Physicochemical Characteristics Based on Hydrothermal Aging of Prepared DOC

  • Seo, Choong-Kil (Department of Automotive & Mechanical Engineering, Howon University)
  • Received : 2013.07.31
  • Accepted : 2013.10.09
  • Published : 2013.10.31
Download PDF
⟨ Previous Next ⟩

Abstract

This paper reports the investigation of the physical and chemical characteristics of the prepared 3Pt-2MgO-$3ZrO_2$-$2CeO_2/Al_2O_3$ DOC, based on its hydrothermal aging. As a result of impregnating and reducing the $H_2PtCl_6$ $6H_2O$ precursor on a ${\gamma}-Al_2O_3$ basis, it was well dispersed into small particles with the range 2-3nm. This was because the $Al_2O_3$ acted as a barrier to prevent movement of the catalyst particles. For a hydrothermally aged catalyst for 9h at $700^{\circ}C$, its performance when purifying harmful gases decreased compared to a fresh catalyst, but its specific surface area was at the same level. This was because the performance of the catalyst was reduced by the sintering of the precious metal Pt, rather than by washcoat sintering and pore clogging. For an excessively hydrothermally aged catalyst for 9h at $850^{\circ}C$, Pt grew into an approximately 50nm class, formed a cluster compared to a fresh catalyst. The $CeO_2$ promoters also formed clusters among components of the same type, reducing their specific surface area to $114m^2/g$, which was 14% less than a fresh catalyst.

Keywords

References

  1. C. K. Seo, B. C. Choi and Y. K. Kim, 2013, "Volume Optimization of a Combined System of LNT and SCR Catalyst Considering Economic Feasibility and De-NOx Performance", Journal of the Korea Society For Power System, Vol. 17, pp. 19-26. https://doi.org/10.9726/kspse.2013.17.1.019
  2. W. S. Kang, B. C. Choi and H. N. Kim, 2013, "Characteristics of the Simultaneous Removal of PM and NOx Using CuNb-ZSM-5 Coated on Diesel Particulate Filter", Journal of Industrial and Engineering Chemistry, Vol. 19, pp. 1406-1412. https://doi.org/10.1016/j.jiec.2013.01.004
  3. J. Stepanek, P. Koci, F. Plat, M. Marek, and M. Kubicek, 2010, "Investigation of Combinded DOC and NSRC Disel Car Exhaust Catalyst" Computers and Chemical Engineering, Vol. 34, pp.744-752. https://doi.org/10.1016/j.compchemeng.2010.01.003
  4. M. H. Wiebenga, C. H. Kim, S. J. Schmieg, S. H. Oh, D. B. Brown, D. H. Kim, J. H, Lee, C and H. F. Peden, 2012, "Deactivation Mechanism of Pt/Pd-based Oxidation Catalysts", Vol. 184, pp. 197-204. https://doi.org/10.1016/j.cattod.2011.11.014
  5. A. Winkler, D. Ferri and M. Aguirre, 2009, "The Influence of Chemical and Thermal Aging on the Catalytic Activitiy of a Monolithic Diesel Oxidation Catalyst", Applied Catalysis B, Vol. 93, pp. 177-184. https://doi.org/10.1016/j.apcatb.2009.09.027
  6. S. Ye, Y. H. Yap, S. T. Kolaczkowski, k. Robinson and D. Lukyanov, "Catalyst 'Light-off' Experiments on a Diesel Oxidation Catalyst Connected to a Diesel Engine- Methodology and Techniques", Chemical Engineering Research and Design Vol. 90, pp. 834-845. https://doi.org/10.1016/j.cherd.2011.10.003
  7. J. E. Johnson and D. B, Kittelson, 1996, "Depostion, Diffusion and Adsorption in the Diesel Oxidation Catalyst", Applied Catalysis B, Vol. 10, pp. 117-137. https://doi.org/10.1016/0926-3373(96)00027-6
  8. S. Stadlbauer, H. Waschl, A. Schilling and L. D. R, "DOC Temperature Control for Low Temperature Operating Ranges with Post and Main Injection Actuation", SAE 2013-01-1580.
  9. B. C. Choi, C. H. Lee, H. J. Park, M. G. Park and B. S. Shin, "Durability Evaluate of Diesel Oxidation Catalysts", KSAE 03-50054, pp. 336-341.
  10. S. J. Eaton, B. G. Bruce and T. J. Toops, "The Roles of Phosphorus and Soot on the Deactivation of Diesel Oxidation Catalyst", SAE 2009-01-0628.
  11. A. Knafl, M. Han, S. V. Bohac and D. N. Assanis, "Comparison of Diesel Oxidation Catalyst Performance of an Engine and a Gas Flow Reactor", SAE 2007-01-0231.
  12. S. R. Katare, J. E. Patterson and P. M. Laing, "Aged DOC is A Net Consumer of NO2", SAE 2007-01-3984.
  13. C. K. Seo, B. C. Choi, H. N. Kim, C. H. Lee and C. B. Lee, 2012, "Effect of $ZrO_{2}$ Addition on De-NOx Performance of Cu-ZSM-5 for SCR Catalyst", Chemical Engineering Journal, Vol. 191, pp. 331-340. https://doi.org/10.1016/j.cej.2012.03.027
  14. C. K. Seo, H. N, Kim, B. C. Choi, M. T. Lim, C. H. Lee and C. B. Lee, 2011, "De-NOx Characteristics of a Combined System of LNT and SCR Catalysts According to Hydrothermal Aging and Sulfur Poisoning", Catalysis Today, Vol. 164, pp. 507-514. https://doi.org/10.1016/j.cattod.2010.10.010
  15. Z. Q. Tian, 2004, "Preparation of High Loading Pt Supported by Carbon by On-site Reduction", Journal of Materials Science, Vol. 39, pp. 1507-1509. https://doi.org/10.1023/B:JMSC.0000013930.18552.41
  16. K. W. Park, J. O. Choi and Y. E. Sung, 2003, "Structural, Chemical, and Electronic Properties of Pt/Ni Thin Film Electronics for Methanol Electrooxidation", Journal Phys. Chem. B, Vol. 107, pp. 5851-5856. https://doi.org/10.1021/jp0340966
  17. Catalyst Fundamentals, DieselNet Technology Guide, www.dieselnet.com, 2000.11.

Cited by

  1. Vanadia SCR의 열적 열화에 따른 조촉매의 영향 vol.18, pp.3, 2013, https://doi.org/10.9726/kspse.2014.18.3.014