• Journal of the Korean institute of surface engineering
• /
• v.34 no.3
• /
• pp.258-263
• /
• 2001

Siloxane thin films were fabricated on a silicon wafer by spin-coating using a siloxane solution made by the sol-gel process. Fluorine was doped using$ CF_4$ plasma treatment. The film was then annealed in-situ state in the nitrogen atmosphere. In order to examine the influence of annealing and fluorine doping on the siloxane thin film, thermogravimetric-differential thermal analysis (TG-DTA), Fourier transform-infrared spectroscopy (FT-IR) and X-ray photoelectron spectroscopy (XPS) were used and the dielectric constant was determined by the high-frequency capacitance-voltage method. Stable siloxane films could be obtained by in-situ annealing in a nitrogen atmosphere after $CF_4$ plasma treatment, and the dielectric value of the film was $\varepsilon$ 2.5.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.05b
• /
• pp.67-70
• /
• 2001

$SrBi_2Ta_2O_9$ thin films were etched at high-density $Cl_2/CF_4/Ar$ in inductively coupled plasma system. The chemical reactions on the etched surface were studied with x-ray photoelectron spectroscopy and secondary ion mass spectrometry. The etching of SBT thin films in $Cl_2/CF_4/Ar$ were chemically assisted reactive ion etching. The maximum etch rate was 1060 Am /min in $Cl_2$(20)/CF_4(20)/Ar(80). The small addition of $Cl_2$ into $CF_4$(20)/Ar(80) plasma will decrease the fluorine radicals and the increase CI radical. The etch profile of SBT thin films in $Cl_2/CF_4/Ar$ plasma is steeper than in $CF_4$/Ar plasma.Ā저會Ā저ﶖ⨀⡌ឫഀĀ᐀會Ā᐀㡆ﶖ⨀쁌ឫഀĀ᐀會Ā᐀遆ﶖ⨀郞ග堂瀀ꀏ會Āﶖ⨀〲岒ऀĀ᐀會Ā᐀䁇ﶖ⨀젲岒Ā㰀會Ā㰀顇ﶖ⨀끩Ā㈀會Ā㈀ﶖ⨀䡪Ā᐀會Ā᐀䡈ﶖ⨀Ā᐀會Ā᐀ꁈﶖ⨀硫Ā저會Ā저ﶖ⨀샟ගကĀ저會Ā저偉ﶖ⨀栰岒ఀĀ저會Ā저ꡉﶖ⨀1岒Ā저會Ā저Jﶖ⨀惝ග؀Ā؀會Ā؀塊ﶖ⨀ග㼀Ā切會Ā切끊ﶖ⨀⣟ගఀĀ搀會Ā搀ࡋﶖ⨀큭킢Ā저會Ā저

• Journal of Electrical Engineering and Technology
• /
• v.12 no.5
• /
• pp.2007-2013
• /
• 2017

In order to give hydrophobic surface properties on carbon steel, the fluorinated amorphous carbon films were prepared by using linear 2.45GHz microwave PECVD device. Two different process approaches have been tested. One is direct deposition of a-C:H:F films using admixture of $Ar/CH_4/CF_4$ working gases and the other is surface treatment using $CF_4$ plasma after deposition of a-C:H film with $Ar/CH_4$ binary gas system. $Ar/CF_4$ plasma treated surface with high $CF_4$ gas ratio shows best hydrophobicity and durability of hydrophobicity. Nanometer scale surface roughness seems one of the most important factors for hydrophobicity within our experimental conditions. The properties of a-C:H:F films and $CF_4$ plasma treated a-C:H films were investigated in terms of surface roughness, hardness, microstructure, chemical bonding, atomic bonding structure between carbon and fluorine, adhesion and water contact angle by using atomic force microscopy (AFM), nano-indentation, Raman analysis and X-ray photoelectron spectroscopy (XPS).

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.23 no.11 s.170
• /
• pp.2014-2021
• /
• 1999

The present investigation is concerned with the degradation characteristics of cast stainless steel(CF8M), exposed to the $\sigma$-phase degradation at $700^{\circ}C$. In the present paper, the degradation of CF8 M at $700^{\circ}C$ is evaluated by a non-destructive test, DL-EPR(double loop electrochemical potentiokinetic reactivation). The surface of specimens is observed by using scanning electron microscopy after DL-EPR test. Also. chromium contents of matrix, grain boundary and ferrite phase are analyzed by electron probe X-ray micro analyzer. Through the experiments, the following results are obtained 1) The degree of sensitization(DOS) of CF8M aged up to 15hr at $700^{\circ}C$ is increased with acing time while that is decreased with aging time from 15hr to 150hr. 2) The impact energy decreases with increase of $\sigma$-phase while DOS increases with $\sigma$-phase until aging time reaches to 15hr. After the aging time. 15hr, the $\sigma$-phase and the rate of impact energy with respect to aging time decreases. Therefore the degradation behavior of the CF8M can be evaluated by comparing SEM micrographs and the value of DOS.

• Bulletin of the Korean Chemical Society
• /
• v.32 no.4
• /
• pp.1187-1194
• /
• 2011

The hydrogen abstraction reaction of $CF_3CH_2CHO$ + OH has been studied theoretically by dual-level direct dynamics method. Two stable conformers, trans- and cis-$CF_3CH_2CHO$, have been located, and there are four distinct OH hydrogen-abstraction channels from t-$CF_3CH_2CHO$ and two channels from c-$CF_3CH_2CHO$. The required potential energy surface information for the kinetic calculation was obtained at the MCG3-MPWB//M06-2X/aug-cc-pVDZ level. The rate constants, which were calculated using improved canonical transitionstate theory with small-curvature tunneling correction (ICVT/SCT) were fitted by a four-parameter Arrhenius equation. It is shown that the reaction proceeds predominantly via the H-abstraction from the -CHO group over the temperature range 200-2000 K. The calculated rate constants were in good agreement with the experimental data between 263 and 358 K.

• Nuclear Engineering and Technology
• /
• v.31 no.2
• /
• pp.133-138
• /
• 1999

Research on the etching reaction of UO$_2$ with CF$_4$/O$_2$gas mixture plasma is carried out. The reaction rates are investigated as a function of CF$_4$/O$_2$ ratio, plasma power, and substrate temperature. It is found that there exists an optimum CF$_4$/O$_2$ ratio around 4:1 at all temperatures up to 37$0^{\circ}C$ and surface analysis using XPS X-ray Photoelectron Spectroscopy) confirms the result. Peak rate at the optimum gas composition increases with increasing temperature. Highest rate obtained in this study leaches 1050 monolayers/min. at 37$0^{\circ}C$ under r. f. power of 150 W, which is equivalent to about 0.5${\mu}{\textrm}{m}$/min. The rate also increases with increasing r. f. power, thus, higher power and higher substrate temperature will undoubtedly raise the etching reaction rate much further. This reaction seems to be an activated process, whose activation energy will be derived in the following experiments.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.12
• /
• pp.996-1002
• /
• 2000

Ferroelectric (Ba, Sr) TiO$_3$(BST) thin films have attracted much attention for use in new capacitor materials of dynamic random access memories (DRAMs). In order to apply BST to the DRAMs, the etching process for BST thin film with high etch rate and vertical profile must be developed. However, the former studies have the problem of low etch rate. In this study, in order to increase the etch rate, BST thin films were etched with a magnetically enhanced inductively coupled plasma(MEICP) that have much higher plasma density than RIE (reactive ion etching) and ICP (inductively coupled plasma). Experiment was done by varying the etching parameters such as CF$_4$/(CF$_4$+Ar) gas mixing ratio, rf power, dc bias voltage and chamber pressure. The maximum etch rate of the BST films was 170nm/min under CF$_4$/CF$_4$+Ar) of 0.1, 600 W/-350 V and 5 mTorr. The selectivities of BST to Pt and PR were 0.6 and 0.7, respectively. Chemical reaction and residue of the etched surface were investigated with X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.209-212
• /
• 2001

Polyimide(PI) films have been considered as the interlayer dielectric materials due to low dielectric constant, low water absorption, high gap-fill and planarization capability. The PI mm Was etched with using inductively coupled plasma (ICP). The etching characteristics such as etch rate and selectivity were evaluated to gas mixing ratio. High etch rate was $8300{\AA}/min$ and vertical profile was approximately acquired $90^{\circ}$ at $CF_{4}/(CF_{4}+O_{2})$ of 0.2. The selectivies of polyimide to PR and $SiO_{2}$ were 1.2, 5.9, respectively. The etching profiles of PI films with an aluminum pattern were measured by a scanning electron microscope (SEM). The chemical states on the PI film surface were investigated by x-ray photoelectron spectroscopy (XPS). Radical densities of oxygen and fluorine in different gas mixing ratio of $O_{2}/CF_{4}$ were investigated by optical emission spectrometer (OES).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.217-220
• /
• 2001

The possibility of cerium dioxide $(CeO_2)$ thin films as insulators of metal erroelectric insulator semiconductor (MFIS) structures have been studied. The etching $CeO_2$ thin films have been perfonned in an inductively coupled $Cl_{2}/CF_{4}/Ar$ plasma. The high etch rate of the $CeO_2$ thin film was $250\AA /m$ at a 10 % addition of $Cl_2$ into the $Ar(80)/CF_{4}(20)$. The surface reaction of the etched $CeO_2$ thin films was investigated using X-ray photoelectron spectroscopy (XPS) analysis. There are Ce-Cl and Ce-F bonding by chemical reaction between Cl, F and Ce. These products can be removed by the physical bombardment of incident Ar ions.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.217-220
• /
• 2001

The possibility of cerium dioxide (CeO$_{7}$ ) thin films as insulators of metal erroelectric insulator semiconductor (MFIS) structures have been studied. The etching CeO$_2$ thin films have been performed in an inductively coupled C1$_2$/CF$_4$/Ar plasma. The high etch rate of the CeO$_2$ thin film was 250 ${\AA}$/m at a 10% addition of Cl$_2$ into the Ar(80)/CF$_4$(20). The surface reaction of the etched CeO$_2$ thin films was investigated using X-ray photoelectron spectroscopy (XPS) analysis. There are Ce-Cl and Ce-F bonding by chemical reaction between Cl, F and Ce. These products can be removed by the physical bombardment of incident Ar ions.