• Journal of Sensor Science and Technology
• /
• v.4 no.3
• /
• pp.22-29
• /
• 1995

Lithium ionic solid electrolyte was synthesized at $60^{\circ}C$ in $N_{2}$ ambience by sol-gel method, using tetraethyl orthosilcate, lithium methoxide, zirconium n-propoxide, and tributyle phosphate as precursors. The prepared material was dried and crushed into powder, and it was pressed into disk type samples. These samples were sintered at $900^{\circ}C{\sim}1100^{\circ}C$ for 50 hours. The physical characteristics of the samples were investigated by TG/DTA, SEM, AES and XRD methods. $CO_{2}$ sensor based on lithium ionic solid electrolyte was fabricated and its operational characteristics were measured. The sensing characteristics of the sensor sintered at $1000^{\circ}C$ shows the variation of e.m.f. about $35{\sim}63\;mV/decade$ for the variation of $CO_{2}$ concentration at $200^{\circ}C{\sim}300^{\circ}C$ of operating temperature, and good linearity for $300{\sim}6000\;ppm$.

• Journal of the Korean Ceramic Society
• /
• v.33 no.1
• /
• pp.7-16
• /
• 1996

${CO_3}^{2-}$ containing whisker-like hydroxyapatite powders were synthesized byhomogeneous precipitation method using urea, Dicalcium phosphate anhdrate[DCPA; $CaHPO_4$] and octacalcium phosphate [OCP; $Ca_8H_2(PO_4_)6\cdot5H_20$]were obtained as precursors and they transformed to high crystalline hydroxyapatites at pH 5.62, and 6.54 respectively. According to the condition of the final pH in the solutions for the solution products and urea contents OCP was remained. When the solution product of $Ca^{2-}$ and ${PO_4}^{3-}$ was $1.5\times 10^4$[$mM^2$] and the content of urea was 0.25 mol.$dm^{-3}$ well crystallized whisker-like hydroxyapatite tens of micrometer in length was obtained. By heat treatment DCPA and OCP were decomposed into $\beta$-tricalcium phosphate [$\beta$-TCP ; $\beta$-$Ca_3{PO_4}_2$] and $\beta$-dicalcium phosphate [$\beta$-DCP ;$\beta$-$Ca_2P_2O_4}_2$]. And well-crystallized hydroxyapatite was partially decomposed into $\beta$-TCP at $800^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.28 no.11
• /
• pp.851-858
• /
• 1991

Spherical fine BaTiO3 powders with an average diameter of 0.3${\mu}{\textrm}{m}$ to 0.9${\mu}{\textrm}{m}$ are prepared at 100$0^{\circ}C$ by the ultrasonic spray pyrolysis of solutions containing Ba(NO3)2 and TiCl4. Experimental variables are adjusted to produce BaTiO3 powders and its effect on the phase, the size and the morphology of the particles are investigated by XRD, SEM, TEM. Each particle consists of small primary particles and has a hollow around its center. The dependence of particle diameters on the concentrations of source solutions indicates that metal salt precursors are dried to precipitate solid particles and decompose to form BaTiO3 phase without gas phase reactions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.7-10
• /
• 2001

Orthorhombic type $LiCo_{x}Mn_{1-x}O_{2}$(0 ${\times}$ 0.14) oxides have been synthesized by hydrothermal treatment of $(Co_{x}Mn_{1-x})_{3}O_{4}$ precursors and LiOH aqueous solution at $170^{\circ}C$. As-synthesized powders showed well-ordered ${\beta}-NaMnO_{2}$ structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic $LiCo_{0.1}Mn_{0.9}O_{2}$, comparing to orthorhombic $LiMnO_2$.

• Korean Journal of Pharmacognosy
• /
• v.25 no.1
• /
• pp.31-34
• /
• 1994

The callus was induced from the seedlings of Schizonepeta tenuifolia Brig. (Labiatae) and the effects of culturing conditions on growth rate and essential oil formation of the callus were experimented. It was found in the experiments, that the proper culturing temperature is $23^{\circ}C$ and the addition of biosynthetic precursors(leucine, mevalonic acid lactone) inhibits the growth of the callus. The growth rate of the callus and the amount of essential oils of the callus in the medium containing NAA were higher than the medium containing 2,4-D. The essential oils from the callus and the leaves of the cultivated Schizonepeta tenuifolia showed different GC pattern, but pulegone was found in both oils.

• Electrical & Electronic Materials
• /
• v.14 no.12
• /
• pp.7-10
• /
• 2001

Orthorhombic type LiCo$_{x}$Mn$_{1-x}$ O$_2$(0$\leq$x$\leq$0.14) oxides have been synthesized by hydrothermal treatment of (Co$_{x}$Mn$_{1-x}$ )$_3$O$_4$precursors and LiOH aqueous solution at 17$0^{\circ}C$. As-synthesized powders showed well-ordered $\beta$-MaMnO$_2$structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic LiCo$_{0.1}$Mn$_{0.9}$O$_2$, comparing to orthorhombic LiMnO$_2$./TEX>.EX>.

• Journal of Magnetics
• /
• v.16 no.3
• /
• pp.216-219
• /
• 2011

Mn doped ZnO films were prepared on Si (100) substrates using sol-gel method. The prepared films were annealed at $550^{\circ}C$ for decomposition and oxidation of the precursors. XRD analysis revealed the presence of ZnMnO hexagonal wurtzite phase along with the presence of small quantity of $ZnMn_2O_3$ secondary phase and poor crystalline nature. The 2D, 3D views of magnetic domains and domain profiles were obtained using magnetic force microscopy at room temperature. Rectangular shaped domains with an average size of 4.16 nm were observed. Magnetic moment measurement as a function of magnetic field was measured using superconducting quantum interference device (SQUID) magnetometry at room temperature. The result showed the ferromagnetic hysteresis loop with a curie temperature higher than 300 K.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.7-10
• /
• 2001

Orthorhombic type $LiCo_{x}Mn_{1-x}O_2$ (0 x 0.14) oxides have been synthesized by hydrothermal treatment of ($Co_{x}Mn_{1-x}$)$_3O_4$ precursors and LiOH aqueous solution at $170^{\circ}C$. As-synthesized powders showed well-ordered ${\beta}$-$NaMnO_2$ structures, and the products were single crystalline particle oxides from TEM observations. The particle size decreased with increasing the amount of Co substituent. Much more improved capacity upon 100 cyclings was clearly seen in orthorhombic $LiCo_{0.1}Mn_{0.9}O_2$, comparing to orthorhombic $LiMnO_2$.

• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2003.05a
• /
• pp.106-111
• /
• 2003

Tantalum nitride(TaN) films were deposited by atomic layer deposition(ALD) and plasma assisted atomic layer deposition(PAALD). The deposition of the TaN thin film has been performed using pentakis (ethylmethlyamino) tantalum (PEMAT) and ammonia($NH_3$) as precursors at temperature of $250^{\circ}C$, where the temperature was proven to be ALD window for TaN deposition from our previous experiments. The PAALD deposited TaN film shows better physical properties than thermal ALD deposited TaN film, due to its higher density$(~11.59 g/\textrm{cm}^3$) and lower carbon(~ 3 atomic %) and oxygen(~ 4 atomic %) concentration of impurities.

• Journal of Magnetics
• /
• v.18 no.1
• /
• pp.1-4
• /
• 2013

Structural and magnetic properties of $Fe_{50}Mn_{50}$ nanocrystalline alloys prepared by the mechanical alloying technique (using commercial Fe and Mn powders as the precursors) are studied as a function of milling time, 1 hr to 48 hrs. The nano-crystallite size and shape are examined by using scanning electron microscopy (SEM). The effect of milling time on structural characterization was investigated using X-ray diffractometer (XRD) and extended X-ray absorption fine structure spectroscopy (EXAFS). Both XRD and EXAFS studies showed that the alloying process should be completed after 36 hrs milling. Concerning the magnetic behavior, the data obtained from superconducting quantum interference devices (SQUID) exhibited both magnetic saturation ($M_s$) and coercivity ($H_c$) depend strongly on the milling time, which are related to the changes in the crystallite size and magnetic dilution.