The Effect of Substrate Temperature on Superconducting Properties of YBCO Films Prepared by Spray Pyrolysis Method using Metal Nitrate Precursors

분사열분해 CVD 법으로 증착된 YBCO 박막의 특성에 미치는 기판 온도의 영향

YBCO films have been synthesized using a spray pyrolysis method. We used nitrates of Y, Ba, Cu as precursors. Deposition was made on $LaAlO_3$ (100) single crystal substrate by spraying the mist of aqueous precursor solution generated by a concentric nozzle. The distance between concentric nozzle and substrate was 15 cm. C-axis oriented films were obtained at deposition temperature of $740{\sim}800^{\circ}C$ and working pressure of 20 Torr. Oxygen partial pressure was 3 Torr and substrate was transported with the speed ranging from 0.23 cm/min to 0.7 cm/min by reel to reel. Scanning electron microscope (SEM) and X-ray diffraction (XRD) observation revealed that films are smooth and highly textured with (001) planes parallel to substrate. Highest critical current density (Jc) was $1.38\;MA/cm^2$ at 77K and self-field for the film with a thickness of $0.5\;{\mu}m$ prepared at a substrate temperature of $780^{\circ}C$ and $PO_2\;=3\;Torr$. The effect of temperature on the microstructure and YBCO phase formation will be discussed.