• Korean Journal of Soil Science and Fertilizer
• /
• v.11 no.1
• /
• pp.17-24
• /
• 1978

A field experiment was conducted on a soil where habitual zinc deficiency has been observed, to investigate the effectiveness of two forms of zinc containing fertilizers: zinc enriched fused phosphate and zinc enriched compound fertilizer. The result of present study is summarized as following. 1. The sail used for the study contained relatively large amount of 1N $CH_2COONH_4$ extractable Ca and the pH was 7.03. Available Zn extracted by 0.1 HCl and available $SiO_2$ extracted by NaOAc were 3.35 ppm and 67.7 ppm respectively. 2. In control plots Zinc content of rice plant measured at 20 days after transplanting was 22-23 ppm, which was a little higher than the critical level (20ppm). But at harvesting stage it dropped to 15ppm. 3. The ratios of $P_2O_5/Zn$ and N/Zn tended to lower as the zinc applied to the soil increased. 4. Application of Zinc clearly increased the number of tillers and plant height as compared to the control. It was also observed that the plots received znic headed and matured earlier compared to the control plots by two weeks. 5. Application of zinc increased all of the yield components and the yield of rice. However, there were no statistical differences in yield and yield components among the forms and levels of zinc fertilizers.

• Journal of the Korean Chemical Society
• /
• v.42 no.6
• /
• pp.618-628
• /
• 1998

Pure CaO, Mn-doped CaO, Mn/CaO, and K/CaO catalysts were prepared and tested as catalysts for the oxidative coupling of methane in the temperature range of 600 to 800$^{\circ}C$ to investigate the effects of Mn- and K-addition on the catalytic activity of calcium oxide. To characterize the catalysts, X-ray powder diffraction(XRD), XPS, SEM, DSC, and TG analyses were performed. The catalytic reaction was carried out in a single-pass flow reactor using on-line gas chromatography system. Normalized reaction conditions were generally $p(CH_4)/p(O_2)=250$ Torr/50 Torr, total feed flow rate=30 mL/min, and 1 atm of total pressure with He being used as diluent gas. Among the catalysts tested, 6.3 mol% Mn-doped CaO catalyst showed the best $C_2$ yield of 8.0% with a selectivity of 43.2% at 775$^{\circ}C$. The $C_2$ selectivity increased on lightly doped CaO catalysts, while decreased on heavily doped CaO([Mn] > 6.3 mol%) catalysts. 6 wt.% Mn/CaO and 6 wt.% K/CaO catalysts showed the $C_2$ selectivities of 13.2% and 30.9%, respectively, for the reaction. Electrical conductivities of CaO and Mn-doped CaO were measured in the temperature range of 500 to 1000$^{\circ}C$ at Po2's of $10^{-3}\; to\;10^{-1}\;atm.$ The electrical conductivity was decreased with Mn-doping and increased with increasing $P0_2$in the range of $10^{-3}\;to\;10^{-1}\;atm,$ indicating the specimens to be p-type semiconductors. It was suggested that the interstitial oxygen ions formed near the surface can activate methane and the formation of interstitial oxygen ions was discussed on the basis of solid-state chemistry.

• Journal of the Korean Electrochemical Society
• /
• v.8 no.3
• /
• pp.139-145
• /
• 2005

[ $SnO_x$ ] films on the flexible substrate of PET film were prepared at ambient temperature under a $(CH_3)_4Sn(TMT: tetra-methyl tin)-H_2-O_2$ atmosphere in order to obtain transparent conductive polymer by using ECR-MOCVD(Electro Cyclotron Resonance Metal Organic Chemical Yfpor Deposition) system. The prepared $SnO_x$ thin films show generally over $90\%$ of optical transmittance at wavelength range of 380-780nm and about $1\times10^{-2\~3}ohm{\cdot}cm$ of electrical resistivity. In the present study, effects of $O_2/TMT\;and\;H_2/TMT$ mole ratio on the properties of $SnO_x$ films are investigated and the other process parameters such as microwave power, magnetic current power, substrate distance and working pressure are fixed. Based on our experimental results, the $SnO_x$ film composition ratio of Sn and O directly influences on the electrical and optical properties of the films prepared. The $SnO_x$ film with low electric resistivity and high transmittance could be obtained by controlling the process parameters such as $O_2/TMT\;and\;H_2/TMT$ mole ratio, which play an important role to change the composition ratio between Sn and O. An increase of $O_2/TMT$ mole ratio brought on the increases 0 content in the $SnO_x$ film. On the other hand, an increase of $H_2/TMT$ mole ratio lead to decreases the oxygen content in the film. The optimized composition ratio of oxygen : tin Is determined as 2.4: 1 at $O_2/TMT$ of 80 and $H_2/TMT$ of 40 mole ratio, respectively.