• 한국정보디스플레이학회:학술대회논문집
• /
• 한국정보디스플레이학회 2000년도 제1회 학술대회 논문집
• /
• pp.37-38
• /
• 2000

The ZnS:Tb thin-film electroluminescent devices were grown by atomic layer deposition with utilizing single-layer aluminum oxide and/or multilayered tantalum aluminum oxide, $Ta_xAl_yO$, as upper and lower insulating layers. These devices were investigated in terms of the luminescent and electrical characteristics. From this analysis, the devices using the $Ta_xAl_yO$ instead of $Al_2O_3$ were observed to have a lower threshold voltage for emission due to the higher relative dielectric constant of $Ta_xAl_yO$ insulators than that of the $Al_2O_3$ device. And there was a large amount of dynamic space charge generation in the phosphor of the device with the $Ta_xAl_yO$ insulators seemingly due to electron multiplication such as trap ionization.

• 한국표면공학회지
• /
• 제54권1호
• /
• pp.25-29
• /
• 2021

The fabrication of nanopore membrane by deposition of Al2O3 film using electron-beam evaporation, which is fast, cost-effective, and negligible dependency on substance material, is investigated for potential applications in water purification and sensors. The decreased nanopore diameter owing to increased wall thickness is observed when Al2O3 film is deposited on anodic aluminum oxide membrane at higher deposition rate, although the evaporation process is generally known to induce a directional film deposition leading to the negligible change of pore diameter and wall thickness. This behavior can be attributed to the collision of evaporated Al2O3 particles by the decreased mean free path at higher deposition rate condition, resulting in the accumulation of Al2O3 materials on both the surface and the edge of the wall. The reduction of nanopore diameter by Al2O3 film deposition can be applied to the nanopore membrane fabrication with sub-100 nm pore diameter.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2004년도 하계학술대회 논문집 Vol.5 No.2
• /
• pp.1278-1282
• /
• 2004

수열처리법으로 nano-sized $CeO_2$ 입자를 $Al_3O_3$ 입자의 표면에 균일하게 코팅하여 $AL_2O_3/O_2$ composite 연마 입자를 제조하었다. 제조된 $Al_2O_3\CeO_2$ composite 입자의 뭍성을 TEM, XRD, zeta potential analyzer 및 particle size analyzer로 측징하였다. $Al_2O_3/CeO_2$ composite 입자와 구성된 슬러리와 비교 시료로서 $Al_2O_3$와 $CeO_2$ 입자를 혼합한 슬러리를 사용하여 thermal oxide film에 대한 연마특성을 평가하였다. 연마슬러리에 포함된 $A1_2O_3/CeO_2$ composite 입자와 $Al_2O_3$와 $CeO_2$ 혼합입자에서 나노 크기의 세리아 입자가 sub-micron 크기의 알루미나 입자의 표면에 균일하게 코팅되므로서 $Al_2O_3$ 단일 성분의 슬러리에 비해 removal rate(RR)는 106 nm/min, WIWNU는 $8\sim9%$, roughness는 $2.6{\AA}$의 향상된 연마 특성을 나타내었다. 알루미나 입자의 불규칙한 형상 때문에 $Al_2O3/CeO_2$ composite 슬러리와 $Al_2O_3$ 와 $CeO_2$ 혼합슬러리의 연마 특성이 비슷한 수준을 나타내었다.

• 센서학회지
• /
• 제9권5호
• /
• pp.389-395
• /
• 2000

본 논문에서는 보호용 실리콘 산화층과 Al 층을 이용한 $Al_2O_3$ 예비층의 형성을 제안하였다. 실리콘 기판 위의 보호용 산화막 위에 알루미늄을 증착하고 이를 $800^{\circ}C$에서 열처리함으로써 에피텍시 $Al_2O_3$ 예비층 형성시킬 수 있었다. 그리고 형성된 $Al_2O_3$ 예비층위에 ${\gamma}-Al_2O_3$ 층을 형성하였다. ${\gamma}-Al_2O_3$막 성장시 공정의 초기 상태에서 발생하는 $N_2O$ 가스에 의한 Si 기판의 식각을 $Al_2O_3$ 예비층을 이용함으로써 방지할 수 있었다. $Al_2O_3$ 예비층이 초박막 ${\gamma}-Al_2O_3$의 표면의 형태를 개선하는데 많은 효과가 있었다.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2009년도 제40회 하계학술대회
• /
• pp.1096_1097
• /
• 2009

Aluminium doped zinc oxide(ZnO:Al) thin film, which is mainly used as a transparent conducting electrode in electronic devices, has many advantages compared with conventional indium tin oxide(ITO). In this paper in order to investigate the possible application of ZnO:Al thin films as a transparent conducting electrode for flexible film-typed dye sensitized solar cell (FT-DSCs), ZnO:Al and ITO thin films were prepared on the polyethylene terephthalate (PET) substrate by r. f. magnetron sputtering method. Specially one-inched FT-DSCs using either a ZnO:Al or ITO electrode were also fabricated separately under the same manufacturing conditions. Some properties of both the FT-DSCs with ZnO:Al and ITO transparent electrodes, such as conversion efficiency, fill factor, and photocurrent were measured and compared with each other. The results showed that by doping the ZnO target with 2 wt% of $Al_2O_3$, the film deposited at discharge power of 200W resulted in the minimum resistivity of $2.2\times10^{-3}\Omega/cm$ and at ransmittance of 91.7%, which are comparable with those of commercially available ITO. Two types of FT-DSCs showed nearly the same tendency of I-V characteristics and the same value of conversion efficiencies. Efficiency of FT-DSCs using ZnO:Al electrode was around 2.6% and that of fabricated FT-DSCs using ITO was 2.5%. This means that ZnO:Al thin film can be used in FT-DSCs as a transparent conducting layer.

• Current Photovoltaic Research
• /
• 제5권4호
• /
• pp.135-139
• /
• 2017

We fabricated two different transparent conducting oxide thin films of ZnO doped with Ga ($Ga_2O_3$ 0.9 wt%) as well as Al ($Al_2O_3$ 2.1 wt%) (GAZO) and ZnO doped only with Al ($Al_2O_3$ 3 wt%) (AZO). It was investigated how it affects the moisture resistance of the transparent electrode. In addition, $Cu(In,Ga)Se_2$ thin film solar cells with two transparent oxides as front electrodes were fabricated, and the correlation between humidity resistance of transparent electrodes and device performance of solar cells was examined. When both transparent electrodes were exposed to high temperature distilled water, they showed a rapid increase in sheet resistance and a decrease in the fill factor of the solar cell. However, AZO showed a drastic decrease in efficiency at the beginning of exposure, while GAZO showed that the deterioration of efficiency occurred over a long period of time and that the long term moisture resistance of GAZO was better.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2016년도 추계학술대회 논문집
• /
• pp.107-107
• /
• 2016

TiCrAlSiN films were developed in order to improve the high-temperature oxidation resistance, corrosion resistance, and mechanical properties of conventional TiN films that are widely used as hard films to protect and increase the lifetime and performance of cutting tools or die molds. In this study, a nano-multilayered TiAlCrSiN film was deposited by cathodic arc plasma deposition. It displayed relatively good oxidation resistance at $700-900^{\circ}C$, owing to the formation protective oxides of $Al_2O_3$, $Cr_2O_3$, and $SiO_2$, and semiprotective $TiO_2$. At $1000^{\circ}C$, the increased temperature led to the formation of the imperfect oxide scale that consisted primarily of the outer ($TiO_2$,$Al_2O_3$)-mixed scale and inner ($TiO_2$, $Al_2O_3$, $Cr_2O_3$)-mixed scale.

• JSTS:Journal of Semiconductor Technology and Science
• /
• 제14권1호
• /
• pp.40-47
• /
• 2014

In this paper, $Al_2O_3$ film deposited by thermal atomic layer deposition (ALD) with diluted $NH_4OH$ instead of $H_2O$ was suggested for passivation layer and anti-reflection (AR) coating of the p-type crystalline Si (c-Si) solar cell application. It was confirmed that the deposition rate and refractive index of $Al_2O_3$ film was proportional to the $NH_4OH$ concentration. $Al_2O_3$ film deposited with 5 % $NH_4OH$ has the greatest negative fixed oxide charge density ($Q_f$), which can be explained by aluminum vacancies ($V_{Al}$) or oxygen interstitials ($O_i$) under O-rich condition. $Al_2O_3$ film deposited with $NH_4OH$ 5 % condition also shows lower interface trap density ($D_{it}$) distribution than those of other conditions. At $NH_4OH$ 5 % condition, moreover, $Al_2O_3$ film shows the highest excess carrier lifetime (${\tau}_{PCD}$) and the lowest surface recombination velocity ($S_{eff}$), which are linked with its passivation properties. The proposed $Al_2O_3$ film deposited with diluted $NH_4OH$ is very promising for passivation layer and AR coating of the p-type c-Si solar cell.

• 한국표면공학회지
• /
• 제52권5호
• /
• pp.246-250
• /
• 2019

Nano-multilayered $Cr_{25.2}Al_{19.5}Si_{4.7}N_{50.5}$ films were deposited on the steel substrate by cathodic arc plasma deposition. They were corroded at $900^{\circ}C$ in $Ar/1%SO_2$ gas in order to study their corrosion behavior in sulfidizing/oxidizing environments. Despite the presence of sulfur in the gaseous environment, the corrosion was governed by oxidation, leading to formation of protective oxides such as $Cr_2O_3$ and ${\alpha}-Al_2O_3$, where Si was dissolved. Iron diffused outward from the substrate to the film surface, and oxidized to $Fe_2O_3$ and $Fe_3O_4$. The films were corrosion-resistant up to 150 h owing to the formation of thin ($Cr_2O_3$ and/or ${\alpha}-Al_2O_3$)-rich oxide layers. However, they failed when corroded at $900^{\circ}C$ for 300 h, resulting in the formation of layered oxide scales due to not only outward diffusion of Cr, Al, Si, Fe and N, but also inward movement of sulfur and oxygen.

• 대한화학회지
• /
• 제53권4호
• /
• pp.466-470
• /
• 2009