• 한국초전도학회:학술대회논문집
• /
• 한국초전도학회 2006년도 High Temperature Superconductivity Vol.XVI
• /
• pp.85-85
• /
• 2006

• Progress in Superconductivity
• /
• 제10권2호
• /
• pp.103-107
• /
• 2009

$Bi_2Sr_2Ca_1Cu_2O_x$(BSCCO 2212) superconductors for current lead were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted at $1200^{\circ}\C$ in a resistance furnace using a Pt crucible and poured in a rotating cylindrical mold preheated at $550^{\circ}\C$ for 2 hour. The solidified BSCCO-2212 samples were heat-treated by partial melting process in oxygen atmosphere. The current-voltage curves at 77 K of the samples were obtained by transport measurement, and the microstructure was investigated by scanning electron microscope. The $J_c$ values at 77 K of the tubes partially melted at $840^{\circ}C,\;860^{\circ}C\;and\;880^{\circ}C$ were 492, 430 and 398 $A/cm^2$, respectively. It was observed that the plate-like grains in BSCCO 2212 tube was more developed in the sample heat-treated at $840^{\circ}C$. It was found that the critical current of the BSCCO 2212 samples was dependent on the partial melting schedule regarding the grain shape and size of the BSCCO 2212.

• Progress in Superconductivity
• /
• 제8권1호
• /
• pp.98-103
• /
• 2006

[$Bi_2Sr_2Ca_1Cu_2O_x$](BSCCO 2212) tubes were fabricated by centrifugal melting process(CMP). BSCCO 2212 powder was melted in a Pt crucible and solidified in a rotating steel mold. The BSCCO 2212 tube samples separated from steel mold were heat-treated at $800^{\circ}C\;and\;810^{\circ}C$ in oxygen flow. The critical current($I_c$) of the samples was measured by transport measurement at 77K, and the microstructure was investigated by scanning electron microscope. The $J_c$ at 77K of the tubes heated treated at $800^{\circ}C\;and\;810^{\circ}C$ were 197 and 240 $A/cm^2$, respectively. It was observed that the plate like grains in BSCCO 2212 tube was more developed in the sample heat treated at $810^{\circ}C\;and\;800^{\circ}C$ heated tube. It is found that the critical current($I_c$) of the BSCCO 2212 sample was dependent on the heating schedule regarding the growth of the BSCCO 2212 grains.