• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.55 no.7
• /
• pp.339-343
• /
• 2006

In this study, the variations of the important characteristics of solenoid-type RF chip inductors utilizing a low-loss A1203 core material on inductor dimensions were investigated systematically. Four dimensions of the chip inductors fabricated in this work were $1.0\times0.5\times0.5mm^3,\;1.5\times1.0\times0.7mm^3,\;2.1\times1.5\times1.0mm^3,\;and\;2.4\times2.0\times1.4mm^3$ and copper (Cu) wire with $40{\mu}m$ diameter was used as the coils. High frequency characteristics of the inductance, quality factor, and impedance of developed inductors as a function of inductor dimensions were measured using an RF Impedance/Material Analyzer (HP4291B with HP16193A test fixture). It was observed that the developed inductors with the number of turns of 6 have the inductance (L) of 12 to 82 nH and exhibit the self-resonant frequency (SRE) of 3.6 to 1.2 GHz. The SRF of inductors decreases with increasing the inductor size while the L increases with the inductor size. The smallest inductors of $1.0\times0.5\times0.5mm^3$ exhibited the L of 12 nH, SRF of 3.6 GHz, and the quality factor of 67 near the frequency of 1.1 GHz. The calculated data predicted the high-frequency data of the L, and Q of the developed inductors well.

• Journal of the Microelectronics and Packaging Society
• /
• v.23 no.3
• /
• pp.57-61
• /
• 2016

In order to protect the solar cells from the moisture and oxygen, we evaluated the electrical and optical properties for the $Cu(In,Ga)Se_2$ (CIGS) solar cells which were prepared by the spray coating method. Generally, the EVA (ethylene-vinyl acetate) films are laminated to protect the CIGS flexible solar cells, which results in a high cost process due to complicated devices. In this study, we tried to prepare the protection layers of the flexible CIGS flexible solar cells by using spray coating method instead of conventional laminating films in order to reduce the device weight as well as the process time. The CIGS solar cells with spray coating method showed an enhanced efficiency than the before treated sample (2.77% to 2.93%) and relatively proper water vapor transmission rate of the solar cells about 62.891 gm/[$m^2-day$].

• Restorative Dentistry and Endodontics
• /
• v.9 no.1
• /
• pp.101-106
• /
• 1983

It was the purpose of this study to investigate the fracture mode of dental amalgam by observing the crack propagation, and to relate this to the microstructure of the amalgam. Caulk 20th Century Regular, Caulk Spherical, Dispersalloy, and Tytin amalgam alloys were used for this study. After each amalgam alloy and Hg measured exactly by the balance was triturated by the mechanical amalgamator (Capmaster, S.S. White), the triturated mass was inserted into the cylindrical metal mold which was 4 mm in diameter and 12 mm in height and was pressed by the Instron Universal Testing Machine at the speed of 1mm/min with 120Kg. The specimen removed from the mold was stored in the room temperature for a week. This specimen was polished with the emery papers from #100 to #200 and finally on the polishing cloth with 0.06${\mu}Al_2O_3$ powder suspended in water. The specimen was placed on the Instron testing machine in the method similar to the diametral tensile test and loaded at the crosshead speed of 0.05mm/min. The load was stopped short of fracture. The cracks on the polished surface of specimen was examined with scanning electron microscope (JSM-35) and analyzed by EPMA (Electron probe microanalyzer). The following results were obtained. 1. In low copper lathe-cut amalgam, the crack went through the voids and ${\gamma}_2$ phase, through the ${\gamma}_1$ phase around the ${\gamma}$ particles. 2. In low copper spherical amalgam, it was observed that the crack passed through the ${\gamma}_2$ and ${\gamma}_1$ phase, and through the boundary between the ${\gamma}_1$ and ${\gamma}$ phase. 3. In high copper dispersant (Dispersalloy) amalgam, the crack was found to propagate at the interface between the ${\gamma}_1$ matrix and reaction ring around the dispersant (Ag-Cu) particles, and to pass through the Ag-Sn particles. 4. In high copper single composition (Tytin) amalgam, the crack went through the ${\gamma}_1$ matrix between ${\eta}$ crystals, and through the unreacted alloy particle (core).

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.65-70
• /
• 2006

We fabricated $YBa_2Cu_33O_{7-x}$(YBCO) films on(00l) $LaAlO_3$ substrates prepared by metal organic deposition(MOD) method using trifluoroacetate(TFA) solution and evaluated the effects of the humidity on the microstructure, phase purity, and critical properties. The films calcined at $430^{\circ}C$ were fired at $775^{\circ}C$ at 0%, 4.2%, 12.1%, and 20.0% humidified As gas mixed with 0.1% $O_2$. We observed that the amount of $BaF_2$ phase was effectively reduced and that a sharp and strong biaxial texture formed under a humidified atmosphere, leading to increased critical properties. For the films fired at 0% humidity, the $T_c\;and\;I_c$ were undetectably small. When the humidity was increased to 4.2%, the corresponding $T_c$(onset) and $I_c$ were increased to 90.5 K and 8 A/cm-width, respectively. For the films at the humidity range of 12.1-20.0%, the $I_c$ was found to be 35 A/cm-width. According to the results of the XRD, pole-figure, and SEM, these improved critical properties are probably attributed to the formation of a purer YBCO phase, larger grain size, and stronger c-axis orientation.

• Progress in Superconductivity
• /
• v.8 no.1
• /
• pp.71-74
• /
• 2006

High $J_c$ over 1 $MA/cm^2$ YBCO film has been successfully prepared using nitrate precursors by spray pyrolysis method. Aerosol drolpets generated using a concentric spray nozzle were directly sprayed on a $LaAlO_3$(100) single crystal substrate. The cation ratio of precursor solution was Y:Ba:Cu=1:2.65:1.35. The distance between nozzle and substrate was 15 cm. Deposition temperature was ranging from $750^{\circ}C\;to\;800^{\circ}C$. Deposition pressure was 100 Torr, and oxygen partial pressure was varied from 10 Torr to 50 Torr. The microstructure, phase formation, texture development and superconducting properties of deposited films were largely changed with oxygen partial pressure. Deposited films showed a texture with(001) planes parallel to substrate plane. High quality film was obtained when film was deposited at $760^{\circ}C$ with an oxygen partial pressure of 30 Torr. The critical current density($J_c$) of the YBCO film was 1.75 $MA/cm^2$ at 77 K and self-field.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.39 no.2
• /
• pp.106-117
• /
• 2006

We measured the concentrations of organic matter and metallic elements (Al, Fe, Cr, Mn, Ni, Cu, Zn, As, Cd, Pb and Hg) in the surface sediments of Masan Harbor (in the southern sea, Korea) to evaluate the geochemical characters of sediment and the pollutions by organic matter and metallic elements. The mean grain size of the surface sediments in the study area ranged from $5.6{\phi}$ to $7.8{\phi}$, indicating silt sediment. The water content of the surface sediments exceeded 60% except at some stations. The contents of ignition loss (IL), total organic carbon (TOC) and total nitrogen (TN) ranged from 7.2-14.3%, 1.2-3.2%, and 0.10-0.28%, respectively. Based on the C/N ratios, the organic matter in the surface sediments of Masan Harbor may originate from terrigenous sources including fluvial inputs (mainly sewage in urban areas). The chemical oxygen demand (COD) and acid volatile sulfide (AVS) ranged from $11.3-29.9\;mgO_2/g\;dry$ and 0.20-4.47 mgS/g dry, respectively, and low concentrations were observed near a shipping route. In addition, the concentrations of metallic elements showed large spatial variations in Masan Harbor and the distributions of metallic elements were also comparable to those of organic matter. This implies that the distributions of organic matter and metallic elements in the surface sediments of Masan Harbor are mainly controlled by biogenic matter and artificial action (mainly dredging). In addition, we calculated the enrichment facto. (EF) and geoaccumulation index (Igeo) in order to evaluate pollution by metallic elements. The enrichment of metallic elements relative to Al was three to eighteen times higher at the study sites, compared to levels in the Earth's crust except for Fe, Ni and Mn. In addition, the Igeo class indicated that the surface sediments in the study area were moderately to strongly polluted in terms of metallic elements.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2015.08a
• /
• pp.245-245
• /
• 2015

Cu(In,Ga)Se2 (CIGS) 박막 태양전지는 높은 효율과 낮은 제조비용, 높은 신뢰성으로 인해 박막 태양전지 중 가장 각광받고 있다. 특히 유리기판 대신 가볍고 유연한 철강소재나 플라스틱 소재를 이용하여 발전분야 외에 건물일체형, 수송용, 휴대용등 다양한 분야에 적용이 가능하다. 이러한 유연 기판을 이용한 CIGS 태양전지의 개발을 위해서는 기판의 특성에 따른 다양한 공정개발이 선행되어야 한다. 특히 CIGS 태양전지에서는 Na의 역할이 매우 중요한데 유연기판의 경우 이러한 Na이 없을 뿐만 아니라 철강기판의 경우 Fe, Ni, Cr등의 불순물이 확산되어 흡수층의 특성을 저하시켜 효율을 감소시킨다. 따라서 이러한 철강 기판의 경우 불순물의 확산을 방지하는 확산방지막이 필수적이다. 또한 플라스틱기판의 경우 내열성이 낮아 저온에서 공정을 진행해야하는 단점이 있다. 이러한 유연기판의 특성을 고려하여 본 연구에서는 유연기판으로 STS 430 stainless steel과 poly-imide를 이용하여 특성 개선을 진행하였다. 먼저 stainless steel과 Poly-imide, soda-lime glass, coning glass의 기판을 이용하여 기판에 따른 흡수층의 특성을 비교 분석하였으며 stainless steel 기판을 이용하여 확산 방지막의 유무 및 두께에 따른 흡수층 및 소자의 특성을 분석하였다. 이때 확산 방지막은 기존 TCO 공정에서 사용되는 i-ZnO를 사용하였으며 RF sputter를 이용하여 50~200nm로 두께를 달리하며 특성 비교를 실시하였다. 이때 효율은 확산방지막을 적용하지 않았을 때 약 5.9%에서 확산 방지막 적용시 약 10.6%로 증가하였다. 또한 poly-imide 기판을 이용하여 $400^{\circ}C$이하에서 흡수층을 제조하여 특성평가를 진행하였으며 소자 제조 후 효율은 약 12.2%를 달성하였다. 모든 흡수층은 Co-Evaporation 방법을 이용하여 제조하였으며 제조된 흡수층은 SEM, XRF, XRD, GD-OES, PL, Raman등을 이용하여 분석하였으며 그 외 일반적인 방법을 이용하여 Mo, CdS, TCO, Al grid를 제조하였다. AR 코팅은 제외 하였으며 제조된 소자는 솔라 시뮬레이터를 이용하여 효율 특성 분석을 실시하였으며 Q.E. 분석을 실시하였다.

• Progress in Superconductivity
• /
• v.9 no.1
• /
• pp.102-106
• /
• 2007

YBCO films have been synthesized using a spray pyrolysis method. We used nitrates of Y, Ba, Cu as precursors. Deposition was made on $LaAlO_3$ (100) single crystal substrate by spraying the mist of aqueous precursor solution generated by a concentric nozzle. The distance between concentric nozzle and substrate was 15 cm. C-axis oriented films were obtained at deposition temperature of $740{\sim}800^{\circ}C$ and working pressure of 20 Torr. Oxygen partial pressure was 3 Torr and substrate was transported with the speed ranging from 0.23 cm/min to 0.7 cm/min by reel to reel. Scanning electron microscope (SEM) and X-ray diffraction (XRD) observation revealed that films are smooth and highly textured with (001) planes parallel to substrate. Highest critical current density (Jc) was $1.38\;MA/cm^2$ at 77K and self-field for the film with a thickness of $0.5\;{\mu}m$ prepared at a substrate temperature of $780^{\circ}C$ and $PO_2\;=3\;Torr$. The effect of temperature on the microstructure and YBCO phase formation will be discussed.

• Proceedings of the KIEE Conference
• /
• 2002.07c
• /
• pp.1524-1526
• /
• 2002

본 논문에서는 $1.62{\times}1.0{\times}0.88mm^3$ 크기의 C-type과 $1.58{\times}0.82{\times}0.94mm^3$ 크기의 H-type RF 칩 인덕터를 제작하고 그들의 고주파 특성을 비교하였다. 본 연구에서는 저손실 $Al_2O_3$ 코아 물질과 직경 $40{\mu}m$의 구리(Cu) 코일을 사용하였다. 권선수를 $2{\sim}14$회로 하여 인덕턴스(L), 품질계수(Q), 임피던스의 크기와 위상, 커패시턴스(C)를 HP4291B Impedance/Material Analyzer로 측정하였다. 10회 권선시 C-type은 55nH, H-type은 67nH, 14회 권선시 C-type은 100nH, H-type은 122nH 정도로 측정되었다. 실험 결과 H-type이 C-type보다 동일 권선수에 대하여 높은 인덕턴스와 높은 자기공진주파수(SRF)를 나타냄을 확인하였다. 또한 최대 품질계수는 두 형태가 거의 비슷한 값($55{\sim}87$)을 가짐을 관찰하였다. 따라서 H-type이 C-type보다 우수한 성질을 나타냄을 알 수 있다.

• Economic and Environmental Geology
• /
• v.12 no.2
• /
• pp.79-93
• /
• 1979

Twenty five samples of the scheelite-powellite series from twelve Korean tungsten deposits of various geologic settings were studied mineralogically and geochemically. Variations in the trace-element contents of the scheelite minerals are considered in relation to geologic settings and mineralogic properties. Scheelites from ore deposits developed in similar geologic settings and under similar physicochemical conditions are characterized by specific combinations of trace elements.