A Li$[Co_{0.17}Li_{0.28}Mn_{0.55}]O_2$ cathode compound was prepared by a simple combustion method. The X-ray diffraction pattern showed that this compound could be classified as ${\alpha} -NaFeO_2$ structure type with the lattice constants of a = 2.8405(9) ${\AA}$ and c = 14.228(4) ${\AA}$. According to XANES analysis, the oxidation state of Mn and Co ions in the compound were 4+ and 3+, respectively. During the first charge process, the irreversible voltage plateau at around 4.65 V was observed. The similar voltage-plateau was observed in the initial charge profile of other solid solution series between $Li_2MnO_3\;and\;LiMnO_2$ (M=Ni, Cr...). The first discharge capacity was 187 mAh/g and the second discharge capacity increased to 204 mAh/g. As the increase of cycling number, one smooth discharge profile was converted to two distinct sub-plateaus and the discharge capacity was slowly decreased. From the Co and Mn K-edge XANES spectra measured at different cyclic process, it can be concluded that irreversible transformation of phase is occurred during continuous cycling process.

• Journal of Electrochemical Science and Technology
• /
• v.13 no.3
• /
• pp.407-415
• /
• 2022

Surface coating of cathodes is an essential process for all-solid-state batteries (ASSBs) based on sulfide electrolytes as it efficiently suppresses interfacial reactions between oxide cathodes and sulfide electrolytes. Based on computational calculations, Li₃PO₄ has been suggested as a promising coating material because of its higher stability with sulfides and its optimal ionic conductivity. However, it has hardly been applied to the coating of ASSBs due to the absence of a suitable coating process, including the selection of source material that is compatible with ASSBs. In this study, polyphosphoric acid (PPA) and (NH₄)₂HPO₄ were used as source materials for preparing a Li₃PO₄ coating for ASSBs, and the properties of the coating layer and coated cathodes were compared. The Li₃PO₄ layer fabricated using the (NH₄)₂HPO₄ source was rough and inhomogeneous, which is not suitable for the protection of the cathodes. Moreover, the water-based coating solution with the (NH₄)₂HPO₄ source can deteriorate the electrochemical performance of high-Ni cathodes that are vulnerable to water. In contrast, when an alcohol-based solvent was used, the PPA source enabled the formation of a thin and homogeneous coating layer on the cathode surface. As a consequence, the ASSBs containing the Li₃PO₄-coated cathode prepared by the PPA source exhibited significantly enhanced discharge and rate capabilities compared to ASSBs containing a pristine cathode or Li₃PO₄-coated cathode prepared by the (NH₄)₂HPO₄ source.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.16.2-16.2
• /
• 2011

Graphene has attracted significant attention due to its unique characteristics and promising nanoelectronic device applications. For practical device applications, it is essential to synthesize high-quality and large-area graphene films. Graphene has been synthesized by eloborated mechanical exfoliation of highly oriented pyrolytic graphite, chemical reduction of exfoliated grahene oxide, thermal decomposition of silicon carbide, and chemical vapor deposition (CVD) on metal substrates such as Ni, Cu, Ru etc. The CVD has advantages over some of other methods in terms of mass production on large-areas substrates and it can be easily separated from the metal substrate and transferred to other desired substrates. Especially, plasma-enhanced CVD (PECVD) can be very efficient to synthesize high-quality graphene. Little information is available on the synthesis of graphene by PECVD even though PECVD has been demonstrated to be successful in synthesizing various carbon nanostructures such as carbon nanotubes and nanosheets. In this study, we synthesized graphene on $Ni/SiO_2/Si$ and Cu plate substrates with CH4 diluted in $Ar/H_2$ (10%) by using an inductively-coupled PECVD (ICPCVD). High-quality graphene was synthesized at as low as $700^{\circ}C$ with 600 W of plasma power while graphene layer was not formed without plasma. The growth rate of graphene was so fast that graphene films fully covered on substrate surface just for few seconds $CH_4$ gas supply. The transferred graphene films on glass substrates has a transmittance at 550 nm is higher 94%, indicating 1~3 monolayers of graphene were formed. FETs based on the grapheme films transferred to $Si/SiO_2$ substrates revealed a p-type. We will further discuss the synthesis of graphene and doped graphene by ICPVCD and their characteristics.

• Journal of Society of Preventive Korean Medicine
• /
• v.3 no.2
• /
• pp.151-170
• /
• 1999

This study was to investigate the metal accumulation from SipJeonDaeBo-Decoction to rat blood of Sprague Dawley. 1. There were no significance in body weight, water dose feed ingestion quantity, liver, kidney, brain, bone weights between the control and the experimental groups. Under the experiment with drinking waters was no metal ${\sim}\;0.65mg/L$ detected. Metal level within feed found 0.0001-376.983mg/kg. 2. In the pack of SipJeonDaeBo-decoction, there detected no metal ${\sim}2.086mg/L$ 3. After P.O(per os) SipJeonDaeBo-decoction, As is detected $2.390{\pm}0.812mg/kg$ in blood; Cd $0.001{\pm}0.001mg/kg$, Co $0.003{\pm}0.001mg/kg$, Cr $0.432{\pm}0.234mg/kg$, Cu $1.013{\pm}0.373mg/kg$, Fe $426.293{\pm}114.842mg/kg$, no Hg, Mn $0.109{\pm}0.082mg/kg$, Ni $0.122{\pm}0.068mg/kg$, Zn $3.584{\pm}1.270mg/kg$. 4. The concentration of Hazardous heavy metal (As, Cd, Co, Cr, Hg, Ni, Pb) within blood control group is searched $0.488{\pm}0.138\;mg/l$; experiment I group $0.432{\pm}0.080mg/l$, experiment II group $0.588{\pm}0.213mg/l$. In the concentration of non hazardous heavy metal(Cu, Fe, Mn, Zn) control group $101.409{\pm}6.832mg/l$; experiment I group $96.062{\pm}5.732\;mg/l$, experiment II group $125.139{\pm}044.820mg/l$. 5. Correlation among every metal in blood Zn and Cr was 0.87956 ; Cd and As -0.02316, Pb and As -0.08738, Ni and As 0.07824, Mn and As 0.07824, Mn and Cd 0.04999. Briefly under the injection of SipJeonDaeBo-decoction, this study was defined within safety in blood level by P.O. during 10 days.

• Journal of Environmental Health Sciences
• /
• v.24 no.3
• /
• pp.1-5
• /
• 1998

A spectrophotometric method was developed for the acidic solution stripped after an extraction of 0.5 to 2.5 ppm of Lead(II) from 50 mL of $Na_2S_2O_3$ solution into chloroform as the ion-pairs formed between their thiosulfate complexes and alkylamine, Aliquat336. Pb(II) in the stripped solution forms an complex with DDTC in pH 7.3 buffer solution, and was developed in yellow by copper replacement. The ydlow-colored solution have the maximum absorbance at 435 nm in the measurement of absorbance by UV-Visible spectrophotometer. The interference ions such as Fe(III), Hg (II), Al(III), Co, Cu, Ni, Zn, Ca, Sn, have great effects on the extraction, but they were overcomed by the usage of adequate masking agents before an extraction. At last, a good result was obtained in applying this method to synthetic water.

• Corrosion Science and Technology
• /
• v.7 no.2
• /
• pp.119-124
• /
• 2008

Steel is generally not corrosion resistant to water with formation of non protective rusts on its surface. Rusts are composed of iron oxides such as $Fe_3O_4$, $\alpha-$, $\beta-$, $\gamma-$and ${\delta}-FeOOH$. However, steel, particularly weathering steel containing small amounts of Cu, Ni and Cr etc., shows good corrosion resistance against rural, industrial or marine environment. Its corrosion rate is exceedingly small as compared with that of carbon steel. According to the exposure test results undertaken in outdoor environments, the atmospheric corrosion rate for weathering steel is only 1 mm for a century. Atmospheric corrosion for steels proceeds under alternate dry and wet conditions. Dry condition is encountered on steel surface on fine or cloudy days, and wet condition is on rainy or snowy days. The reason why weathering steel shows superior atmospheric corrosion resistance is due to formation of corrosion protective rusts on its surface under very thin water layer. The protective rusts are usually composed of two layer rusts; the upper layer is ${\gamma}-FeOOH$ termed as lepidocrocite, and inner layer is nano-particle ${\alpha}-FeOOH$ termed as goethite. This paper is aimed at elucidating the atmospheric corrosion mechanism for steel in comparison with corrosion in bulky water environment by use of empirical data.The summary is as follows: 1. No corrosion protective rusts are formed on steel in bulky water. 2. Atmospheric corrosion for steel is the corrosion under wetting and drying conditions. Corrosion and passivation occur alternately on steel surface. Steel, particularly weathering steel with small amounts of alloying elements such as Cu, Ni and Cr etc. enhances forming corrosion protective rusts by passivation.

• Korean Journal of Materials Research
• /
• v.9 no.7
• /
• pp.657-662
• /
• 1999

Mn-Ni oxide thin films for NTC thermistor application were sputtered on alumina substrates at $320^{\circ}C$ Effects of various oxygen partial pressures and annealing temperatures on the microstructure, crystal phase, resistivity and B constant were investigated. In general, microstructure of the films deposited was columnar grain structure. After annealing at $700^{\circ}C$, the microstructure was begun to transform to equiaxed grain structure. Most of the phases were mixture of cubic spinel and $Mn_2$$O_3$. As the oxygen concentration increased, the resistivity and B constant were greatly decreased, and these values become low and stable after annealing between $600^{\circ}C$ and $700^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.12 no.1
• /
• pp.3-9
• /
• 2002

The corrosion behavior of alloys in a molten salt was investigated along with the oxidation characteristics in the air. The basic composition of alloys in the study was Fe-25Ni-7Cr with Si and RE(rare-earth metal) as additives. The corrosion rate of the alloys was low in a molten salt of LiCl while the rate was high in the mixed molten salt of LiCl and $Li_2O$. When Si is added to the base alloy of Fe-25Ni-7Cr, corrosion resistance was improved as the Si content is increased up to 3%, however, it was observed that the corrosion resistance was getting worse as the Si content is increased. The base alloy with 2.43% of Si and 0.9% of RE(KSA-65), showed higher corrosion rate compared to that of KSA-63 alloy with an equivalent amount of only Si. The corrosion resistance of KSA-65 was similar to that of the base alloy(KSA-60). The oxidation resistance of KSA-65 alloy was greatly increased even at $850^{\circ}C$ for a long term exposure.

• Applied Chemistry for Engineering
• /
• v.34 no.6
• /
• pp.619-625
• /
• 2023

In order to solve problems caused by the heat load of hypersonic aircraft, this study examined the optimization of the Si/Al ratio of the catalyst and nickel ion exchange to improve the performance of the hydrocarbon decomposition reaction (endothermic reaction). It was confirmed that the catalysts prepared through Si/Al ratio optimization and nickel ion exchange showed about 10% improvement in heat absorption performance compared to thermal cracking at 4 MPa and 550 ℃. FT-IR and NH₃-TPD analyses were found to identify factors affecting activity changes, and it was observed that the Si/Al ratio of the HZSM-5 catalyst was closely correlated with acid site development and catalytic activity. In addition, TGA and O₂-TPO analyses were conducted to observe the carbon deposition inhibition properties of the nickel-added catalyst.

• Journal of the Mineralogical Society of Korea
• /
• v.23 no.4
• /
• pp.305-313
• /
• 2010

Mineralogical characteristics of Cu-Co ores from the Central African Copperbelt in the Democratic Repblic of Congo are studied using powder X-ray diffractometer, general area detector X-ray diffractometer, and electron proble microanalyzer. Black ores are mainly composed of heterogenite (cobalt oxide/hydroxide mineral) and malachite (copper carbonate mineral), whereas green ores are only composed of malachite. Heterogenite shows very bright white color under the reflected microscope, and belongs to 3R polytype, because it has d-spacings at $4.39{\AA}$ and $2.316{\AA}$. Since NiO and $Fe_20_3$ content of heterogenite are lower than those of 3R polytype from other localities, it cannot completely exclude the presence of 2H polytype in heterogenite from this study. Malachite is light grey color under the reflected microscope with approximate chemical formula of $Cu_{1.97}Co_{0.02}Fe^{2+}{_{0.01}}CO_3(OH)_2$. Heterogenite and malachite were probably formed at the supergene emichment stage, the last mineralization stage in the Central African Copperbelt. Cobalt seems to be much more emiched in the black supergene (oxy)hydroxide ore than those in the primary sulfide ore.