• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.410-418
• /
• 1992

Si3N4, AlN and Y2O3 powder mixtures of the Y0.1(Si, Al)12(N, O)16 composition were hot-pressed at 1900℃ for 0 to 60 min under 30 MPa in order to fabricate the partially-stabilized α-Sialon ceramics (X=0.1). Room and high temperature flexural strengths of the specimens were compared with those of Si3N4-5 wt%Y2O3, Si3N4-5 wt%Y2O3-2 wt%Al2O3, and β-Sialon (Z=0.5) ceramics. The flexural strength of the α-Sialon ceramics which was hot-pressed for 15 min showed the highest value of 820 MPa at 1400℃ that is relatively higher temperature. It is guessed that a little amount of glassy phase existed in grain boundary because Y2O3 and AlN components were incoperated in Si3N4 grains, or transient liquid phase sintering, and microstructure with the smaller grain size and the interlocked grains of α'-and β-Si3N4 was obtained by the hot-pressing at high temperature of 1900℃ for the short time (15 min).

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.201-209
• /
• 1989

Fine Si-Al-OH coprecipitate powders were prepared from Si- and Al-alkoxides by the hydrolysis method. $\beta$-Sialon powder was obtained from prepared Si-Al-OH coprecipitate by the simultaneous reduction and nitridation method. The syntehsized Sialon powder was pressureless sintered at 175$0^{\circ}C$ for 90 min in N2 atmosphere. The characterization of the Sialon powder was performed with XRD, BET, SEM, TEM and particle size analysis. The sinterability and mechanical properties of sintered bodies were investigated in terms of relative density, M.O.R., fracture toughness, hardness and the morphology of microstructure. The highest values of their mechanical properties were obtained for the $\beta$-Sialon ceramics at Z=1 and those values are as follows : M.O.R., KIC and HV of $\beta$-Sialon ceramics(Z=1) are 499.1 MPa, 5.9MN/m3/2 and 18.7GPa, respectively.

• Journal of Korea Foundry Society
• /
• v.20 no.1
• /
• pp.13-20
• /
• 2000

In the present study,($10%Al_2O_3+5%Si$)/AZ91 Mg hybrid composite was fabricated using the squeeze casting method. During squeeze casting, Molten Mg was infiltrated into the preform of $10%Al_2O_3+5%Si$ and reaction product of $Mg_2Si$ intermetallic compound was formed by the reaction between molten Mg and Si Powder. Microstructure has been observed and mechanical properties were evaluated for the reaction squeeze cast(RSC) hybrid composite. It was found that Si powder totally reacted with molten Mg to form $Mg_2Si$. Reinforcement($Al_2O_3$) and the reaction product ($Mg_2Si$) are fairly uniformly distributed in Mg Matrix for the squeeze cast hybrid composite. Mechanical Properties were improved with hybridization of reinforcements, namely higher hardness and enhanced wear resistance comparing squeeze cast($15%Al_2O_3$)/AZ91 Mg composite.

• Journal of the Korean Ceramic Society
• /
• v.29 no.1
• /
• pp.9-14
• /
• 1992

Some of non-isothermal analysis methods are applied to CaO-MgO-Al2O3-SiO2 glass system to find the kinetics parameters of crystallisation, activation energy, Avrami component and frequency factor. The results using the non-isothermal analysis were compared to that of microstructure experiment. Analysis of the result has enabled to some methods to be to recommend as being the most appropriate equation to use in a glass system. It was shown that in the thermal analysis using the non-isothermal method of Kissinger, Augis-Bennett, Bansal, and Marotta, the calculation of activation energy is not much different, while Avrami component and frequency factor are different from applied each methods.

• Journal of Welding and Joining
• /
• v.22 no.5
• /
• pp.46-52
• /
• 2004

AlSi-Al$_2$O$_3$ composite layer was prepared by plasma spray on steel substrate. The composite powder for plasma spray was prepared by simple mechanical blending. The wear resistance of the composite layers and matrix aluminum alloy were performed in terms of size distribution of ceramic particles. Friction coefficients of AlSi were decreased with incorporation of $Al_2$O$_3$. The tribological properties of coated layers were affected by the size of incorporated $Al_2$O$_3$ particle. The reinforcement of $Al_2$O$_3$ particle into aluminum alloy matrix decreased the friction coefficient as well as wear loss.

• Korean Journal of Materials Research
• /
• v.24 no.12
• /
• pp.715-719
• /
• 2014

(PDDA/$SiO_2$) thin films that consisted of positively charged poly (diallyldimethylammonium chloride) (PDDA) and negatively charged $SiO_2$ nanoparticles were fabricated on a glass substrate by an applying voltage layer-by-layer (LBL) self-assembly method. In this study, the microstructure and optical properties of the (PDDA/$SiO_2$) thin films coated on glass substrate were measured as a function of the applied voltage on the Pt electrodes. When 1.0 V was applied to a Pt electrode in a PDDA and $SiO_2$ solution, the thickness of the $(PDDA/SiO_2)_{10}$ thin film increased from 79 nm to 166 nm. The surface roughness also increased from 15.21 nm to 33.25 nm because the adsorption volume of the oppositely charged PDDA and $SiO_2$ solution increased. Especially, when the voltage was applied to the Pt electrode in the $SiO_2$ solution, the thickness increase of the (PDDA/$SiO_2$) thin film was larger than that obtained when using the PDDA solution. The refractive index of the fabricated (PDDA/$SiO_2$) thin film was ca. n = 1.31~1.32. The transmittance of the glass substrate coated by (PDDA/$SiO_2$)6 thin film with a thickness of 106 nm increased from ca. 91.37 to 95.74% in the visible range.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.37-42
• /
• 2000

The comparative study of texture of Al/Ti thin films deposited on low-dielectric polymer and $SiO_2$substrates has been investigated. Fifty-nm-thick Ti films and 500-nm-thick Al-1%Si-0.5%Cu (wt%) films were deposited sequentially onto low-k polymers and $SiO_2$by using a DC magnetron sputtering system. The texture of Al thin film was determined using X-ray diffraction (XRD) theta-2theta ($\theta$-2$\theta$) and rocking curve and the microstructure of Al/Ti films on low-k polymer and $SiO_2$substrates was characterized by cross-sectional transmission electron microscopy (TEM). Both the $\theta$-2$\theta$ method and rocking curve measurement suggest that Al/Ti thin films deposited on $SiO_2$have stronger texture than those deposited on low-k polymer. The texture of Al thin films strongly depended on that of Ti films. Cross-sectional TEM revealed that grains of Ti films on $SiO_2$substrates had grown perpendicular to the substrate, while the grains of Ti alms on SiLK substrates were formed randomly. The lower degree of (111) texture of Al thin films on low-k polymer was due to Ti underlayer.

• Korean Journal of Materials Research
• /
• v.11 no.12
• /
• pp.1086-1090
• /
• 2001

Composition effects on microstructure and metallizing properties of the alumina sintered body were evaluated to develop the metallized alumina tubes having superior properties for electronic devices. SEM observation revealed that resultant micrographs and fractographs were varied with composition chance of additives and $SiO_2$-rich specimens showed better microstructural characteristics with uniform distribution of fine and round particles than other CaO-rich or MgO-rich ones. The resultant interfacial microstructure of the $SiO_2$-rich metallized alumina tubes also showed good metallizing properties with no defects between layers and uniform thickness of metallizing layer.

• Journal of the Korean Ceramic Society
• /
• v.45 no.2
• /
• pp.94-98
• /
• 2008

Silicon nitride($Si_3N_4)$ is one of the most widely used structural ceramic materials. However silicon nitride is difficult to sinter because of its strong covalent bonding characteristics. In this study, $Si_3N_4$ ceramics were fabricated by spark plasma sintering process with $Y_2O_3$ and $Al_2O_3$ addition to improve the sinterability and the mechanical properties and their phase transformation behavior, microstructure and mechanical properties were evaluated. Fully densified $Si_3N_4$ ceramics could be obtained by spark plasma sintering process at a lower temperature than conventional sintering method. The formation of network microstructure was affected by the addition of $Al_2O_3$ because it could accelerate a to ${\alpha}$ to ${\beta}$ phase transformation of $Si_3N_4$. As a result, the mechanical properties depended on amounts of $Al_2O_3$ addition. The hardness value increased with increasing ${\alpha}$-phase fraction, but fracture toughness value increase with increasing ${\beta}$-phase fraction.

• Journal of Conservation Science
• /
• v.22
• /
• pp.43-60
• /
• 2008

This study is investigated the characteristics and the comparison on blackware and whiteware at Gilmyeong-ri kilns, located Poncheon-si, Geonggi province at AD 19c using scientific analysis. It is measured by scientific analysis classified as microstructure observation, physical methods which involved chromaticity, specific gravity, absorption ratio and porosity, and chemical analysis of components of body and glaze. As a result, a particle and a pore of body surface appeared differently by the degree of vitrification. In glaze, Blackware have better on good vitrification than whiteware in the microstructure observation. The physical characteristics of chromaticity, specific gravity, absorption ratio and porosity differed according to degree of vitrification rather than porcelain types. In composition, body of blackware have higher ratio of $Fe_2O_3$ and $TiO_2$ than of whiteware. Also glaze of blackware have higher ratio of $Fe_2O_3$ and $TiO_2$, and lower ratio of $SiO_2$ and $Al_2O_3$ than whiteware. Especially, blackware have higher ratio in the composition of CaO and $P_2O_5$ by which ash is used or not.