• Journal of the Korean Recycled Construction Resources Institute
• /
• v.2 no.3
• /
• pp.180-187
• /
• 2014

The purpose of this study is to evaluate on the mechanical properties of High Volume Mineral Admixture(HVMA) high strength concrete to reduce the amount use of Ordinary Potland Cement, to discover the optimized HVMA binder and to test HVMA concrete based on the change of W/B and curing temperature. The results were shown as follows: The HVMA binder using the mixture of combined heat power plant fly ash and anhydrous gypsum known as inorganic activators with the mixture of blast furnace slag and fly ash was optimized. The mixture of HVMA high strength concrete at 26% of W/B ratio had a good result on flow characteristic and mechanical properties. High strength HVMA concrete over 50MPa is possibly manufactured over curing temperature $20^{\circ}C$.

• Journal of the Korea Concrete Institute
• /
• v.13 no.3
• /
• pp.277-284
• /
• 2001

Hardened concrete contains pores of varying types and sizes, and therefore the transport of air through concrete can be considered. The rate of permeability will not only depends on the continuity of pores, but also on the moisture contents in concrete and finishing material on concrete. Also it knows that the durability of reinforced concrete structure is concerned with air permeability which effects on the carbonation occurred by invasion of CO2 gas and the corrosion of steel bar occurred by O$_2$. In this paper, the effects of curing conditions and finishing materials on carbonation and air permeability are investigated according to the accelerated carbonation test. As results, carbonation velocity and air permeability are effected by curing conditions and finishing materials, and air permeability coefficient is effected by moisture content. Also the relationship between carbonation velocity coefficients and air permeability coefficients has been quite well established.

• Journal of the Korean Geosynthetics Society
• /
• v.17 no.2
• /
• pp.41-49
• /
• 2018

The purpose of this study is to fabricate a full scale road embankment using lightweight air foamed soil as a soil material on soft ground and to investigate its material characteristics and behavior in order to promote dredged soil utilization and minimize ground improvement. As a result of the laboratory test of the onsite mixed samples, the total unit weight of the specimens decreased almost linearly until curing 28 days. In particular, the total unit weight after 28 days of curing was reduced to about 81% of the slurry state before curing, which will be useful in the formulation of similar native soil materials in the future. The unconfined compressive strength began to decrease with the 14th day of curing as shown in the previous study. When the cement content is increased, the strength decreases sharply at a small strain change after the occurrence of the maximum compressive strength, and the maximum strength is exhibited in a range of a smaller axial strain than normal range. The settlement at the surface layer of the ground due to the lightweight embankment was about 1 / 2.75 of the soil embankment and was in agreement with the unit weight ratio (1 / 2.7) of the embankment materials. This indicates the cause and effect of the settlement due to the difference in self weight of the embankments. Also, the difference in settlement between soil and lightweight embankment increased with increasing depth. This shows that the difference in the point at which the settlement is terminated is clear. The ground horizontal displacement under the lightweight embankment was about 15~20% smaller than that of the soil embankment and the depth of occurrence was also 4.5~5.0m shallower in the lightweight embankment.

• Journal of the Korea Concrete Institute
• /
• v.15 no.4
• /
• pp.574-584
• /
• 2003

The most common deterioration cause of concrete structures in urban environment is carbonation. Recently, the $CO_2$ concentration and temperature at atmosphere is sharply increased with time due to global warming phenomena. In this study, the climate scenario IS92a, which was suggested by the IPCC, is used to consider temperature and atmospheric $CO_2$ concentration change in the model of service life prediction. The modified mathematical solution, which was based on the Fick's 1st law of diffusion, was used to reflect concrete materials properties such as the degree of hydration of concrete with elapsed time, and important parameters, which associated with deterioration rate. The techniques of service life prediction are developed introducing the method of reliability and stochastic concept to consider microclimatic condition in Seoul, South Korea. From the result of service life prediction, concrete containing high W/C ratio is shown fast carbonation rate due to $CO_2$ concentration increase. It is concluded that the deterioration of concrete structures due to carbonation is insignificant problem on the conditions that below W/C 55%, well curing concrete.

• Journal of the Korea Concrete Institute
• /
• v.28 no.3
• /
• pp.317-328
• /
• 2016

This research intends to understand the impact of super-absorbent polymer (SAP) as an internal curing agent in Ultra-High Performance Concrete (UHPC). Two different types of SAPs of acrylic acid (SAP_AA) and acrylic acid-co-acrylamide (SAP_AM) were examined with UHPC formulation. Isothermal calorimetry and x-ray diffraction experiments revealed the impact of polymers with the different chemical bonds on cement hydration. To test its feasibility as a shrinkage reducing admixture for UHPC, a series of experiments including flowability, compressive strength, rapid chloride permeability and autogenous shrinkage profile was performed. While both SAPs showed a reduction in autogenous shrinkage, it has been concluded that the SAP size and chemical form significantly affect the performance as an internal curing agent in UHPC by controlling cement hydration and porosity modification. Between the tested SAPs, SAP_AM which absorbs more water in UHPC than SAP_AA, shows better mechanical and durability performance.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.4
• /
• pp.416-424
• /
• 2023

Concrete emits a large amount of carbon dioxide throughout its life cycle, and due to the societal demand for carbon dioxide reduction, research on storing carbon dioxide in concrete in the form of minerals is ongoing. In this study, cyanobacteria, which absorb carbon dioxide through photosynthesis and fix it as calcium carbonate, were applied to a porous concrete substrate, and the changes in the properties of the concrete substrate due to their special environmental curing condition were analyzed. The results showed that the calcium carbonate precipitation by the microorganisms was concentrated in the light-exposed surface area, and most of the precipitation occurred in the cement paste part, not in the aggregate. This microbially induced calcium carbonate precipitation enhanced the mechanical performance of the paste and improved the overall compressive strength as the curing age progressed. In addition, the increase in microbial biofilm and calcium carbonate improved the pore structure, which influenced the reduction in water permeability.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.525-526
• /
• 2009

On this paper we induce calcite($CaCO_3$) precipitation using microbial biomineralization of the Sporosarcina pasteurii and evaluate required performance evaluation by adjusting it to mortar. As a result carbonation normal mortar test piece(C3S-W) and mortar test piece(C3S-S.p) mixed with Sporosarcina pasteurii, reaction of C3S-S.p was late than C3S-W. Also, in the case of carbonation experiment of C3S-S.p curing in the Urea-CaCl2 aqueous solution(Medium) during 28days and durability of the C3S-W, durability of the mortar test piece(C3S-S.p) mixed with Sporosarcina pasteurii become higher than normal mortar test piece(C3S-W).

• Journal of the Korean Wood Science and Technology
• /
• v.8 no.2
• /
• pp.9-16
• /
• 1980

The problem of tauns having the characteristics of severe variations in quality and unequally distributed moisture content in veneer sheets after drying for plywood could be cured to a proper even moisture distribution by the peeling of veneers in a prolonged period. The poor gluability of tauns was improved by applicaton of increased resin content of glue in spreading. Combinations of tauns with lauan and kapur for plywood showed good shear strength.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.06a
• /
• pp.179-180
• /
• 2020

CO2 emissions are caused by cement manufacturing process. To solve this problem construction industry are using industrial by-products to replace cement. In this study, three different industrial by products were used and mixed with hybrid fibers to enhance bond strength. As the result, Regardless of the mixing rate of silica fume, the compressive strength of the ternary non cent mortar was higher than that of OPC and binary. And mixed hybrid fibers cured by room temperature compressive strength were 23% higher than those without hybrid fibers.

• Proceedings of the Korea Water Resources Association Conference
• /
• 2023.05a
• /
• pp.464-464
• /
• 2023

최근 이산화탄소(Carbon Dioxode, CO₂) 배출량 증가로 인하여 지구온난화와 같은 기후변화 문제가 심각한 사회 문제로 대두되고 있다. 이에 따라 2015년 12월 12일 프랑스 파리에서 열린 제21차 유엔기후변화협약에서 교토의정서를 대체하는 파리협정(Paris Agreement)을 채택하였으며, 국내에서는 이러한 국제사회의 기후변화 대응에 동참하고 온실가스 감축을 이행하기 위한 2050 탄소중립 정책을 추진하였다. 이산화탄소를 다량으로 발생시키는 철강·산업·건설·에너지 분야 중건설 분야에서 배출되는 이산화탄소는 전체 배출량의 19.9%로 특히 시멘트를 제조하는 과정에서 많은 양의 이산화탄소가 배출되고 있다. 기존의 건설 분야 에서는 이산화탄소를 저감하기 위해 콘크리트 배합 또는 양생과정에서 챔버 내 이산화탄소를 가스 형태로 주입하여 탄산화 반응을 통해 콘크리트 내부에 이산화탄소를 영구히 저장시키고자 하였다. 그러나 이는 챔버 사용, 양생조건 등 적용 조건이 제한적이며, 콘크리트 내 이산화탄소 흡수 효율이 높지 않아 이를 개선할 수 있는 기술이 필요하다. 이를 개선하기 위해 최근에는 콘크리트 배합수 내 이산화탄소를 용해시켜 배합과정에서 콘크리트 내부로 이산화탄소를 강제로 인입시키는 연구들이 진행되고 있다. 그러나 콘크리트 배합수로 사용되고 있는 일반물이나 지하수의 경우 가압을 하여도 약 1,400mg/L의 이산화탄소를 용해시키며, 가압을 통해 용해된 이산화탄소는 쉽게 대기 중으로 방출되는 한계점을 지니고 있어 현장에서 사용하기 어려운 문제가 있다. 이러한 한계점을 극복하기 위해서 본 연구에서는 200nm 이하의 크기를 가지는 나노버블기술을 이용해 압력을 가하지 않은 상태에서 수중에 이산화탄소를 용해시킬 수 있는 시스템을 개발하고자 한다. 나노버블기술을 이용한 수중 이산화탄소용해 시스템을 통해 수중에 이산화탄소를 용해시켜 콘크리트 배합수로 활용하기 위한 기초 연구가 될 것으로 판단된다.