• Proceedings of the KIEE Conference
• /
• 2003.07c
• /
• pp.1538-1540
• /
• 2003

The composites were fabricated respectively 61vol.% ${\beta}$-SiC and 39vol.% $TiB_2$ spray-dried powders with the liquid forming additives of 12wt% $Al_2O_3+Y_2O_3$ by pressureless annealing at $1700^{\circ}C,\;1750^{\circ}C\;1800^{\circ}C$ for 4 hours. The result of phase analysis of composites by XRD revealed ${\alpha}$-SiC(6H), $TiB_2$, and YAG($Al_5Y_3O_{12}$) crystal phase. The relative density, the Young's modulus and fracture toughness showed respectively the highest value of 92.97%, 92.88Gpa and $4.4Mpa{\cdot}m^{1/2}$ for composites by pressureless annealing temperature $1700^{\circ}C$ at room temperature. The electrical resistivity showed the lowest value of $8.09{\times}10^{-3}{\Omega}{\cdot}cm$ for composite by pressureless annealing tempe rature $1700^{\circ}C$ at $25^{\circ}C$. The electrical resistivity of the SiC-$TiB_2$ composites was all positive temperature cofficient resistance (PTCR) in the temperature ranges from $25^{\circ}C$ to $700^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.17 no.1
• /
• pp.18-24
• /
• 2007

Mullite-PSZ composite was prepared by sol-gel method using $Al(sec-OC_4H_9)_3,\;Si(OC_2H_5)_4,\;ZrOCl_2\;8H_2O\;and\;Y_2O_3$. The sinterability ana mechanical properties of powder compacts sintered at $1,650^{\circ}C$ for 4 hrs were investigated for various PSZ contents. In result Al-Si spinel formed at $980^{\circ}C$ from amorphous dried gel, and zirconia as well as mullite crystal formed above $1,200^{\circ}C$. The sintered body was densified to $97{\sim}98%$ except the specimen containing 25vol% PSZ which showed the relative density of about 95% obtained by sintering at $1,650^{\circ}C$ for 4 h. The flexural strength of the sintered body was a maximum value of 290 MPa in 20 vol% PSZ, which was also considerably larger than the value of 200 MPa without PSZ. The value of the fracture toughness increased linearly with increase of PSZ content and showed a maximum value of $4.3MPam^{1/2}$ in 25 vol% PSZ, Namely this value was remarkably larger than the $value(2.6MPam^{1/2})$ of pure mullite without PSZ.

• Korean Journal of Materials Research
• /
• v.9 no.3
• /
• pp.307-314
• /
• 1999

The effect of manufacturing variables, such as reactant powder$(TiB_2, B_4C)$, sintering temperature, and sintering time has been investigated on the microstructure and the mechanical properties of in-situ processed Ti/TiB composites. The mechanical properties were evaluated by measuring the compressive yield strength. The compressive yield strength of the in-situ processed composites was higher than that of the Ti-6AI-4V. The compressive yield strength of the composite made with TiE, reactant powder was higher than that of $B_4C$, mixed at the same volume fraction of reinforcement. It is because bonding nature between the matrix and the $TiB_2$, reactant powder was more strong than that of the other materials. It was proven by the examining the crack propagation path.

• Applied Biological Chemistry
• /
• v.35 no.4
• /
• pp.281-285
• /
• 1992

Composite seasioning was stored at different temperature with PE/Al/PE/PET packaging. $Q_{10}$ value due to temperature was 2.54 and shelf-lie of composite seasoning was predicted 29, 73 and 185 weeks at $35^{\circ}C$, $25^{\circ}C$ and $15^{\circ}C$, respectively. L value was decreased during storage but a and b value had little change. Correlation coefficient between sensory score and cole. value was low. Browning development and carbonyl value were increased with storage temperature and correlation coefficient between sensory score and those was comparatively high. Moisture content, salinity and total sugar content were within KS-standard during 18 weeks storage.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.17 no.12
• /
• pp.3083-3093
• /
• 1993

Friction and wear at ceramic coated surfaces of aluminum alloy were experimentally studied using a Ring-on-Block wear test machine. Ceramic materials coated on aluminum alloy surfaces were WC, CrC, $Al_{2}O_{3}$ by a plasma spray; and $Al_{2}O_{3}$,$Al_{2}SiO_{5}$, $Na_{2}B_{4}O_{7}$,$Na_{4}P_{2}O_{7}$, and $Al_{2}O_{3}-ZrO_{2}$ composite coating by an Anodic Spark Depositon. They were tested under the sliding wet contact and compared with aluminum alloys and steels. Test results showed that ceramic coated surfaces, in general, have better anti-wear property than those of aluminum alloys due to increase in the surface hardness ; however, they also showed higher coefficients of friction and changes in wear mechanisms, resulting in brittle fractures.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.304-304
• /
• 2007

고주파 모률에서 사용되는 기판소재는 저유전율과 낮은 loss 특성을 요구함으로 지속적인 연구를 필요로 한다. 지금까지의 ceramic/glass composite 에서 주로 사용된 ceramic filler는 Al2O3로 낮은 유전률을 구현에 한계가 있었다. Cordierite는 낮은 유전율 (${\varepsilon}_r$ < 4)을 나타내는 filler로서 그 가능성이 높지만 아직까지 보고된 결과들이 미흡한 실정이다. 따라서 본 연구에서는 cordierite filler와 SiO2-B2O3-Al2O3-RO (R : Zn, Sr, Ba, Ca)계의 glass를 혼합하여 LTCC용 기판소재로서의 가능성을 확인하고자 저온 동시소성이 가능한 소결온도인 $850^{\circ}C{\sim}1.000^{\circ}C$ 사이에서 소재의 소결실험을 진행하였다. 소결온도에 따른 상변화, 유전특성을 확인한 결과 filler로 사용된 cordierite상만이 관찰 되었으며 소결조건에 따라 5.0~5.5의 낮은 유전율과 1.000~1,500의 Q를 나타내는 것을 확인 하였다.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.5
• /
• pp.665-674
• /
• 2007

Purpose: The purpose of this study was to investigate the effect of sire and shape of retention element on the bond strength of indirect composite resin and metal. Material and method: The metal disk specimens, each 6mm in diameter, were cast from CrCo alloy. They were divided into 8 groups by applied retention element. retention bead group $B2\;({\phi}\;0.2mm),\;B4\;({\phi}\;0.4mm),\;B6\;({\phi}\;0.6mm),\;B8\;({\phi}\;0.8mm)$, retention crystal group C2 (0.2mm), C5 (0.5mm), C8 (0.8mm) and sandblasting group SB ($110{\mu}m\;Al_2O_3$ blasting) as control. Eighty-eight metal specimens were veneered with $TESCERA^{(R)}$ Indirect resin system. One specimen of each group was sectioned and the resin-metal bonding pattern at the interface was observed under measuring microscope. Other specimens were then tested for tensile bond strength on an Instron universal testing machine at a crosshead speed of 2mm/min. Results: 1. Compared to sandblasting, beads or crystals increased the resin-metal bond strength (P<.05). 2. 0.2mm retention crystals were most effective in improving the resin-metal bond strength (P>.05). 3. 0.2mm beads showed the highest bond strength among retention bead groups, but there was no statistically significant difference (P>.05). 4. Retention crystals tend to be higher in bond strength than retention beads due to wider surface area. 5. The larger retention element, the larger the undercut for the mechanical retention, but the gap at resin-metal interface was also increased. Conclusion: Within the limitations of this study, 0.2mm retention crystals were most effective in improving the resin-metal bond strength.

• Korean Journal of Metals and Materials
• /
• v.50 no.2
• /
• pp.176-182
• /
• 2012

The main purpose of this study was to evaluate the endurance against Al alloy melts and wear resistance of an in-situ synthesized titanium matrix composite (TMC) sleeve for aluminum alloy die-casting. The conventional die-casting shot sleeve material was STD61 tool steel. TMCs have great thermal stability, wear and oxidation resistance. The in-situ reaction between Ti and $B_4C$ leads to two kinds of thermodynamically stable reinforcements, such as TiBw and TiCp. To evaluate the feasibility of the application to a TMCs diecasting shot sleeve, the interfacial reaction behavior was examined between Al alloys melts with TMCs and STD61 tool steel. The pin-on-disk type dry sliding wear test was also investigated for TMCs and STD61 tool steel.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.8
• /
• pp.335-341
• /
• 2003

The composites were fabricated respectively 61vo1.% $\beta$ -SiC and 39vo1.% Ti $B_2$ spray-dried powders with the liquid forming additives of l2wt% $Al_2$ $O_3$＋ $Y_2$ $O_3$ by pressureless annealing at 1$700^{\circ}C$, 175$0^{\circ}C$, 180$0^{\circ}C$ for 4 hours. The result of phase analysis of composites by XRD revealed $\alpha$ -SiC(6H), Ti $B_2$, and YAG(A $l_{5}$ $Y_3$ $O_{12}$ ) crystal phase. The relative density, the Young's modulus and fracture toughness showed respectively the highest value of 92.97%, 92.88Gpa and 4.4Mpaㆍ $m^{\frac{1}{2}}$ for composites by pressureless annealing temperature 1$700^{\circ}C$ at room temperature. The electrical resistivity showed the lowest value of 8.09${\times}$10$^{-3}$ ㆍcm for composite by pressureless annealing temperature 1$700^{\circ}C$ at $25^{\circ}C$. The electrical resistivity of the SiC-Ti $B_2$ composites was all positive temperature cofficient resistance(PTCR) in the temperature ranges from $25^{\circ}C$ to $700^{\circ}C$.

• The Journal of Korean Academy of Prosthodontics
• /
• v.45 no.6
• /
• pp.743-752
• /
• 2007

Statement of problem. The aims of the study were to evaluate the effect of current surface conditioning methods on the bond strength of a resin composite luting cement bonded to ceramic surfaces and to identify the optimum cement type. Material and methods. The sixty zirconia ceramic specimens(10 per group) with EVEREST milling machine and 60 tooth block were made. The zirconia ceramic surface was divided into two groups according to surface treatment: (1) airborne abrasion with $110{\mu}m$ aluminum oxide particles; (2) Rocatec system, tribochemical silica coating. The zirconia ceramic specimens were cemented to tooth block using resin cements. The tested resin cements were Rely X ARC, Panavia F and Superbond C&B. Each specimen was mount in a jig of the universal testing machine for shear strength. The results were subjected to 2-way ANOVA and Post hoc tests was performed using Tukey, Scheffe, and Bonferroni test. Results. The mean value of shear bond strength(MPa) were as follows: $$RelyXARC(+Al_2O_3),5.35{\pm}1.69$$; $$RelyXARC(+Rocatec),8.50{\pm}2.13$$; $$PanaviaF(+Al_2O_3),9.58{\pm}1.13$$; $$PanaviaF(+Rocatec),12.98{\pm}1.71$$; $$SuperbondC&B(+Al_2O_3)8.27{\pm}2.04$$; $$SuperbondC&B(+Rocatec),14.46{\pm}2.39$$. There was a significant increase in the shear bond strength when the ceramic surface was subjected to the tribochemical treatment(Rocatec 3M) in all cement groups(P<0.05). Bonding strengths of cements applied to samples treated with $Al_2O_3$ were compared; Rely X ARC showed the lowest values, whereas Panavia F cement showed higher value than that of Superbond C&B group with no statistical significance. When the bond strength of cements with of Rocatec treatment was compared, Rely X ARC showed lowest values. Overall, it was apparent that tribochemical treated Super-Bond possessed higher mean bond strength (14.46MPa; P<0.05) than that of Panavia F cement group with no significance. Conclusions. Silica coating followed silanization(Rocatec treatment) increase the bond strength between resin cement and zirconia ceramic. Panavia F containing phosphate monomer and Superbond C&B comprised of 4-META tend to bond chemically with zirconia ceramic, thus demonstrating higher bond strength compared to BisGMA resin cement. Superbond C&B has shown to have highest value of bonding strength to zirconia ceramic after Rocatec treatment compared to other cement.