• Bulletin of the Korean Chemical Society
• /
• v.28 no.11
• /
• pp.2089-2092
• /
• 2007

Tantalum-containing metal oxides, well known for their efficiency in water splitting and H2 production, have never been used in visible light driven photodecomposition of H2S and H2 production. The present work is an attempt in this direction and investigates their efficiency. A mixed metal oxide, ZnFe2Ta2O9, with the inclusion of Fe2O3 to impart color, was prepared by the conventional ceramic route in single- and double-calcinations (represented as ZnFe2Ta2O9-SC and ZnFe2Ta2O9-DC respectively). The XRD characterization shows that both have identical patterns and reveals tetragonal structure to a major extent and a minor contribution of orthorhombic crystalline system. The UV-visible diffuse reflection spectra demonstrate the intense, coherent and wide absorption of visible light by both the catalysts, with absorption edge at 650 nm, giving rise to a band gap of 1.9 eV. Between the two catalysts, however, ZnFe2Ta2O9-DC has greater absorption in almost the entire wavelength region, which accounts for its strong brown coloration than ZnFe2Ta2O9-SC when viewed by the naked eye. In photocatalysis, both catalysts decompose H2S under visible light irradiation (λ ≥ 420 nm) and produce solar H2 at a much higher rate than previously reported catalysts. Nevertheless, ZnFe2Ta2O9-DC distinguishes itself from ZnFe2Ta2O9-SC by exhibiting a higher efficiency because of its greater light absorption. Altogether, the tantalum-containing mixed metal oxide proves its efficient catalytic role in H2S decomposition and H2 production process also.

• Development and Reproduction
• /
• v.4 no.2
• /
• pp.203-213
• /
• 2000

To investigate the effects of reactive oxygen species (ROS) on capacitation, acrosome reaction in human spermatozoa. Human spermatozoa were incubated with xanthine-xanthine oxidase (X-XO), $H_2O$$_2$, sodium nitroprusside (SNP) or lymphocyte. Otherwise, spermatozoa were incubated under low $O_2$ (5 ％) condition. Chlortetracycline (CTC) staining was conducted to assess capacitation and acrosome reaction. Analysis of lipid peroxidation was done by spectrophotometric determination of malondialdehyde (MDA) production in spermatozoa. $H_2O$$_2$, X-XO, SNP and lymphocyte treatment significantly increased capacitated spermatozoa within 1 h of incubation. There was no significant difference in capacitation between low- and high $O_2$ groups. In the presence of low concentration of $H_2O$$_2$, lipid peroxidation decreased significantly. However, under the high concentration of $H_2O$$_2$, lipid peroxidation significantly increased at the end of incubation compared to control. In the presence of high concentration of lymphocytes, lipid peroxidation significantly increased compared to control at 1hr of incubation. There was no significant difference in lipid peroxidation according to $O_2$ concentration examined. Acrosome reaction (AR) was evaluated by CTC staining after the progesterone challenge. In all ROS groups, AR increased compared to control. The X(100 $\mu$M) - XO (100mIU) system was the most potent to induce AR. Taken together, it suggested positive control of AR by ROS and the positive relationship between the lipid peroxidation and AR. The early onset of capacitation in the presence of ROS suggest that ROS might be a positive regulator of sperm capacitation and hyperactivation.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.2
• /
• pp.47-51
• /
• 2007

F-doped SiOC : H thin films with low refractive index were deposited on Si wafer and glass substrate by plasma enhanced chemical vapor deposition (PECVD) as a function of rf powers, substrate temperatures, gas rates and their composition flow ratios ($SiH_4,\;CF_4$ and $N_2O$). The refractive index of the F-doped SiOC : H film continuously decreased with increasing deposition temperature and rf power. As $N_2O$ gas flow rate decreased, the refractive index of the deposited films decreased down to 1.3778, reaching a minimum value at rf power of 180W and $100^{\circ}C$ without $N_2O$ gas. The fluorine content of F-doped SiOC : H film increased from 1.9 at% to 2.4 at% as the rf power was increased from 60 W to 180 W, which results in the decrease of refractive index.

• The Plant Pathology Journal
• /
• v.23 no.4
• /
• pp.300-307
• /
• 2007

Previously, a chloroplast-localized Cu,Zn superoxide dismutase (chCu,ZnSOD) was isolated from lily and the sense- and antisense- sequences of the lily chCu,ZnSOD were used to transform potato plants. Two selected lines, the sense- and anti-sense strand of transgenic plants, were further characterized for resistance to Erwinia carotovora, which is a severe pathogen affecting potato plants. Only the sense-strand transgenic potato, which contained less $O_2^{.-}$ and more $H_2O_2$ than wild-type and antisense-strand transgenic plants, showed increased resistance to E. carotovora. Additional studies using $O_2^{.-}$ or $H_2O_2$ scavengers in wild-type, sense-strand, and antisense-strand transgenic plants suggest that resistance to E. carotovora is induced by reduced $O_2^{.-}$ and is not influenced by $H_2O_2$. To the best of our knowledge, this report is the first study suggesting that resistance to E. carotovora is enhanced by reduced $O_2^{.-}$, and not by increased amounts of $H_2O_2$.

• Journal of Power System Engineering
• /
• v.17 no.5
• /
• pp.13-22
• /
• 2013

This paper reports the investigation of the physical and chemical characteristics of the prepared 3Pt-2MgO-$3ZrO_2$-$2CeO_2/Al_2O_3$ DOC, based on its hydrothermal aging. As a result of impregnating and reducing the $H_2PtCl_6$ $6H_2O$ precursor on a ${\gamma}-Al_2O_3$ basis, it was well dispersed into small particles with the range 2-3nm. This was because the $Al_2O_3$ acted as a barrier to prevent movement of the catalyst particles. For a hydrothermally aged catalyst for 9h at $700^{\circ}C$, its performance when purifying harmful gases decreased compared to a fresh catalyst, but its specific surface area was at the same level. This was because the performance of the catalyst was reduced by the sintering of the precious metal Pt, rather than by washcoat sintering and pore clogging. For an excessively hydrothermally aged catalyst for 9h at $850^{\circ}C$, Pt grew into an approximately 50nm class, formed a cluster compared to a fresh catalyst. The $CeO_2$ promoters also formed clusters among components of the same type, reducing their specific surface area to $114m^2/g$, which was 14% less than a fresh catalyst.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.4
• /
• pp.149-153
• /
• 2021

ε-Ga₂O₃ thin films were grown on 4H-SiC substrates by metal organic chemical vapor deposition (MOCVD) and crystalline quality were evaluated depend on growth conditions. It was found that the best conditions of the ε-Ga₂O₃ were grown at a growth temperature of 665℃ and an oxygen flow rate of 200 sccm. Two-dimensional growth was completed after the merge of hexagonal nuclei, and the arrangement direction of hexagonal nuclei was closely related to the crystal direction of the substrate. However, it was confirmed that crystal structure of the ε-Ga₂O₃ had an orthorhombic rather than hexagonal. Crystal phase transformation was performed by thermal treatment. And a β-Ga₂O₃ thin film was grown directly on 4H-SiC for the comparison to the phase transformed β-Ga₂O₃ thin film. The phase transformed β-Ga₂O₃ film showed better crystal quality than directly grown one.

• Journal of Environmental Health Sciences
• /
• v.42 no.2
• /
• pp.112-117
• /
• 2016

Objectives: In this study, we investigated the biodegradation rates of 8 perfluorooctanesulfonate (PFOS) alternatives synthesized at the at Changwon National University in comparison to those of PFOS potassium salt and PFOS sodium salt. Methods: A biodegradability test was performed for 28 days with microorganisms cultured in the good laboratory practice laboratory at the Korea Environment Corporation following the OECD Guidelines for the testing of chemicals, Test No. 301 C Results: While $C_5H_8F_3SO_3K$, $C_8F_{17}SO_3K$ and $C_8F_{17}SO_3Na$ were not degraded after 28 days, the 3 alternatives were biodegraded at the rates of 31.4% for $C_8H_8F_9SO_3K$, 25.6% for $C_{10}H_8F_{13}SO_3K$, 23.6% for $C_{25}F_{17}H_{32}S_3O_{13}Na_3$, 20.9% for $C_{15}F_9H_{21}S_2O_8Na_2$, 15.5% for $C_{23}F_{18}H_{28}S_2O_8Na_2$, 8.5% for $C_{17}F_9H_{25}S_2O_8Na_2$ and 4.8% for $C_6H_8F_5SO_3K$. When the concentration was the same(500 mg/L), $C_{23}F_{18}H_{28}S_2O_8Na_2$ had the lowest tension with 20.94 mN/m, which was followed by $C_{15}F_9H_{21}S_2O_8Na_2$ (23.36 mN/m), $C_{17}F_9H_{25}S_2O_8Na_2$ (27.31 mN/m), $C_{25}F_{17}H_{32}S_3O_{13}Na_3$ (28.17 mN/m), $C_{10}H_8F_{13}SO_3K$ (29.77 mN/m) and $C_8H_8F_9SO_3K$ (33.89 mN/m). Having higher surface tension of 57.64 mN/m and 67.57 mN/m, respectively, than those of the two types of PFOS salts, $C_6H_8F_5SO_3K$ and $C_5H_8F_3SO_3K$ were found valueless as substitute for PFOS. Conclusion: The biodegradation test suggest that 6 compounds could be used as substitutes for PFOS. $C_{23}F_{18}H_{28}S_2O_8Na_2$ and $C_{15}F_9H_{21}S_2O_8Na_2$ were found to be the best substitutes based on biodegradation rate and surface tension, followed by $C_{25}F_{17}H_{32}S_3O_{13}Na_3$, $C_8H_8F_9SO_3K$ and $C_{10}H_8F_{13}SO_3K$. $C_{17}F_9H_{25}S_2O_8Na_2$ was found to have relatively low value as an alternative but it still had a potential to substitute the conventional PFOS.

• Journal of the Korean Ceramic Society
• /
• v.24 no.5
• /
• pp.431-436
• /
• 1987

High purity Al2O3 has been extracted from serlcite of clayminerals, selicite was treated by H2SO4(2N∼18N) solution, NH4OH treatment(PH8.5∼10.0) and metallic impurities such as Fe were removed by NaOH treatment. The tendency of extraction yield of ${\alpha}$-Al2O3 have been investigated by relating reaction time, acid concentration. Reaction products were analyzed by DT-TGA, chemical analysis and X-ray diffractometer. Prepared ${\alpha}$-Al2O3 power is fired in air at 1400$^{\circ}C$, 1600$^{\circ}C$ 2hr. The results are as follows; 1. The most suitable extracting conditions of ${\alpha}$-Al2O3 from Selicite were N-H2SO4, 120 min acidtreating time. 2. The optimum pH condition was 9.0. 3. Physical properties of sintered Al2O3 bodies were as follows. Relative density is 99%. Water absorption is 0.26%. Rock well hardness is 89.

• Proceedings of the Korean Vacuum Society Conference
• /
• 1997.07a
• /
• pp.162-162
• /
• 1997

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2000.05a
• /
• pp.55-56
• /
• 2000