• Journal of Ceramic Processing Research
• /
• v.20 no.4
• /
• pp.395-400
• /
• 2019

This study was conducted on the structural and electrical properties of (Ba0.7Sr0.3)TiO3 thin films prepared by the sol-gel and spin-coating methods in order to investigate their applicability to electrocaloric devices. All specimens showed a tetragonal crystal structure and lattice constants of a = 3.972 Å, c = 3.970 Å. The mean grain size of specimens sintered at 800 ℃ was about 30 nm, and the average thickness of 5 times coated specimens was 304~311 nm. In the specimen sintered at 750 ℃, The relative dielectric constant and loss of specimens measured at 20 ℃ were 230 and 0.130, respectively, while dependence of the dielectric constant on unit DC voltage was -8.163 %/V. The remanent polarization and coercive fields were 95.5 μC/㎠ and 161.3 kV/cm at 21 ℃, respectively. And, the highest electrocaloric property of 2.69 ℃ was observed when the electric field of 330 kV/cm was applied.

• Journal of Ceramic Processing Research
• /
• v.20 no.spc1
• /
• pp.86-91
• /
• 2019

A solid-state route was used to prepare sodium titanium oxide (NTO, Na2Ti3O7) as a solar heat protecting material with an impressive solar reflectance (TSR = 94.3%) using a high refractive index rutile TiO2. The solar reflectance of the synthesized NTO was measured using UV-Vis-NIR spectrophotometer. Solar reflectance property of the synthesized compound depends on the calcination temperature. The solar reflectance property of the synthesized NTO powder was compared with commercial rutile TiO2. The compound synthesized at 900 ℃ for 24 hrs had remarkable solar reflectance 94.3% than that calcined below 900 ℃. Crystalline nature, structural property, morphology and optical properties of NTO powders were characterized and analyzed using XRD, FE-SEM, EDS and UV-Vis-NIR spectrophotometer. From the results, we guessed that NTO would be a suitable "solar heat protecting candidate" for energy-saving applications in coating industries.

• Journal of Environmental Science International
• /
• v.18 no.1
• /
• pp.49-60
• /
• 2009

Fabrication and oxidants formation of 1 and 2 component metal oxide electrode, which is known to be so effective to destruct non-biodegradable organics in wastewater, were studied. Five electrode materials (Ru, Pt, Sn, Sb and Gd) were used for the 1 and 2 component electrode. The metal oxide electrode was prepared by coating the electrode material on the surface of the titanium mesh and then thermal oxidation at $500^{\circ}C$ for 1 h. The removed RhB per 2 min and unit W for one component electrode decreased in the following sequences: Ru/Ti>Sb/Ti>Pt/Ti>Gd/Ti>Sn/Ti. The concentration of oxidants generated in 1 and 2 component electrodes was in the order of: $ClO_2$> free Cl>$H_2O_2>O_3$. OH radical was not generated from in entire one and two component electrodes. RhB degradation rate and generated oxidants of the Ru-Sn=9:1 electrode was higher than that of the two component electrode. The exact relationship between the removal of RhB and the generated oxidants concentration was not obvious. However, it was assumed that electrode with high RhB decolorization had high oxidant concentration.

• Journal of the Korean Ceramic Society
• /
• v.47 no.3
• /
• pp.256-261
• /
• 2010

Physical properties of Plasma electrolytic oxidized 8 different types of Al alloys, A-1100, A-2024, A-5052, A-6061, A-6063, A-7075, ACD-7B and ACD-12 were investigated. The electrolyte for PEO was $Na_2SiO_3$ solutions with NaOH and some alkali earthen metal salts. Porous layer near the surface of PEO coating was not found, and surface roughness Ra50 was below 2.5 ${\mu}m$. Surface roughness was affected by growth rate of plasma electrolytic oxidized layer, not by Si content in Al alloy.

• Carbon letters
• /
• v.6 no.2
• /
• pp.71-78
• /
• 2005

Anti-oxidation coatings are the key technique for carbon/carbon (C/C) composites used as the thermal structural materials. The microstructure and oxidation behavior of several kinds of high-performance ceramic coatings for C/C composites prepared in Northwestern Polytechnical University were introduced in this paper. It showed that the ceramic coatings such as SiC, Si-$MoSi_2$, SiC-$MoSi_2$, $Al_2O_3$-mullite-SiC and SiC/yttrium silicate/glass coatings possessed excellent oxidation resistance at high temperatures, and some of these coatings were characterized with excellent thermal shock resistance. The SiC-$MoSi_2$ coating system has the best oxidation protective property, which can effectively protect C/C composites from oxidation up to 1973 K. In addition, the protection and failure reasons of some coatings at high temperature were also provided.

• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.3
• /
• pp.31-35
• /
• 2014

$TiO_2$-nanoparticle-dispersed silicone was applied to a LED package and the light efficiency of the LED package was evaluated in this study. The addition of $TiO_2$ nanoparticles in silicone increased refractive index, which improved the light efficiency of the LED package. The $TiO_2$ nanoparticles were fabricated by hydrothermal synthesis and were dispsersed by a vinyl silane coating treatment. After the silane treatment, the $TiO_2$ nanoparticles dispersed with diameters of 10~40 nm but rod-shape $TiO_2$ nanoparticles with lengths of 100 nm were also observed. The refractive index increased with the $TiO_2$ concentration in silicone, while the transmittance decreased with the $TiO_2$ concentration. The light efficient of the LED package with $TiO_2$+silicone encapsulant was higher than that of the LED package with no $TiO_2$ in silicone encapsulant.

• Journal of Power System Engineering
• /
• v.12 no.3
• /
• pp.66-71
• /
• 2008

Diamond-like-carbon (DLC) coatings could be good candidates as solid lubricants for cutting tools in dry machining of aluminum alloy. In this work, DLC thin films were produced as a friction reduction coating for WC-Co insert tip using the plasma immersion ion beam deposition (PIIED) technique. DLC coatings were also coated on $Al_2O_3$ specimens and high temperature wear tested up to $400^{\circ}C$ in dry air to observe the survivability of the DLC coating in simulated severe cutting conditions using a pin-on-disc tribotester with Hertzian contact stress of 1.3GPa. It showed reduced friction coefficients of minimum 0.02 up to $400^{\circ}C$. And cutting performance of DLC coated WC-Co insert tips to Al 6061 alloy were conducted in a high speed machining center. The main problems of built-up edge formation in aluminum machining are drastically reduced with improved surface roughness. The improvements were mainly related to the low friction coefficient of DLC to Al alloy and the anti-adhesion of Al alloy to WE due to the inertness of DLC.

• Journal of the Korean Society for Heat Treatment
• /
• v.24 no.4
• /
• pp.209-216
• /
• 2011

Surface coatings were prepared on SKD11 core mold steel by plasma electrolytic oxidation (PEO). The coatings were investigated about the formation condition of core mold steel. SKD11 were coated by PEO in a mix solution of Sodium Aluminate $NaAlO_2$ (10 g/l), Sodium Silicate powder $Na_2SiO_3$ (0.5 g/l), Sodium tungstate dihydrate $Na_2WO_42H_2O$ (0.5 g/l) at less than $30^{\circ}C$. The electrical condition were voltage : 500~600 V; Pulse : 600~1800 Hz; current density 15~20 $A/dm^2$ various time : 3 min~40 min. The coatings surface morphology, cross-section, friction coefficient, hardness were investigated. The PEO coatings on SKD11 core mold steel showed the extended service life.

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.11a
• /
• pp.382-382
• /
• 2009

염료감응형 태양전지의 구성체 중 전극으로 연구 되어 지고 있는 $TiO_2$는 기존에 대량 생산이 가능한 spin coating법, screen printing법, spray법의 연구가 이루어져 왔으나 고 효율 태양전지에 쓰이는 전극 시스템에 비해 고 분산성을 지닌 $TiO_2$페이스트를 제조 하는데 어려움이 있다. 그리고 플렉시블 디스플레이 소자의 응용을 위해서는 소자 공정 온도인 $250^{\circ}C$ 이하의 공정 온도가 요구 되어 지므로 고온공정인 CVD법은 이에 적합하지 않다. 이에 본 연구는 진공 증착 방법인 광원자층증착법을 이용하여 $150^{\circ}C$이하의 저온공정온도에서도 적용이 가능한 $TiO_2$ 박막을 185nm의 UV light를 조사하여 glass 기판위에 제조 하고 그에 따른 박막의 물성 분석을 하였다. Mo source로는 titanium tetraisopropoxide(TTIP)와 reactant gas 로는 $H_2O$를 사용하였으며 불활성 기체인 Ar 가스는 purge 가스로 각각 사용하였다. $100^{\circ}C{\sim}250^{\circ}C$ 공정온도를 변수로 $TiO_2$ 박막을 제조 하였으며 제조된 $TiO_2$ 박막의 물성 분석을 위해 FESEM, TEM을 이용하여 표면 및 두께를 분석하였다. 또한 $100^{\circ}C$ 400 cycles에서 약 12nm 막 두께를 관찰 할 수 있었으며 그 결과 박막의 성장률이 $0.3{\AA}$/cycle 임을 확인 할 수 있었다. 그리고 UV-VIS을 이용하여 박막의 좌외선에 대한 흡수도 및 투과도 분석을 하였다. 또한 XPS 성분 분석을 통하여 $100^{\circ}C$의 저온 공정에서 형성된 박막이 $TiO_2$임을 확인 하였다. 이러한 결과에서 185nm의 UV light에 의한 광원자층 증착법으로 $100^{\circ}C$의 저온에서도 $TiO_2$ 박막이 증착 되는 것을 확인 할 수 있었다.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.412-412
• /
• 2014

Zinc oxide (ZnO) is one of the most powerful materials for purifying organic pollutants using photocatalytic activity. In this study, we have introduced a novel method to design highly photoreactive flexible 3 dimensional (3D) ZnO nanocomposite [F-ZnO-m (m: reaction time, min)] by electrospinning and simple-step ZnO growth processing (one-step ZnO seed coating/growth processing). Significantly, the F-ZnO-m could be a new platform (or candidate) as a photocatalytic technology for both morphology control and large-area production. The highest photocatalytic degradation rate ([k]) was observed for F-ZnO-m at 2.552 h-1, which was 8.1 times higher than that of ZnO nanoparticles (NPs; [k] = 0.316 h-1). The enhanced photocatalytic activity of F-ZnO-m may be attributed to factors such as large surface area. The F-ZnO-m is highly recyclable and retained 98.6% of the initial decolorization rate after fifteen cycles. Interestingly, the F-ZnO-m samples show very strong antibacterial properties against both Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus) after exposure to UV-light for 30 min. The antibacterial properties of F-ZnO-m samples are more effective than those of ZnO NPs. More than 96.6% of the E. coli is sterilized after ten cycles. These results indicate that F-ZnO-m samples might have utility in several promising applications such as highly efficient water/air treatment and inactivation of pathogenic microorganisms.