• Journal of the Korean Ceramic Society
• /
• v.44 no.6 s.301
• /
• pp.291-296
• /
• 2007

Porous $Al_2O_3-(m-ZrO_2)$ composites were fabricated by pressureless sintering, using different volume percentages (40% - 60%) of poly methyl methacrylate (PMMA) powders as a pore-forming agent. The pore-forming agent was successfully removed, and the pore size and shape were well-controlled during the burn-out and sintering processes. The average pore size in the porous $Al_2O_3-(m-ZrO_2)$ bodies was about $200\;{\mu}m$ in diameter. The values of relative density, bending strength, hardness, and elastic modulus decreased as the PMMA content increased; i.e., in the porous body (sintered at $1500^{\circ}C$) using 55 vol % PMMA, their values were about 50.8%, 29.8 MPa, 266.4 Hv, and 6.4 GPa, respectively. To make the $Al_2O_3-(m-ZrO_2)$/polymer hybrid composites, a bioactive polymer, such as PMMA, was infiltrated into the porous $Al_2O_3-(m-ZrO_2)$ composites. After infiltration, most of the pores in the porous $Al_2O_3-(m-ZrO_2)$ composites, which were made using 60 vol % PMMA additions, were infiltrated with PMMA, and their values of relative density, bending strength, hardness, and elastic modulus remarkably increased.

• Journal of the Korean Ceramic Society
• /
• v.38 no.10
• /
• pp.936-941
• /
• 2001

The influence of the ${Al_2}{O_3}$ particle size on flaw tolerance of the $ZrO_2/{Al_2}{O_3}$ composites prepared by mixing 5.31 mol% ${Y_2}{O_3}$-4.45 mol% ${Nb_2}{O_5}$-90.31 mol% $ZrO_2$ and ${Al_2}{O_3}$ was investigated. The composites exhibited rising R-curve behavior and plateau fracture toughness of 7.9 and $8.8MPam^{1/2}$ for the additions of 20 vol% of 0.2 and $2.8{\mu}m$ ${Al_2}{O_3}$ particles, respectively. The difference in the fracture toughness resistance was attributed mainly to the grain size of tetragonal $ZrO_2$ phase in the composites, which scaled with the ${Al_2}{O_3}$ particle size.

• Journal of the Korean Ceramic Society
• /
• v.37 no.4
• /
• pp.359-367
• /
• 2000

Particulate composites of Al2O3/SiC, Al2O3/ZrO2 and Al2O3/ZrO2/SiC have been fabricated to investigate their R-curve behaviors and toughening mechanisms. Al2O3 containing 30 vol% SiC particles of 3${\mu}{\textrm}{m}$ showed rising R-curve behavior owing to the strong crack bridging by SiC particles. The fracture toughness reached 9.1 MPa {{{{ SQRT {m} }} at the crack length of 1000${\mu}{\textrm}{m}$. On the other hand, ZrO2-toughened Al2O3 had a high flat R-curve since it rose steeply in the short crack region due to the well known transformation toughening. For Al2O3/ZrO2/SiC composites, the R-curve behavior was similar to that of Al2O3/SiC but with slightly higher toughness. The SiC particles in this composite decreased the amount of transformable tetragonal phase to reduce the effect of transformation toughening by 50%. It was also found that the fracture toughness of this composite with two different toughening mechanisms was markedly lower than that estimated by the simple addition of two contributions.

• Korean Journal of Materials Research
• /
• v.2 no.3
• /
• pp.172-179
• /
• 1992

$Al_2O_3/ZrO_2$ composites were fabricated by pressureless sintering from commercial powders and/or nano composite powder of $Al_2O_3/ZrO_2$. The Properties of the composites such as density, strength, hardness and fracture toughness were evaluated. Microstructures and fracture surfaces ware also examined. The flexural strength remains unchanged(~640 MPa) as long as the content of commercial powders is not extreamly high, and depends on microstructures of the composites. Fracture toughness(4.3-5.3 $Mpa{\cdot}m^{1/2}$) increases with increasing content of commercial powders. Fractography shows that failure-initiating sources are 1)surface flaws resulting from machining damage, 2)crack-shaped voids formed due to $ZrO_2$ agglomeration, and 3)surface separation caused by inhomogeneous blending and by sinterability difference between nato composite powder and commercial powders of $Al_2O_3/ZrO_2$. Failure mode of the composites was mainly transgranular.

• Proceedings of the KIEE Conference
• /
• 1998.11c
• /
• pp.853-855
• /
• 1998

The electrical resistivity and mechanical properties of the hot-pressed and annealed ${\beta}$-SiC+39vol.%$ZrB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of $Al_{2}O_{3}+Y_{2}O_{3}$(6:4wt%). In this microstructures. no reactions were observed between $\beta$-SiC and $ZrB_2$, and the relative density is over 97.6% of the theoretical density. Phase analysis of composites by XRD revealed mostly of a $\alpha$-SiC(6H, 4H), $ZrB_2$ and weakly $\beta$-SiC(15R) phase. The fracture toughness decreased with increased $Al_{2}O_{3}+Y_{2}O_{3}$ contents and showed the highest for composite added with 4wt% $Al_{2}O_{3}+Y_{2}O_{3}$ additives. The electrical resistivity increased with increased $Al_{2}O_{3}+Y_{2}O_{3}$ contents because of the increasing tendency of pore formation according to amount of liquid forming additives $Al_{2}O_{3}+Y_{2}O_{3}$. The electrical resistivity of composites is all positive temperature coefficient resistance(PTCR) against temperature up to $700^{\circ}C$.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.49 no.9
• /
• pp.516-522
• /
• 2000

The mechanical and electrical properties of the hot-pressed and annealed $\beta-SiC-ZrB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of$Al_2O_3+Y_2O_3$ Phase analysis of composites by XRD revealed $\alpha-SiC(6H) ZrB_2\; and YAG(Al_5Y_3O_{12})$ The relative density of composites were increased with increased Al2O3+Y2O3 contents. The Flexural strength showed the highest value of 390.6MPa for composites added with 20wt% Al2O3+Y2O3 additives at room temperature. Owing to crack deflection crack bridging phase transition and YAG of fracture toughness mechanism the fracture toughness showed the highest value of 6.3MPa.m1/2 for composites added with 24wt% Al2O3+Y2O3 additives at room temperature. The resistance temperature coefficient showed the value of$ 2.46\times10^{-3}\;, 2.47\times10^{-3},\; 2.52\times10^{-3}/^{\circ}C$ for composite added with 16, 20, 24wt% Al2O3+Y2O3 additives respectively. The electrical resistivity of the composites was all positive temperature coefficient resistance(PTCR) in the temperature range of $256{\circ}C\; to\; 900^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.25 no.3
• /
• pp.225-230
• /
• 1988

The strength and thermal shock resistance of $Al_2O_3-ZrO_2$ composites have been studied. The tetragonal $ZrO_2$ powder containing 1 mol.% $Y_2O_3$ and monoclinic $ZrO_2$ powder were prepared by coprecipitation method and subsequently mixed with $Al_2O_3$ powder and granulated by sieving. Duplex composites were prepared by dry mixing matrix agglomerate with 15 to 30 vol.% of dispersion agglomerate, followed by pressing and sintering at 1$600^{\circ}C$ for1 hr. These $Al_2O_3-ZrO_2$ 2 composites having heterogeneous structure showed improved thermal shock behaviors because of the microcracking and pores in dispersed granules, and compressive stresses around dispersed granules resulting from $ZrO_2$ transformation.

• Journal of the Korean Ceramic Society
• /
• v.22 no.5
• /
• pp.76-84
• /
• 1985

Mechanical property enhancing mechanisms of $Al_2O_3-ZrO_2$ two phase ceramic composites were studied for several compositions of different $ZrO_2$/$Al_2O_3$ ratio. Microstructural analysis of $Al_2O_3-ZrO_3$(pure) composites indicated that pre-existing microcrack due to larger $ZrO_2$ particle at grain boundary extended along alumina grain boundaries within process zone. Microcracks also nucleated when very small $ZrO_2$ particles at the grain boundaries transformed to monoclinic phase at near of main crack tip. These types of microcracks could contribute to the toughening achieved by creating additional crack surface area during crack propagation. Microstructural analyses also showed that the average grain size and abnormal grain size of $Al_2O_3$ were decreased with increasing $ZrO_2$ vol% in $Al_2O_3$ matrix. As a result it could be concluded as follows In TEX>$Al_2O_3-ZrO_3$(pure) system 1. Microcrack nucleation (stress-induced microcracking) and extension was effective mechanism for absorpiton of fracture energy 2, More narrow distribution and smaller grain size of $Al_2O_3$ due to $ZrO_2$particles mainly contributed to main-tatin the strength and hardness.

• Journal of the Korean Ceramic Society
• /
• v.37 no.11
• /
• pp.1058-1064
• /
• 2000

연속슬립캐스팅 및 상압소결법으로 $Al_2$O$_3$/ZrO$_2$적층복합체를 제조하였으며, 적층복합체에서 ZrO$_2$층을 단사정, 정방정 및 입방정으로 각각 달리 적층하여 균열생성 및 전파 거동에 미치는 ZrO$_2$상의 영향을 고찰하였다. 균열 생성은 냉각시 $Al_2$O$_3$층과 ZrO$_2$층 간의 열팽창 계수의 차이에 의한 열적불일치응력이 가장 큰 요인으로 작용하였다. 적층체 내에 존재하는 균열은 tetra-ZrO$_2$의 경우 적층두께 조절로 가능하였으며, cubic-ZrO$_2$의 경우는 냉각속도 조절로 균열밀도로 크게 낮출 수 있었다. $Al_2$O$_3$/ZrO$_2$적층체를 구성하는 세가지 ZrO$_2$상(mono, tetra, cubic)들 중에서 cubic-ZrO$_2$가 포함된 적층체의 경우 $Al_2$O$_3$와 ZrO$_2$계면에 형성된 잔류압축응력으로 인한 균열굴절 효과를 얻을 수 있었다.

• Journal of the Korean Ceramic Society
• /
• v.41 no.4
• /
• pp.284-288
• /
• 2004

To improve mechanical properties of $Al_2$O$_3$/ZrO$_2$composites have been controlled dispersion of ultra low size ZrO$_2$ particles in $Al_2$O$_3$ ceramics by polymeric precursor method (Pechini process). In case of coprecipitation or mechanical mixing of ZrO$_2$ powders with $Al_2$O$_3$, homogeneous dispersion and controlling the ZrO$_2$ size were relatively difficult due to high sintering temperature. So the polyesterization process of Zr/Y(NO$_3$)$_3$-citric acid solution in ethylene glycol with the commercial sub-micron sized o(-alumina powder (Sumitomo AES-11(0.4 ${\mu}{\textrm}{m}$)) was adopted in order to obtain homogeneous dispersion of ZrO$_2$ in A1203. By this partial polyesterization process, the homogeneous dispersion of relatively low sized ZrO$_2$in $Al_2$O$_3$/ZrO$_2$composites was achieved at 1450∼1$600^{\circ}C$ of sintering temperature range and their mechanical properties were measured.