• Korean Journal of Materials Research
• /
• v.18 no.1
• /
• pp.22-25
• /
• 2008

In this study, calcium titanate $(CaTiO_3)$ gel was prepared by mixing calcium nitrate and titanium isopropoxide in 2-methoxy-ethanol. $CaTiO_3$ gel was single-layer coated on Ti-6Al-4V using a sol-gel dip-coating technique. The coating was calcined at $750^{\circ}C$ in air by utilizing a very slow heating rate of $2^{\circ}C/min$. The crystalline phases of the coating were characterized by x-ray diffraction using a slow scan rate of $1^{\circ}/min$. The morphology of the coating was analyzed by scanning electron microscopy. The corrosion behavior of Ti-6Al-4V samples coated with $CaTiO_3$ films were tested in an artificial saliva solution by potentiodynamic polarization and were quantified by the Tafel extrapolation method. The electrochemical parameters showed a considerable increase in the corrosion resistance for the $CaTiO_3$-coated Ti-6Al-4V samples compared to bare substrates.

• Journal of the Korean Ceramic Society
• /
• v.45 no.11
• /
• pp.688-693
• /
• 2008

This paper presents a study on the photocatalytic reaction about the composite particles of $TiO_2$-coated phosphors under visible light irradiation. Nanocrystalline titanium dioxide layers were directly coated on the alkaline earth aluminate phosphor, $CaAl_2O_4:Eu^{2+},\;Nd^{3+}$ particles by an sol-gel processing method. The photocatalytic reaction was analyzed with the degradation of methylene blue (MB) aqueous solution under UV and visible light irradiations. $TiO_2$-coated phosphor powders showed different photocatalytic mechanism, compared with pure $TiO_2$ (P-25, Degussa). Under UV-irradiation, $TiO_2$-coated phosphor powders showed slow photocatalytic reactivity in the early stage and fast in the latter, compared with that of pure $TiO_2$. However, $TiO_2$-coated phosphor powders showed much faster photocatalytic reactivity than that of pure $TiO_2$ under visible irradiation. In addition, the characterizations of the $TiO_2$-coated phosphor powders were conducted by a X-ray diffractometer (XRD), transmission electron microscope (TEM), and energy dispersive spectroscopy (EDS).

• The korean journal of orthodontics
• /
• v.51 no.4
• /
• pp.270-281
• /
• 2021

Objective: The aim of this in vitro study was to evaluate the changes in friction between orthodontic brackets and archwires coated with aluminum oxide (Al₂O₃), titanium nitride (TiN), or chromium nitride (CrN). In addition, the resistance of the coatings to intraoral conditions was evaluated. Methods: Stainless steel canine brackets, 0.016-inch round nickel-titanium archwires, and 0.019 × 0.025-inch stainless steel archwires were coated with Al₂O₃, TiN, and CrN using radio frequency magnetron sputtering. The coated materials were examined using scanning electron microscopy, an X-ray diffractometer, atomic force microscopy, and surface profilometry. In addition, the samples were subjected to thermal cycling and in vitro brushing tests, and the effects of the simulated intraoral conditions on the coating structure were evaluated. Results: Coating of the metal bracket as well as nickel-titanium archwire with Al₂O₃ reduced the coefficients of friction (CoFs) for the bracket-archwire combination (p < 0.01). When the bracket and stainless steel archwire were coated with Al₂O₃ and TiN, the CoFs were significantly lower (0.207 and 0.372, respectively) than that recorded when this bracket-archwire combination was left uncoated (0.552; p < 0.01). The friction, thermal, and brushing tests did not deteriorate the overall quality of the Al₂O₃ coatings; however, some small areas of peeling were evident for the TiN coatings, whereas comparatively larger areas of peeling were observed for the CrN coatings. Conclusions: Our findings suggest that the CoFs for metal bracket-archwire combinations used in orthodontic treatment can be decreased by coating with Al₂O₃ and TiN thin films.

• Tribology and Lubricants
• /
• v.22 no.5
• /
• pp.282-289
• /
• 2006

This paper is to investigate the wear behaviors of two type ceramics, $Al_{2}O_{3}\;and\;TiO_{2}$, by coated plasma thermal spray method under the lubricative environment. The lubricative environments are grease fluids, a general hydraulic fluids, and bearing fluids. The wear testing machine used a pin on disk type. Wear characteristics, which were friction force, friction coefficient and the specific wear rate, according to the lubricative environments were obtained at the four kinds of load and sliding velocity is 0.2 m/sec. After the wear experiments, the wear surfaces of the each test specimen were observed by a scanning electronic microscope.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.259-270
• /
• 1997

Reaction kinetics for the solid-state reaction of $\alpha-Al_2O_3$ with amorphous $TiO_2$ to produce $Al_2TiO_5$ (Tialite) was studied in the temperature range of $1200~1300^{\circ}C$. Rate of kinetic reaction were determined by using $TiO_2$-coated $Al_2O_3$ compact containing 50 mol% $TiO_2$ and heating the reactant mixtures in MgO at definite temperature for various times. Amount of products and unreacted reactants were determined by X-ray diffractometry. Data from the volume fraction and ratio of peak intensities of $\beta-Al_2TiO_5$ indicated that the reaction of $\alpha-Al_2O_3$ with $TiO_2$ to form pseudobrookite starts between 1280 and $1300^{\circ}C$. The activation energy for solid-state reaction was determined by using the Arrhenius equation ; The activation energy was 622.4 kJ/mol.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.2
• /
• pp.411-414
• /
• 2013

In order to enhance the photovoltaic property of the CdS/CdSe co-sensitized quantum dot sensitized solar cells (QDSSCs), the surface of nanoporous $TiO_2$ photoanode was modified by ultrathin $Al_2O_3$ layer before the deposition of quantum dots (QDs). The $Al_2O_3$ layer, dip-coated by 0.10 M Al precursor solution, exhibited the optimized performance in blocking the back-reaction of the photo-injected electrons from $TiO_2$ conduction band (CB) to polysulfide electrolyte. Transient photocurrent spectra revealed that the electron lifetime (${\tau}_e$) increased significantly by introducing the ultrathin $Al_2O_3$ layer on $TiO_2$ surface, whereas the electron diffusion coefficient ($D_e$) was not varied. As a result, the $V_{oc}$ increased from 0.487 to 0.545 V, without appreciable change in short circuit current ($J_{sc}$), thus inducing the enhancement of photovoltaic conversion efficiency (${\eta}$) from 3.01% to 3.38%.

• Korean Chemical Engineering Research
• /
• v.57 no.1
• /
• pp.111-117
• /
• 2019

This study proposed the fabrication and deposition of high purity crystalline $core-TiO_2/shell-Al_2O_3$ nanoparticles. Morphological properties of $core-TiO_2$ and coated $shell-Al_2O_3$ were confirmed by transmission electron microscope (TEM) and transmission electron microscope - energy dispersive spectroscopy (TEM-EDS). The electrical properties of the prepared $core-TiO_2/shell-Al_2O_3$ nanoparticles were evaluated by applying them to a working electrode of a Dye-Sensitized Solar Cell (DSSC). The particle size, growth rate and the main crystal structure of $core-TiO_2$ were analyzed through dynamic light scattering system (DLS), scanning electron microscope (SEM) and X-ray diffraction (XRD). The $core-TiO_2$, which has a particle size of 17.1 nm, a thin film thickness of $20.1{\mu}m$ and a main crystal structure of anatase, shows higher electrical efficiency than the conventional paste-based dye-sensitized solar cell (DSSC). In addition, the energy conversion efficiency (6.28%) of the dye-sensitized solar cell (DSSC) using the $core-TiO_2/shell-Al_2O_3$ nanoparticles selectively controlled to the working electrode is 26.1% higher than the energy conversion efficiency (4.99%) of the dye-sensitized solar cell (DSSC) using the conventional paste method.

• Korean Journal of Materials Research
• /
• v.15 no.3
• /
• pp.155-160
• /
• 2005

The electrolytic reduction of spent oxide fuel involves the liberation of oxygen in a molten LiCl electrolyte, which results in a chemically aggressive environment that is very corrosive fir typical structural materials. So, it is essential to choose the optimum material f3r the process equipment handling molten salt. In this study, the corrosion behavior of Al-Y coated Haynes 263 in a molten salt of $LiCl-Li_2O$ under oxidation atmosphere was investigated at $650^{\circ}C$ for $72\~168$ hours. The corrosion rate of Al-Y coated Haynes 263 was low while that of bare Haynes 263 was high in a molten salt of $LiCl-Li_2O$. Al-Y coated Haynes 263 improved the corrosion resistance better than bare Haynes 263 alloy. An Al oxide layer acts as a protective film which Prohibits Penetration of oxygen. Corrosion Products were formed $Li(Ni,Co)O_2$ and $LiTiO_2$ on bare Haynes 263, but $LiAlO_2,\;Li_5Fe_5O_8\;and\;LiTiO_2$ on Al-Y coated Haynes 263.

• Journal of the Korean institute of surface engineering
• /
• v.33 no.1
• /
• pp.17-24
• /
• 2000

The microstructures and corrosion properties of Al-Si diffusion coated PWA1426 and PWA658 alloys have been investigated. The coated layer and corrosion properties were analysed by SEM, EDS and hot corrosion test. According to the results of SEM, it is supposed that the coated layers were composed of mixed, denuded and inter-diffusion layer. The coated PWA1426 alloy improved corrosion properties, compared to the PWA658 alloy. Corrosion debris generated during hot corrosion test of PWA658 alloy are identified as NiO, $TiO_2$and $NiAl_2$$O_4$from coated layer which increase oxidation rate and decrease adhesion. The PWA1426 alloy heat treated at $1080^{\circ}C$ showed that NiAl and $Al_2$$O_3$formed on coated layer.

• Applied Chemistry for Engineering
• /
• v.3 no.1
• /
• pp.88-99
• /
• 1992

For the development of semiconducting photoelectrode to be more stable and efficient in the process of photoelectrolysis of the water, pure titanium rods were oxidized by anodic oxidation, furance oxidation and flame oxidation and used as electrodes. The Indium islands were formed by electrodeposition of "In" thin film on $TiO_2$ and Ti by electrodeposition. Also $A1_2O_3$ and NiO islands were coated on Ti by the electron-beam evaporation technique. The maximum photoelectrochemical conversion efficiency(${\eta}$) was 0.98% for flame oxidized electrode($1200^{\circ}C$ for 2min in air). Anodically oxidized electrodes have photoelectrochemical conversion efficiency of 0.14%. Furnace oxidized electrode($800^{\circ}C$ for 10min in air) has 0.57% of photoelectrochemical efficiency and shows a band-gap energy of about 2.9eV. The $In_2O_3$ coated $TiO_2$ exhibits 0.8% of photoelectrochemical efficiency but much higher value of ${\eta}$ was obtained with the Increase of applied blas voltage. However, $Al_2O_3$ or NiO coated $TiO_2$ shows much low value of ${\eta}$. The efficiency was dependent on the presence of the metallic interstitial compound $TiO_{0+x}$(x<0.33) at the metal-semiconductor interface and the thickness of the suboxide layer and the external rutile scale.