• 한국세라믹학회지
• /
• 제36권1호
• /
• pp.50-54
• /
• 1999

양이온 결손 La0.970Mn0.970O3의 x-ray photoemission spectroscopy를 온도를 함수로 측정하였다. 온도의 변화에 따라서 Mn 2p와 3d core level의 화학적 변동 및 이동이 관측되었다. 즉 Mn 2p 3/2와 1/2 및 La 3d core 스펙트럼은 온도의 증가와 함께 저 결합 에너지 측으로 이동이 관측되었다. 이러한 XPS 관측 결과는 Mn3+의 localization의 강도 변화에 의한 것으로 사료되며, Mn3+에 의한 Jahn-Teller효과 이외에도 conventional random potential 효과 역시 La0.790Mn0.970O3의 전도 carrier의 localization에 기여하는 것으로 사료된다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 추계학술발표대회
• /
• pp.29.1-29.1
• /
• 2011

The selective catalytic reduction (SCR) of $MnO_x$ with $NH_3$ is an effective method for the removal of $MnO_x$ from stationary system. The typical catalyst for this method is $V_2O_5-WO_3(MoO_3)/TiO_2$, caused by the high activity and stability. However, This catalyst is active within $300{\sim}400^{\circ}C$ and occurs the pore plugging from the deposition of ammonium sulfate salts on the catalysts surface. It needs to locate the SCR unit after the desulfurizer and electrostatic precipitator without reheating of the flue gas as well as deposition of dust on the catalyst. The manganese oxides supported on titania catalysts have attracted interest because of its high SCR activity at low temperature. The catalytic activity of $MnO_x/TiO_2$ SCR catalyst with different manganese precursors have investigated for low-temperature SCR in terms of structural, morphological, and physico-chemical analyses. The $MnO_x/TiO_2$ were prepared from three different precursors such as manganese nitrate, manganese acetate (II), and manganese acetate (III) by the sol-gel method and then it calcinated at $500^{\circ}C$ for 2 hr. The structural analysis was carried out to identify the phase transition and the change intensity of catalytic activity by various manganese precursors was analyzed by FT-IR and Raman spectroscopy. These different precursors also led to various surface Mn concentrations indicated by SEM. The Mn acetate (III) tends to be more suppressive the crystalline phase (rutile), and it has not only smaller particle size, but also better distributed than the others. It was confirmed that the catalytic activity of MA (III)-$MnO_x/TiO_2$ was the highest among them.

• 한국재료학회지
• /
• 제10권6호
• /
• pp.437-444
• /
• 2000

기판온도, 박막조성 및 증착후 열처리 등의 조건에 따른 ${La_{1-x}}{Sr_x}{MnO_{3-{\delta}}}$(0.19$\leq$x$\leq$0.31) 박막의 결절구조와 전기전도 특성을 조사하였다. 스퍼터법을 이용하여 $500^{\circ}C$에서 증착된 박막은 강한 <001> 우선배향성과 유사정방정(pseudo-tetrag-onal, a/c-=0.97) 결정체를 나타냈다. 이러한 박막의 단위포는 산소분위기 내에서 증착후 열처리에 의하여 입장정 결정계로 변하였다. $La_{0.67}Sr_{0.33}MnO_3$ 조성의 주타겟과 $La_{0.3}Sr_{0.7}MnO_3$조성의 보조타겟을 동시에 이용하여 박막의 조성을 조절하였다. 보조타겟의 개수에 따라 박막내의 Sr 함량(x)은 0.19-0.31 범위의 값을 나타내었으며, x값이 0.19로부터 0.31로 증가시 금소-반도체의 전이 온도가 상승하였고, 전지비저항이 대체로 감소하였다. 0.18 T의 자기장 하에서, $La_{0.69}Sr_{0.31}MnO_3$조성의 박막의 자기저항변화 MR((%) = (${\rho}_o-{\rho}_H/{\rho}_H$)는 약 390% 이었다.

• 한국세라믹학회지
• /
• 제44권1호
• /
• pp.52-57
• /
• 2007

We synthesized $(La_{1-x}Sr_x)MnO_3$ as a cathode for SOFC by glycine nitrate process (GNP) and knew the different properties of $(La_{1-x}Sr_x)MnO_3$ by using nitrate solution and oxide solution as a starting material. In case of using nitrate solution as a starting material, main crystal phase peak of $LaMnO_3$ increased as Sr content added up and a peak of $Sr_2MnO_4\;and\;La_2O_3$ was showed as a secondary phase. We added Mn excess to control a crystal phase. In this case, the electrical conductivity had a high value 210.3 S/cm at $700^{\circ}C$. On the other side, when we used oxide solution as a starting material, we found main crystal phase of $LaMnO_3$ to increase as Sr content added up and a peak of $La_2O_3$ as a secondary phase. Similary, we added Mn excess to control a crystal phase in this case. We knew $(La,Sr)MnO_3$ powder to sinter well and the electrical conductivity of the sintered body at $1200^{\circ}C$ for 4 h was 152.7 S/cm at $700^{\circ}C$. The sintered $(La,Sr)MnO_3$ powder at $1000^{\circ}C$ for 4 h got the deoxidization peak, depending on the temperature and in case of using nitrate solution as a starting material, the deoxidization peak was showed at $450^{\circ}C$ which is lower than used a oxide solution as a starting material. As a result, when $(La,Sr)MnO_3$ powder was synthesized to add Mn excess and to use nitrate solution as a starting material, we found it to have the higher deoxidization property and considered it as a cathode for SOFC properly. And we found it to have different electrical conductivity the synthesized $(La,Sr)MnO_3$ powder by using different starting materials like nitrate solution and oxide solution which influence a sintering density and crystal phase.

• 한국결정성장학회지
• /
• 제11권6호
• /
• pp.246-251
• /
• 2001

수열법으로 $(Pb_{1-x}$La_{2x/3})TiO_3$(PLT, X=0.2) 분말을 합성한 후, $MnO_2$를 0.00~0.02 mol% 첨가하여 그에 따른 소결거동 및 유전특성을 조사하였다. PLT 소결체의 상대밀도는, Mn이 0.02 mol% 첨가되고 $1150^{\circ}C$에서 5시간 소결할 경우 96.7%이였다. PLT의 유전특성은, $MnO_2$의 함량과 소결온도의 변화에 따라 변하였다. Mn의 첨가나 소결온도의 증가시 유전손실값은 측정온도의 증가에 따라 증가되었다. Curie 온도는 Mn 첨가량의 증가와 더불어 감소하였으며, Mn이 0.02 mol% 첨가될 경우, 첨가하지 않은 경우보다 60~$70^{\circ}C$ 감소하였다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 추계학술대회 논문집 Vol.14 No.1
• /
• pp.7-10
• /
• 2001

Orthorhombic type $LiCo_{x}Mn_{1-x}O_{2}$(0 ${\times}$ 0.14) oxides have been synthesized by hydrothermal treatment of $(Co_{x}Mn_{1-x})_{3}O_{4}$ precursors and LiOH aqueous solution at $170^{\circ}C$. As-synthesized powders showed well-ordered ${\beta}-NaMnO_{2}$ structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic $LiCo_{0.1}Mn_{0.9}O_{2}$, comparing to orthorhombic $LiMnO_2$.

• 한국재료학회지
• /
• 제23권4호
• /
• pp.219-226
• /
• 2013

Activated magnetite ($Fe_3O_{4-{\delta}}$) has the capability of decomposing $CO_2$ proportional to the ${\delta}$-value at comparatively low temperature of $300^{\circ}C$. To enhance the $CO_2$ decomposition capability of $Fe_3O_{4-{\delta}}$, $(Fe_{1-x}Co_x)_3O_{4-{\delta}}$ and $(Fe_{1-x}Mn_x)_3O_{4-{\delta}}$ were synthesized and then reacted with $CO_2$. $Fe_{1-x}Co_xC_2O_4{\cdot}2H_2O$ powders having Fe to Co mixing ratios of 9:1, 8:2, 7:3, 6:4, and 5:5 were synthesized by co-precipitation of $FeSO_4{\cdot}7H_2O$ and $CoSO_4{\cdot}7H_2O$ solutions with a $(NH_4)_2C_2O_4{\cdot}H_2O$ solution. The same method was used to synthesize $Fe_{1-x}Mn_xC_2O_4{\cdot}2H_2O$ powders having Fe to Mn mixing ratios of 9:1, 8:2, 7:3, 6:4, 5:5 with a $MnSO_4{\cdot}4H_2O$ solution. The thermal decomposition of synthesized $Fe_{1-x}Co_xC_2O_4{\cdot}2H_2O$ and $Fe_{1-x}Mn_xC_2O_4{\cdot}2H_2O$ was analyzed in an Ar atmosphere with TG/DTA. The synthesized powders were heat-treated for 3 hours in an Ar atmosphere at $450^{\circ}C$ to produce activated powders of $(Fe_{1-x}Co_x)_3O_{4-{\delta}}$ and $(Fe_{1-x}Mn_x)_3O_{4-{\delta}}$. The activated powders were reacted with a mixed gas (Ar : 85 %, $CO_2$ : 15 %) at $300^{\circ}C$ for 12 hours. The exhaust gas was analyzed for $CO_2$ with a $CO_2$ gas analyzer. The decomposition of $CO_2$ was estimated by measuring $CO_2$ content in the exhaust gas after the reaction with $CO_2$. For $(Fe_{1-x}Mn_x)_3O_{4-{\delta}}$, the amount of $Mn^{2+}$ oxidized to $Mn^{3+}$ increased as x increased. The ${\delta}$ value and $CO_2$ decomposition efficiency decreased as x increased. When the ${\delta}$ value was below 0.641, $CO_2$ was not decomposed. For $(Fe_{1-x}Co_x)_3O_{4-{\delta}}$, the ${\delta}$ value and $CO_2$ decomposition efficiency increased as x increased. At a ${\delta}$ value of 0.857, an active state was maintained even after 12 hours of reaction and the amount of decomposed $CO_2$ was $52.844cm^3$ per 1 g of $(Fe_{0.5}Co_{0.5})_3O_{4-{\delta}}$.

• 자원환경지질
• /
• 제42권5호
• /
• pp.479-486
• /
• 2009

자연환경에서 망간은 +2, +3, +4가의 다양한 산화수로 존재하며 환경적으로 중요한 여러 원소들과 활발한 산화/환원반응을 함으로써 원소의 지화학적 순환에 중요한 역할을 하고 있다. 특히 망간은 다양한 산화물로 존재하며 각각 특징적인 망간의 산화상태를 나타내고 있다. 망간산화물의 지화학적 특성, 즉 망간산화물의 용해도, 흡착력, 산화/환원 능력은 산화물을 구성하는 망간의 산화수에 의해 크게 좌우되는 것으로 알려져 있다. 따라서 망간의 산화수를 결정하는 인자를 밝히는 것이 산화/환원에 민감한 여러 오염원소의 지화학적 거동을 예측하는 데 매우 중요하다. X-선 광전자 분광법(X-ray photoelectron spectroscopy, XPS)은 고체상으로 존재하는 다양한 원소의 산화상태를 밝히는데 매우 유용한 도구이다. 본 연구에서 MnO, $Mn_2O_3$, $MnO_2$에 대한 망간의 산화수를 결정하기 위해 XPS $Mn2p_{3/2}$와 Mn3s 결합에너지 스펙트럼을 측정하여 기존에 보고 된 값들과 비교하였다. 망간산화물에 대한 $Mn2p_{3/2}$ 결합에너지는 MnO, 640.9 eV; $Mn_2O_3$, 641.5 eV; $MnO_2$, 641.8 eV로서, 망간의 산화수가 증가할수록 $Mn2p_{3/2}$ 의 결합에너지가 증가하는 것으로 나타났다. 시료준비 방법 중 하나인 Ar 에칭의 경우 시료 표면의 전자구조를 변화시킬 수 있는 가능성이 확인되었다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 영호남학술대회 논문집
• /
• pp.196-199
• /
• 2000

Since the reports of CMR(colossal magnetoresistance) effects in some single crystal R-P phase $La_{1+x}Sr_{2-x}Mn_2O_7$, considerable researches have been carried out to find optimum composition and to understand the role of dimensionality in the CMR mechanism of this system. In this study, layered perovskite $Ln_xCa_{1-x}MnO_{4}$ (x=0.5, Ln=Pr, Nd, Sm, Gd) phases were synthesized by solid state reaction and their structures were refined by Rietveld method. Electrical and magnetic properties were measured between room temperature and liquid helium temperature and compared with those of two dimensional $La_{1.4}Sr_{1.6}Mn_2O_7$ phase.

• 한국결정성장학회지
• /
• 제13권2호
• /
• pp.63-67
• /
• 2003

Synthesis of $PbLaTiO_{3}$ : Mn powders containing La and Mn was carried out using $PbO,\;TiO_{2},\;La_{2}O_{3}\;and\;MnO_{2}$ as starting materials by hydrothermal method. In the synthesis of single phase $PbLaTiO_{3}$ : Mn powder containing La and Mn, the optimal x value corresponding to La substitution was 0.01 which corresponds to $0.99(Pb_{1-x}La_{2x/3}TiO_{3})+0.01MnO_{2}$. The optimal conditions for the preparation of the powder synthesis were 8 M-KOH solvent of hydrothermal solvent, $270^{\circ}C$ of reaction temperature and 24 hrs of run time. It was found that the synthesized powders had spherical morphology with average particle size of 70 nm and specific surface area of $5.5\;m^{2}/g$.