• Bulletin of the Korean Chemical Society
• /
• v.21 no.12
• /
• pp.1193-1198
• /
• 2000

The preparation of nanocrystalline hematite, ${\alpha}-Fe_2O_3$, paricles and their surface coating with silica layers are described. The hematite particles with the size of 30~60 nm are firstly prepared by thermal decomposition of trinuclear acetate-hydroxo iron (III) nitrate complex, $[Fe_3$(OCOCH_3)_7$OH${\cdot}$2H_2O]NO_3$, at $400^{\circ}C$. Subsequently the hematite surfaces are coated with siliva layers by a controlled hydrolysis and condensation reaction of TEOS with varying the TEOS concentration and pH. Monodispersed and spherical $SiO_2-coatedFe_2O_3$ particles with the average particle diameter of ~90 nm and extremely narrow size distribution can be obtained at the pH of 11 and the TEOS concentration of 0.68M, which are found to be the optimum conditions in the present study in achieving the homogeneous deposition of silica layers on hematite surfaces. Diffuse reflectance UV-Vis spectra reveal that the characteristic optical reflectance of ${\alpha}-Fe_2O_3$ particles is preserved almost constant even after coating the surfaces, suggesting that the $SiO_2$ layers can be regarded as protecting layers without degrading the optical properties of hematite particles.

• Economic and Environmental Geology
• /
• v.24 no.4
• /
• pp.335-346
• /
• 1991

It is observed that calcareous nodules of the Hwajeol Formation are locally skarnized in the Sangdong district, in which the skarn mineralization extends 5 Km westward from the Sangdong mine area to the Hwajeolchi area. After a hidden granite beneath the Sangdong mine was discovered by exploration drillings, the exploration teams of the Sangdong mine and the Korean Mining Promotion Corporation have assumed that the skarn nodule of the Hwajeol Formation was derived from emplacement of a granite in deep place and the occurrence of hidden ore bodies below the skarn, and they have discovered high grades of tungsten orebody in the same horizon of the Sangdong ore body. Mutual genetic relatioships between epidote and garnet may be explained by following chemical reactions $Ca_2FeA_{12}$ $Si_3O_{12}(OH)+CaCO_3=Ca_3(Fe,\;Al)_2$ $SiO_{12}+1/2CO_2+1/2H^+Ca_3FeSi_3O_{12}+SiO_2+CO_2=2CaFeSi_{12}O_6+CaCO_3+1/2O_3$. It is concluded that epidote and garnet are useful as target minerals indicating a potential occurrence of deep seated hidden ore body. Since the epidote may inform the emplacement of the granite, while the garnet in the skarn nodule of the Hwajeol Formation may reflect a strong hydrothermal mineralization taking place from the depth.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.3
• /
• pp.312-319
• /
• 2017

For high value-added applications of natural blue diatomite, the physical refining process and synthesis of SiC from refined diatomite were investigated. Approximately 30 percent Fe ($Fe_2O_3$) in raw blue diatomite was removed by a particle sieve separation process; the Fe composition for 325 mesh down powder was approximately 2 percent. Although a wet and/or dry magnetic separation process had some influence on the separation and/or refining of Fe composition, the Fe composition in the non-magnetic by-product was approximately 2 percent. Water leaching separation was effective in removing the Fe composition; approximately 40 percent of the Fe in raw blue diatomite was removed. The synthesis of ${\beta}$-SiC by a carbothermal reduction of the $SiO_2$ in the refined diatomite using carbon (graphite, carbon black), the effects of an acid-treatment on removing the Fe, and the specific surface area for the synthesized powder were also investigated. The impurities were mostly eliminated and the specific surface area was increased to $52.5m^2/g$.

• Journal of the Korean Ceramic Society
• /
• v.41 no.9
• /
• pp.642-646
• /
• 2004

Na$_2$Si$_2$O$_{5}$ added to the solution affects the hydration of 4CaOㆍAl$_2$O$_3$ㆍFe$_2$O$_3$ with calcium sulfate. The reaction between 4CaOㆍAl$_2$O$_3$ Fe$_2$O$_3$and CaSO$_4$ㆍ 2$H_2O$ decrease with increasing amount of Na$_2$Si$_2$O$_{5}$ in solution, owing to low hydraulic reactivity of 4CaOㆍAl$_2$O$_3$ㆍFe$_2$O$_3$by the adsorption of silicate ions on the surface of 4CaOㆍAl$_2$O$_3$ㆍ Fe$_2$O$_3$ particles. The dissolution rate of 4CaOㆍAl$_2$O$_3$ㆍ Fe$_2$O$_3$ particles deceased with the increase of the concentration of silicate ion in solution. When the 4CaOㆍAl$_2$O$_3$ㆍFe$_2$O$_3$ particles was hydrated in gypsum - Na$_2$Si$_2$O$_{5}$ solution, the hydration was retarded and the rate could not discriminate between formation of ettringite and that of monosulfate, and it stopped in high concentration of silicate ions. However, silicate ion did not any effect on the dissolution rate of gypsum.ypsum.

• Journal of Surface Science and Engineering
• /
• v.44 no.5
• /
• pp.201-206
• /
• 2011

Fe-2%Mn-0.5%Si alloys were corroded at 600, 700 and $800^{\circ}C$ for up to 70 h in 1 atm of $N_2$ gas, or 1 atm of $N_2/H_2O$-mixed gases, or 1 atm of $N_2/H_2O/H_2S$-mixed gases. Oxidation prevailed in $N_2$ and $N_2/H_2O$ gases, whereas sulfidation dominated in $N_2/H_2O/H_2S$ gases. The oxidation/sulfidation rates increased in the order of $N_2$ gas, $N_2/H_2O$ gases, and, much more seriously, $N_2/H_2O/H_2S$ gases. The base element of Fe oxidized to $Fe_2O_3$ and $Fe_3O_4$ in $N_2$ and $N_2/H_2O$ gases, whereas it sulfidized to FeS in $N_2/H_2O/H_2S$ gases. The oxides or sulfides of Mn or Si were not detected from the XRD analyses, owing to their small amount or dissolution in FeS. Since FeS was present throughout the whole scale, the alloys were nonprotective in $N_2/H_2O/H_2S$ gases.

• Journal of the Korean Magnetics Society
• /
• v.20 no.6
• /
• pp.222-227
• /
• 2010

$BiFeO_3$ (BFO) thin films were deposited on Pt/Ti/$SiO_2$/Si(100) substrates by RF magnetron sputtering method at room temperature. The influence of the flow rate of $O_2$ gas on the preparation of $BiFeO_3$ thin films was studied. XRD results indicate that the $BiFeO_3$ thin films were crystallized to the perovskite structure with the presence of small amount of impurity phases. The flow rate of $O_2$ gas has great affect on the microstructures and magnetic properties of $BiFeO_3$ thin films. As flow rate of $O_2$ gas increased, roughness and grain size of the thin films increased. $BiFeO_3$ thin films exhibited weak ferromagnetic behavior at room temperature. The PFM images revealed correlation between the surface morphology and the piezoresponse, indicating that the piezoelectric coefficient is related to microstructure.

• Journal of Korean Society of Environmental Engineers
• /
• v.30 no.11
• /
• pp.1116-1122
• /
• 2008

The existing technology which is for recycling aggregate using dried swage sludge have been limited for practical application, because the properties of aggregate are not regular and don't meet the recycling aggregate standard. In this research, an innovative slag-producing technology is developed by addition of oyster shell, waste cast-sand and iron-rust as inorganic waste additives. The mixed slag with the additives was evaluated at the various ratio of CaO/SiO$_2$, SiO$_2$/Al$_2$O$_3$ and Fe$_2$O$_3$/SiO$_2$. When the waste sludge was melted at 1,400$^{\circ}C$ during 20 minutes, the optimal ratio of CaO/SiO$_2$ for the slag added the oyster shell, SiO$_2$/Al$_2$O$_3$ for added the waste cast-sand and Fe$_2$O$_3$/SiO$_2$ for added the iron-rust were 1.00, 3.00 and 0.60, respectively. At the optimal condition, the bulk density of the slag was 2.24 g/cm$^3$, 2.45 g/cm$^3$ and 2.73 g/cm$^3$, And the 24 h water adsorption was 4.72%, 1.44% and 0.37%, respectively. Therefore it is proved that adding the waste additives to the process of the slag production contributed for elevation of recycling aggregate properties. And also it is expected that production cost can be reduced by decreased melting temperature.

• Journal of the Korean Ceramic Society
• /
• v.36 no.4
• /
• pp.410-416
• /
• 1999

The reactivity of three kinds of spinels which CaO-Al2O3-SiO2 slag was investigated in terms of mineral phases and microstructures. New crystal products were not formed by reaction of 12CaO.7Al2O3 in the slag with spinels and free MgO components was preferenctially dissolved into slag for MgO-rich spinel and stoichiometric spinel. Meanwhile mineral phase was changed from 12CaO.7Al2O3 to CaO.Al2O3 to CaO.2Al2O3 finally to CaO.6Al2O3 having high melting point for Al2O3 -rich spinel. The Fe-oxide component of the slag was taken up by only stoichiometric spinel grains within the spinel clinker and the trapped amount of Fe-oxide was independent of MgO content of MgO in spinel clinker the more th resistance to slag corrosion but the less resistance to slag penetration.

• Journal of the Korean Magnetics Society
• /
• v.9 no.6
• /
• pp.296-300
• /
• 1999

Cross-shape structures of spin tunneling junctions were fabricated using DC magnetron sputtering and metal masks. The film structures were $substrate/Ta/NiFe/FeMn/NiFe/CoFe/Al_2O_3/CoFe/NiFe$ and $substrate/Ta/NiFe/CoFe/ Al_2O_3/CoFe/NiFe/FeMn/NiFe$. Fabrication conditions of insulating layer ($Al_2O_3$) and thickness and sputtering power of each film layer were varied, and maximum magnetoresistance ratio of 24.3 % was obtained. Magnetic characteristic variations in the above mentioned two structures and two types of substrates (Corning glass 7059 and Si(111)) were compared. Annealing of the junctions was performed to find out magnetic characteristic variations expected from the device fabrication. Magneoresistance Ratio were observed to maintain as-deposited value up to 150 $^{\circ}C$ annealing and then to drop rapidly after 180 $^{\circ}C$ annealing.

• Journal of the Korean Ceramic Society
• /
• v.36 no.8
• /
• pp.829-834
• /
• 1999

The silica aerogels opacified via adding oxides were prepared by the sol-gel supercritical drying technique and their characteristics of mechanical strength and thermal conduction were investigated. The compressive strength of SiO2-10 mol% TiO2 and SiO2-10mol% Fe2O3 aerogels were 0.11 and 0.047 MP a respectively much higher than 0.025 MPa of pure silica aerogels. The thermal conductivity of silica aerogels opacified by TiO2 was as low as 0.02505 W/m${\cdot}$K at $400^{\circ}C$ It was found that the TiO2 -opacifier for improving mechanical strength and suppressing high temperature conduction of pure silica aerogels was more effective than the Fe2O3 -opacifier