• 대한기계학회논문집
• /
• 제17권10호
• /
• pp.2498-2508
• /
• 1993

$Al/SiC/Al_{2}O_{3}$ hybrid composites are fabricated by squeeze infiltration method. From the misconstructive of $Al/SiC/Al_{2}O_{3}$ hybrid composites fabricated by squeeze infiltration method, uniform distribution of reinforcements and good bondings are found. Hardness value of $Al/SiC/Al_{2}O_{3}$ hybrid composites increases linearly with the volume fraction of reinforcement because SiC whisker and $Al_{2}$O$_{3}$ fiber have an outstanding hardness. Optimal aging conditions are obtained by examining the hardness of $Al/SiC/Al_{2}O_{3}$ hybrid composites with different aging time. Tensile properties such as Young's modulus and ultimate tensile strength are improved up to 30% and 40% by the addition of reinforcements, respectively. Failure mode of $Al/SiC/Al_{2}O_{3}$ hybrid composites is ductile on microstructural level. Through the abrasive wear test and wear surface analysis, wear behaviour and mechanism of 6061 aluminum and $Al/SiC/Al_{2}O_{3}$ hybrid composites are characterized under various testing conditions. The addition of SiC whisker to $Al/SiC/Al_{2}O_{3}$ composites gives rise to improvement of the wear resistance. The wear resistance of $Al/SiC/Al_{2}O_{3}$ hybrid composites is superior to that of Al/SiC composites. The wear mechanism of aluminum alloy is mainly abrasive wear at low speed range and adhesive and melt wear at high speed range. In contrast, that of $Al/SiC/Al_{2}O_{3}$ hybrid composites is abrasive wear at all speed range, but severe wear when counter material is stainless steel. As the testing temperature increases, wear loss of aluminum alloy decreases because the matrix is getting more ductile, but that of $Al/SiC/Al_{2}O_{3}$ hybrid composites is hardly varied. Oil lubricant is more effective to reduce the wear loss of aluminum alloy and $Al/SiC/Al_{2}O_{3}$ hybrid composites at high speed range.

• 한국세라믹학회지
• /
• 제35권12호
• /
• pp.1266-1273
• /
• 1998

Al2O3/(5~20vol%)LaAl11O18 composites in which the second phase was dispersed with a elongated grain shape were fabricated using Al2O3 and La2O3 composition by hot-pressing. In order investigate the in-fluence of LaAl11O18 on the toughening of LaAl11O18 on the toughening of Al2O3 matrix composites AE(acoustic emission) analysis was con-ducted together with an evaluation of fracture toughness using of SEPB technique. The degree of AE events occurred in composites were more than those in monolithic alumina. The occurrences of AE event increased with increasing the amount of LaAl11O18 phase in the Al2O3/LaAl11O18 composite is two times higher compared to monolithic alu-mina. The main toughening mechanism was attributed to the bridging of LaAl11O18 grains at tip of pro-pagating crack.

• 한국세라믹학회지
• /
• 제29권9호
• /
• pp.719-728
• /
• 1992

ZrO2/Al2O3-Mullite composites were prepared by infiltration of the silica sol to the porous ZrO2/Al2O3 bodies. The porous ZrO2/Al2O3 bodies for infiltration were fabricated using ZrO2 (20wt%)/Al2O3 composite powders synthesized by the emulsion-hot kerosene drying method. The preparation of silica sols was conducted by the hydrolysis-peptization of an alcoholic TEOS solution. When ZrO2/Al2O3-Mullite and ZrO2/Al2O3 composites were sintered at 1$650^{\circ}C$ for 4 hrs, both of them showed an excellent sinterability. As the amount of mullite added in the composites increased, the ratio of the tetragonal phase of zirconia to the monoclinic phase at the room temperature became higher. It was known that values of the fracture toughness of the ZrO2/Al2O3-Mullite composites were about 5.48 MPa.m1/2 much larger than that of the ZrO2/Al2O3 system.

• 한국세라믹학회지
• /
• 제26권3호
• /
• pp.423-437
• /
• 1989

Al2O3/ZrO2 composites were prepared by precipitation method using Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O as starting materials and NH4OH as a precipitation agent. Al2O3/ZrO2 composites(series A) were prepared by mixing Al2O3 powder obtained by single precipitation method with ZrO2(＋3m/o Y2O3) powder obtained by co-predipitation method. Al2O3/ZrO2 composites (series B) were prepared by co-precipitation method using the three starting materials. In all cases, the composition was controlled as Al2O3-15v/o ZrO2(＋3m/o Y2O3). The composites of series A showed higher final relative densities than those of series B and tetagonal ZrO2 in all cases was retained to about 95% at room temperature. ZrO2 particles were coalesced more rapidly in grain boundary of Al2O3 than within Al2O3 grain. ZrO2 particles were located at 3-and 4-grain junction of Al2O3 and limited the grain growth of Al2O3. It was observed that MgO contributed to densification of Al2O3 but limited grain growth of Al2O3 by MgO was not remarkable. In all Al2O3/ZrO2 composites, exaggerated grain growth of Al2O3 was not observed and Al2O3/ZrO2 composites were found to have homogeneous microstructures.

• 한국주조공학회지
• /
• 제17권4호
• /
• pp.338-346
• /
• 1997

Mechanical properties of ($10%Al_2O_3{\cdot}SiO_2+5%Ni$)/Al hybrid composites fabricated by the reaction squeeze casting were compared with those of ($15%Al_2O_3{\cdot}SiO_2$)/Ai composites. Al-Ni intermetallic compounds ($10{\sim}20 {\mu}m$) formed by the reaction between nickel powder and molten aluminum were uniformly distributed in the Al matrix. These intermetallic compounds were identified as $Al_3Ni$ using X-ray diffraction analysis and they resulted in beneficial effects on room and high temperature strength and wear resistance. Microhardness values of ($10%Al_2O_3{\cdot}SiO_2+5%Ni$)/Al hybrid composite were greater by about 100Hv than those of ($15%Al_2O_3{\cdot}SiO_2$)/Al composite. Wear resistance of ($10%Al_2O_3{\cdot}SiO_2+5%Ni$)/Al hybrid composites was superior to that of ($15%Al_2O_3{\cdot}SiO_2$)/Al composites regardless of the applied load. While tensile and yield strength of ($10%Al_2O_3{\cdot}SiO_2+5%Ni$)/Al hybrid composites were greater at room temperature and $300^{\circ}C$, strength drop at high temperature was much smaller in hybrid composites.

• 한국세라믹학회지
• /
• 제27권8호
• /
• pp.991-1003
• /
• 1990

A precipitation method, one of the most effective liquid phase reaction methods, was adopted in order to prepare high-tech Al2O3/ZrO2 composite ceramics. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent, various types of metal hydroxides were obtained by single precipitation(series A) and co-precipitation(series B) method at the pH condition between 7 and 11. Fine Al2O3-ZrO2 powders were prepared at optimum calcination condition and the effects of ZrO2 on microstructures and mechanical properties of Al2O3 were investigated. The composition of Al2O3/ZrO2 composites wax fixed as Al2O3-15 v/o ZrO2(＋3m/o Y2O3). ZrO2 limited the grain growth of Al2O3 and increased grain size homogeneity of Al2O3 more effectively than MgO.Flexural strength values in Al2O3 and Al2O3/ZrO2 composites were 340-430 MPa and 540-820 MPa, respectively, and the effect of strength improvement showed 20-50% by adding ZrO2 to Al2O3. Fracture toughness of Al2O3/ZrO2 composites was improved by stress-induced phase transformation of tetragonal ZrO2 and toughening effect by microcrack was not observed. Also, ZrO2 particles located at Al2O3 grain junction contributed to toughening, while spherical ZrO2 particles located within Al2O3 grain did not contribute to toughening. Weibull moduli of Al2O3 ceramics and Al2O3/ZrO2 composites of series A and series B were 4.34, 5.17 and 9.06, respectively. Above 0.5 of failure probability, strength values in Al2O3 ceramics and Al2O3/ZrO3 composites of series A and series B were above 400 MPa, 700 MPa and 650 MPa, respectively.

• 한국전기전자재료학회논문지
• /
• 제30권1호
• /
• pp.7-12
• /
• 2017

3YSZ + (x) $Al_2O_3$ composites (x = 20, 40, 60, 80 wt%) were fabricated and the influences of particle sizes of $Al_2O_3$ on their microstructures and mechanical properties were investigated with XRD, SEM, vickers hardness and fracture toughness. $Al_2O_3$-3YSZ composites containing $Al_2O_3$ powder of a $0.3{\mu}m$ and an $1.0{\mu}m$, which are here in after named as $Al_2O_3$($0.3{\mu}m$)-3YSZ and $Al_2O_3$($1.0{\mu}m$)-3YSZ, respectively, were made by mixing raw materials, uni-axial pressing and sintering at $1,400^{\circ}C$, $1,500^{\circ}C$, and $1,600^{\circ}C$. $Al_2O_3$($0.3{\mu}m$)-3YSZ composites show the higher density and the better mechanical properties than $Al_2O_3$($1.0{\mu}m$)-3YSZ composites. The Vickers hardness of the $Al_2O_3$($0.3{\mu}m$)-3YSZ composites show a peak value of 1,997 Hv at the content of 60 wt% $Al_2O_3$, which is a slightly higher value in comparison with 1,938 Hv of the $Al_2O_3$($1.0{\mu}m$)-3YSZ composite. However, the fracture toughness of $Al_2O_3$-3YSZ composites monotonically increases with decreasing the content of $Al_2O_3$ without any peak values. $Al_2O_3$($0.3{\mu}m$)-3YSZ and $Al_2O_3$($1.0{\mu}m$)-3YSZ composites sintered at $1,600^{\circ}C$ have a maximum value of a $6.9MPa{\cdot}m^{1/2}$ and a $6.2MPa{\cdot}m^{1/2}$, respectively at the composition of containing 20 wt% $Al_2O_3$. It should be noticed that the mechanical properties and the sintering density of the $Al_2O_3$-3YSZ composites can be enhanced by using more fine $Al_2O_3$ powder due to their denser microstructure and smaller grain size.

• 한국세라믹학회지
• /
• 제35권9호
• /
• pp.923-932
• /
• 1998

Al2O3/Al composites were produced by displacement reaction method which was carried out by imm-ersing the sintered silica preform which was prepared form fused silica powder in molten aluminu. an ac-tivation energy of 94kJ/mole was calculated from Al-SiO2 reaction data in 1000-130$0^{\circ}C$ temperature range With increase of reaction temperature the alumina particle in the Al2O3/Al composites produced with pur metal Al showed grain growth and the growth of alumina particle in Al2O3/Al composite produced by using of Mg contained Al alloy was inhibited. The flexural strength of Al2O3/Al composites produced at 100$0^{\circ}C$ showed the highest value as 393 MPa. Flexural strength of the composite fabricated at 85$0^{\circ}C$ showed higher deviation than that of the composite produced at above 100$0^{\circ}C$ Low flexural strength of the composite fa-bricated at 120$0^{\circ}C$ due to the growth of pore and alumina particle size. The hardness of composites de-pended on alumina content in Al2O3/Al composite decreased with increasing of aluminium content in case the same alumina content and increased with increasing of silicon content in composite.

• 대한기계학회논문집
• /
• 제19권4호
• /
• pp.968-980
• /
• 1995

Al/Al$_{2}$O$_{3}$/C hybrid metal matrix composites are fabricated by the direct squeeze infiltration method. From the microstructure of Al/Al$_{2}$O$_{3}$/C composites, uniform distribution of reinforcements and good bondings are found. Optimum processing conditions for preforms and squeeze castings are suggested. Mechanical properties, such as elastic modulus, elongation, 0.2% offset yield strength and ultimate tensile strength are obtained. Through the abrasive were test and wear surface analsis, wear behavior and its mechanism of AC2B aluminum and Al/Al$_{2}$O$_{3}$/C composites can be characterized under various sliding speed conditions. Tensile strenght elongation of Al/Al$_{2}$O$_{3}$/C composites are decreased with increasing the addition of carbon fiber. On the contrary, elastic modulus of Al/Al$_{2}$O$_{3}$/C composites is slightly improved compared with that of the unreinforced matrix alloy. The addition of carbon fiber to al/al$_{2}$O$_{3}$/C composites gives rise to improvement of the wear resistance. Specially, carbon chopped fibers play an important role in interfering sticking between the counter material and metal matirix composites. Al/Al$_{2}$O$_{3}$/C composites are suitable to high speed due to solid lubication of carbon. And wear model of Al/Al$_{2}$O$_{3}$/C composites is suggested by the examination of worn surfaces.

• 한국복합재료학회:학술대회논문집
• /
• 한국복합재료학회 2000년도 춘계학술발표대회 논문집
• /
• pp.67-70
• /
• 2000

Mechanical properties of (10%$AI_20_3{\cdot}SiO_2$+5%Ni)/Al hybrid composites fabricated by the reaction squeeze casting were compared with those of (15%$AI_20_3{\cdot}SiO_2$)/Al composites. Intermetallic compound formed by reaction between molten aluminum and reinforcing powder was uniformly distributed in the Al matrix. These intermetallic compounds were identified as $Al_3$NI using EDS and X-ray diffraction analysis. Microhardness and flexural strength of hybrid composites were higher than that of (15%$AI_20_3{\cdot}SiO_2$)/Al Composite. In-Situ fracture tests were Conducted on (15%$AI_20_3{\cdot}SiO_2$)/Al Composites and (10%$AI_20_3{\cdot}SiO_2$+5%Ni)/Al hybrid composites to identify the microfracture process. It was identified from the in-situ fracture test of (10%$AI_20_3{\cdot}SiO_2$+5%Ni)/Al composites, microcracks were initiated mainly at the short fiber / matrix interfaces. As the loading was continued, the crack propagated mainly along the separated interfacial regions and the well developed shear bands. It was identified from the in-situ fracture test of (10%$AI_20_3{\cdot}SiO_2$+5%Ni)/Al hybrid composites, microcracks were initiated mainly by the short fiber/matrix interfacial debonding. The crack proceeded mainly through the intermetallic compound clusters