• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.625-625
• /
• 1991

The specimens for the corrosion test were made by hot-pressing of SiC power with 2 wt% Nl2O3 and 10wt% Al2O3 additions at 2000℃ and 2050℃. The specimens were corroded in 37 mole% NaCl and 63 mole% Na2SO4 salt mixture at 1000℃ up to 60 min. SiO2 layer was formed on SiC and then this oxide layer was dissolved by Na2O ion in the salt mixture. The rate of corrosion of the specimen containing 10 wt% Al2O3 was slower than that of the specimen containing 2 wt% Al2O3. This is due to the presence of continuous grain boundary phase in the specimen containing 10 wt% Al2O3. The oxidation of SiC produced gas bubbles at the SiC-SiO2 interface. The rate of corrosion follows a linear rate law up to 50 min. and then was accelerated. This acceleration is due to the disruption oxide layer by the gas evolution at SiC-SiO2 interface. Pitting corrosion has found at open pores and grain boundaries.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.9 no.1
• /
• pp.70-73
• /
• 1999

Amorphous silica was hydrothermally reacted for 48~120h at $170~180^{\circ}C$ in molar ratios of $SiO_{2}/(NaOH+Na_{2}CO_{3})=2~20\;and\;H_{2}O/(NaOH+Na_{2}CO_{3})=200~250$. Na-kenyaite nuclei were formed directly from amorphous silica without formation of Na-magadiite nuclei in wide range with $SiO_{2}/(NaOH+Na_{2}CO_{3})=3~20$. Above $SiO_{2}/(NaOH+Na_{2}CO_{3})=10$, Na-kenyaite always produced with a residual amorphous silica. Well-crystallized Na-kenyaite without residual amorphous silica were obtained in the range of $SiO_{2}/(NaOH+Na_{2}CO_{3})=3~10$. Morphology of Na-kenyaite exhibited that a large spherical and loosely packed aggregates changed into the smaller and individual platelets according to increase of reaction time.

• The Journal of Natural Sciences
• /
• v.8 no.2
• /
• pp.111-118
• /
• 1996

In order to improve the chemical durability of glass in the $Na_2O$-CaO-$SiO_2$ system, it was investigated in the effect of $B_2O_3$ and ZnO addition and changing amount of each composition, $Na_2O$, $Al_2O_3$, $Li_2O$. In this minimize the change of softening point of glass was as follow.(wt%)$B_2O_3$:3.36%, ZnO:2.88%, $Na_2O$:9.93%, $Al_2O_3$, $Li_2O$:0.19%, $SiO_2$:70.56%, CaO:11.22%, $K_2O$:0.14%

• Journal of Surface Science and Engineering
• /
• v.53 no.2
• /
• pp.59-66
• /
• 2020

Effects of Na₂SiO₃ concentration added into 0.1 M NaOH + 0.05 M NaF solution on the formation behavior and properties of PEO films on AZ91 Mg alloy were investigated under 1200 Hz of alternating current (AC) by voltage-time curves, in-situ observation of arc generation behavior and measurements of film thickness, surface roughness and micro vickers hardness. In the absence of Na₂SiO₃ in the 0.1 M NaOH + 0.05 M NaF solution, about 4 ㎛ thick PEO film was formed within 1 min and then PEO film did not grow but white spots were formed by local burning. Addition of Na₂SiO₃ up to 0.2 M caused more increased formation voltage and growth of PEO film with uniform generation of arcs. Addition of Na₂SiO₃ from 0.2 M to 0.4 M showed nearly the same voltage-time behavior and uniform arc generation. Addition of Na₂SiO₃ more than 0.5 M resulted in a decrease of formation voltage and non-uniform arc generation due to local burning. PEO film growth rate increased with increasing added Na₂SiO₃ concentration but maximum PEO film thickness was limited by local burning if added Na₂SiO₃ concentration is higher than 0.5 M. Surface roughness of PEO film increased with increasing added Na₂SiO₃ concentration and appeared to be proportional to the PEO film thickness. PEO film hardness increased with increasing added Na₂SiO₃ concentration and reached a steady-state value of about 930 H_V at more than 0.5 M of added Na₂SiO₃ concentration.

• Journal of the Korean Chemical Society
• /
• v.55 no.4
• /
• pp.570-574
• /
• 2011

Large colorless single crystals of analcime with diameters up to 0.20 mm have been synthesized from gels with the composition of $3.00SiO_2$ : $1.50NaAlO_2$ : 8.02NaOH : $454H_2O$ : 5.00TEA. The fully $Na^+$-exchanged analcime have been prepared with aqueous 0.1 M NaCl (pH adjusted from 6 to 11 by dropwise addition of NaOH). The single-crystal structure of hydrated $|Na_{0.94}(H_2O)|[Si_{2.06}Al_{0.94}O_6]$-ANA per unit cell, a=13.703(3) ${\AA}$, has been determined by single-crystal X-ray diffraction technique in the orthorhombic space group Ibca at 294 K. The structure was refined using all intenties to the final error indices (using only the 1,446 reflections for which $F_o$ > $4{\sigma}(F_o))R_1/wR_2$ = 0.054/0.143. About 15 $Na^+$ ions are located at three nonequivalent positions and octahedrally coordinated. The chemical composition is $Na_{0.94}(H_2O)Si_{2.06}Al_{0.94}O_6$. The Si/Al ratio of synthetic analcime is 2.19 determined by the occupations of cations, 14.79, in the single-crystal determination work.

• Journal of the Korean Ceramic Society
• /
• v.28 no.8
• /
• pp.626-634
• /
• 1991

The specimens for the corrosion test were made by hot-pressing of SiC power with 2 wt% Nl2O3 and 10wt% Al2O3 additions at 200$0^{\circ}C$ and 205$0^{\circ}C$. The specimens were corroded in 37 mole% NaCl and 63 mole% Na2SO4 salt mixture at 100$0^{\circ}C$ up to 60 min. SiO2 layer was formed on SiC and then this oxide layer was dissolved by Na2O ion in the salt mixture. The rate of corrosion of the specimen containing 10 wt% Al2O3 was slower than that of the specimen containing 2 wt% Al2O3. This is due to the presence of continuous grain boundary phase in the specimen containing 10 wt% Al2O3. The oxidation of SiC produced gas bubbles at the SiC-SiO2 interface. The rate of corrosion follows a linear rate law up to 50 min. and then was accelerated. This acceleration is due to the disruption oxide layer by the gas evolution at SiC-SiO2 interface. Pitting corrosion has found at open pores and grain boundaries.

• Horticultural Science & Technology
• /
• v.30 no.3
• /
• pp.250-255
• /
• 2012

The effect of different source silicon ($CaSiO_3$, $K_2SiO_3$, and $NaSiO_3$) and their application methods (foliar application and subirrigation) on the growth of potted kalanchoe was investigated. Rooted terminal cuttings of Kalanchoe blossfeldiana 'Peperu' were transplanted into 10.5 cm plastic pots containing a commercial growing medium. Then, a nutrient solution, containing 0 or $50mg{\cdot}L^{-1}$ Si as $K_2SiO_3$, $Na_2SiO_3$, or $CaSiO_3$ and adjusted to EC 1.4-$1.6mS{\cdot}cm^{-1}$ and pH 6.0, was supplied through subirrigation along with the nutrient solution or by a foliar application. Plants were grown in a glasshouse under a mean temperature of $23^{\circ}C$ and RH of 70-80%. After 12 weeks of cultivation, plant growth characteristics and leaf tissue contents of P, K, Ca, Mg, Na, S, and Si were measured. Both subirrigational supply and foliar application of Si decreased the plant height and flower stem length. However, the plant condition in the foliar application resulted in disease-like soft rot on the leaf. Among three silicon sources tested, $CaSiO_3$ supplied through a subirrigation system increased shoot tissue contents of Si and chlorophyll as compared to the $Na_2SiO_3$ or $K_2SiO_3$ treatment. Shoot tissue contents of Ca, K, and Na increased when the plant was supplied with $CaSiO_3$, $K_2SiO_3$, and $Na_2SiO_3$, respectively. Subirrigational supply of $K_2SiO_3$ and $NaSiO_3$ decreased the shoot tissue contents of Ca and Mg, and K and Ca, respectively. Therefore, $CaSiO_3$ supplied through a subirrigation system could improve plant quality of kalanchoe 'Peperu' making compact potted plants.

• Resources Recycling
• /
• v.17 no.4
• /
• pp.57-65
• /
• 2008

The behavior of Na-A type zeolite formed in hydrothermal synthesis of melting slag from municipal incineration ash has been investigated with varying synthesis time and $SiO_2/Al_2O_3$ ratio. Sodium silicate and sodium aluminate feed was found to initially form nuclei of Na-A type zeolite in the behavioral study of the reaction products with different synthesis times. As the synthesis time increased, the nuclei have grown to Na-A type zeolite crystals by reacting with $SiO_2$ and $Al_2O_3$ dissolved from the melting slag. The hydrothermal synthesis was completed in 10 hr in the $SiO_2/Al_2O_3$ ratio of 1.38 and after that time, the Na-A type zeolite formed was dissolved and transformed into hydroxysodalite. Only Na-A type zeolite was formed in the $SiO_2/Al_2O_3$ ratio ranging 0.80 to 1.96, whereas Na-P type zeolite as well as Na-A type was formed in the $SiO_2/Al2O_3$ ratio of 2.54.

• Bulletin of the Korean Chemical Society
• /
• v.8 no.1
• /
• pp.6-9
• /
• 1987

The study of the $Na_3YSi_3O_9$ structure, by x-ray diffraction and infrared spectrum, showed that $Na_3YSi_3O_9$ is similar to $Na_4CaSi_3O_9$ except for its being pseudo-cubic instead of cubic. The peaks in the x-ray diffraction pattern of $Na_3YSi_3O_9$ could therefore be indexed on the basis of the $Na_4CaSi_3O_9$ cell. Also, modified $Na_3MSi_3O_9$ (M = Lu, Yb, Tm, Er, Y, Ho, Dy, Gd, Eu, and Sm) type compounds were synthesized by introducing excess sodium, decreasing M(III) concentration, and substituting small amount of phosphorus for silicon. The unit cell parameters of the composition $Na_{3.2}M_{0.7}Si_{2.9}P_{0.1}O_{8.7}$ were estimated from x-ray powder diffraction patterns using the Cohen method.

• Journal of Korean Ophthalmic Optics Society
• /
• v.5 no.1
• /
• pp.49-53
• /
• 2000

Sodium borate silicate glass of composition $10Na_2O-39B_2O_3-50SiO_2-CoO$ and $20Na_2O-14B_2O_3-65SiO_2-CoO$ were prepared by melting oxide mixtures in alumina crucible at $1210^{\circ}C$ in an electric furance in air for 2h, and then quenching in air. The dielectric behavior of the quenched glasses are the subject of the present work. Properties such as dielectric constant and resistivity as a function frequency and temperature are reported. From the dielectric spectra, the glass phase transition temperature has been found to decrease at a rate $Na_2O$ 20 mol% and the dielectric constants increase with increasing $Na_2O$ content. The frequency dependent resistivity response of glass exhibits a non-Debye type relaxation.