture was heated at 135$0^{\circ}C$ for as long as 20h in 80%$N_2-20%H_2$ atmosphere a homogeneous $eta$-Sialon$(Si_{3.5}Al_{2.5}O_{2.5}N_{2.5})$ was mainly formed together with a small amount of $\alpha$-$Si_3N_4$.

• 한국세라믹학회지
• /
• 제42권1호
• /
• pp.16-21
• /
• 2005

The effect of additive composition, using AlN and $Er_{2}O_{3}$ as sintering additives, on the mechanical properties of liquid-phase-sintered, and subsequently annealed SiC ceramics was investigated. The microstructures developed were quantitatively analyzed by image analysis. The average thickness of SiC grains increased with increasing the $Er_{2}O_{3}/(AlN + Er_{2}O_{3})$ ratio in the additives whereas the aspect ratio decreased with increasing the ratio. The mechanical properties versus $Er_{2}O_{3}/(AlN + Er_{2}O_{3})$ ratio curve had a maximum; i.e., there was a small composition range at which optimum mechanical properties were realized. The best results were obtained when the ratio ranged from 0.4 to 0.6. The flexural strength and fracture toughness of the SiC ceramics were $550\~650\;MPa$ and $5.5\~6.5$ MPa${\cdot}m^{1/2}$, respectively.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2000년도 춘계총회,특별강연,심포지움,연구발표회
• /
• pp.126.2-126.2
• /
• 2000

• 한국세라믹학회지
• /
• 제29권5호
• /
• pp.357-366
• /
• 1992

Residual organics were considered as impurity in Sol-Gel method. The purpose of this study was to find the conditions to contain as much residual organics as possible in silica gel prepared from TEOS(tetraethylortho-silicate) by Sol-Gel method. Residual organics are to be expected to have reduction effect on synthesizing Si3N4 from silica gel. The results of this study are follows: 1) The maximum content of entrapped carbon was 19.8 wt.%(C/SiO2=0.25 wt.ratio) in silica gel synthesized under the conditions 1.5 fold mole water for incomplete hydrolysis, 2.5 fold mole phenol as a solvent and 0.1 fold mole HCl as a catalyst to TEOS. 2) Silica gel with organics entrapped by Sol-Gel method had a positive effect on the formation of Si3N4 compared with commercial silica gel. 3) Sintered body of synthesized $\alpha$-Si3N4 with Y2O3 and Al2O3 as additives at 175$0^{\circ}C$ in N2 atmosphere showed bending strength, 602$\pm$20 MPa and frature toughness 4.45$\pm$0.15 MPa.m1/2.

• 한국세라믹학회지
• /
• 제35권8호
• /
• pp.827-835
• /
• 1998

Blanket Copper films were chemically vapor deposited on six kinds for substrates for scrutinizing the change of characteristics induced by the difference of substrates and seeding layers. Both TiN/Si and {{{{ { SiO}_{2 } }}/Si wafers were used as-recevied and with the Cu-seeding layers of 40${\AA}$ and 160${\AA}$ which were produced by sputtering The CVD processes were exectued at the deposition temperatures between 130$^{\circ}C$ and 260$^{\circ}C$ us-ing (hfc)Cu(VTMS) as a precursor. The deposition rate of 40$^{\circ}C$ Cu-seeded substrates was higher than that of other substrates and especially in seeded {{{{ { SiO}_{2 } }}/Si substrate because of the incubation period reducing in-duced by seeding layer at the same deposition time and temperature. The resistivity of 160${\AA}$ Cu seeded substrate was lower then that of 40 ${\AA}$ because the nucleation and growth behavior in Cu-island is different from the behavior in {{{{ { SiO}_{2 } }} substrate due to the dielectricity of {{{{ { SiO}_{2 } }}.