• Bulletin of the Korean Chemical Society
• /
• v.23 no.8
• /
• pp.1166-1168
• /
• 2002

• Journal of Power System Engineering
• /
• v.21 no.2
• /
• pp.14-19
• /
• 2017

The corrosion characteristics of Al-Si-Mg alloy were investigated in $O_2$ and $H_2S/H_2$ environments at high temperature. The weight gain and the reaction rate constant of the Al-Si-Mg alloy were measured in the oxygen and hydrogen sulfide environments at 773K. The weight gain of Al-Si-Mg alloy was showed parabolic increase in the oxygen and hydrogen sulfide environments. The reaction rate constants were confirmed to be $1.45{\times}10^{-4}mg^2cm^{-4}sec^{-2}$ in the oxygen environment and $6.19{\times}10^{-4}mg^2cm^{-4}sec^{-2}$ in the hydrogen sulfide environment respectively. As a result of XPS analysis on the specimen surface, $Al_2O_3$ and MgO compounds were detected in oxygen environment and $Al_2(SO_4)_3$ sulfate was detected in the hydrogen sulfide environment. Corrosion rate of Al-Si-Mg alloy was about 4.3 times faster in hydrogen sulfide environment than oxygen environment.

• Bulletin of the Korean Chemical Society
• /
• v.21 no.12
• /
• pp.1239-1244
• /
• 2000

A study of K addition to the catalyst of CoMo/ ${\gamma}-Al_2O_3$ was studied. The catalyst with 10 at% of K to Mo atoms in 3C10M, the catalyst added 3 wt% CoO to 10 wt% $MoO_3/{\gamma}-Al_2O_3$, showed the highest activity for water gas shift reaction. The addition of K retarded the reducibility of cobalt-molybdenum catalysts. It gave, however, good dispersion and large BET surface area to the catalysts which were attributed to the disappearance of polymolybdate clustyer such as $Mo_7O_{24}^{6-}$ and the formation of small Mo$O_4^{2-}$ cluster. It was confirmed by the analyses of pore size distribution, activation energy, Raman spectroscopy, and electron diffraction. The activation energies and the frequency factors of the catalysts 3C10M and 5KC10M (the catalyst added 5 at% K for Mo to the catalyst 3C10M) were 43.1 and 47.8 kJ/mole, and 4,297 and 13,505 $sec^{-1}$, respectively. These values were also well correlated with our suggestion. These phenomena were attributed to the direct interaction between K and CoMo oxides irrelevant to the support.

• Journal of the Semiconductor & Display Technology
• /
• v.16 no.4
• /
• pp.1-4
• /
• 2017

Encapsulation of organic based devices is essential issue due to easy deterioration of organic material by water vapor. Atomic layer deposition (ALD) is a promising solution because of its low temperature deposition and quality of the deposited film. Moisture permeation has a mechanism to pass through defects, Thin Film Encapsulation using inorganic / organic / inorganic hybrid film has been used as promising technology. $Al_2O_3$ / Polymer / $Al_2O_3$ multilayer film has shown excellent environmental protection characteristics despite of thin thicknesses of the films.

• Bulletin of the Korean Chemical Society
• /
• v.16 no.12
• /
• pp.1148-1152
• /
• 1995

Oxidative dimerization of methane to C2-hydrocarbons was performed over lead aluminate spinel catalysts. These spinel catalysts were prepared by co-precipitation, aerogel, and sol-gel methods. The active phase of lead aluminate oxides was found to be PbAl2O4 spinel. The activities of the catalysts were strongly dependent on the preparation method as well as the composition of PbAl2O4 phase. The proper oxygen mobility of PbAl2O4 spinel oxides appeared to be important to get high catalytic activity and selectivity for C2-hydrocarbon formation.

• Journal of the Korean Ceramic Society
• /
• v.25 no.4
• /
• pp.364-372
• /
• 1988

The mechanical properties and microstructure of ceramics of the system Al2O3-ZrO2-Y2O3 sintered at 1$650^{\circ}C$ for 2h after powder preparation by the precipitation method from Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were investigated. The Al2O3-ZrO2-Y2O3 ceramics sintered at 1$650^{\circ}C$ for 2h after mixing alpha-Al2O3 and ZrO2-Y2O3 powders, both were separately precipitated and calcined, were found to have the relative density higher than 97.5% so that the strengthening and toughening mechanisms could be explained mainly as the stress-induced phase transformation. On the other hand, the sintered bodies prepared by co-precipitating the three starting materials were measured to have the relative density lower than 85% so that the degradation of strength were observed above 15 vol% ZrO2 contents due to the high porosity by which the effect of stress-induced phase transformation was assumed to be depressed.

• Journal of the Korean Ceramic Society
• /
• v.28 no.1
• /
• pp.11-18
• /
• 1991

A precipitation method, one of the most effective liquid phase reaction methods, was adopted in order to prepare high-tech Al2O3/ZrO2 composite ceramics, and the effects of stress-induced phase transformation of ZrO2 on thermal shock behavior of Al2O3-ZrO2 ceramics were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Metal hydroxides were obtained by single precipitation(process A) and co-precipitation(process B) method at the condition of pH=7, and the composition of Al2O3-ZrO2 composites was fixed as Al2O3-15v/o ZrO2(+3m/o Y2O3). Critical temperature difference showing rapid strength degradation by thermal shock showed higher value in Al2O3/ZrO2 composites(process A : 20$0^{\circ}C$, process B : 215$^{\circ}C$) than in Al2O3(175$^{\circ}C$). The improvement of thermal shock property for Al2O3/ZrO2 composites was mainly due to the increase of strength at room temperature by adding ZrO2. The strength degradation was more severe for the sample with higher strength at room temperature. Crack initiation energies by thermal shock showed higher values in Al2O3/ZrO2 composites than in Al2O3 ceramics due to increase of fracture toughness by ZrO2.

• Korean Chemical Engineering Research
• /
• v.55 no.3
• /
• pp.436-442
• /
• 2017

Fischer-Tropsch synthesis is the technology of converting a syngas (CO+$H_2$) derived from such as coal, natural gas and biomass into a hydrocarbon using a catalyst. The catalyst used in the Fischer-Tropsch synthesis consists of active metal, promoter and support. The types of these components and composition affect the reaction activity and product selectivity. In this study, we manufactured an iron catalyst using ${\gamma}-Al_2O_3/SiO_2$ mixed support (100/0 wt%, 75/25 wt%, 50/50 wt%, 25/75 wt%, 0/100 wt%) by an impregnation method to investigate how the composition of ${\gamma}-Al_2O_3/SiO_2$ mixed support effects on the reaction activity and product selectivity. The physical properties of catalyst were analyzed by $N_2$ physical adsorption and X-Ray diffraction method. The Fischer-Tropsch synthesis was conducted at $300^{\circ}C$, 20bar in a fixed bed reactor for 60h. According to the results of the $N_2$ physical adsorption analysis, the BET surface area decreases as the composition of ${\gamma}-Al_2O_3$ decreases, and the pore volume and pore average diameter increase as the composition of ${\gamma}-Al_2O_3$ decreases except for the composition of ${\gamma}-Al_2O_3/SiO_2$ of 50/50 wt%. By the results of the X-Ray diffraction analysis, the particle size of ${\alpha}-Fe_2O_3$ decreases as the composition of ${\gamma}-Al_2O_3$ decreases. As a result of the Fischer-Tropsch synthesis, the CO conversion decreases as the composition of ${\gamma}-Al_2O_3$ decreases, and the selectivity of C1-C4 decreases until the composition of ${\gamma}-Al_2O_3$ was 25 wt%. In contrast, the selectivity of C5+ increases until the composition of ${\gamma}-Al_2O_3$ is 25 wt%.

• Journal of the Korean Chemical Society
• /
• v.13 no.2
• /
• pp.157-164
• /
• 1969

Aoolphane was treated with 30% Hydrochloric acid at $18^{\circ}C$ for two hows with stirring in order to obtain the insoluble form of SiO2 gel and to extract quantitatively both $Al_2O_3$as and $Fe_2O_3AlCl_3{\cdot}6H_2O Fe$ and $Cl_3{\cdot}6H_2O$ forms, respectively, at the same time. $SiO_2$ gel was filtered and to the filterate Ammonia was added to precipitate $Al(OH)_3[Fe(OH)_3 Contaminated ]$ The precipitate was separated by filteration and the filterate was recovered as the form of $NH_4Cl$. The precipitate was treated with 200g (NaOH)/l Concentration of NaOH a little excessively to the equivalent at $65~70^{\circ}C$ as $Fe(OH)_3$ formed was insoluble, it was filtered of and to the filterate containing $NaAl(OH)_4(OH_2)_2$Carbon dioxide gas was bubbled at $50^{\circ}C~90^{\circ}C$ to obtain the precipitate with excellent filterability and crystallinity. The product was certified to be Dawsonite $(NaAl(OH)_2CO_3)$ by X-Ray diffraction analysis at below $40^{\circ}C$, when $CO_2$ gas was bubbled into the relatively lower concentration of $NaAl(OH)_4(OH_2)_2$ solution, the precipitate of very fine particles was formed, which was hard to filter and with the Composition of $\alpha-Al_2O_3-H_2O$ (Boehmite).

• Journal of the Korean Ceramic Society
• /
• v.47 no.1
• /
• pp.61-65
• /
• 2010

Ultrathin atomic layer deposition (ALD) coatings were found to enhance the performance of lithium-ion batteries (LIBs). Previous studies have demonstrated that $LiCoO_2$ cathode powders coated with metal oxides with thicknesses of $\sim100-1000{\AA}$ grown using wet chemical techniques improved LIB performance. In this study, $LiCoO_2$ powders were coated with conformal $Al_2O_3$ ALD films with thicknesses of only $\sim3-4{\AA}$ established using 2 ALD cycles. The coated $LiCoO_2$ powders exhibited a capacity retention of 89% after 120 charge-discharge cycles in the 3.3~4.5 V (vs. $Li/Li^+$) range. In contrast, the bare $LiCoO_2$ powders displayed only a 45% capacity retention. This dramatic improvement may result from the ultrathin $Al_2O_3$ ALD film acting to minimize Co dissolution or to reduce surface electrolyte reactions.