• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.30 no.12 s.255
• /
• pp.1211-1217
• /
• 2006

This study is focused on oxidation prevention of STS430, which is generally used as solid oxide fuel cell(SOFC) interconnect at intermediate operating temperatures with oxidation-proof coatings. Inconel, $La_{0.6}Sr_{0.4}CoO_3(LSCo)$ and $La_{0.6}Sr_{0.4}CoO_3(LSCr)$ were chosen as coating materials. Using a radio frequency magnetron sputtering method, each target material was deposited as thin film on STS430 and was analyzed to find out favorable conditions. In this study, LSCr-coated STS430 can reduce electrical resistance to 1/3 level, compared with uncoated STS430. Also, long-term durability test at $700^{\circ}C$ for 1000 hours tells that LSCr thin layer performs an important role to prohibit serious degradations. Superior oxidation-resistant characteristic of LSCr-coated STS430 is attributed to the inhibition of spinel structure formation such as $MnCr_2O_4$.

• Journal of Electrochemical Science and Technology
• /
• v.11 no.1
• /
• pp.92-98
• /
• 2020

SnO₂-based high-capacity anode materials are attractive candidate for the next-generation high-performance lithium-ion batteries since the theoretical capacity of SnO₂ can be ideally extended from 781 to 1494 mAh g^-1. Here 3D etched Cu foam is applied as a current collector for electron path and simultaneously a substrate for the SnO₂ coating, for developing an integrated electrode structure. We fabricate the 3D etched Cu foam through an auto-catalytic electroless plating method, and then coat the SnO₂ onto the self-supporting substrate through a simple sol-gel method. The catalytic dissolution of Cu metal makes secondary pores of both several micrometers and several tens of micrometers at the surface of Cu foam strut, besides main channel-like interconnected pores. Especially, the additional surface pores on etched Cu foam are intended for penetrating the individual strut of Cu foam, and thereby increasing the surface area for SnO₂ coating by using even the internal of Cu foam. The increased areal capacity with high structural integrity upon cycling is demonstrated in the SnO₂-coated 3D etched Cu foam. This study not only prepares the etched Cu foam using the spontaneous chemical reactions but also demonstrates the potential for electroless plating method about surface modification on various metal substrates.

• Journal of Welding and Joining
• /
• v.22 no.5
• /
• pp.46-52
• /
• 2004

AlSi-Al$_2$O$_3$ composite layer was prepared by plasma spray on steel substrate. The composite powder for plasma spray was prepared by simple mechanical blending. The wear resistance of the composite layers and matrix aluminum alloy were performed in terms of size distribution of ceramic particles. Friction coefficients of AlSi were decreased with incorporation of $Al_2$O$_3$. The tribological properties of coated layers were affected by the size of incorporated $Al_2$O$_3$ particle. The reinforcement of $Al_2$O$_3$ particle into aluminum alloy matrix decreased the friction coefficient as well as wear loss.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2001.11a
• /
• pp.96-102
• /
• 2001

plasma-sprayed Cr$_2$O$_3$-based coatings containing MoO$_3$ were studied to gain a better understanding of the influence of MoO$_3$ composition in the coatings on their tribological behaviour. A reciprocal type tribo-tester was employed to examine friction and wear behavior of the specimens at high temperature(450。C). The physical characteristics of worn surfaces were investigated by scanning electron microscopy and chemical composition of the coating surfaces was analyzed using a X-ray photoelectron spectrometer. The results showed that friction coefficient of the MoO$_3$-added coatings were lower than those without MoO$_3$ addition. The larger protecting layers were observed at the worn surface of plasma spray coated specimens with MoO$_3$ addition. XPS analysis of the protecting layer indicated that MoO$_3$ composition was dominantly formed at the surface. MoO$_3$ composition in the protecting layer appears to be more favorable in reducing the friction.

• Journal of the Korean Ceramic Society
• /
• v.40 no.2
• /
• pp.153-158
• /
• 2003

Self-patterning of thin films using photosensitive sol solution has advantages such as simple manufacturing process compared to photoresist/dry etching process. In this study,$La_{0.5}SR_{0.5}CoO_3$(LSCO) thin films as an electrode material for ferroelectric memories have been prepared by spin coating method using photosensitive sol solution. La-2methoxyethoxide, Sr-ethoxide, Co-2methoxyethoxide were used as starting materials. As UV exposure time to the LSCO gel thin film increased, the UV absorption peak intensity of metal${beta}$-diketonate decreased due to reduced solubility by M(metal)-O-M bond formation. Solubility difference by UV irradiation on LSCO gel thin film allows to obtain a fine patterning of thin film. The LSCO thin films annealed over$680{\circ}C$ in air showed perovskite phase and the lowest resistivity$(4{ imes}10^{-3}{Omega}cm)$ of the thin films were obtained by annealing at$740{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.51 no.6
• /
• pp.598-604
• /
• 2014

Considerable research efforts have been explored attempting to enhance the thermal durability of thermal barrier coatings (TBCs) at the high operating temperatures of gas turbines. In this study, the suspension plasma spray (SPS) process was applied to produce TBCs with a segmented structure by using an yttria-stabilized zirconia (YSZ) suspension. Four different experiment sets were carried out by controlling the ratio between surface roughness of the bond coat and feed stock size ($R_a/D_{50}$) in order to examine the effect of $R_a/D_{50}$ ratio on the microstructure of SPS-prepared coatings. When the $R_a/D_{50}$ had a high value of 11.8, a deposited thick coating turned out to have a cone-type columnar microstructure. In contrast, at the low $R_a/D_{50}$ values of 2.9 and 0.18, a deposited thick coating appeared to have a dense, vertically-cracked microstructure. However, with the very low $R_a/D_{50}$ value of 0.05 the coating was delaminated.

• Korean Journal of Materials Research
• /
• v.4 no.2
• /
• pp.166-176
• /
• 1994

Ni base superalloys are composed of solid sohltion hardening elements(Co, Cr. Mo. W and so on) and $\gamma '$ precipitation hardening elements(A1, Ti, Nb, Ta and so on). To Improve the mechanical properties and oxidation resistanre of superalloys, rare earth elements(%r, Hf, Y and so on) are added to the inner substrate, or are used as coating materials. Their pffects on the growth rate and adhes~on of oxide are changed according to the kinds of oxides such as $AI_2O_3$ and $Cr_2O_3$. The effect of yttrium on the oxidation rate, grain size of oxide, internal structure, and crack resistance was investigated for two kinds of Ni-base superalloys. One in AF'115 superalloy containing Hf and the other is MA6000 superalloy containing $Y_2O_3$. They werr owid~zed at high temperature after yttrium surface modification using ion coater. Yttrium coating on the AF115 and MA6000 superalloys results in a marked change in the growth of the inner oxide. For AF115 superalloy, the degree of gram boundary segregation of $Cr_2O_3$, and prefer en^ tial oxidation of Hf are decreased, and the shape of inner oxidation layer was changed from triangle to plate type. For MA6000 superalloy, $Cr_2O_3$ oxide scale was transformed as outer oxidation layer of CrZOI and inner oxidation layer of $Cr_2O_3$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.351-354
• /
• 1998

The formation of the $YBa_2Cu_30_{7_\delta}$(Y123) thick films has been investigated by a surface diffusion Imcess between $3BaCu0_2$+2CuO composite coating powder and a $Y_2BaCuO_5$(Y211). This reaction has been studied in the temperature of $930^{\circ}C$ and $940^{\circ}C$ for 2h to 10h in an oxygen atmosphere. The Y211 substrates becomes covered by co-precipitation of Y123 grains and CuO inclusions. X-ray diflractotnctn. revealed that the lager consisted of an orthorhombic crystal structure. The maximum Jc of $400A/\textrm{cm}^2$ is abtained when the specimen was heat-treated at $930^{\circ}C$ for 6h on the Y211 substrate.

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.114-116
• /
• 2003

The multi function sprayed coating is used for direct-heating, wear resistance and high bonding strength. The merits of surface direct-heating coatings are short warming time, low power consumption and better wear resistance that can be used in many organization parts. In this study, the surface direct-heating and wear resistance can be improved by spraying the proper materials on the surface $Al_2$O$_3$40%TiO$_2$ powder and Ni-20%Cr powder that had the properties of conduction and high wear resistivity are used in order to improve wear resistance, electrical properties and bonding strength.

• Korean Journal of Materials Research
• /
• v.29 no.5
• /
• pp.328-335
• /
• 2019

Nb-doped $TiO_2$(NTO) coated NiCrAl alloy foam for hydrogen production is prepared using ultrasonic spray pyrolysis deposition(USPD) method. To optimize the size and distribution of NTO particles based on good physical and chemical stability, we synthesize particles by adjusting the weight ratio of the Nb precursor solution(5 wt%, 10 wt% and 15 wt%). The morphological, chemical bonding, and structural properties of the NTO coated NiCrAl alloy foam are investigated by X-ray diffraction(XRD), X-ray photo-electron spectroscopy(XPS), and Field-Emission Scanning Electron Microscopy(FESEM). As a result, the samples of controlled Nb weight ratio exhibit a common diffraction pattern at ${\sim}25.3^{\circ}$, corresponding to the(101) plane, and have chemical bonding(O-Nb=O) at 534 eV. The NTO particles with the optimum weight ratio of N (10 wt%) show a uniform distribution with a size of ~18.2-21.0 nm. In addition, they exhibit the highest corrosion resistance even in the electrochemical stability estimation. As a result, the introduction of NTO coated NiCrAl alloy foam by USPD improves the chemical stability of the NiCrAl alloy foam by protecting the direct electrochemical reaction between the foam and the electrolyte. Thus, the optimized NTO coating can be proposed for excellent protection of NiCrAl alloy foam for hydrocarbon-based steam methane reforming(SMR).