MOD-processed YBCO coated conductor on the IBAD-MgO template

  • Published : 2007.11.30
Download PDF
⟨ Previous Next ⟩

Abstract

We report the results of MOD-processed YBCO coated conductors on the IBAD-MgO template. The precursor solution was coated on the $CeO_2-buffered$ IBAD-MgO template using a slot-die coating method, calcined at a temperature of $550^{\circ}C$, and fired at high temperatures for 2.5 h in a reduced oxygen atmosphere. The $J_C$ value of YBCO coated conductors was found to be very sensitive to the microstructure, and thus higher $J_C$ value could be achieved when the in-plane texture was higher and the difference in $T_{C,zero}$. was negligible. Optimally processed YBCO coated conductor exhibited $J_C$ value of $0.75MA/cm^2$ at 77 K in self-field, which might be due to somewhat depressed $T_{C,zero}$ of 87.3 K caused by possible $Sm^{3+}$ substitution on the $Ba^{2+}$ site.

Keywords

References

  1. A. Gupta, R. Jagannathan, E. I. Cooper, E. A. Giess, J. I. Landman, and B. W. Hussey, "Superconducting oxide films with high transition temperature prepared from metal trifluoroacetate precursors," Appl. Phys. Lett., vol. 52, pp. 2077-2079, 1988 https://doi.org/10.1063/1.99752
  2. Paul C. Mclntyre, Michael J. Cima, Man fai Ng, "Metalorganic deposition of $high-J_C\;Ba_2YCu_3O_{7-x}$ thin films from trifluacetate precursors onto (100) $SrTiO_3$," J. Appl. Phys., vol. 68, pp. 4183-4187, 1990 https://doi.org/10.1063/1.346233
  3. Robert A. Hawsey, David K. Christen, "Progress in research, development, and pre-commercial deployment of second generation HTS wires in the USA," Physica C, vol. 445-448, pp. 488-495, 2006 https://doi.org/10.1016/j.physc.2006.04.062
  4. Yuh Shiohara, Yutaka Kitoh, Teruo Izumi, "Highlights in R&D for coated conductors in Japan," Physica C, vol. 445-448, pp. 496-503, 2006 https://doi.org/10.1016/j.physc.2006.04.043
  5. C. P. Wang, K. B. Do, M. R. Beasley, T. H. Geballe, and R. H. Hammond, "Deposition of in-plane textured MgO on amorphous Si3N4 substrates by ion-beam-assisted deposition and comparisons with ion-beam-assisted deposited yttria-stabilized-zirconia," Appl. Phys. Lett., vol. 71, pp. 2955-2957, 1997 https://doi.org/10.1063/1.120227
  6. Y.-Y. Xie, A. Knoll, Y. Chen, Y. Li, X. Xiong, Y. Qiao, P. Hou, J. Reeves, T. Salagaj, K. Lenseth, L. Civale, B. Maiorov, Y. Iwasa, V. Solovyov, M. Suenaga, N. Cheggour, C. Clickner, J.W. Ekin, C. Weber, V. Selvamanickam, "Progress in scale-up of second-generation high-temperature superconductors at SuperPower Inc," Physica C, vol. 426-431, pp. 849-857, 2005 https://doi.org/10.1016/j.physc.2005.03.071
  7. X. Li, M.W. Rupich, W. Zhang, N. Nguyen, T. Kodenkandath, U. Schoop, D.T. Verebelyi, C. Thieme, M. Jowett, P.N. Arendt, S.R. Foltyn, T.G. Holesinger, T. Aytug, D.K. Christen, and M.P. Paranthaman, "High critical current MOD ex situ YBCO films on $RABiTS^{TM}$ and MgO-IBAD templates," Physica C, vol. 390, pp. 249-253, 2003 https://doi.org/10.1016/S0921-4534(03)00803-7