• Journal of Photoscience
• /
• v.1 no.2
• /
• pp.83-88
• /
• 1994

The synergic effect of iron plus blue light on the peroxidation of membrane lipid was investigated, using liposomes made of phospholipid. While strong irradiation did not affect Fe$^{+2}$-promoted lipid peroxidation that turned out to be O$_2$-dependent, ferric iron in bright light exerted a pronounced effect on the initiation of lipid peroxidation: this combined action of light and Fe$^{+3}$ on liposomal membranes was apparently independent of O$_2$. When liposomal samples containing Fe$^{+3}$ were subjected to irradiation, some portions of Fe$^{+3}$ were converted into Fe$^{+2}$. The extent of the Fe$^{+3}$-Fe$^{+2}$ conversion increased with increasing time of irradiation, which resembled the dependence of Fe$^{+3}$-promoted lipid peroxidation on irradiation. Further, it was observed that the effect of irradiation in liposomal samples containing Fe$^{+2}$ was strikingly mimicked by that of Fe$^{+2}$ addition to the same samples. The obligatory requirement of a suitable Fe$^{+3}$/Fe$^{+2}$ ratio for the genesis of iron-dependent lipid peroxidation, a controversial proposition, was also confirmed by the observation that lipid peroxidation was substantially enhanced by the addition of a mixture of Fe$^{+3}$ and Fe$^{+2}$, as compared to the addition of Fe$^{+3}$ or Fe$^{+2}$ alone. The results obtained in this study not only suggest that light acts as an effector for initiating lipid peroxidation, when Fe$^{+3}$ is present in membrane systems, but also imply that any chemical or physical factor that influences the redox states of iron in membranes can play a role in lipid peroxidation reactions.

• Applied Chemistry for Engineering
• /
• v.31 no.1
• /
• pp.43-48
• /
• 2020

Fe₂O₃ nanoparticles with the mixed structure of cubic and nanorod were synthesized by precipitation, hydrothermal, sol-gel method, etching process and heat treatment. Fe₂O₃/TiO₂ core-shell (CS) of type Fe₂O₃@TiO₂ composite was fabricated on a 20 nm nanolayer of TiO₂ coated on the surface of Fe₂O₃ nanoparticles. Fe₂O₃/TiO₂ yolk-shell (YS) composite was prepared by chemical etching and heat treatment of Fe₂O₃/TiO₂ CS nanoparticles. Physical properties of Fe₂O₃, Fe₂O₃@TiO₂ CS and Fe₂O₃@TiO₂ YS nanoparticles were characterized by FE-SEM, HR-TEM and X-ray diffraction. The solar reflectance, commission internationale de l'Elcairage (CIE) color coordinate and heat shield temperatures of Fe₂O₃, CS and YS type Fe₂O₃@TiO₂ pigments filled with poly acrylate (PA) paints were investigated by UV-Vis-NIR spectrometer and homemade heat shield temperature measuring device. The Fe₂O₃@TiO₂ YS red pigment filled PA composite exhibited excellent near infrared light reflecting performance and also reduced the heat shield temperature of 13 ℃ than that of Fe₂O₃ filled counterparts.

• Journal of the Korean Institute of Telematics and Electronics
• /
• v.27 no.9
• /
• pp.1393-1401
• /
• 1990

The physical properties of \ulcorner-Fe2O3 raw materials were investigated. \ulcorner-Fe2O3/Pd thick film gas sensors were fabricated with screen-printing method and their electrical and sensitivity characteristics were analyzed. The irreversible phase transition from \ulcorner-Fe2O3 to \ulcorner-Fe2O3 occured at 500\ulcorner. At this time, the cation of tetrahedral sites moved into the octahedral sites. \ulcorner-Fe2O3 raw materials contained only trivalent and no divalent iron. Thecontents of divalent iron (Fe+\ulcorner were increased as detecting gases were adsorbed. The addition of Pd (1w/o) to \ulcorner-Fe2O3 enhanced the sensitivity to gases. The sentivity of \ulcorner-Fe2O3/Pd(1w/o) thick film to 5000ppm C4H10 was 97% at the operating temperature of 300\ulcorner.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2003.11a
• /
• pp.373-378
• /
• 2003

As a part of assessment of the structural material for the molten salt handling system, corrosion behavior of austenitic alloys, Fe-base and Ni-base in the molten salt of $LiCl-Li_2O_2$ was investigated in the range of temperature; 650~$725^{\circ}C$, time; 24- 168h, $Li_2O$; 3wt%, mixed gas; Ar-10%$O_2$. In the molten salt of $LiCl-Li_2O_2$, Ni-base alloys showed higher corrosion resistance than Fe-base alloys. Fe-base alloy with low Fe and high Ni contents exhibited better corrosion resistance. The scales of $Cr_2O_3$, $FeCr_2O_4$ on Fe-base alloys were showed, and $Cr_2O_3$, $NiFe_2O_4$ on Ni-base alloys were also showed.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.5
• /
• pp.974-978
• /
• 2008

Removal of heavy metal ions ($Cd^{2+}$ and $Zn^{2+}$) by electrocoagulation (ECG) was investigated in an acidic condition, which is necessary for re-using or discharging the mediated electrochemical oxidation (MEO) media. Effects of various parameters such as electrolytes, current densities, and electrode materials were examined for a metal-contaminated MEO system using $Fe^{2+}/Fe^{3+}$ pairs as a mediator. It was found that ECG with Al electrodes is greatly affected by the presence of $Fe^{2+}$. [$Cd^{2+}$] and [$Zn^{2+}$] remain constant until [$Fe^{2+}$] reaches a certain concentration level (ca. 10 mM). This preferential removal of $Fe^{2+}$ during ECG with Al electrodes is not alleviated by controlling current densities, potential programs, and solution mixing. ECG with Fe electrodes, on the other hand, resulted in relatively fast removal of $Cd^{2+}$ and $Zn^{2+}$ under coexistence of $Fe^{2+}$, indicative of the different role between $Fe^{n+}$ generated from an electrode and $Fe^{2+}$ initially present in a solution. When ECG was performed with Fe electrodes until [$Fe^{n+}$] became the same as the concentration of initially present $Fe^{2+}$, [$Cd^{2+}$] and [$Zn^{2+}$] were reduced to one-tenth of the initial concentrations, suggesting the possibility of a continuous use of the medium for a subsequent MEO process.

• Resources Recycling
• /
• v.26 no.4
• /
• pp.95-100
• /
• 2017

In this study, $Fe_2O_3$ was added as a flux to decrease melting temperature and refine during melting of Cu powder from scraped surface of the waste PCB (printed circuit board). The effect of $Fe_2O_3$ ratio to Cu powder and temperature on the recovery of Cu and content of impurities were investigated. It was found that the recovery of Cu was increased with increasing addition ratio of $Fe_2O_3$ and reaction temperature. The contents of O, Si and Fe in Cu phase were also decreased with increasing addition ratio of $Fe_2O_3$ and temperature. The formation of fayalite ($2FeO{\cdot}SiO_2$) and iron oxides phases in the slag was confirmed by XRD analysis after reaction with $Fe_2O_3$. Therefore, it was considered that the decrease of melting temperature and viscosity of slag by formation of fayalite slag contributed remarkably to the Cu recovery.

• Korean Journal of Materials Research
• /
• v.19 no.9
• /
• pp.481-487
• /
• 2009

The photocatalysts of Fe-ACF/$TiO_2$ compositeswere prepared by the sol-gel method and characterized by BET, XRD, SEM, and EDX. It showed that the BET surface area was related to adsorption capacity for each composite. The SEM results showed that ferric compound and titanium dioxide were distributed on the surfaces of ACF. The XRD results showed that Fe-ACF/$TiO_2$ composite only contained an anatase structure with a Fe mediated compound. EDX results showed the presence of C, O, and Ti with Fe peaks in Fe-ACF/$TiO_2$ composites. From the photocataytic degradation effect, $TiO_2$ on activated carbon fiber surface modified with Fe (Fe-ACF/$TiO_2$) could work in the photo-Fenton process. It was revealed that the photo-Fenton reaction gives considerable photocatalytic ability for the decomposition of methylene blue (MB) compared to non-treated ACF/$TiO_2$, and the photo-Fenton reaction was improved by the addition of $H_2O_2$. It was proved that the decomposition of MB under UV (365 nm) irradiation in the presence of $H_2O_2$ predominantly accelerated the oxidation of $Fe^{2+}$ to $Fe^{3+}$ and produced a high concentration of OH radicals.

• Journal of the Korean Magnetics Society
• /
• v.2 no.1
• /
• pp.8-14
• /
• 1992

To improve the coercivity of ${\gamma}-Fe_{2}O_{3}$ particles. We have made cobalt ferrite epitaxial ${\gamma}-Fe_{2}O_{3}$ particles by crystallizing cobalt ferrite on the surface of ${\gamma}-Fe_{2}O_{3}$ particles. The coercivity of $Co_{x}Fe_{3-x}O_{4}$ which is conform to coating layer showed the most superior characteristic when the value of x was 1. On the formation of cobalt epitaxial ${\gamma}-Fe_{2}O_{3}$ particles, controlling reaction atmosphere as oxidation at. mosphere after non-oxidation atmosphere was the optimum condition to prepare cobalt epitaxial ${\gamma}-Fe_{2}O_{3}$ particles with superior magnetic properties. Epitaxial growth of cobalt ferrite on the surface of ${\gamma}-Fe_{2}O_{3}$ particles was accomplished at $90^{\circ}C$ for 30 minutes.

• Journal of Surface Science and Engineering
• /
• v.52 no.5
• /
• pp.251-257
• /
• 2019

Fe-9Cr-2W steels were corroded at $600-800^{\circ}C$ for up to 100 hr in ($Na_2SO_4-K_2SO_4-Fe_2O_3$)-($CO_2-0.3%SO_2-6%O_2$) mixed gas. The poor condition samples formed thick oxide scales that consisted primarily of $Fe_2O_3$ as the major oxide and $Fe_3O_4$, FeO as the minor one through preferential oxidation of Fe. Fe-9Cr-2W steels corroded fast, forming thick and non-protective scale. The scale divided into the outer and inner layer, which consisted of the outer Fe-O layer and the inner (Fe,Cr)-O layer containing some (Fe,Cr)-S.

• Korean Journal of Materials Research
• /
• v.8 no.8
• /
• pp.720-725
• /
• 1998

As a basic study on the production of $Sm_{2}Fe_{17}N_{x}$ system rare earth permanent magnet by the reduction and diffusion(R- D) process, firstly the reduction reaction of $Sm_2O_3$ by metallic Ca and diffusion of Sm into Fe powder was investigated for the production the $Sm_{2}Fe_{17}$intermetallic compound. We concluded that the former case was very rapidly completed under the high temperature greater than 100$0^{\circ}C$ and the latter case of completion of diffusion reaction of Sm into the center of Fe powder(perfect homogenization condition) was required through 3h R- D reaction at 110$0^{\circ}C$ and identified as a rate determining step(RDS) on the whole reaction. Though $SmFe_2,SmFe_3$, and $Sm_{2}Fe_{17}$phases in the growth of phases of intermetallic compound in the Sm - Fe binary system were obseved below 100$0^{\circ}C$, but only $Sm_{2}Fe_{17}$phase was observed at lIOO$^{\circ}C$. Oxygen and Ca contents of the final sample in this work were 0.72wt% and O. 11 wt% respectively.