• Journal of the Korean Ceramic Society
• /
• v.24 no.6
• /
• pp.586-592
• /
• 1987

The role of the strain energy and phase stability in the diffuse phase transition have been investigated in the highly disordered solid solution, (Pb1-xBax)(Zr0.4Ti0.6)O3 (0.2 x 0.4). X-ray diffraction analysis indicates that tetragonality (c/a) decreases with the increasing Ba content. Also as the Ba content increases, phase transition becomes more diffuse and at the same time dielectric relaxation as a function of measured frequencies in the 1KHz-10MHz range occurs very pronouncedly. In the Ba content range, 0.2 x 0.35, hysteresis loops are routinely observed and the loop is observed to narrow shape as the Ba content increases but becomes very slim at 40mol% Ba content. Moreover thermal analysis shows that there is no abrupt change in the thermal expansion coefficient below the apparent transition temperature at which dielectric constant becomes maximum. From the above results, it has been concluded that creation of the strain energy due to the distorthion that occurred during the phase transition suppresses diffuse phase transition.

• Korean Journal of Materials Research
• /
• v.34 no.7
• /
• pp.321-329
• /
• 2024

In this work, a series of BaTiO₃-based ceramic materials, Ba(Al_0.5Nb_0.5)_xTi_1-xO₃ (x = 0, 0.04, 0.06, 0.08), were synthesized using a standard solid-state reaction technique. X-ray diffraction profiles indicated that the Al+Nb co-doping into BaTiO₃ does not change the crystal structure significantly with a doping concentration up to 8 %. The doping ions exist in Al³⁺ and Nb⁵⁺ chemical states, as revealed by X-ray photoelectron spectroscopy. The frequency-dependent complex dielectric properties and electric modulus were studied in the temperature range of 100~380 K. A colossal dielectric permittivity (>1.5 × 10⁴) and low dielectric loss (<0.01) were demonstrated at the optimal dopant concentration x = 0.04. The observed dielectric behavior of Ba(Al_0.5Nb_0.5)_xTi_1-xO₃ ceramics can be attributed to the Universal Dielectric Response. The complex electric modulus spectra indicated the grains exhibited a significant decrease in capacitance and permittivity with increasing co-doping concentration. Our results provide insight into the roles of donor and acceptor co-doping on the properties of BaTiO₃-based ceramics, which is important for dielectric and energy storage applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.04a
• /
• pp.309-313
• /
• 1997

(Ba$_{x}$Sr$_{l-x}$)TiO$_3$(BST) thin fi1ms with various Ba/Sr ratios were deposited on Pt(80nm)/SiO$_2$(100nm)/Si by RF magnetron sputtering. BST thin films which have x=0.6, 0.5, 0.4 were studied dielectric properties with temperature variation. The frequency was used from 100Hz to 1MHz for measuring dielectric constant. The measurement conditions of dielectric constant with Temperature Variation were 1KHz and 2$0^{\circ}C$. As a result, the dielectric constant of BST thin film was about 425 and loss factor was 0.013. Also, with increasing Temperature, the dielectric constants of BST thin films were gradually decreased.sed.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.44 no.8
• /
• pp.1068-1074
• /
• 1995

Effect of (Zn$_{1}$3/Nb$_{2}$3/) $O_{2}$ addition on the phase changes and microwave dielectric properties of BaTi $O_{3}$-3Ti $O_{2}$ ceramics were investigated. Addition of (Zn$_{1}$3/Nb$_{2}$3/) $O_{2}$ to BaTi $O_{3}$-3Ti $O_{2}$ resulted in the formation of Ba $Ti_{4}$$O_{9}$, $Ba_{2}$ $Ti_{9}$ $O_{20}$, Ba(Zn$_{1}$3/Nb$_{2}$3/) $O_{3}$, and Ti $O_{2}$ phases. Ba $Ti_{4}$$O_{9}$ phase was gradually transformed to $Ba_{2}$ $Ti_{9}$ $O_{20}$. This was identified by XRD and microstructure. As the Ba $Ti_{4}$$O_{9}$ phase transformed to $Ba_{2}$ $Ti_{9}$ $O_{20}$ phase, the dielectric constant increased to 37.5. Q*f$_{o}$ value was 40000 at x=0.04, and the temperature coefficient of resonant frequency was +10ppm/.deg. C.C.. C.C.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.52-52
• /
• 2008

The positive temperature coefficient of resistivity (PTCR) effect in (1-x)$BaTiO_3$ - $x(Bi_{0.5}K_{0.5})TiO_3$ doped with $Nb_2O_5$ was investigated. $(Bi_{1/2}K_{1/2})TiO_3$ (BKT) is more environment-friendly than $PbTiO_3$ in order to use in PTC thermistors. The incorporation of 1 mol% BKT to $BaTiO_3$ increased the Curie temperature (Tc) to $148^{\circ}C$. Doping of $Nb_2O_5$ to $Ba_{0.99}(Bi_{0.5}K_{0.5})_{0.01}TiO_3$ (BaBKT) ceramic has enhanced its PTCR effects. For the sample containing 0.025 mol% $Nb_2O_5$, it showed good PTCR properties; low resistivity at room temperature (${\rho}_r$) of 30 $\Omega{\cdot}cm$, a high PTCR intensity of approximately $3.3\times10^3$, implying the ratio of maximum resistivity to minimum resistivity (${\rho}_{max}/{\rho}_{min}$) in the measured temperature range, and a large resistivity temperature factor (a) of 13.7%/$^{\circ}C$ along with a high Curie temperature (Tc) of $167^{\circ}C$. In addition, the cooling rate of the samples during the sintering process had an influence on their PTCR behavior. All the samples showed the best ${\rho}_{max}/{\rho}_{min}$ ratio when they have cooled down at a rate of $600^{\circ}C$/min.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.3
• /
• pp.205-209
• /
• 2009

In this study, in order to develop the composition ceramics for lead-free ultrasonic motor, (1-x-0.09)$NaNbO_{3-x}BaTiO_3-0,09LiNbO_3$ ceramics were fabricated using a conventional mixed oxide process and their piezoelectric and dielectric characteristics were investigated according to the $BaTiO_3$ substitution. All the specimens showed orthorhombic phase structure without secondary phase, $BaTiO_3$ substitution enhanced density, dielectric constant(${\epsilon}_r$) and electromechanical coupling factor($k_p$), However, mechanical quality factor was deteriorated. Curie temperature of specimens was observed as about $380^{\circ}C$. At the $BaTiO_3$ substitution of 4 mol%, density, electromechanical coupling factor($k_p$), dielectric constant(${\epsilon}_r$) and piezoelectric constant($d_{33}$) of specimen showed the optimum value of $4.493g/cm^3$, 0.236, 175, 70 pC/N, respectively.

• Broadcasting and Media Magazine
• /
• v.6 no.1
• /
• pp.78-87
• /
• 2001

Seven kinds of most representative photorefractive crystals expected to contribute to the realization of the volume holographic storage were reviewed The growth conditions and problems for highly homogeneous optical qualities of the following crystals depending on the growth methods were discussed;(1) $LiNbO_3$ and $Bi_2SiO_{20}$ by Czochralski method (2) $Bi_{12}TiO_{20}$, $KNbO_3$ and $BaTiO_3$ by top seeded solution growth and (3) $(Sr_{1-x}Ba_{x})Nb_{2}O_{6}$ and $(K_{1-y}Na_y)_{2A-2}(Sr_{1-x}Ba_x)_{2-A}Nb_2O_6$ by Stepanov method, And then the figure of merits for the estimation of phororefractive materials on performances, such as $Q_1$, $Q_2$ and sensitivity, were discussed.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.23 no.12
• /
• pp.929-935
• /
• 2010

$(1-x)BaTiO_3-x(Bi_{0.5}Na_{0.5})TiO_3$ ($0.01{\leq}x{\leq}0.10$) ceramics were fabricated with muffled sintering by a modified synthesis process. Their positive temperature coefficient of resistivity (PTCR) characteristics were investigated systematically. All specimen showed a perovskite structure with a tetragonal symmetry. Both the lattice parameter of a and c axes were slightly decreased with increasing $(Bi_{0.5}Na_{0.5})TiO_3$ (BNT) content. Grain growth was achieved when the incorporated BNT was increased to 6 mol% and the inhibition of grain growth is considered to be due to the appearance of Ba vacancy ($V^{"}_{Ba}$) in the $(1-x)BaTiO_3-x(Bi_{0.5}Na_{0.5})TiO_3$ ($0.08{\leq}x$). With 4 mol% BNT addition, room temperature resistivity decreased to $48 \Omega{\cdot}cm$ and a resistivity jump ($\rho_{max}/\rho_{min}$) was as high as $1.1{\times}10^4$, respectively. Curie temperature was also increased to $171^{\circ}C$ with increasing BNT content.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.288-288
• /
• 2007

본 연구에서 내환원성 $BaTiO_3$의 PTCR(Positive Temperation Coefficient Resistance) 특성 및 미세구조에 대한 분쇄 및 출발 원료들의 하소 조건의 영향을 연구하였다. $BaCO_3$, $TiO_2$, $CeO_2$를 Attrition milling 하여 1차 혼합 및 분쇄한 후 건조하여 혼합분말을 얻었으며, $(Ba_{1-x}Ce_x)TiO_3$를 합성하기 위하여 $1000^{\circ}C{\sim}1200^{\circ}C$ 공기중에서 하소하였다. 각 하소온도에서 제조한 $(Ba_{1-x}Ce_x)TiO_3$에 첨가제를 2차 혼합하고 초미분쇄하여 분말을 제조하였다. 직경 5mm 의 시편을 제조하여 환원 및 재산화 분위기에서 소결을 한 후 상온저항값 및 R-T특성을 측정하였고 SEM 을 통해 미세구조를 관찰하였다. 또한 하소 후 온도에 따른 상분석을 XRD를 통하여 분석하였다. 그 결과 하소온도가 증가함에 따라 상온저항값은 감소하는 경황을 보였으며 PTC특성은 감소하다가 증가하는 경향을 보였다. 초미분쇄에 따른 입자크기는 $1{\mu}m$이하로 작아졌으며 미립화가 됨에 따라 하소/소결온도에 앙향을 줄 것으로 사료된다.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.134.2-134
• /
• 2000