• 한국표면공학회지
• /
• 제34권5호
• /
• pp.409-413
• /
• 2001

In this study, high rate deposition of thick CrNx films was carried out by crossed field unbalanced magnetron sputtering for the special application such as piston ring employed in automobile engine. For the high rate deposition and thick CrNx films formation with thickness of 30$\mu\textrm{m}$, high power density of $35W/cm^2$ in each target was induced and the multi-layer films of Cr/CrN and $\alpha$-Cr/CrN were synthesized by control of $N_2$ flow rate. The dynamic deposition rate of Cr and $\alpha$-CrN film was reached to 0.17$\mu\textrm{m}$/min and 0.12$\mu\textrm{m}$/rnin and the thick CrN$_{x}$. film of 30$\mu\textrm{m}$ could be obtained less than 5 hours. The maximum hardness was obtained above 2200 kg/mm$^2$ and adhesion strength was measured in about 70N, in case of multi-layers films. And the friction coefficient was measured by 0.4, which was similar to the value of CrN single-layer film.m.

• 한국표면공학회지
• /
• 제45권6호
• /
• pp.232-241
• /
• 2012

Cr-Ti-B-N coatings were synthesized by a hybrid coating system combining high power impulse magnetron sputtering (HIPIMS) and DC pulse magnetron sputtering from a $TiB_2$ and a Cr target in argon-nitrogen environment, respectively. By changing the power applied on the Cr and $TiB_2$ cathodes, the Cr-Ti-B-N coatings with various Ti/Cr ratio and B content were deposited. The phase structure, microstructure and chemical compositions of the Cr-Ti-B-N coatings were studied by X-ray diffraction (XRD), transmission scanning electron microscopy (TEM), and X-ray photoelectron spectroscopy (XPS). With increase of Cr element in the coatings, the nanocomposite microstructure consisting of nano-sized (Cr, Ti) N crystallites and amorphous BN phase were obtained in the coatings. The microhardness of the Cr-Ti-B-N coatings exhibited a peak value of ~41 GPa for the $CrTi_{0.1}B_{0.4}N_{1.3}$, and then decreased with further increase of Cr content in the coatings, and all the coatings exhibited low friction coefficient. The oxidation and corrosion behavior of the Cr-Ti-B-N coatings revealed better properties due to the formation of a nanocomposite microstructure.

• 한국재료학회지
• /
• 제13권7호
• /
• pp.420-423
• /
• 2003

Coatings of TiCrN ion-plated on a steel substrate was oxidized at $800^{\circ}C$ in air, and their oxidation mechanism was presented. During oxidation, substrate elements and Ti and Cr in the coating always diffused outwardly to form the oxide scale. Simultaneously, oxygen from the atmosphere diffused inward1y to react with Ti and Cr to form $TiO_2$and $Cr_2$$O_3$, respectively. Also, the counter-diffusion of cations and oxygen resulted in some oxygen dissolution in the unoxidized TiCrN coating, and Fe dissolution in the oxide scale. When the Ti content in the coating was high, the $TiO_2$-forming tendency was strong, while when the Cr content was high, the $Cr_2$$O_3$-forming tendency was strong.

• Bulletin of the Korean Chemical Society
• /
• 제26권4호
• /
• pp.634-640
• /
• 2005

The reaction of cis-[Cr([14]-decane)(OH$_2)_2]^+$ ([14]-decane = rac-5,5,7,12,12,14-hexamethyl-1,4,8,11-teraazacyclotetradecane) with auxiliary ligands {$L_a$ = citrate(cit)} leads to a new dimeric complex cis-[{Cr([14]-decane)($\mu$-cit)}$_2](ClO_4)_2$. This binuclear complex has been structurally characterized by a combination of elemental analysis, conductivity, IR and Vis spectroscopy, mass spectrometry, and X-ray crystallography. Analysis of the crystal structure of cis-[{Cr([14]-decane)($\mu$-cit)})($_2]^+$ reveals that each chromium has a distorted octahedral coordination environment and citrato ligands are monodentate to the two chromium atoms via the carboxyl groups. For dimeric complex the bridging geometry is as follows: Cr$\ldots$Cr = 7.361 $\AA$; Cr-O(average) = 1.958 (8) $\AA$; Cr-N range = 2.108 (9)-2.147(9) $\AA$; N(1)-Cr-N(3) (equatorial position) = 98.0(4)$^{\circ}$; N(2)-Cr-N(4) (axial position) = 166.4(4)$^{\circ}$; O(1)-Cr-N(2) = 98.1(4)$^{\circ}$; O(3)-Cr-N(4) = 96.6(3)$^{\circ}$; O(1)-Cr-O(3) = 90.4$^{\circ}$. The FAB mass spectrum of the dimeric complex displays peak due to the molecular ions cis-[{Cr([14]-decane)($\mu$-cit)})($_2]^+$ at m/z 1053.

• 한국기계가공학회지
• /
• 제10권4호
• /
• pp.96-101
• /
• 2011

The thin films of TiN have been used extensively as wear-resistant materials, for instance, such as tools of high-speed cutting, metal mold forming etc. In these days, because the thin films capable of being used more severe conditions are needed, the technologies of arc ion plating are tried to improve its characteristics. The purpose of this study is to investigate the characteristics of thin films of (Ti,Cr)N compared with those of TiN. The method of arc ion plating, which is known as showing good tight-adherence and productivity, was used. After manufacturing thin films of ($Ti_{1-x}Cr_{x}$)N (x=0~1) with change of Cr in (Ti,Cr) target, atomic concentration, structure, size of crystallite, residual stress and surface roughness of thin films on substrate were investigated. As the results, it was confirmed that Cr atomic concentrations of thin films were proportionally changed with Cr atomic concentrations of target, and thin films of ($Ti_{1-x}Cr_{x}$)N (x=0~1) showed NaCl type and CrN existed as solid solution to TiN.

• 한국세라믹학회지
• /
• 제50권6호
• /
• pp.390-395
• /
• 2013

Nanocrystalline CrN films were deposited on Si (100) substrates by means of asymmetric pulsed DC reactive magnetron sputtering. We investigated the growth behavior, corrosion resistance and mechanical properties of CrN films with a change in the duty cycle and pulse frequency. The grain size of the CrN films decreased from 25.4 nm to 11.2 nm upon a decrease in the duty cycle. The corrosion potentials for the CrN films by DC sputtering was approximately - 0.6 V, and it increased to - 0.3 V in the CrN films which underwent pulsed sputtering. The nanoindentation hardness of the CrN films also increased with a decrease in the duty cycle. This enhancement of the corrosion resistance and mechanical properties of pulsed sputtered CrN films could be attributed to the densification and surface smoothness of the microstructure of the films.

• 한국결정성장학회지
• /
• 제21권6호
• /
• pp.235-239
• /
• 2011

두 가지 조성의 TiCrN 코팅층(Ti : Cr = 20 : 80 및 5 : 95wt%)을 Inconel 617 합금 위에 증착하고, 1000oC까지의 온도영역에서 TiCrN 코팅이 Inconel 617 합금의 고온안정성에 미치는 영향을 조사하였다. XRD 분석과 미세구조 관찰을 통해 표면으로의 불균일한 Cr 확산이 TiCrN 층에 의해 억제되었음을 알 수 있었다. 그 결과 Inconel 617의 열산화 저항성이 현저하게 향상되었음을 확인하였다.

• 한국자기학회지
• /
• 제4권2호
• /
• pp.135-141
• /
• 1994

스퍼터방식으로 제조한 FeZrCrN 미결정박막의 질소 유입량의 변화와 Cr 첨가량 변화에 따라 연자기특성과 내반응성 및 내식성을 조사하였다. 질소 유립량 증가에 따라 포화자속밀도는 감소하고 적 절한량(질소 유입량 3%)의 질소가 유입 되었을 때 열처리후에도 이방성 분산 감소효과 등에 의하여 우수 한 연자기특성이 출현 하였으며, 이때 보자력은 0.4 Oe, 투자율은 5 MHz에서 2600 정도를 나타내었다. FeZrN 박막에 Cr을 7.5 at.% 정도 첨가하였을때 포화자속밀도는 12.5kg까지 감소하였지만 양호한 연자기 특성이 그대로 유지되었고 Cr 첨가에 의해 현저한 내식성의 향상과 집합 glass와의 내반응성의 개선이 있었다.

• 한국세라믹학회지
• /
• 제56권1호
• /
• pp.49-55
• /
• 2019

$Ti_{0.33}Al_{0.67}N/CrN$ nano-multilayers, which are known to have excellent wear resistance, were prepared using an unbalanced magnetron sputter to have various periods of 2-5 nm. $Ti_{0.33}Al_{0.67}N$ had a hexagonal structure in a single layer, but converted to a cubic structure by forming a multilayer with CrN, which has a cubic structure. Thus, $Ti_{0.33}Al_{0.67}N$ formed a superlattice in the multilayer. The $Ti_{0.33}Al_{0.67}/CrN$ multilayer with a period of 2.5 nm greatly exceeded the hardness of the $Ti_{0.33}Al_{0.67}N$ and the CrN single layer, reaching 39 GPa. According to the low angle X-ray diffraction results, the $Ti_{0.33}Al_{0.67}N/CrN$ multilayer maintained its as-coated structure to a temperature as high as $700^{\circ}C$ and exhibited hardness of 30 GPa. The thickness of the oxide layer of the $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating was less than one-tenth of those of the single layers. Thus, $Ti_{0.33}Al_{0.67}N/CrN$ multilayered coating had hardness and oxidation resistance far superior to those of its constituent single layers.

• 한국표면공학회지
• /
• 제42권6호
• /
• pp.272-275
• /
• 2009

The purpose of this study is to show the friction and wear characteristic behaviors of TiN and CrN coated SKD61 which is applied to Al 6xxx extrusion mold material. The friction and wear characteristic behaviors of both coating layers were investigated by the reciprocating friction wear tester under atmospheric pressure and un-lubricated state. The processing parameters in this study were temperature (50 and $120^{\circ}C$) and load (3, 5, and 11 kgf). This study was carried out while comparing the coefficient of friction and microstructure of TiN and CrN coating layers on SKD61. The coefficient of friction of CrN became lower than that of TiN at all conditions. Therefore, CrN was suggested to be more advantageous than TiN for extrusion mold.