본 연구에서는 RF Magnetron Sputtering 법으로 94:6 wt%의 비율로 Sb가 첨가된 $SnO_2$ 타겟을 사용하여 실온에서 ATO(Antimony doped Tin Oxide) 박막을 증착하고, 열처리가 ATO 박막의 구조적, 전기적, 광학적 특성에 미치는 효과를 연구하고자 하였다. ATO 박막의 두께는 약 200 nm로 증착하였으며, 실험 조건으로는 Ar 유량을 100 seem, 진공도는 1, 5, 10 mTorr로 변화시켰으며 스퍼터링 파워는 100, 150, 200, 250 W로 조절하였다. 증착되어진 박막은 vacuum 상태에서 300, $600^{\circ}C$의 온도에서 열처리를 수행하였으며 결과적으로 스퍼터링 파워가 증가함에 따라 비저항이 감소하였고, 250 W의 파워와 10 mTorr의 공정압력 조건에서 $600^{\circ}C$로 열처리한 ATO 박막은 $5{\times}10^{-3}{\Omega}-cm$의 저항률과 85.3%의 높은 투과도를 가지는 우수한 투명 전도막을 얻을 수 있었다.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2003.10a
• /
• pp.119-119
• /
• 2003

Plasma polymerized organic thin films were deposited on Si(100) glass and Copper substrates at 25 ∼ 100 $^{\circ}C$ using cyclohexane and ethylcyclohexane precursors by PECVD method. In order to compare physical and electrochemical properties of the as-grown thin films, the effects of the RF plasma power in the range of 20∼50 W and deposition temperature on both corrosion protection efficiency and physical properties were studied. We found that the corrosion protection efficiency (P$\_$k/), which is one of the important factors for corrosion protection in the interlayer dielectrics of microelectronic devices application, was increased with increasing RF power. The highest P$\_$k/ value of plasma polymerized ethylcyclohexane film (92.1% at 50 W) was higher than that of the plasma polymerized cyclohexane film (85.26% at 50 W), indicating inhibition of oxygen reduction. Impedance analyzer was utilized for the determination of I-V curve for leakage current density and C-V for dielectric constants. To obtain C-V curve, we used a MIM structure of metal(Al)-insulator(plasma polymerized thin film)-metal(Pt) structure. Al as the electrode was evaporated on the ethylcyclohexane films that grew on Pt coated silicon substrates, and the dielectric constants of the as-grown films were then calculated from C-V data measured at 1㎒. From the electrical property measurements such as I-V ana C-V characteristics, the minimum dielectric constant and the best leakage current of ethylcyclohexane thin films were obtained to be about 3.11 and 5 ${\times}$ 10$\^$-12/ A/$\textrm{cm}^2$ and cyclohexane thin films were obtained to be about 2.3 and 8 ${\times}$ 10$\^$-12/ A/$\textrm{cm}^2$.

• Journal of electromagnetic engineering and science
• /
• v.7 no.3
• /
• pp.103-108
• /
• 2007

In this paper, a low-power 2.4 GHz front-end for sensor network application (IEEE 802.15.4 LR-WPAN) is designed in a 0.18 um CMOS process. A power supply circuit with a novel temperature-compensation scheme is presented. The simulation and measurement results show that the front-end (LNA, Mixer) can achieve a voltage gain of 35.3 dB and a noise figure(NF) of 3.1 dB while consuming 5.04 mW (LNA: 2.16 mW, Mixer: 2.88 mW) of power at $27^{\circ}C$. The NF includes the loss of BALUN and BPF. The low-IF architecture is used. The voltage gain, noise figure and third-order intercept point (IIP3) variations over -45$^{\circ}C$ to 85$^{\circ}C$ are less than 0.2 dB, 0.25 dB and 1.5 dB, respectively.

• Journal of Integrative Natural Science
• /
• v.13 no.3
• /
• pp.87-91
• /
• 2020

Molybdenum carbide (MoC_x) thin films (TFs) were deposited by reactive radio frequency (rf) magnetron co-sputtering in high vacuum chamber. We compared the properties of MoC_x thin films as the rf power changed on C target. The result of alpha step measurement showed that the thickness of the MoC_x TFs varied from163.3 to 194.86 nm as C power was increased from 160 to 200 W. The crystallinity of MoC_x such as b-Mo₂C, Mo₂C, and diamond like carbon (DLC) structures were observed by XRD. The oxidation states of Mo and C were determined using high resolution XPS spectra of Mo 3d and C 1s were deconvoluted. Molybdenum was consisted of Mo, Mo⁴⁺, and Mo⁶⁺ species. And C was deconvoluted to C-Mo, C, C-O, and C=O species.

• The Korean Journal of Ceramics
• /
• v.7 no.2
• /
• pp.85-92
• /
• 2001

Thin films of ZnO and Al doped ZnO were prepared by rf magnetron sputter techniques. When the oxygen fraction in Ar-O$_2$ sputter gas was about 2.0%, the films exhibited the composition of Zn:O=1.05:1. The films prepared at 250 W contain larger grains than the films grown at 100 W. However, high deposition rate seems to deteriorates the crystallinity as well as Al-substitution, resulting in lower concentration of mobile electrons. The Al-doped ZnO films which were deposited at $500^{\circ}C$ show resistance of 1$\times$10$^-2$ Wcm; optical band gap of the films ranges from 3.25 to 3.40 eV. These electrical and optical features are related with microstructural as well as crystalline characteristics of the films.

• 한국생물공학회:학술대회논문집
• /
• 2000.11a
• /
• pp.626-629
• /
• 2000

The Pseudomonas aeruginosa BYK-2(KCTC 18012p) produced three kinds of glycolipids on olive oil as a substrate and purified two types of major glycolipids(Rf=0.48, BS-1; Rf=0.65, BS-2) using silica gel chromatography, TLC, HPLC, etc. From the analysis of the chemical structure, the glycolipid of BS-1 was estimated as rhamnolipid($2-O-{\alpha}-L-rhamnopyranosyl- {\alpha}-L-rhamnopyranosyl-{\beta}-hydroxyldecanoyl-{\beta}-hydroxydecanoic$ acid; M.W. 650) and BS-2 was detected as rhamnolipid methyl ester($2-O-{\alpha}-L-rhamnopyranosyl-{\alpha}-L-rhamnopyranosyl-{\beta}-hydroxyldecanoyl-{\beta}-hydroxydecanoic$ acid methyl ester; M.W. 664) by FT-IR, FAB Mass spectrometry, $^1H-NMR$, $^{13}C$ FT-NMR, DEPT, 2D-NMR (TOCSY, RELAY, NOESY, HSQC, HMBC). In particular, It was found that a marine bacterium Pseudomonas aeruginosa BYK-2(KCTC 18012P) remarkably produced rhamnolipid and rhamnolipid methyl ester simultaneously.

• KIEE International Transactions on Electrophysics and Applications
• /
• v.5C no.3
• /
• pp.124-130
• /
• 2005

In this paper, we designed a cylindrical type light source having an electromagnetic principle of inductively coupled plasma, and measured its electrical-optical properties. Using the transformer principle, an electrically equivalent circuit cylindrical type light source was analyzed. According to the parameters of electromagnetic induction, which were diameter of coil with cpO.3$\~$ 1.2mm, number of turns with 4$\~$ 12 turns, distance with 40$\~$ l20mm and RF power with 10$\~$ 150W, the electrical .md optical properties were measured. When the diameter of the coil was cp0.3mm, number of turns was 8 and distance was 40mm, and the maximum brightness of 29,730 cd/m$^{2}$ was shown with RF power l50W. The relationship between electromagnetic induction and plasma discharges was demonstrated using the mode transition from E-mode to H-mode

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.8 no.2
• /
• pp.440-448
• /
• 2004

In this paper, to make a solar cell of II-Ⅵ ZnTe compound semiconductor, we studied for the property of the transparent electrode(AZO) and Buffer layer(ZnO), and for reducing the energyband gap of optical absorber layer which are most effective on its efficiency. The ZnTe thin film was used the optical absorber layer of solar cell. Zn and Te were deposited using the co-sputtering method. The thin film was sputtered RF power of Zn/50W and Te/30W, respectively and a substrate temperature of foot under Ar atmosphere of 10mTorr. The energy band gap of the thin film was 1.73ev Then the thin film was annealed at $400^{\circ}C$ for 10sec under a vacuum atmosphere. The energy band gap of 1.67eV was achieved and the film composition ratio of Zn and Te was 32% and 68%. At the best condition, the Solar Cell was manufactured and the efficiency of 6.85% (Voc: 0.69V, Jsc: 21.408㎃/$cm^2$, Fill factor (FF): 0.46) was achieved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.18-19
• /
• 2006

The bismuth zinc niobate(BZN) pyrochlore thin films were fabricated on Pt(111)/Ti/$SiO_2$/p-Si(100) substrates using a reactive rf magnetron sputtering method at the conditions of working gas ratio Ar:$O_2$=90:10, substrate temperate $R.T{\sim}600^{\circ}C$, rf power 50 W. The dielectric constant, tunability, leakage current density and crystallinity of thin films changed with a substrate temperate. The BZN pyrochlore thin films sputtered with a substrate temperature of $600^{\circ}C$ and RTA at $800^{\circ}C$ showed a leakage current density lower than $10^{-8}\;A/cm^2$ at the range of ${\pm}300\;kV/cm$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.892-895
• /
• 2003

This paper describes on RIE(Reactive Ion Etching) characteristics of 3C-SiC(Silicon Carbide) grown on Si(100) wafers. During RIE of 3C-SiC films in this work, $CHF_3$ gas is used to form of polymer as a side wall for excellent anisotropy etching. From this process, etch rates are obtained a $60{\sim}980{\AA}/min$ by various conditions such as $CHF_3$ gas flux, $O_2$ addition ratio, RF power and electrode distance. Also, approximately $40^{\circ}$ mesa structures are successfully formed at 100 mTorr $CHF_3$ gas flow ratio, 200 W RF power and 30 mm electrode distance. Moreover, vertical side wall is fabricated by anisotropy etching with 50% $O_2$ addition ratio and 25 mm electrode distance. Therefore, RIE of 3C-SiC films using $CHF_3$ could be applicable as fabrication process technology for high-temperature 3C-SiC MEMS applications.