• Progress in Superconductivity and Cryogenics
• /
• v.9 no.4
• /
• pp.16-18
• /
• 2007

We report the results of MOD-processed YBCO coated conductors on the IBAD-MgO template. The precursor solution was coated on the $CeO_2-buffered$ IBAD-MgO template using a slot-die coating method, calcined at a temperature of $550^{\circ}C$, and fired at high temperatures for 2.5 h in a reduced oxygen atmosphere. The $J_C$ value of YBCO coated conductors was found to be very sensitive to the microstructure, and thus higher $J_C$ value could be achieved when the in-plane texture was higher and the difference in $T_{C,zero}$. was negligible. Optimally processed YBCO coated conductor exhibited $J_C$ value of $0.75MA/cm^2$ at 77 K in self-field, which might be due to somewhat depressed $T_{C,zero}$ of 87.3 K caused by possible $Sm^{3+}$ substitution on the $Ba^{2+}$ site.

• Transactions on Electrical and Electronic Materials
• /
• v.8 no.3
• /
• pp.125-130
• /
• 2007

DLC coating on ceramics is very useful for manufacturing the materials with hardness and low friction. Adhesion of DLC thin film on ceramics, on the other hand, is usually very weak. Adhesion of DLC film depends on many parameters such as contamination and chemical bonding between thin film and substrate. In this study, adhesion of DLC film on ceramics was improved by the intermediate layer when the plasma immersion ion deposition (PIID) technique was applied. It is found that the chemical composition and the thickness of intermediate layer have significantly an effect on the adhesion of DLC thin film on $Al_2O_3$.

• Korean Journal of Metals and Materials
• /
• v.49 no.7
• /
• pp.583-588
• /
• 2011

$Cd_xZn_{1-x}O$ thin films were grown on quartz substrates by using the sol-gel spin-coating method. The mole fraction, x, of the $Cd_xZn_{1-x}O$ thin films was controlled from 0 to 1 by changes in the content ratio of the cadmium acetate dehydrate [$Cd{(CH_3COO)}_2{\cdot}2H_2O$] and zinc acetate dehydrate [$Zn{(CH_3COO)}_2{\cdot}2H_2O$]. The effects of the mole fraction on the morphological, structural, and optical properties of the $Cd_xZn_{1-x}O$ thin films were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), and UV-visible spectroscopy. The $Cd_xZn_{1-x}O$ thin films exhibited the polygonal surface morphology and their grain size was increased ranging from 42.1 to 63.9 nm with the increase in the mole fraction. It was observed that the absorption bandgap of the $Cd_xZn_{1-x}O$ thin films decreased from 3.25 to 2.16 eV as the mole fraction increased and the Urbach energy ($E_U$) values changed inversely to the optical bandgap of the $Cd_xZn_{1-x}O$ thin films.

• Korean Journal of Materials Research
• /
• v.22 no.3
• /
• pp.155-158
• /
• 2012

In this work, AlON-$Al_2O_3$ coatings were prepared on Al2021 alloy by the electrolytic plasma processing (EPP) method. The experimental electrolytes include: 2 g/l NaOH as the electrolytic conductive agent, 10 g/l $Na_2AlO_2$ as the alumina formative agent, and 0.5 g/l $NaNO_2$, $NaNO_3$, and $NH_4NO_3$ as the nitride inducing agents. The effects of different nitrogen inducing agents were studied by a combined compositional and structural analyses of the ceramic coatings carried out by Xray diffractometry (XRD) and scanning electron microscopy (SEM) for the specimens EPP-treated at room temperature for 15 min under a hybrid voltage of 260 DC along with an AC 50 Hz power supply (200 V). Microhardness tests and wear tests were carried out to correlate the evolution of the microstructure and the resulting mechanical properties. Potentiodynamic polarizations and immersion corrosion tests were carried out in 3.5wt% NaCl water solutions under static conditions in order to evaluate the corrosion behavior of the coated samples. The results demonstrate that $NaNO_2$ is proven to be a good nitrogen inducing agent to produce high quality AlON-$Al_2O_3$ ceramic coatings.

• Journal of Surface Science and Engineering
• /
• v.54 no.6
• /
• pp.365-370
• /
• 2021

In this research, we proceeded with research on plasma resistance of the cleaning process of APS(Atmospheric Plasma Spray)-Y₂O₃ coated parts used for semiconductor and display plasma process equipment. CF₄, O₂, and Ar mixed gas were used for the plasma environment, and respective alconox, surfactant, and piranha solution was used for the cleaning process. After APS-Y₂O₃ was exposed to CF₄ plasma, the surface changed from Y₂O₃ to YF₃ and a large amount of carbon was deposited. For this reason, the plasma corrosion resistance was lowered and contamination particles were generated. We performed a cleaning process to remove the defect-inducing surface YF₃ layer and carbon layer. Among three cleaning solutions, the piranha cleaning process had the highest detergency and the alconox cleaning process had the lowest detergency. Such results could be confirmed through the etching amount, morphology, composition, and accumulated contamination particle analysis results. Piranha cleaning process showed the highest detergency, but due to the very large thickness reduction, the base metal was exposed and a large number of contaminated particles were generated. In contrast, the surfactant cleaning process exhibit excellent properties in terms of surface detergency, etching amount, and accumulated contamination particle analysis.

• Journal of Powder Materials
• /
• v.23 no.1
• /
• pp.38-42
• /
• 2016

$BaTiO_3$-coated Fe nanofibers are synthesized via a three-step process. ${\alpha}-Fe_2O_3$ nanofibers with an average diameter of approximately 200 nm are first prepared using an electrospinning process followed by a calcination step. The $BaTiO_3$ coating layer on the nanofiber is formed by a sol-gel process, and a thermal reduction process is then applied to the core-shell nanofiber to selectively reduce the ${\alpha}-Fe_2O_3$ to Fe. The thickness of the $BaTiO_3$ shell is controlled by varying the reaction time. To evaluate the electromagnetic (EM) wave-absorbing abilities of the $BaTiO_3@Fe$ nanofiber, epoxy-based composites containing the nanofibers are fabricated. The composites show excellent EM wave absorption properties where the power loss increases to the high frequency region without any degradation. Our results demonstrate that the $BaTiO_3@Fe$ nanofibers obtained in this work are attractive candidates for electromagnetic wave absorption applications.

• Journal of the Korean Ceramic Society
• /
• v.40 no.9
• /
• pp.909-915
• /
• 2003

Anodic oxide films on aluminum play an important role as a dielectrics in aluminum electrolytic capacitor. In order to obtain the high capacitance, ZrO$_2$ films were coated on aluminum foils by sol-gel method and then, the properties of anodized films were studied. The coating and drying of the films were repeated 4-10 times and annealed at 300～$600^{\circ}C$ and the triple layer of ZrO$_2$/Al-ZrO$_{x}$ /Al$_2$O$_3$ was formed onto aluminum substrates after anodizing of ZrO$_2$/Al film. The thickness of $Al_2$O$_3$ layer was decreased with increasing the annealing temperature due to the densification of ZrO$_2$ film. The ZrO$_2$ films were crystallized even at 30$0^{\circ}C$ and showed nanocrystalline structure. The. capacitance of aluminum foil annealed at low temperature was higher than that at high temperature. The increase of capacitance was due to the high capacitance of ZrO$_2$ film annealed at low temperature. The capacitance of ZrO$_2$ coated aluminum increased about 3 times compared to that without a ZrO$_2$ layer after anodizing to 400 V. From these results, the aluminum foils with composite oxide layers are found to be applicable to the aluminum electrolytic capacitor.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.4 no.2
• /
• pp.199-209
• /
• 1994

$PbTiO_3$ thin films were prepared on soda-lime-silica slide glasses, Si-wafer and sapphire substrate by the dip-coating of precursor solution. As starting materials, titanium tetra iso-propoxide and lead acetate trihydrate were used. Then acetylacetone was added to prepare stable sol. The effect of the parameters such as viscosity and composition of sol were investigated. The optical transmittance at visible range, refractive index, IR spectra were measured in varying compositions, thickness and heat treatment temperature. The crystallization of $PbTiO_3$ films were measured by using XRD and SEM. Diffusion of compositions from slide glass to thin film were investigated by using EDX, too. These sols not precipitated for 20 days. Transmittance of $PbTiO_3$ films at visible range were decreased with the increase of thickness and heat treatment temperatures, and were exhibited flat spectra. Pyrochlore type appeared in the films on slide glass and perovskite type appeared in the films on Si-wafer or sapphire at $600^{\circ}C$. Perovskite crystals transformed to $PbTi_3O_7$ phase at $800^{\circ}C$.

• Current Photovoltaic Research
• /
• v.8 no.2
• /
• pp.60-65
• /
• 2020

In perovskite solar cells with planar heterojunction configuration, selection of proper charge-transporting layers is very important to achieve stable and efficient device. Here, we developed solution processible Cu doped NiO_x (Cu:NiO_x) thin film as a hole-transporting layer (HTL) in p-i-n structured methylammonium lead trihalide (MAPbI₃) perovskite solar cell. The transmittance and thickness of NiO_x HTL is optimized by control the spin-coating rate and Cu is additionally doped to improve the surface morphology of undoped NiO_x thin film and hole-extraction properties. Consequently, a perovskite solar cell containing Cu:NiO_x HTL with optimal doping ratio of Cu exhibits a power conversion efficiency of 14.6%.

• Progress in Superconductivity and Cryogenics
• /
• v.5 no.1
• /
• pp.13-16
• /
• 2003

Adhesion of $SrZrO_3$ resistive oxide barrier on Ag sheathed Bi(2223) tapes prepared by the sol-gel and dip-coating method was evaluated with an aid of Taguchi method and Lie($2^1{\times}3^7$) orthogonal arrays to determine the optimal process combination of levels of factors that best satisfy the bigger is better quality characteristic (QC=B). For analyses of results statistical calculations such as average and analysis of variance (ANOVA) were employed to analyze the results for improving the performance qualities of the dip-coated $SrZrO_3$ film. Experimentally, the performance of the films was evaluated in terms of bond strength by varying Sr/Zr moi ratio (A), amount of organic vehicle additives (B), drying temperature (C) and time (D), heat treatment temperature (E) and time (F), respectively. The optimal combination of levels of factors was determined to be $A_3B_2C_3D_2E_1F_3$ having a 90% confidence level.