• Economic and Environmental Geology
• /
• v.37 no.4
• /
• pp.375-381
• /
• 2004

Pyrochlore was known as one of the most promising materials for the immobilization of radioactive actinide. This study includes the synthesis, phase relation and characteristics of pyrochlores (CaCeH$f_xTi_{2-x}O_7$=0.2, 0.6, 1.0, 1.4, 1.8, 2.0) in the system of Ca-Ce-Hf-Ti-O. The samples were prepared from high purity of starting materials under the pressure of 400kg/cm$^2$ at room temperature, and were sintered at 1200∼1$600^{\circ}C$ The synthesized samples were analyzed and identified with XRD. The optimal formation conditions of pyrochlores were at 1300∼150$0^{\circ}C$ under $O_2$ atmosphere with batch compositions. During synthesis, pyrochlore, perovskite and $A_{2}BO_{5}$ oxide were formed. The characteristics of this system is that parameter of pyrochlore was increased with the content of hafnium. This phenomenon was due to the difference of ionic size between hafnium and titanium in six coordinated site.

• Journal of the Korean Ceramic Society
• /
• v.32 no.2
• /
• pp.155-162
• /
• 1995

Solid oxide electrolytes of the MCe1-xGdxO3-x/2 (M: Ba, Mg. x=0.0-0.20) system were prepared using powders synthesized by the "liquid mix" method and calcined from the cross-linked polyacrylic polymer. The specimens were analyzed using XRD and SEM with EDX, and the sintering behavior of the electrolytes and their electrical conductivity were also studied. Although Mg-cerate is relatively inferior to Ba-cerate in the sinterability and chemical homogenity(EDX analysis data), both the Ba- and the Mg-cerate electrolytes at 80$0^{\circ}C$ show their maximum conductivities at x=0.10 and their values are in the same order of magnitude, i.e., 3.5$\pm$0.17.10-2(ohm.cm)-1.ohm.cm)-1.

• Progress in Superconductivity
• /
• v.10 no.2
• /
• pp.128-132
• /
• 2009

Polycrystalline samples of $(Ru_{0.8}Nb_{0.2})Sr_2(Gd_{1.5-x}Nd_xCe_{0.5})Cu_2O_z$($ 0{\leq}x{\leq}1.25$) have been synthesized by a solid-state reaction route. The X-ray diffraction data revealed that the Nd solubility limit can be placed between x=0.5 and x=0.75. The superconducting transition temperature decreased with increasing Nd content, confirming that Nd entered the lattice. Room-temperature thermoelectric power measurements showed that all the samples are in the underdoped state and the partial substitution of Nd for Gd resulted in a decrease in the carrier density on the superconducting layers.

• 한국태양에너지학회:학술대회논문집
• /
• 2012.03a
• /
• pp.463-469
• /
• 2012

Solar thermochemical syngas and hydrogen production process bv redox system of metal oxide was performed under direct irradiation of the metal oxide on the SiC ceramic foam device using solar simulator. $CeO_2/ZrO_2$ nanotube has been synthesized by anodic oxidation method. Syngas and hydrogen production process is one of the promising chemical pathway for storage and transportation of solar heat by converting solar energy to chemical energy. The produced syngas had the $H_2/CO$ ratio of 2, which was suitable for methanol synthesis or Fischer-Tropsch synthesis process. After ten cycles of redox reaction, $CeO_2$ was analyzed using XRD pattern and SEM image in order to characterize the physical and chemical change of metal oxide at the high temperature.

• Clean Technology
• /
• v.16 no.4
• /
• pp.284-291
• /
• 2010

Nitrous oxide ($N_2O$) is a greenhouse material which is hard to remove. Even with a catalytic process it requires a reaction temperature, at least, higher than 670 K. This study has been performed to see the effects of Ce addition to the mixed oxide catalyst which shows the highest activity in decomposing $N_2O$ completely at temperature as low as 473 K when CO is used as a reducing agent. Mixed metal oxide(MMO) catalyst was made through co-precipitation process with small amount of Ce added to the base components of Co, Al and Rh or Pd. Consequently, the surface area of the catalyst decreased with the contents of Ce, and the catalytic activity of direct decomposition of $N_2O$ also decreased. However, in the presence of CO, the activity was found high enough to compensate the portion of activity decrease by Ce addition, so that it can be ascertained that the catalytic activity and stability can be maintained in the CO involved $N_2O$ reduction system when Ce is added for the physical stability of the catalyst.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.130-134
• /
• 2006

Buffer layers such as $CeO_2\;and\;Yb_2O_3$ films for YBCO coated conductors were deposited on (100) $SrTiO_3$ single crystals and (100) textured Ni substrates by a metal organic chemical vapor deposition (MOCVD) system of the hot-wall type. The substrates were moved with the velocity of 40 cm/hr. Source flow rate, $Ar/O_2$ flow rate and deposition temperature were main processing variables. The degree of film epitaxy and surface morphology were investigated using XRD and SEM, respectively. On a STO substrate, the $CeO_2$ film was well grown epitaxially above the deposition temperature of $450^{\circ}C$. However, on a Ni substrate, the XRD showed NiO (111) and (200) peaks due to Ni oxidation as well as (111) and (200) film growth. For the films deposited with $O_2$ gas as oxygen source, it was found that the NiO film was formed at the interface between the buffer layer and the Ni substrate. The NiO layer interrupts the epitaxial growth of the buffer layer. It seems that the epitaxial growth of the buffer layer on Ni metal substrates using $O_2$ gas is difficult. We are considering a new method avoiding Ni oxidation with $H_2O$ vapor instead of $O_2$ gas.

• Korean Journal of Optics and Photonics
• /
• v.17 no.5
• /
• pp.480-486
• /
• 2006

Generally, IR cut-off filters for mobile phone is coated on the glass substrate at high temperature(above $300^{\circ}C$). In this work, we prepared IR cut-off filters on the poly(methyl methacrylate)(PMMA) substrates at low temperature(about $70^{\circ}C$ ). using the $CeO_2\;and\;SiO_2$ coatings by physical vapor deposition. The surface energies of coated and uncoated PMMA, and adhesive properties of IR cut-off filters coatings were examined using contact angle measurements. We demonstrate the improve of mobile phone optical system using these results.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.11 no.4
• /
• pp.754-759
• /
• 2007

Field emission displays (FED) are currently being explored as a potential flat panel display technology. Specifically, the optimization pf efficient bin emitting phosphors in the $Y_2O_3-Nb_2O_5$ system and influence of particle size of phosphors on the luminescent properties was studied. Under 254 nm excitation, Bi activated $YNbO_4$ phosphors showed a strong and relatively narrow blue omission band, peaking at about 420-450 nm. Especially 0.4 wt% Bi doped yttrium phosphors showed the maximum emission intensity which is almost three times as much as that of $Y_2SiO_5:Ce$ phosphors. Finally, Ce doped $Y_2SiO_5$ phosphors exhibited strong and broad blue emission band, centered at 390-420 nm and maximum emission intensity at the doping concentration of 0.02-0.03 mol.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.301-304
• /
• 2002

We investigated the structural and electrical properties of Ce-doped Ba($Zr_{0.2}Ti_{0.8}$)$O_3$(BCZT) thin films with a mole fraction of x=0.2 and a thickness about 100 nm. BCZT films were prepared on Pt/Ti/$SiO_2$/Si substrate by a RF magnetron sputtering system. We have measured the thickness profile with Ar/$O_2$ ratio and the surface roughness. It was observed that the oxygen gas, which introduced during the film deposition, have an influence on the roughness of the film and the film roughness was reduced by annealing from 2.33 nm to 2.02 m (RMS at $500^{\circ}C$, Ar:6 scrim, $O_2$:6 sccm). We have found that annealing procedure after top electrode deposit can reduce the dissipation factor.