• Bulletin of the Korean Chemical Society
• /
• v.28 no.12
• /
• pp.2333-2337
• /
• 2007

Nanoporous TiO2 and ZrO2 thin films were spin-coated using a surfactant-templated approach from Pluronic P123 (EO20PO70EO20) as the templating agent, titanium alkoxide (Ti(OC4H9)4) as the inorganic precursor, and butanol as a the solvent. The control of the electronic structure of TiO2 is crucial for its various applications. We found that the band gap of the hybrid nanoporous thin films can be easily tuned by adding an acetylacetonestabilized Zr(OC4H9)4 precursor to the precursor solution of Ti(OC4H9)4. Pores with a diameter of 5 nm-10 nm were randomly dispersed and partially connected to each other inside the films. TiO2 and ZrO2 thin films have an anatase structure and tetragonal structure, respectively, while the TiO2-ZrO2 hybrid film exhibited no crystallinity. The refractive index was significantly changed by varying the atomic ratio of titanium to zirconium. The band gap for the nanoporous TiO2 was estimated to 3.43 eV and that for the TiO2-ZrO2 hybrid film was 3.61 eV.

• Korean Journal of Materials Research
• /
• v.9 no.4
• /
• pp.414-418
• /
• 1999

Typical metal oxide thin films having optical and electrical properties are widely used as inorganic functional materials. Liquid phase deposition(LPD) method, a new low temperature process, has been developed for the several advantages of no vacuum system, low cost, high throughput, and low processing temperature(<$50^{\circ}C$). Silica powder was added to 40wt% hydrofluoro-silicic acid($H_2$SiF\ulcorner) to obtain an immersing solution of silica-saturated hydrofluorosilicic acid solution. Boric acid solution was continuously added in the range from 0 to 0.05M to prepare supersaturated hydrofluorosilicic acid solution. LPD $SiL_2$film was formed with the variation of added amount of $H_2$O. The SiO$_2$thin film could be prepared from hydrofluorosilicic acid by LPD method. The thickness of LPD $_SiO2$film was influenced by the boric acid concentration and added amount of $H_2$O. Silicon in thin film existed as SiF\ulcorner by Raman spectrum.

• Journal of the Korean Ceramic Society
• /
• v.30 no.8
• /
• pp.615-622
• /
• 1993

In order to increase chemical durability of thin films in binary system B2O3-SiO2 and Al2O3-SiO2 on the slide glass by the dip-coating technique from TEOS(Tetraethyl Orthosilicate) and boric acid or aluminum nitrate, phosphoric acid(5~20mol%) was added, respectively. Corrosion of acid and alkali of samples treated with 1N, HCl, NaOH and distilled water at 10$0^{\circ}C$ for 15 minute, were measured IR transmittance and variance of transmittance at visible range. Surface structure of thin film was investigated with SEM and formation of crystal phase according to additiion of phosphoric acid was measrued with XRD. In Al2O3-SiO2 system, change of remarkable characteristic was not obtained at the addition of P2O5 but transmittance of thin film was decreased with addition of P2O5 in B2O3-SiO2 system.

• Journal of the Korean Ceramic Society
• /
• v.44 no.1 s.296
• /
• pp.32-36
• /
• 2007

Zinc gallate $(ZnGa_2O_4)$ thin film phosphors have been formed on ITO glass substrates by a sol-gel spinning coating method. For the formation of the film phosphors, the starting materials of zinc acetate dihydrate, gallium nitrate hydrate and 2-methoxyethanol as a solution were used. The thin films deposited were firstly dried at $100^{\circ}C$ and fired at $500^{\circ}C\;or\;600^{\circ}C$ for 30 min and then, annealed $500^{\circ}C\;or\;600^{\circ}C$ at for 30 min under an annealing atmosphere of 3% $H_2/Ar$. The thin films deposited on ITO glass plates showed the (220), (222), (400), (422), (511), and (440) peaks of spinel structure as well as the (311) peak indicating a standard powder diffraction pattern. The surface morphologies of the thin film phosphors were observed with a firing and an annealing condition. The $ZnGa_2O_4$ film phosphors showed the blue emission spectra around 410 nm as well as the emission spectra in the UV region (360-380 nm).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.439-440
• /
• 2008

Indium Zinc Tin Oxide (IZTO) thin films for transparent thin film transistor (TTFT) were deposited on glass substrate at room temperature by facing targets sputtering (FTS). The FTS system was designed to array two targets facing each other and forms the high- density plasma between. Two different kinds of targets were installed on FTS system. One is ITO ($In_2O_3$ 90wt.%, $SnO_2$ 10wt.%), the other is IZO($In_2O_3$ 90wt%, ZnO 10wt%). The conductive and optical properties of IZTO thin film is determined depending on variation of DC power and working pressure. Therefore, IZTO thin films were prepared with different DC power and working pressure. As-deposited IZTO thin films were investigated by a UV/VIS spectrometer, an X-ray diffractometer (XRD), a scanning electron microscopy (SEM), a Hall Effect measurement system. As a result, all IZTO thin films deposited on glass substrate showed over 80% of transmittance in visible range (400~800 nm) at $O_2$ gas flow rate. We could obtain IZTO thin films with the lowest resistivity $5.67\times10^{-4}$ [$\Omega{\cdot}cm$] at $O_2$ gas flow rate 0.4 [sccm).

• Journal of Sensor Science and Technology
• /
• v.18 no.2
• /
• pp.110-115
• /
• 2009

Polystyrene (PS) microspheres were used to good advantage as a template material to prepare macroporous $TiO_2$ thin films. This is enabled to run the thermal decomposition of the PS without the collapsing of the 3-D macroporous framework during the calcination step. $TiO_2$ thin films were deposited onto the colloidal templated substrates at room temperature by RF sputtering, and then samples were thermally treated at $450^{\circ}C$ for 40.min in air to remove the organic colloidal template and induce crystallization of the $TiO_2$ film. The macroporous $TiO_2$ thin film exhibited a quasi-ordered partially hexagonal close-packed structure. Burst holes, estimated to be formed during PS thermal decomposition, are seen as the hemisphere walls. the inner as well as the outer surfaces of the hollow hemispheres formed by the method of thermal decomposition can be easily accessed by the diffusing gas species. As a consequence, the active surface area interacting with the gas species is expected to be enlarged about by a factor of fourth as large as compared to that of a planar films. Also the thickness at neighboring hemisphere could be controlled a few nm thickness. If the acceptor density becomes as large that depletion width reaches those thickness, the device is in the pinch off-situation and a strong resistance change should be observed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.07b
• /
• pp.1023-1028
• /
• 2004

RF magnetron sputtering을 이용하여 증착한 투명전도성 ZnO 박막의 F 도핑량에 따른 전기, 구조, 광학적 특성에 대해 고찰하였다. 순수 ZnO와 ZnO : $ZnF_2$(1.3 wt%) 그리고 ZnO : $ZnF_2$(10 wt%) 3개의 타겟들을 2개씩 조합 각각의 rf 파워를 조절하여 co-sputtering 방법으로 $ZnF_2$ wt%를 변화시켜 박막내의 F 도핑량을 조절하였다. 증착된 박막들은 열처리에 따른 물성 변화를 분석하기 위해 $5{\times}10^{-7}$ torr 이하의 진공 분위기에서 $300^{\circ}C$에서 2 시간 동안 열처리하였다. XRD 분석 결과 제작된 모든 ZnO 박막은 (002) 우선 방위 특성을 보였고 F 도핑량 증가에 따라 (101), (110), (100) 방향의 약한 피크들이 나타났으며, 이러한 구조적 특성 변화는 이동도의 변화와 밀접한 관계가 있는 것으로 나타났다. Auger로 박막 내의 F 량을 분석한 결과 최대 5.9 at%의 F이 포함되어 있었으며, 열처리 후 캐리어 농도와 이동도는 증가하였고 최고 $37cm^2/Vs$의 이동도를 나타내었으며, 모든 박막들은 가시광 영역에서 81 % 이상의 투과도를 가졌다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.228-231
• /
• 1999

The preparation and electrical properties of LIPON electrolyte were investigated in order to fabricate all solid state thin film battery. The LIPON thin film was deposited by r.f. sputtering of Li$_3$PO$_4$ target in O$_2$-N$_2$ mixtures. The LIPON deposited at N$_2$+10% O$_2$ ratio had a conductivity at 25 $^{\circ}C$ of 1.8${\times}$10$\^$-6/S/cm. The ion conductivity of the LIPON films decreased as the O$_2$ content of the process gas increased.

• Journal of the Korean Ceramic Society
• /
• v.40 no.2
• /
• pp.153-158
• /
• 2003

Self-patterning of thin films using photosensitive sol solution has advantages such as simple manufacturing process compared to photoresist/dry etching process. In this study,$La_{0.5}SR_{0.5}CoO_3$(LSCO) thin films as an electrode material for ferroelectric memories have been prepared by spin coating method using photosensitive sol solution. La-2methoxyethoxide, Sr-ethoxide, Co-2methoxyethoxide were used as starting materials. As UV exposure time to the LSCO gel thin film increased, the UV absorption peak intensity of metal${beta}$-diketonate decreased due to reduced solubility by M(metal)-O-M bond formation. Solubility difference by UV irradiation on LSCO gel thin film allows to obtain a fine patterning of thin film. The LSCO thin films annealed over$680{\circ}C$ in air showed perovskite phase and the lowest resistivity$(4{ imes}10^{-3}{Omega}cm)$ of the thin films were obtained by annealing at$740{\circ}C$.

• Journal of Surface Science and Engineering
• /
• v.54 no.2
• /
• pp.96-101
• /
• 2021

NaNbO₃:Eu³⁺ phosphor thin films were grown on quartz substrates by radio-frequency magnetron sputtering at a growth temperature of 100 ℃, with subsequent annealing at temperatures of 800, 900, and 1000 ℃. The effects of annealing temperature on the structural, morphological, and optical properties of the thin films were investigated. The NaNbO₃:Eu³⁺ sputtering target was synthesized by a solid-state reaction of raw materials Na₂CO₃, Nb₂O₅, and Eu₂O₃. The X-ray diffraction patterns exhibited that the thin films had two mixed phases of NaNbO₃ and Eu₂O₃. Surface morphologies were investigated by using field emission-scanning electron microscopy and indicated that the grains of the thin film annealed at 1000 ℃ showed irregular shapes with an average size of approximately 300 nm. The excitation spectra of Eu³⁺-doped NaNbO₃ thin film consisted of a strong charge transfer band centered at 304 nm in the range of 240-350 nm and two weak peaks at 395 and 462 nm, respectively, resulting from the ⁷F₀→⁵L₆ and ⁷F₀→⁵H₂ transitions of Eu³⁺ ions. The emission spectra under excitation at 304 nm exhibited an intense red band centered at 614 nm and two weak bands at 592 and 681 nm. As the annealing temperature increased from 800 ℃ to 1000 ℃, the intensities of all the emission bands and the band gap energies gradually increased. These results indicate that the higher annealing temperature enhance the luminescent properties of NaNbO₃:Eu³⁺ thin films.