• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.79-79
• /
• 2012

A high temperature and a low temperature plasma process technologies were developed and demonstrated for synthesis, hybrid formation, surface treatment and CVD engineering of nano powder. RF thermal plasma is used for synthesis of spherical nano particles in a diameter ranged from 10 nm to 100 nm. A variety of nano particules such as Si, Ni, has been synthesized. The diameter of the nano-particles can be controlled by RF plasma power, pressure, gas flow rate and raw material feed rate. A modified RF thermal plasma also produces nano hybrid materials with graphene. Hemispherical nano-materials such as Ag, Ni, Si, SiO2, Al2O3, size ranged from 30 to 100 nm, has been grown on graphene nanoplatelet surface. The coverage ranged from 0.1 to 0.7 has been achieved uniformly over the graphene surface. Low temperature AC plasma is developed for surface modification of nano-powder. In order to have a three dimensional and lengthy plasma treatment, a spiral type of reactor has been developed. A similar plasma reactor has been modfied for nano plasma CVD process. The reactor can be heated with halogen lamp.

• Proceedings of the KIEE Conference
• /
• 2008.07a
• /
• pp.1203-1204
• /
• 2008

본 논문에서는 ICP-CVD(Inductively Coupled Plasma Chemical Vapor Deposition)를 이용해 기판을 가열하지 않고 증착한 $SiO_2$ 절연막의 플라즈마 처리 효과를 분석하였다. 플라즈마 처리를 하지 않은 $SiO_2$ 절연막의 경우 평탄화 전압이 -7.8V, 유효 전하 밀도가 $4.77{\times}10^{13}cm^2$로 열악한 특성을 보였다. 이를 개선하기 위해 헬륨 플라즈마 전처리(Pre-treatment)와 수소 플라즈마 후처리(Post-treatment)를 통해서 $SiO_2$ 절연막의 전기적인 특성을 개선하였다.

• Resources Recycling
• /
• v.25 no.6
• /
• pp.92-97
• /
• 2016

Spray dried $Cr_2O_3$ powder having an agglomerated structure of particles was twice treated into a plasma flame to increase its apparent density. The powder subjected to the first densification treatment did not show the entirely melted state keeping inner particle hollows, and it was fully melted after the second processing only. The powder size as a result of the second treatment decreased, and the apparent density as well as flowability were increased due to melting and surface smoothing effects. But a part of particles after the second densified treatment showed the hollow structure, especially those which were above $30{\mu}m$ in size. This densification behavior of the powder has been qualitatively discussed in terms of the thermal conductivity and inner gas pressure within aggregates exposed to the plasma flame.

• Bulletin of the Korean Chemical Society
• /
• v.31 no.2
• /
• pp.335-338
• /
• 2010

In this study, the atmospheric plasma treatment with $He/O_2$ was conducted to modify the surface chemistry of carbon fibers. The effects of plasma treatment parameters on the surface energetics of carbon fibers were experimentally investigated with respect to gas flow ratio, power intensity, and treatment time. Surface characteristics of the carbon fibers were determined by X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM), Fourier transform infrared (FT-IR), Zeta-potential, and contact angle measurements. The results indicated that oxygen plasma treatment led to a large amount of reactive functional groups onto the fiber surface, and these groups can form together as physical intermolecular bonding to improve the surface wettability with a hydrophilic polymer matrix.

• Journal of the Korean Vacuum Society
• /
• v.19 no.4
• /
• pp.275-280
• /
• 2010

The influence of $O_2$-plasma treatment on $H_2$ post-treated BZO (ZnO:B) thin film using MOCVD (Metal-Organic Chemical Vapor Deposition) are investigated. An $O_2$-plasma treatment of the $H_2$ post-treated BZO thin films resulted in XRD peak of (100), (101) and (110). Also, electrical properties resulted in an increase in sheet resistance and work function. The weighted optical transmittance and haze at 300~1,100 nm of BZO thin films with $O_2$-plasma treatment on the $H_2$ post-treatment show approximately 86% and 15%, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.2
• /
• pp.111-117
• /
• 2008

We have studied surface roughness, contamination of impurity, bonding with some gas element, reflectance and zeta potential on masks to be generated or changed during photolithography/dry or wet etching process. Mask surface roughness was not changed after photolithography/dry etching process. But surface roughness was changed on some area under MoSi film of Cr/MoSi/Qz. There was not detected any impurity on mask surface after plasma dry etching process. Reflectance of mask was increased after variable plasma etching treatment, especially when mask was treated with plasma including $O_2$ gas. Blank mask was positively charged when the mask was treated with Cr plasma etching gas($Cl_2:250$ sccm/He:20 $sccm/O_2:29$ seem, source power:100 W/bias power:20 W, 300 sec). But this positive charge was changed to negative charge when the mask was treated with $CF_4$ gas for MoSi plasma etching, resulting better wet cleaning. There was appeared with negative charge on MoSi/Qz mask treated with Cr plasma etching process condition, and this mask was measured with more negative after SC-1 wet cleaning process, resulting better wet cleaning. This mask was charged with positive after treatment with $O_2$ plasma again, resulting bad wet cleaning condition.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.118-120
• /
• 2009

We reported that the evidence of oxygen doping to copper-phthalocyanine (CuPc) by $O_2$-plasma treatment to Au electrode of inverted top emitting organic light emitting diodes (ITOLEDs). The operation voltage of OLEDs at 150 mA/$cm^2$ decreased from 16.1 to 10.3 V as oxygen atoms indiffued to CuPc layer using $O_2$-plasma. Synchrotron radiation photoelectron spectroscopy results showed that a new bond of Cu-O appeared and the energy difference between the highest occupied molecular orbital and $E_F$ is lowered by 0.20 eV after plasma treatment. Thus the hole injection barrier was lowered, reducing the turn-on voltage and increasing the quantum efficiency of OLEDs.

• Textile Coloration and Finishing
• /
• v.4 no.2
• /
• pp.76-83
• /
• 1992

Wool tropical and nylon taffeta were treated with low temperature plasma of $O_2$, $N_2$, NH$_3$, CF$_4$ and CH$_4$ for the intervals of 10 to 300 sec, and then dyed with leveling and milling type acid dyes in presence or absence of buffer solution. From the color depth of dyed fabrics, effect of plasma gases, treated time, dyeing time and temperature on dyeing property was studied. The results of the experiment can be summarized as follows: 1) The plasma treatments except methane gas increased the color depth of dyed wool fabrics, but not that of dyed nylon fabrics regardless of the plasma gases used. 2) The color depth of wool fabrics dyed in the dye bath without buffer solution was increased by the low temperature plasma, especially increased much more by CF$_4$ plasma treatment. It is found that with the identification of F- ion in the residual dye bath the hydrogen fluoride gas was adsorbed on wool fabrics in the plasma treatment. 3) The color depth of wool fabrics was increased with the time of $O_2$ and CF$_4$ plasma treatments. 4) In both cases of the leveling and milling type acid dyes, the rate of dyeing was increased in the low temperature plasma treatments, and it is found that the leveling type acid dye increased the color depth at relatively low temperature below 4$0^{\circ}C$, compared with the milling type acid dye.

• Proceedings of the KIEE Conference
• /
• 1993.07b
• /
• pp.1147-1149
• /
• 1993

ZnO/$SnO_2$:F bilayer films have been prepared by pyrosol deposition method to develop optimum transparent electrode for use in amorphous silicon solar cells. The solution for $SnO_2:F$ film was composed of $SnCl_4{\cdot}5H_2O,\;NH_4F,\;CH_3OH$ and HCl, and ZnO films have been deposited on the $SnO_2:F$ films by using the solution of $ZnO(CH_3COO){_2}{\cdot}2H_2O,\;H_2O\;and\;CH_3OH$. These films have been investigated the variation of electrical and optical properties under the hydrogen plasma exposure. The sheet resistance of the $SnO_2:F$ film was sharply increased and its transmittance was decreased with the blackish effect after plasma treatment. However, the ZnO/$SnO_2:F$ bilayer film was shown hydrogen plasma durability because the electrical and optical properties was almost unchanged more then 60 seconds exposure time.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2002.08a
• /
• pp.621-624
• /
• 2002

In this study, outgassing characteristics of MgO films, and the plasma cleaning effects of the deposited MgO films by atmospheric pressure plasma on outgassing rate were compared. The MgO layer was heated up to 350 $^{\circ}C$ and the outgassing characteristics were observed for the heated conditions. As the main impurity species $H_2,\;H_2O,\;N_2,\;CO_2,\;and\;H_2O$ were released from this panel. Impurity species of plasma treatment panel were lower than non-treated panels for the heating temperature