• 한국세라믹학회지
• /
• 제31권5호
• /
• pp.471-476
• /
• 1994

The influence of TiO2 addition on the sintering and microstructure of magnesia ceramics was studied. An excess amount of TiO2 over the solid solubility limit reacted with magnesia to form Mg2TiO4 compound above 130$0^{\circ}C$. The deviation of lattice parameter of MgO was estimated to be under 0.2% when existence of TiO2 in MgO. The addition of TiO2 markedly promoted the densification of MgO at comparatively low temperature and the sintered density of about 98% of the theorectical was obtained at 150$0^{\circ}C$, 2h. The densification was mainly governed by grain growth of MgO and the effect of Mg2TiO4 existing as a second phase on depression of grain growth of MgO was not exhibited.

• 한국세라믹학회지
• /
• 제30권9호
• /
• pp.740-746
• /
• 1993

TiO2-SnO2 fine powders prepared by coprecipitation from TiCl4-SnCl4 aqueous solution, and their crystal structures were studied. All the TiO2-SnO2 fine powders calcined at 180~$700^{\circ}C$ showed the complete solid solution between TiO2(rutile structure) and SnO2(rutile structure). This crystal structure of TiO2-SnO2 powders is thought to be originated mainly from the heterogeneous nucleation of Ti-hydroxde on the Sn-hydroxide with coherent structure.

• 대한환경공학회지
• /
• 제22권3호
• /
• pp.511-521
• /
• 2000

디젤자동차와 같이 희박연소 상태에서 많이 배출되는 질소산화물을 선택적 촉매환원(SCR)으로 제거하기 위하여 제올라이트와 금속산화물을 조합한 촉매를 석영 반응로에서 설험하였다. 환원제는 자동차 배출가스에 포함되어 있어 실용 가능성이 크다고 판단되는 탄화수소 중 안전성 및 환원효율이 좋은 올레핀계 탄화수소인 프로필렌을 사용하였다. 본 연구에서는 제올라이트 및 금속산화물계의 단일촉매 상태에서의 NOx 전환율을 파악하고, 저옹 및 고온에서 활성이 다른 촉매를 기계적으로 조합하여 NOx 전환 활성 온도창(Temperature Window)을 확대하고 내구성이 좋은 촉매를 찾고자 하였다 0.55wt%Pt-$TiO_2$/5wt%Cu-ZSM-5 촉매와 0.28wt%Pt-$TiO_2$/$Al_2O_3$ 촉매 및 1.1 wt%Pt-$TiO_2$/$Mn_2O_3$ 촉매 모두 $400^{\circ}C$를 변곡점으로 저온과 고온에서 NOx 제거활성이 있었는데, 저온에서 활성이 가장 큰 것은 0.28wt%Pt-$TiO_2$/$Al_2O_3$ 촉매이었고, 고온에서는 1.1wt%Pt-$TiO_2$/$Mn_2O_3$(21) 촉매가 제일 높은 활성을 보였다. 그러나 수분 및 아황산가스 공존시와 열적 내구성 면에서는 0.55wt%Pt-$TiO_2$/5wt% Cu-ZSM-5 촉매가 가장 우수하게 나타났다.

• Carbon letters
• /
• 제11권4호
• /
• pp.332-335
• /
• 2010

The photodegradation of the model compounds Quinol, an aromatic organic compound and Acid blue FFS, an acid dye of chemical class Triphenylmethane was studied by using illumination with UV lamp of light intensity 250W. $TiO_2$ and $TiO_2$ doped with Boron and Nitrogen was used as catalyst. The sol-gel method was followed with titanium isopropoxide as precursor and doping was done using Boron and Nitrogen. In photocatalytic degradation, $TiO_2$ and doped $TiO_2$ dosage, UV illumination time and initial concentration of the compounds were changed and examined in order to determine the optimal experimental conditions. Operational time was optimized for 360 min. The optimum dosage of $TiO_2$ and BN doped $TiO_2$ was obtained to be 2 $mgL^{-1}$ and 2.5 $mgL^{-1}$ respectively. Maximum degradation % for quinol and Blue FFS acid dye was 78 and 95 respectively, at the optimum dosage of BN-doped $TiO_2$ catalyst. It was 10 and 4% higher than when undoped $TiO_2$ catalyst was used.

• 전기학회논문지
• /
• 제56권7호
• /
• pp.1255-1260
• /
• 2007

[ $TiO_2-V_2O_5$ ] sol was prepared using sol-gel method. Sol changed to gel with hydrolysis and polymerization. DTA properties of gel powder had endothermic reaction due to evaporation of propanol about $80^{\circ}C$, had exothermic reaction due to combustion of propanol about $230^{\circ}C$ and had exothermic reaction due to combustion of alkyl group about $350^{\circ}C$. Crystalline properties of gel powder retained amorphous phase at $50^{\circ}C$, retained anatase phase from $400^{\circ}C\;to\;600^{\circ}C$ and had all rutile phase over $700^{\circ}C$ at 0.01mole $V_2O_5$ additive. The capacitance of thin films increased with increasing heat treatment temperature and thin films had best properties at $700^{\circ}C$. The capacitance of thin films increased a lot with decreasing measurement frequency.

• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제50권8호
• /
• pp.376-381
• /
• 2001

The(1-x) MgTiO$_3$-xSrTiO$_3$(x=0.03~0.04) ceramics were fabricated by the conventional mixed oxide method. The structural and microwave dielectric properties were investigated by XRD, SEM, EDS and network analyzer. The sintering temperature and time were 1275$^{\circ}C$~135$0^{\circ}C$ and 2hours, respectively. In the XRD results of 0.96MgTiO$_3$-0.04SrTiO$_3$ceramics, the perovskite structure of SrTiO$_3$and ilmenite structure of MgTiO$_3$phase were coexisted. The dielectric constant($\varepsilon$(sub)${\gamma}$) and temperature coefficient of resonant frequency($\tau$(sub)f) were increased with addition of SrTiO$_3$. In thie case of 0.96MgTiO$_3$-0.04SrTiO$_3$ ceramics sintered at 13$25^{\circ}C$, the dielectric constant, quality factor(Q) and temperature coefficient of resonant frequency($\tau$(sub)f) were 20.13, 7956(at 7.27GHz), and +1.76ppm/$^{\circ}C$, respectively.

• 한국결정성장학회지
• /
• 제7권2호
• /
• pp.259-270
• /
• 1997

$\alpha-Al_2O_3$와 비정질 $TiO_2$부터 $Al_2TiO_5$를 합성하기 위한 고체상태반응의 반응속도를 $1200~1300^{\circ}C$ 온도 범위에서 연구하였다. 반응속도는 $Al_2O_3$분말을 코팅한 50 mol%의. $TiO_2$와 일정한 온도에서 여러 시간동안 가열하여 생성된 혼합물에 의하여 결정되었다. MgO안의 반응물과 미반응물의 양은 X-선 회절분석에 의하여 결정되었다. $Al_2TiO_5$의 부피율과 peak intensity비의 자료로부터 $Al_2O_3$와 $TiO_2$의 pseudobrookite(Tialite)형태로의 반응은 $1280^{\circ}C$와 $1300^{\circ}C$ 사이에서 시작되었다. 고체상태반응 활성화 에너지는 Arrhenius식에 의하여 결정되었다. 활성화 에너지는 622.4 kJ/mol이다.

• 한국진공학회지
• /
• 제2권1호
• /
• pp.28-33
• /
• 1993

산화분위기에서의 Ti/SiO2 박막의 산화거동 및 계면반응을 조사했다. SiO2막위에 100nm의 티타니움을 스퍼터법으로 형성하여 급속가열로(Rapid Thermal Processor)에서 온도를 달리하여 산화시켰다. 산화거동은 박막의 면저항의 측정, 산화막 두께측정, XPS(X-ray Photoelectron Spectroscopy)에 의한 조성분석으로 평가했다. 산화시 티타니움 면저항은 표면에서 산화로 인해 약 $500^{\circ}C$ 이상에서 증가하기 시작해서 $800^{\circ}C$에서 포화되었다. 이 때 막두께는 약 $700^{\circ}C$ 이상에서 약 2배로 증가한 후 일정한 두께를 나타내었다. 이 결과로부터 산화부산물에 도전성물질이 존재하는 것을 알 수 있었다. TEM과 XPS분석결과 40$0^{\circ}C$ 이상에서 산화시 Ti 표면에서부터 TiO2가 형성되고 $600^{\circ}C$ 이상에서는 TiO2의 형성과 Si의 석출이 확인되었다. 석출되는 Si의 양은 온도에 따라 증가했다.

• 한국세라믹학회지
• /
• 제15권1호
• /
• pp.9-15
• /
• 1978

The possiblity of mullitization from the domestic alunite by adding of $Fe_2O_3-MnO_2$, $Fe_2O_3-MnO_2-TiO_2$, $Fe_2O_3-MnO_2-CaF_2$, and $Fe_2O_3-MnO_2-CaF_2-TiO_2$ mixtures as mineralizers was studied at the temperature range between $1, 250^{\circ}C$~$1, 430^{\circ}C$. The modifying method of domestic alunite was performed by calcination, wet ballmilling, and washing with water. The following results were obtained; 1) When added of 3.0% $Fe_2O_3$ plus 1.0-1.5% $MnO_2$ to modified alunite, the appropriate temperature range of mullite-forming was $1, 350^{\circ}C$-$1, 400^{\circ}C$. 2) When added of $TiO_2$ as mineralizer, the mullite-forming temperature was higher than not added. 3) When added of $CaF_2$ as mineralizer, the synthesized mullite was resolve at the temperature above $1, 350^{\circ}C$.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2011년도 추계학술발표대회
• /
• pp.26-26
• /
• 2011

Fe계 TiC 합금은 미량의 합금원소를 첨가시켜 경화능, 내식성, 내마모성 성질을 개선한 특수 공구용 재료로서 현재 절삭, 내마모성, 광산, 금형재료 등의 분야에 널리 사용되고 있다. 금속과 세라믹의 복합재료인 초경합금은 비열처리용 공구강으로 WC, TiC 등의 4, 5, 6족 금속탄화물에 Co, Ni, Fe등의 철족이 결합금속으로 소결한 복합재료로 WC-Co계 초경합금이 주종을 이루고 있으나, 전략 소재로서 고가인 Co 원료를 대체하기 위한 재료로서 초경재료의 고경도와 공구강의 경제성 및 가공성의 장점을 이용한 Fe-TiC계 초경합금의 연구가 다양하게 진행되고 있다. 본 연구에서는 Fe기지에 서브마이크론 크기의 미세한 TiC 입자가 균일하게 분산된 Fe-TiC 복합분말을 경제적으로 제조하기 위해 순수한 Fe, Ti 원료분말에 비해 단가가 낮고 미세 분쇄가 용이한 FeO, $TiH_2$ 분말을 고에너지 밀링 후 반응 열처리 시키는 유사 기계화학적 공정을 시도하였다. 조성비 Fe-30wt%TiC 복합분말을 제조하기위해 마이크론(micron) 크기의 FeO, $TiH_2$, C 분말을 사용하였고, 1단계로 FeO와 C을 고에너지 밀링으로 혼합 후 반응시켜 환원시키는 공정과 2단계로 이렇게 환원된 분말과 TiH2를 고에너지 밀링으로 다시 혼합, 분쇄한 후 반응열처리 하는 두 단계 공정을 사용하였다. FeO의 환원 단계에서는 $700{\sim}1,000^{\circ}C$ 온도 범위에서 1시간 유지하였고, 고에너지 밀링 시 밀링시간, 회전속도를 변수로 두고 실험하였다. 환원된 분말은 수평관상로를 이용해 아르곤분위기에서 $1,000{\sim}1300^{\circ}C$까지 1시간 유지하여 반응열처리시켜 Fe-TiC 복합분말을 제조하였다. 준비된 복합분말을 XRD와 FE-SEM, EDS, 입도분석기 (LPSA) 등을 이용해 분말의 형태와 특성, 상, 조성, 입도, 분산도 등을 조사하였다. 제조된 Fe-TiC 나노복합분말을 방전플라즈마소결(SPS) 과 상압소결 실험을 진행하였다. Fe-TiC 복합분말 제조공정의 첫 번째 단계인 FeO의 환원반응은 $800^{\circ}C$이상의 온도에서 Fe로 환원이 진행됨을 확인하였다. 두 번째 단계인 반응열처리공정에서는 $1,000^{\circ}C$ 이상에서 TiC가 형성됨을 XRD 상분석을 통해 확인할 수 있었고, $1,100^{\circ}C$ 이상의 온도에서 반응열처리를 했을 때 XRD 분석결과와 산소 조성 분석 결과로부터 반응의 완결성과 순도에서 최적 온도 조건임을 확인하였다. 온도를 $1,300^{\circ}C$로 증가시킬 경우 반응의 완결성에 큰 변화가 없는 반면 분말입자간의 목형성이 일어나 가소결 되는 것을 FE-SEM을 통해 관찰하였다. 또한 최적조건으로 제조된 Fe-TiC 복합분말의 입도분석과 FE-SEM/EDS 관찰/분석을 시행한 결과 평균 입도 0.6 ${\mu}m$의 미세한 Fe-TiC 복합분말 내에 Fe분말 주변과 내부에 나노크기의 TiC입자가 균일하게 분산되어 존재하는 것을 확인하였다.