A Study on the Characteristics of the Multilayer-Type PTC Thermistor for Fire Detection Sensor (화재감지센서 활용을 위한 적층헝 PTC서미스터의 특성에 관한 연구)

  • Chu Soon-Nam;Baek Dong-Hyun
    • Fire Science and Engineering
    • /
    • v.19 no.2 s.58
    • /
    • pp.75-80
    • /
    • 2005

  • This dissertation is about the development of PTC(Positive Temperature Coefficient) thermistor by composition method. A multilayer-type PTC samples were fabricated under optimal conditions after setting the experimental composition equation as $(0.90Ba+0.05Sr+0.05Ca)TiO_3+0.01TiO_3+0.01SiO_2+0.0008MnO_2+0.0018Nb_2O_5$ and their testing results were analyzed. The fabrication method of SMD(Surface Mounted Device) multilayer -type sample based on the composition ratio has the advantages in lowering its resistivity at room temperature, considerably, and increasing maximum current level, as needed. Although there is a disadvantage of peak resistivity drop by the multilayer, causing the increasement of thermal capacity. and thereby, increasing the switching delay time, a high applying voltage can increase the peak resistivity and shorten the switching delay time. The voltage-current characteristic showed that the more multilayers increased the initial maximum current and the transition voltage that increased the resistivity abruptly according to the curie point. The element it could be applied with the sensor for the fire detector.

  • PDF KSCI

Properties Optimization for Perovskite Oxide Thin Films by Formation of Desired Microstructure

  • Liu, Xingzhao;Tao, Bowan;Wu, Chuangui;Zhang, Wanli;Li, Yanrong
    • Journal of the Korean Ceramic Society
    • /
    • v.43 no.11 s.294
    • /
    • pp.715-723
    • /
    • 2006

  • Perovskite oxide materials are very important for the electronics industry, because they exhibit promising properties. With an interest in the obvious applications, significant effort has been invested in the growth of highly crystalline epitaxial perovskite oxide thin films in our laboratory. And the desired structure of films was formed to achieve excellent properties. $Y_1Ba_2Cu_3O_{7-x}$ (YBCO) superconducting thin films were simultaneously deposited on both sides of 3 inch wafer by inverted cylindrical sputtering. Values of microwave surface resistance R$_2$ (75 K, 145 GHz, 0 T) smaller than 100 m$\Omega$ were reached over the whole area of YBCO thin films by pre-seeded a self-template layer. For implementation of voltage tunable high-quality varactor, A tri-layer structured SrTiO$_3$ (STO) thin films with different tetragonal distortion degree was prepared in order to simultaneously achieve a large relative capacitance change and a small dielectric loss. Highly a-axis textured $Ba_{0.65}Sr_{0.35}TiO_3$ (BST65/35) thin films was grown on Pt/Ti/SiO$_2$/Si substrate for monolithic bolometers by introducing $Ba_{0.65}Sr_{0.35}RuO_3$ (BSR65/35) thin films as buffer layer. With the buffer layer, the leakage current density of BST65/35 thin films were greatly reduced, and the pyroelectric coefficient of $7.6\times10_{-7}$ C $cm^{-2}$ $K^{-1}$ was achieved at 6 V/$\mu$m bias and room temperature.

  • https://doi.org/10.4191/KCERS.2006.43.11.715 인용 PDF KSCI