• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.05b
• /
• pp.193-196
• /
• 2006

A carbonation shortens the endurance life of RC structure. So, to lengthen endurance life of RC structure, we use some kinds of surface-finishes. Because surface-finishes have abilities such as restraint against penetration and diffusion of CO2. In this study, we wanted to know whether we can evaluate the restrain effect of each surface-finish against carbonation with using FEM analysis. After study, we found that it is possible and we also evaluate the restrain effect of any other surface-finishes against carbonation through this process.

• Journal of the Korea Concrete Institute
• /
• v.28 no.4
• /
• pp.445-454
• /
• 2016

With the increase of decrepit facilities, construction waste increased to a certain level and now the increase is more or less stabilized. Yet construction waste still constitutes the largest portion of the overall wastes. Also, it is inevitable to spend a huge amount of the national budget due to the aggravating shortage of aggregate caused by prohibition on collection of natural aggregates as well as due to the damage to the land and environment caused by development of the sources of aggregates. As a countermeasure to the situation, the Ministry of Land, Infrastructure and Transport promulgated the quality standard for recycled aggregate to manage the usage of recycled aggregate according to its quality. But use of recycled aggregate for the purpose of high added value still remains nominal. Therefore, this research aims to study the applicability of recycled aggregate concrete as structural concrete by evaluating the quality improvement effects and the performance of the recycled aggregate concrete including recycled fine aggregate and recycled coarse aggregate that have undergone carbonation for 4 days and 14 days respectively in the condition of 60% RH, 20% $CO_2$ and $20^{\circ}C$ temperature, suggested for carbonation modifying from the advance research. The result shows carbonation modify contributed to quality improvement with 0.91% decrease in absorption rate for recycled fine aggregate and 0.7% decrease in absorption rate for recycled coarse aggregate. The physical properties and durability of the recycled aggregate made of aggregate modified by carbonation showed results similar to general concrete, which confirmed the possibility of applying the recycled aggregate made of recycled aggregate modified by carbonation to structural concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.4
• /
• pp.393-400
• /
• 2012

The effect of ground granulated blast-furnace slag (GGBS) and alkaline activator on the properties of setting, compressive strength, drying shrinkage and resistance of carbonation was assessed to develop high volume slag concrete, the GGBS replacement rate of which was more than 80 percent. The changes in the concrete as the replacement rate of GGBS increases were as follows. Initial and final setting time was delayed by two and a half hours, and the compressive strength development properties of concrete in early and long term age were decreased. Drying shrinkage was satisfactory as below $6{\times}10^{-4}$ in every mixture, and yet showed a tangible trend by replacement rate. Carbonation was materially increased. Setting time and early strength development property, however, were extremely advanced by the addition of the alkaline activator. While drying shrinkage was improved by the alkaline activator, resistance to carbonation was not.

• Korean Chemical Engineering Research
• /
• v.53 no.5
• /
• pp.590-596
• /
• 2015

Estimating potential of $CO_2$ emission reduction of non-capture $CO_2$ utilization (NCCU) technology was evaluated. NCCU is sodium bicarbonate production technology through the carbonation reaction of $CO_2$ contained in the flue gas. For the estimating the $CO_2$ emission reduction, process simulation using process simulator (PRO/II) based on a chemical plant which could handle $CO_2$ of 100 tons per day was performed, Also for the estimation of the indirect $CO_2$ reduction, the solvay process which is a conventional technology for the production of sodium carbonate/sodium bicarbonate, was studied. The results of the analysis showed that in case of the solvay process, overall $CO_2$ emission was estimated as 48,862 ton per year based on the energy consumption for the production of $NaHCO_3$ ($7.4GJ/tNaHCO_3$). While for the NCCU technology, the direct $CO_2$ reduction through the $CO_2$ carbonation was estimated as 36,500 ton per year and the indirect $CO_2$ reduction through the lower energy consumption was 46,885 ton per year which lead to 83,385 ton per year in total. From these results, it could be concluded that sodium bicarbonate production technology through the carbonation reaction of $CO_2$ contained in the flue was energy efficient and could be one of the promising technology for the low $CO_2$ emission technology.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2023.11a
• /
• pp.79-80
• /
• 2023

After the Second Industrial Revolution, as global warming caused by environmental issues has intensified, the CO₂ emissions from the cement industry have become an urgent challenge. Therefore, this study aimed to reduce and utilize CO₂ emissions by using CO₂-reducing Calcium Silicate Cement.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.2
• /
• pp.157-166
• /
• 2017

In general, carbonation and chlorine ions are the most harmful causes of deterioration of concrete structures. Recently, a method has been developed to control the corrosion of rebar in concrete containing chloride by impregnating a Surface coating material with a inhibitor. In this study, accelerated carbonation and differential thermogravimetric analysis (TG-DTA) and CASS tests were carried out to evaluate the characteristics of Surface coatings containing Organic Corrosion inhibitors which are excellent in corrosion inhibition and fix degradation causes $CO_2$ and $Cl^-$. As a result of the experiment, TG-DTA analysis and accelerated carbonation showed that $CO_2$ was directly reacted with amine derivative in concrete by the incorporation of Organic Corrosion inhibitor. In other words, $CO_2$ was immobilized and carbonation inhibition effect was confirmed. In addition, in the CASS test, the specimen coated with the Surface coating material containing the Organic Corrosion inhibitor with $Cl^-$ fixing property showed no corrosion until the 28th day and had excellent performance in preventing corrosion of a rebar by the chloride ion.

• Journal of the Korea Institute of Building Construction
• /
• v.18 no.3
• /
• pp.203-210
• /
• 2018

Corrosion of the rebar is one of the main factors affecting the durability of reinforced concrete in the world which lead to the failure of the reinforced concrete structures. In this research, a new method of fixing $CO_2$ is practiced to improve the carbonation resistance of the concrete. Brucite($Mg(OH)_2$), a kind of common $CO_2$ fixation materials, was added into ordinary Portland cement paste. Samples containing 0%, 5%, 10%, and 15% $Mg(OH)_2$ were exposed to an accelerated carbonation curing regime with 20% concentration of $CO_2$, 60% relative humidity, and a temperature of $20^{\circ}C$ until tested at 3d, 7d, 14d and 28d. After 28d of $CO_2$ accelerated curing, in the paste containing $Mg(OH)_2$, magnesian calcite was detected by SEM-EDX. Meanwhile, the paste containing $Mg(OH)_2$ exhibit the better pore distribution than ordinary Portland cement paste and the compressive strength of the cement paste containing $Mg(OH)_2$ were more than 50Mpa.

• Journal of Energy Engineering
• /
• v.26 no.4
• /
• pp.45-56
• /
• 2017

Coal power plants produce electricity for the nation's power grid, but they also produce more hazardous air emissions than any other industrial pollution sources. The quantity is staggering, over 386,000 tons of 84 separate hazardous air pollutants spew from over 400 plants in 46 states. In South Korea also, annual coal ash generation from coal-fired power plants were about 6 million tons in 2015. Pollutants containing particulate matter 10, 2.5 (PM10, PM2.5), heavy metals and dioxins from coal-fired power plant. The emissions threaten the health of people who live near these power plants, as well as those who live hundreds of miles away. These pollutants that have long-term impacts on the environment because they accumulate in soil, water and animals. The present study is to investigate the physical and chemical characteristics of coal-fired power plant fly ash and bottom ash contains particulate matter, whose particulate sizes are lower than $PM_{10}$ and $PM_{2.5}$ and heavy metals. There are wide commercial technologies were available for monitoring the PM 2.5 and ultra-fine particles, among those carbonation technology is a good tool for stabilizing the alkaline waste materials. We collected the coal ash samples from different coal power plants and the chemical composition of coal fly ash was characterized by XRF. In the present laboratory research approach reveals that potential application of carbonation technology for particulate matter $PM_{10}$, $PM_{2.5}$ and stabilization of heavy metals. The significance of this emerging carbonation technology was improving the chemical and physical properties of fly ash and bottom ash samples can facilitate wide re use in construction applications.

• Journal of the Korea Concrete Institute
• /
• v.13 no.3
• /
• pp.277-284
• /
• 2001

Hardened concrete contains pores of varying types and sizes, and therefore the transport of air through concrete can be considered. The rate of permeability will not only depends on the continuity of pores, but also on the moisture contents in concrete and finishing material on concrete. Also it knows that the durability of reinforced concrete structure is concerned with air permeability which effects on the carbonation occurred by invasion of CO2 gas and the corrosion of steel bar occurred by O$_2$. In this paper, the effects of curing conditions and finishing materials on carbonation and air permeability are investigated according to the accelerated carbonation test. As results, carbonation velocity and air permeability are effected by curing conditions and finishing materials, and air permeability coefficient is effected by moisture content. Also the relationship between carbonation velocity coefficients and air permeability coefficients has been quite well established.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.43 no.3
• /
• pp.113-120
• /
• 2011

Precipitated calcium carbonate(PCC), particularly calcite crystal, is extensively used as a pigment, filler or extender in various industries such as paper, paint, textile, detergents, adhesives, rubber and plastics, food, cosmetics, and biomaterials. PCC is conventionally produced through the gas-liquid carbonation process, which consists on bubbling gaseous $CO_2$ through a concentrated calcium hydroxide slurry. This study is aimed to find some factors for controlling the morphology of engineered PCC in lab-scaled mixing batch. The experimental designs were based on temperature variables, $Ca(OH)_2$ concentration, $CO_2$ flow rate, and electrical conductivity. The model of engineered PCC morphology was finally controlled by adjustment of electrical conductivity(6.0~7.0 mS/cm) and $Ca(OH)_2$ concentration(10 g/L). Orthorhombic calcite crystals were mostly created at high concentration and electrical conductivity conditions because the increased ratio of $Ca^{2+}$ and $CO{_3}^{2-}$ ions affects the growth rate of orthorhombic faces. Excess calcium spices were contributed to the growth of faces in calcium carbonate crystal, and the non-stoichiometric reaction was occurred between $Ca^{2+}$ and $CO{_3}^{2-}$ ions during carbonation process.