• 대한전기학회논문지:전기물성ㆍ응용부문C
• /
• 제49권9호
• /
• pp.516-522
• /
• 2000

The mechanical and electrical properties of the hot-pressed and annealed $\beta-SiC-ZrB_2$ electroconductive ceramic composites were investigated as a function of the liquid forming additives of$Al_2O_3+Y_2O_3$ Phase analysis of composites by XRD revealed $\alpha-SiC(6H) ZrB_2\; and YAG(Al_5Y_3O_{12})$ The relative density of composites were increased with increased Al2O3+Y2O3 contents. The Flexural strength showed the highest value of 390.6MPa for composites added with 20wt% Al2O3+Y2O3 additives at room temperature. Owing to crack deflection crack bridging phase transition and YAG of fracture toughness mechanism the fracture toughness showed the highest value of 6.3MPa.m1/2 for composites added with 24wt% Al2O3+Y2O3 additives at room temperature. The resistance temperature coefficient showed the value of$ 2.46\times10^{-3}\;, 2.47\times10^{-3},\; 2.52\times10^{-3}/^{\circ}C$ for composite added with 16, 20, 24wt% Al2O3+Y2O3 additives respectively. The electrical resistivity of the composites was all positive temperature coefficient resistance(PTCR) in the temperature range of $256{\circ}C\; to\; 900^{\circ}C$.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2008년도 제39회 하계학술대회
• /
• pp.1230-1231
• /
• 2008

The effect of content of $Al_2O_3+Y_2O_3$ sintering additives on the densification behavior, mechanical and electrical properties of the pressureless-sintered $SiC-ZrB_2$ electroconductive ceramic composites was investigated. The $SiC-ZrB_2$ electroconductive ceramic composites were pressureless-sintered for 2 hours at 1,700[$^{\circ}C$] temperatures with an addition of $Al_2O_3+Y_2O_3$(6:4 mixture of $Al_2O_3$ and $Y_2O_3$) as a sintering aid in the range of 8${\sim}$20[wt%]. Phase analysis of $SiC-ZrB_2$ composites by XRD revealed mostly of ${\alpha}$-SiC(6H), $ZrB_2$ and In Situ YAG($Al_5Y_3O_{12}$). The relative density, flexural strength, Young's modulus and vicker's hardness showed the highest value of 89.01[%], 81.58[Mpa], 31.437[GPa] and 1.34[GPa] for $SiC-ZrB_2$ composites added with 16[wt%] $Al_2O_3+Y_2O_3$ additives at room temperature respectively. Abnormal grain growth takes place during phase transformation from ${\beta}$-SiC into ${\alpha}$-SiC was correlated with In Situ YAG phase by reaction between $Al_2O_3$ and $Y_2O_3$ additive during sintering. Compositional design and optimization of processing parameters are key factors for controlling and improving the properties of SiC-based electroconductive ceramic composites. In this paper, it is convinced that ${\beta}$-SiC based electroconductive ceramic composites for heaters or ignitors can be manufactured by pressureless sintering.

• 한국재료학회지
• /
• 제21권4호
• /
• pp.220-224
• /
• 2011

Zircon has excellent thermal, chemical, and mechanical properties, but it is hard to make a dense sintered product because of dissociation during the sintering process. This study analyzes how the addition of $SiO_2$ and $Al_2O_3$ affects the mechanical properties of sintered zircon, particularly in regards to reducing the thermal dissociation and improving the mechanical properties of $ZrSiO_4$. Zircon specimens containing different amounts of $SiO_2$ and $Al_2O_3$ were prepared and sintered to observe how the mechanical properties of $ZrSiO_4$ changed according to the differing amount of $SiO_2$ and $Al_2O_3$. The $ZrSiO_4$ that was used for the starting material was ground by ball mill to an average particle size of 3 ${\mu}m$. The $SiO_2$ and $Al_2O_3$ that was used for additives were ground to an average particle size of 3 ${\mu}m$ and 0.5 ${\mu}m$, respectively. Adding $SiO_2$ resulted in transformation in the liquid phase at high temperatures, which had little effect on suppressing the thermal dissociation but enhanced the mechanical properties of $ZrSiO_4$. When $Al_2O_3$ was added, the mechanical properties of $ZrSiO_4$ decreased due to the formation of pores and abnormal grains in the microstructure of the sintered zircon.

• 한국세라믹학회지
• /
• 제37권4호
• /
• pp.354-358
• /
• 2000

Tetragonal (t)-ZrO2/Al2O3 composites doped with Y2O3, Nb2O5, and Fe2O3 ((Y, Nb, Fe)-TZP/Al2O3) were prepared over the range containing Fe2O3 from 0.1 to 0.5 mol% with 0.1 mol% intervals to evaluate the effect of Fe2O3 addition on chromaticity, hydrothermal stability, and mechanical property of the composites. After autoclaving for 20 h at 18$0^{\circ}C$ under 3.5 MPa water vapor pressure, no tlongrightarrowm phase transformation was observed probably due to the preferential solid solubility of Fe2O3 in Al2O3, the presence of the rigid Al2O3 particles, and the inherent phase stability of (Y, Nb)-TZP. The optimized strength and the fracture toughness of the composite were 700 MPa and 8.5 MPa.m1/2, respectively, when 0.1 mol% Fe2O3 was added. The composites have shown a gradual color change from a slightly white ivory to a pale yellowish brown with increasing the Fe2O3 concentration.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1999년도 하계학술대회 논문집 D
• /
• pp.1913-1915
• /
• 1999

The ${\beta}-SiC+ZrB_2$ ceramic composites were hot-press sintered and annealed by adding 1, 2, 3wt% $Al_2O_3+Y_2O_3$(6 : 4wt%) powder as a liquid forming additives at $1950^{\circ}C$ for 4h. In this microstructures, no reactions were observed between $\beta$-SiC and $ZrB_2$, and the relative density is over 90.79% of the theoretical density and the porosity decreased with increasing $Al_2O_3+Y_2O_3$ contents. Phase analysis of the composites by XRD revealed of $\alpha$-SiC(6H, 4H), $ZrB_2$, $Al_2O_3$ and $\beta$-SiC(15R). Flexural strength showed the highest of 315.46MPa for composites added with 3wt% $Al_2O_3+Y_2O_3$ additives at room temperature. Owing to crack deflection and crack bridging of fracture toughness mechanism, the fracture toughness showed the highest of $5.5328MPa{\cdot}m^{1/2}$ for composites added with 2wt% $Al_2O_3+Y_2O_3$ additives at room temperature.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2013년도 춘계학술대회 논문집
• /
• pp.116-116
• /
• 2013

(Ni-22Cr-10Al-1Y)와 ($ZrO_2-25CeO_2-2.5Y_2O_3$)로 구성되는 금속/세라믹 복합코팅을 대기용사(ASP; air plasma spay)으로 철 기판위에 1:3, 2:2, 3:1의 무게비로 혼합하여 제조하였다. 용사된 코팅은 금속이영지역과 세라믹잉여지역으로 구별되고, 용사중에 NiCrAlY중의 Al이 선택적으로 산화되어 Al2O3가 계면에 존재하였다. 복합코팅은 $NaCl-Na_2SO_4$ 용융염에서 $800{\sim}900^{\circ}C$, 50시간 동안 부식실험을 실시하였다. 부식생성물은 NiO, $Cr_2O_3$, ${\alpha}-Al_2O_3$가 생성되는데, 부식이 진행되면서 용해되었다. 용융염 부식이 진행되는 동안에 Cr, Al이 외방확산하였고, Na, Cl, S는 내부로 확산되었다. 시간 및 온도뿐만 아니라 금속의 양이 증가할수록 코팅의 내식성은 저하되었다.

• 한국세라믹학회지
• /
• 제27권4호
• /
• pp.465-472
• /
• 1990

The effects of Al2O3 and Cr2O3 addition on the mechanical properties and microstructures of Y-TZP ceramics obtained by co-precipitation method of ZrO2＋3m/o Y2O3, following pressureless sintering at 150$0^{\circ}C$ for 2h were investigated. The addition of Al2O3 and Cr2O3 improved the Y-TZP sinterability and the Al2O3 addition showed the better effect on Y-TZP sintering than that of the Cr2O3 addition. The density and microstructure had the better effect on the bending strength of specimen more than stressinduced phase transformation (SIPT) of ZrO2 from tetragonal to monoclinic phase. The hardness of the specimens was found to be depend on the relative density and the fracture toughness of Y-TZP was found to rely on the amount of SIPT. The grian size of Cr2O3-doped Y-TZP was observed to be relatively smaller and had a narrower distribution than that of Al2O3-doped Y-TZP. If decomposition reaction of Cr2O3 can be controlled at high temperatures, it is anticipated that the mechanical properties of Y-TZP can be much improved by the Cr2O3 addition.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2012년도 춘계학술발표회 논문집
• /
• pp.174-175
• /
• 2012

음극 아크법으로 증착한 $ZrO_2/Al_2O_3$ 박막의 고온특성을 대기중 $600-900^{\circ}C$에서 50시간동안 노출시킨후 XRD, XPS, AES. SEM, TEM을 이용하여 분석하였다. 증착된 박막은 비정질이었고, 고온에서 가열함에 따라 점차 결정질로 바뀌었다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2009년도 추계학술발표대회
• /
• pp.11.1-11.1
• /
• 2009

Ternary Al2O3.ZrO2.Y2O3 samples with a eutecticcomposition were prepared by slow cooling. The microstructural evolution wasobserved with X-ray diffraction (XRD), scanning electron microscopy (SEM). TheSEM observation of the ternary samples agreed with the XRD with a completion ofcrystallisation by slow cooling. The target materials commonly have 'cantaloupe skin' microstructures as shown inthe previous studies by Han et al. The nanocomposite may have experienceddifferent cooling rates with two different microstructures, near the surfacehaving experienced optimal conditions for the eutectic reaction during theircooling and thus formed the eutectic microstructure, near the centre havingexperienced a slower cooling rate. The crystallised eutectic ternary Al2O3.ZrO2.Y2O3 system had three different phaseswith a 3Y2O3. 5Al2O3 (yttrium.aluminiumgarnet phase), an alumina phase formed by the eutectic reaction, and a solidsolution of ZrO2 and Y2O3.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2014년도 추계학술대회 논문집
• /
• pp.117-117
• /
• 2014

Thin $ZrO_2/Al_2O_3$ films were deposited on a tool steel substrate using Zr and Al cathodes in a cathodic arc plasma deposition system (CAPD), and then oxidized at $600-900^{\circ}C$ in air for up to 50 h. They effectively suppressed the oxidation of the substrate up to $800^{\circ}C$ by acting as a barrier layer against the outward diffusion of the substrate elements and inward diffusion of oxygen. However, rapid oxidation occurred at $900^{\circ}C$ due mainly to the increased diffusion and subsequent oxidation of steel as well as the crystallization of amorphous $Al_2O__3$.