• Proceedings of the KIEE Conference
• /
• 1999.11d
• /
• pp.918-920
• /
• 1999

Recently, the ceramics of high permittivity are applied to DRAM and FRAM. In this study, (Ba, Sr)$TiO_3$ (BST) ceramics thin films were prepared by Sol-Gel method. BST solution was made and spin-coated on Pt/$SiO_2$/Si substrate at 4000[rpm] for 10 seconds. Coating process was repeated 3 times and then sintered at $750[^{\circ}C]$ for 30 minutes. Each specimen was analyzed structure and electrical characteristics. Thickness of BST ceramics thin films are about $2000[\AA]$. Dielectric constant and loss of thin films was little decreased at $1[kHz]{\sim}1[MHz]$. Dielectric constant and loss to frequency were 250 and 0.02 in BST3. In accordance with applied voltage, property of leakage current was stability when the was $0{\sim}3$[V]. According to voltage, leakage current was increased exponentially at $4{\sim}7$[V].

• Korean Chemical Engineering Research
• /
• v.51 no.2
• /
• pp.214-220
• /
• 2013

Hydrophobic coating on a silicate-based yellow phosphor ($Sr_2SiO_4:Eu^{2+}$) was carried out by using hexamethyldisiloxane (HMDSO) precursor in an atmospheric pressure dielectric barrier discharge plasma reactor, eventually to improve the long-term stability and reliability of the phosphor. The phosphor powder samples were characterized by a scanning electron microscope (SEM), a transmission electron microscope (TEM), a fluorescence spectrophotometer and a contact angle analyzer. After the coating was prepared, the contact angle of the phosphor powder increased to $133.0^{\circ}$ for water and to $140.5^{\circ}$ for glycerol, indicating that a hydrophobic layer was formed on its surface. The phosphor coated with HMDSO exhibited photoluminescence enhancement up to 7.8%. The SEM and TEM images of the phosphor powder revealed that the plasma coating led to a morphological change from grain-like structure to smooth surface with 31~46 nm thick hydrophobic layer. The light emitting diode (3528 1 chip LED) fabricated with the coated phosphor showed a substantial enhancement in the reliability under a special test condition at $85^{\circ}C$ and 85% relative humidity for 1,000 h (85/85 testing). The plasma-mediated method proposed in this work may be applicable to the formation of 3-dimensional coating layer on irregular-shaped phosphor powder, thereby improving the reliability.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2012.11a
• /
• pp.16-16
• /
• 2012

Mg and its alloys have been of great interest because of their low density of 1.7, 30% lighter than Al, but their wide applications have been limited because of their poor resistances against corrosion and/or abrasion. Corrosion resistance of Mg alloys can be improved by formation of anodic films using anodic oxidation method in aqueous electrolytes. Plasma electrolytic oxidation (PEO) is one of anodic oxidation methods by which hard anodic films can be formed as a result of micro-arc generation under high electric field. PEO method utilize not only substrate elements but also chemical components in electrolytes to form anodic films on Mg alloys. PEO films formed on AM50 magnesium alloy in an acidic fluozirconate electrolyte were observed to consist of mainly $ZrO_2$ and $MgF_2$. Liu et al reported that PEO coating on AM30 Mg alloy consists of $MgF_2$-rich outer porous layer and an MgO-rich dense inner layer. PEO films prepared on ACM522 Mg die-casting alloy in an aqueous phosphate solution were also reported to be composed of monoclinic $Mg_3(PO_4)_2$. $CeO_2$-incorporated PEO coatings were also reported to be formed on AZ31 Mg alloys in $CeO_2$ particle-containing $Na_2SiO_3$-based electrolytes. Magnesium tin hydroxide ($MgSn(OH)_6$) was also produced on AZ91D alloy by PEO process in stannate-containing electrolyte. Effects of $OH^-$, $F^-$, $PO{_4}^{3-}$ and $SiO{_3}^{2-}$ ions and alloying elements of Al and Sn on the formation of PEO films on pure Mg and Mg alloys and their protective properties against corrosion have been investigated in this work. $PO{_4}^{3-}$, $F^-$ and $SiO{_3}^{2-}$ ions were observed to contribute to the formation of PEO films but $OH^-$ ions were found to break down the surface films under high electric field. The effect of pulse current on the formation of PEO films will be also reported.

• Textile Coloration and Finishing
• /
• v.35 no.1
• /
• pp.8-19
• /
• 2023

Silicone rubber is widely used in most industries due to diverse advantages like heat stability, UV stability, durability, chemical resistance, environment friendliness, inertness and so on. But there is limitation to expand applications due to relatively weak rubber strengths such as tensile strength and tear strength, especially in fabric coating applications. The purpose of this study is to find influence of coating agent on performances of rubber and coated fabrics and their correlation according to different crosslinking densities of silicone rubbers. Addition cure type of silicones were formulated using crosslinked MQ-type silicone resin consisting of M (R₃SiO_1/2) and Q (SiO_4/2) and linear polymers. Raw materials used were; 1) linear vinyl endblocked polymers and vinyl functional MQ resin as main polymers, 2) linear silicone hydride polymers as crosslinkers, 3) platinum catalyst and 4) inhibitor to control curing speed. Rubber specimens were prepared to check mechanical strength using universal testing machine (UTM). Crosslinking density was calculated using Flory-Rhener equation using solvent swelling method. Differential scanning calorimetry (DSC) and scanning electron microscope (SEM-EDS) were used to characterize rubbers. Consequently, it was found that physical properties of silicone rubbers and coated fabrics can be expected by crosslinking density of rubbers. Silicone rubber formulations that contain 20 ~ 30 wt% of vinyl MQ resin showed strongest balanced performances.

• Journal of the Korean Ceramic Society
• /
• v.30 no.1
• /
• pp.17-24
• /
• 1993

Sol-gel spin-coating technique was used to produce Nb2O5 thin films on silicon substrates from Nb(OC2H5)5 precursor. The films were heat-treated at temperatures between $600^{\circ}C$ and 100$0^{\circ}C$ in oxygen atmosphere and their crystalline phases, chemical states, and dielectric characteristics were investigated by X-ray diffractometry (XRD), Auger electron spectroscopy (AES), and C-V measurements, respectively. After 1 hour heat-treatment at 80$0^{\circ}C$, T-type Nb2O5 was formed, and its chemical composition was homogeneous with no appreciable SiO2 oxide at interfaces between the films and substrates. The films heat-treated at temperatures between $600^{\circ}C$ and 80$0^{\circ}C$ exhibit dielectric constant of less than 20 while the films heat treated at 100$0^{\circ}C$ show dielectric constant of 28.

• Korean Journal of Materials Research
• /
• v.33 no.4
• /
• pp.115-123
• /
• 2023

In this paper, we report and discuss the semi-permanently hydrophilic (SPH) treatment of polyester fabric using plasma polymerization and oxidation based on atmospheric pressure dielectric barrier discharge (APDBD) technology. SiO_xC_y(-H) was coated on polyester fabric using Hexamethylcyclotrisiloxane (HMCTSO) as a precursor, and then plasma oxidation was performed to change the upper layer of the thin film to SiO₂-like. The degradation of hydrophilicity of the SPH polyester fabrics was evaluated by water contact angle (WCA) and wicking time after repeated washing. The surface morphology of the coated yarns was observed with scanning electron microscopy, and the presence of the coating layer was confirmed by measuring the Si peak using energy dispersive x-ray spectroscopy. The WCA of the SPH polyester fabric increased to 50 degrees after 30 washes, but it was still hydrophilic compared to the untreated fabric. The decrease in hydrophilicity of the SPH fabric was due to peeling of the SiO_xC_y(-H) thin film coated on polyester yarns.

• Journal of the Korean Ceramic Society
• /
• v.31 no.7
• /
• pp.795-803
• /
• 1994

Ferroelectric BaTiO3 thin film was produced using BaTi-ethoxide sol. This sol was prepared from BaTi-ethoxide by a partial hydrolysis with ammonia as a basic catalyst and ethylene glycol as a chelating agent. BaTiO3 thin film was prepared from three continuous spin-coating layers of the sol on bare Si(100) wafer at 2500 rpm followed by pyrolysis at $700^{\circ}C$ for 30 min. After the heat treatment, the film was 0.200$\pm$0.010 ${\mu}{\textrm}{m}$ thick and its grain size was 0.059 ${\mu}{\textrm}{m}$. On the other hand, electrical properties were measured for BaTiO3 thin film separately prepared on Au-deposited silicon wafer. The dielectric constant and loss of the BaTiO3 thin film at room temperature was 150~160 and 0.04 respectively, which was measured at 10 kHz and oscillation level of 0.1 V. In the measurements of the dielectric properties at high temperatures, it was observed that the capacitance of the thin film increases steeply, while the dielectric loss reaches maximum around 1$25^{\circ}C$, which corresponds a phase transition from tetragonal to cubic BaTiO3.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2010.02a
• /
• pp.451-451
• /
• 2010

최근들어 80인치 이상의 대경 고화질 display 및 휴대용 projection display 제작이 가능한 LCoS (Liquid Crystal on Silicon) display에 대한 관심이 높아지고 있다. LCoS projection display는 높은 개구율, 빠른 응답속도, 고화질, 대형 디스플레이 임에도 불구하고 낮은 제조단가 등의 여러 가지 장점을 가지고 있다. LCoS projection display의 핵심 기술로는 높은 투과도와 낮은 반사율을 갖는 유리기판, 무기 배향막 증착 기술, Si back plane과의 접합기술 등이 있다. 이 중 LCoS projection display 제작을 위한 첫 단계인 유리기판은 가시광선 영역에서 96% 이상의 높은 투과도와 3% 미만의 반사도를 요구하는 기술을 필요로 한다. 본 연구에서는 indium이 doping된 tin oxide (ITO)를 투명 전도성막으로 사용하고, $SiO_2/MgF_2$ 이중 박막을 반사방지막으로 채택하여 고투과도 및 저반사율을 갖는 유리기판 제조에 응용하였다. 먼저 15nm 두께의 ITO 박막을 DC sputtering을 이용하여 8-inch 크기의 corning1737 유리기판 상에 증착한 후, 그 반대편에 e-beam evaporation 장비를 사용하여 120nm 두께의 반사 방지막을 증착하였다. 또한 유리기판 상에 증착된 투명 전도성막의 표면개질을 위하여 Ar plasma를 이용하여 treatment를 수행하였다. 이 때 sputtering 조건은 DC power, Ar 유량 및 압력을 조절함으로서 높은 투과도를 갖는 최적의 조건을 구현하였고, e-beam evaporation을 이용한 반사방지막 증착 조건은 $SiO_2$와 $MgF_2$의 계면에서 빛의 반사를 최소화할 수 있는 최적의 조건을 구현하였다. 제작된 유리기판은 가시광선 영역에서 97% 이상의 투과도를 보였으며, 최대 2.8%의 반사율을 보여, LCoS display 제작에 적합함을 확인할 수 있었다. 또한 Ar plasma 처리 후 ITO 박막의 면저항 값은 $100\;{\omega}/{\Box}$, 표면 거칠기는 rms 값 기준 0.095nm, 접촉각 $20.8^{\circ}$의 특성을 보여, 타 index matched transparent conducting oxide가 coating된 유리기판에 비해 우수한 특성을 보였다.

• Proceedings of the Membrane Society of Korea Conference
• /
• 1994.04a
• /
• pp.57-57
• /
• 1994

졸-겔 침지코팅 (dipcoating) 또는 가압 졸-겔 코팅 (pressurized coating) 법으로 제조한 $\gamma-Al_2O_3, SiO_2, TiO_2$ 및 aluminosilicate 복합막에 대하여 $CO_2$, He, $N_2$, 및 $O_2$ 기체 투과율과 $CO_2$ 분리계수를 측정하였다. 이들 막을 통한 모든 기체의 이동은 Knudsen 유동이 지배적이었으며 $CO_2/N_2$의 분리계수는 0.9 ~ 1.1 정도로 Knudsen 분리계수 ($CO_2/N_2$의 경우 0.8)보다 약간 높은 값을 보여주었다. $CO_2$ 분리계수를 향상시키기 위하여 silane coupling 및 산화물 도핑법에 의한 복합막의 표면개질을 시도하였으며 분리막의 재질 및 표면개질 조건에 따른 $CO_2/N_2$ 분리계수 변화를 측정 비교하였다. Silane coupling에 의한 표면개질이 $CO_2$의 표면 친화성 (affinity)에 의한 표면확산속도를 증가시키기 때문에 $CO_2$ 분리에 있어서 산화물 도핑에 의한 표면개질보다 더욱 효과적이었다.

• Korean Journal of Optics and Photonics
• /
• v.23 no.3
• /
• pp.124-127
• /
• 2012

We designed and fabricated dichroic filters for high-power fiber lasers to protect the pumping laser diode from counterpropagating laser beams. The transmittance at laser diode wavelengths of 905 nm~925 nm was designed to be less than 0.1% and the transmittance at the fiber laser or Brillouin scattering wavelengths of 1020 nm ~ 1100 nm was designed to be more than 99.9%. Since oxide materials have good adhesion to the $SiO_2$ substrate, $SiO_2/Ta_2O_5$ were used as coating materials. The filter was fabricated according to our optimized design and its characteristics were compared with the theoretical design. As a result, the transmittance at laser diode wavelengths of 905 nm~925 nm was measured to be less than 0.1%, and the transmittance at the fiber laser or Brillouin scattering wavelengths of 1020 nm~1100 nm was measured to be more than 95.5%, which coincided well with the theoretical design considering processing errors. The filter was found to operate well over 1W of input laser power.