This study was to measure the dielectric characteristics of 0.05Pb($Al_{0.5}Nb_{0.5}$)-0.95Pb($Zr_{0.52}Ti_{0.48})O_3$[PAN-PZT] system ceramics according to the variation of $Cr_{2}O_3$, $Fe_{2}O_3$ addition amount. 0.0$\sim$1.2[wt%] and according to sintering temperature after creating the specimens with a general sintering way. The results of this study were summarized as follows : the dielectric constant at 20[$^{\circ}C$] reduced dy increasing additive on the whole. The dielectric loss was minimum value of 12.77[%], sintered at 1200[$^{\circ}C$], dopped with $Cr_{2}O_3$ 0.3[wt%] and minimum value of 10.89[%], sintered at 1200[$^{\circ}C$], dopped with $Fe_{2}O_3$ 0.6[wt%]. The variation rate of dielectric constant according to the change of frequency was decreased slowly by increasing frequency. The temperature coefficient of capacitance turned out increasing the stability of the temperature, decreased $Cr_{2}O_3$ 0.3wt% showed its minimum value 0.59[%/$^{\circ}C$], the maximum value 0.9[%/$^{\circ}C$] with $Cr_{2}O_3$ 3wt%.
고체 전해질로 많이 사용되는 이트리아로 안정화된 입방정형(cubic) 지르코니아의 기계적 강도를 향상시키기 위하여, 단사형(monoclinic) 지르코니아(m-$ZrO_2$)를 원료로 지르코니아 안정화시키는 이트리아와 지르코니아의 낮은 기계적 강도를 향상시켜 주기 위한 알루미나를 Yag($Y_3Al_5O_{13}$)졸의 형태로 첨가하여, 졸 형태로 첨가된 이트리아와 알루미나가 입방정 지르코니아 소결체의 기계적, 전기적 특성에 미치는 영향을 조사하였다. 17.8 wt% Yag(6.3mol% $Y_2O_3$)가 첨가된 경우 파괴인성은 3.62MPa${\cdot}m^{1/2}$, 파괴강도는 447MPa로 8mol%의 이트리아로 안정화된 지르코니아(TZ8Y)의 1.44MPa${\cdot}m^{1/2}$, 270MPa에 비하여 기계적 특성이 현저히 향상되었으나, 950$^{\circ}$C, 공기분위기에서의 전기전도도는 0.057${\Omega}^{-1}cm^{-1}$로 TZ8Y에 비해 반 정도로 낮아졌으며, 21.6wt% Yag(8.0mol% $Y_2O_3$)가 첨가된 경우에는 파괴인성은 2.93MPa${\cdot}m^{1/2}$, 파괴강도는 388MPa로 TZ8Y에 비하여 향상되었고, 전기전도도는 0.076${\Omega}^{-1}cm^{-1}$을 나타내었다.
The Metal-Insulator-Silicon (MIS) capacitors with $SiO_2$ and high-k dielectric were investigated. The high-k dielectrics were obtained by atomic layer deposit (ALD) system. The electrical characteristics were investigated by measuring the current-voltage (I-V) characteristics. The conduction mechanisms were analyzed by using the Fowler-Nordheim (FN) plot and Direct Tunneling (DT) plot. As a result, the MIS capacitors with high-k dielectrics have lower leakage current densities than conventional tunnel-barrier with $SiO_2$ dielectrics.
Submicron high-purity mullite powder was prepared by a colloidal sol-gel route. Boehmite and silica were the starting materials. 2wt% $\alpha$-Al2O3 or ZrO2 was used as a seeding material. The gelled powder was calcined at 130$0^{\circ}C$ for 100min and attrition milled for 3hrs. The mullite powder obtained was composed of submicrometer and uniform particles with a narrow size distribution. It was hot-pressed at 1$600^{\circ}C$ for 1hr under 10MPa or was sintered at 1$650^{\circ}C$ for 4hrs. The bulk densities of the products made by both processes were 3.14 and 3.12g/㎤. the mechanical, thermal and electrical properties of the sintered mullite were characterized by bending strength, thermal expansion coefficient, thermal conductivity, dielectric constant and dielectric loss, etc.
연구 목적: 본 연구는 서로 다른 세가지 블라스팅 처리를 한 티타늄 디스크에$Nd:YVO_4$ 레이저 조사 조건을 달리한 후 조사하여 티타늄의 표면 거칠기 및 표면 변화를 관찰하기 위함이다. 연구 재료 및 방법: 디스크 형태의 상용 순수 티타늄 시편을 30개 준비하여 시료 표면을 각각 10개씩 $ZrO_2$ (zirconium dioxide), $Al_2O_3$ (aluminium oxide), RBM (resorbable blasted media)으로 블라스팅(blasting)하고 초음파 세척하였다. $Nd:YVO_4$ 레이저(Laser Pro D-20, Laserval $Korea^{(R)}$, Seoul, South Korea)에서 주사속도(100, 300, 500 mm/s)와 시간당 진동량(반복률) (5, 15, 35 kHz)을 다르게 하여 9가지 조건을 설정하였다. 레이저 조사 후 주사전자현미경, X-선 회절 분석 및 에너지 분산X선 분광분석, 표면 거칠기 분석을 통해 각 시편을 평가하고 분석하였다. 결과: 주사전자현미경의 결과 레이저 조사를 시행하지 않은 티타늄 표면은 방향성이 없는 불규칙한 형상을 보였고 레이저 조사를 처리한 시편은 특징적인 형태가 관찰되었다. X-선회절분석결과$ZrO_2$, RBM 의 고유피크는 관찰되지 않았으나 $Al_2O_3$분사한 군에서는 알루미나의 고유 피크가 관찰되었다. 에너지 분산X선 분광분석을 통해 관찰한 티타늄의 산화도 경향성과 표면 거칠기는 유사하였다. 표면 거칠기는 주사속도와 반복률에 따른 차이를 보였다(P<.05). 결론: 레이저 조사 조건에 따라 티타늄 디스크의 미세구조와 표면 거칠기가 변화되었다. 레이저 조사는 골유착을 증진시키기 위한 임플란트 표면을 변화시키는 방법중의 하나로 여길 수 있을 것이다.
정보화 기술이 급속히 발전함에 따라서 보다 많은 양의 data를 전송, 처리, 저장 하게 되면서 이를 처리 할 수 있는 대용량, 고속, 비휘발성의 차세대 메모리의 개발이 요구 되고 있다. 이 중 저항 변화 메모리(ReRAM)는 일반적으로 전이금속산화물을 이용한 MIM 구조로서 적당한 전기 신호를 가하면 저항이 높아서 전도되지 않는 상태(Off state)에서 저항이 낮아져 전도가 가능한 상태(On state)로 바뀌는 메모리 특성을 가진다. ReRAM은 비휘발성 메모리이며 종래의 비휘발성 기억소자인 Flash memory 보다 access time이 $10^5$배 이상 빠르며, 2~5V 이하의 낮은 전압에서 동작이 가능하다. 또한 구조가 간단하여 공정상의 결함을 현저히 줄일 수 있다는 점 등 많은 장점들이 있어서 Flash memory를 대체할 수 있는 유력한 후보로 여겨지고 있다. 저항 변화의 특징을 잘 나타내는 물질에는 $TiO_2$, $Al_2O_3$, $NiO_2$, $HfO_2$, $ZrO_2$등의 많은 전이금속산화물들이 있다. 본 연구에서는 Reactive DC-magnetron Sputtering 방법과 DC-magnetron sputter를 이용하여 Ti를 증착한 후 Oxidation 방법으로 각각 증착한 $TiO_2$박막을 사용하여 저항변화특성을 관찰하였다. $TiO_2$상부에 Atomic Layer Deposition (ALD)를 이용하여 $HfO_2$ 박막을 증착하여 표면처리를 하고, 또한 $TiO_2$에 다른 전이 금속박막 층을 추가 증착하여 저항변화 특성에 접합한 조건을 찾는 연구를 진행하였다. 하부 전극과 상부 전극 물질로는 Si 100 wafer 위에 Pt 또는 TiN을 사용하였다. 저항변화 특성을 평가하기 위해 Agilent E5270B를 이용하여 current-voltage (I-V)를 측정하였다. X-ray Diffraction (XRD)를 이용하여 증착 된 전기금속 박막 물질의 결정성을 관찰했으며, Atomic Force Microscopy (AFM)을 이용하여 증착 된 샘플의 표면을 관찰했다. SEM과 TEM을 통해서는 sample의 미세구조를 확인 하였다.
The catalytic activity of Ni-0.2%YSZ (Yttria-Stabilized Zirconia) with different promoters was evaluated for $CO_2$ methanation. The catalysts were weighed for mixing and they were dried at $110^{\circ}C$ for molding into disks. The concentration of $CO_2$ and $CH_4$ for conducting of $CO_2$ methanation were analyzed by gas chromatography and the physical characteristics of the disk-type catalyst formed were analyzed by X-ray diffraction, scanning electron microscope and energy dispersive x-ray spectrometer. The addition of $CeO_2$ as a promoter for Ni-0.2%YSZ (denoted as Ni-5%Ce-0.2%YSZ) resulted in the highest $CO_2$ methanation. It also showed catalytic activity at a low temperature($200^{\circ}C$). Following this, $ZrO_2$, $SiO_2$, $Al_2O_3$ and $TiO_2$ were added to Ni-5%Ce-0.2%YSZ to compare the $CO_2$ methanation, and the highest efficiency was found for. Ni-1%Ti-5%Ce-0.2%YSZ Then, the concentration of Ti was increased to 10% and the catalytic activity was estimated using seven different types of commercial $TiO_2$. In conclusion, ST-01 $TiO_2$ showed the highest efficiency for $CO_2$ methanation.
Y-TZP/mullite composites were prepared by the infiltration of Y-TZP precursor into partially reaction-sintered mullite. The addition of Y-TZP(~7.2 wt%) increased the bend strength(207 MPa), fracture toughness(4.6MPa.m1/2) and Vickers microhardness(853kg/$\textrm{mm}^2$) of the uninfiltrated mullite sintered at 162$0^{\circ}C$ for 10h by more than 75, 70 and 105%, respectively. Residual alumina-rich glass was observed at a mullite/mullite junction, due to the mullitization reaction of silica melt with crystalline $\alpha$-Al2O3 during a final sintering. Although ZrO2 inclusions improved the final sintered density of mullite they did not effectively prevent its grain growth.
The W-Cu composite powders were synthesized from W and Cu elemental powders by ball-milling process, and their microstructural changes and sintering behaviors were evaluated. The ball milling process was carried out in a 3-dimensional mixer (Turbula mixer) using zirconic ($ZrO_2$) ball and alumina ($Al_2O_3$) vial up to 300 hrs. The ball-milled W-Cu powders revealed nearly spherical shape. Microstructure of the composite powders showed onion-like structure which consists of W and Cu shells due to the moving characteristic of Turbula mixer. The W and Cu elements in the composite powders milled for 300 hrs were homogeneously distributed, and W grain size in the ball-milled powder was smaller than 0.5 $\mu\textrm{m}$. Fe impurity introduced during ball milling process was very low as of 0.001 wt%. The relative sintered density of ball-milled W-Cu specimens reached about 94% after sintering at $1100^{\circ}C$.
This study aims at investigating the wear behavior of thermally sprayed Ni-based self-flux alloy coatings against different counterparts. Ni-based self-flux alloy powders were flame-sprayed onto a carbon steel substrate and then heat-treated at temperature of $1000^{\circ}C$. Dry sliding wear tests were performed using the sliding speeds of 0.2 and 0.8 m/s and the applied loads of 5 and 20 N. AISI 52100, $Al_2O_3$, $Si_3N_4$ and $ZrO_2$ balls were used as counterpart materials. Wear behavior of Ni-based self-flux alloy coatings against different counterparts were studied using a scanning electron microscope(SEM) and energy dispersive X-ray spectroscopy (EDX). It was revealed that wear behavior of Ni-based self-flux alloy coatings were much influenced by counterpart materials.
본 웹사이트에 게시된 이메일 주소가 전자우편 수집 프로그램이나
그 밖의 기술적 장치를 이용하여 무단으로 수집되는 것을 거부하며,
이를 위반시 정보통신망법에 의해 형사 처벌됨을 유념하시기 바랍니다.
[게시일 2004년 10월 1일]
이용약관
제 1 장 총칙
제 1 조 (목적)
이 이용약관은 KoreaScience 홈페이지(이하 “당 사이트”)에서 제공하는 인터넷 서비스(이하 '서비스')의 가입조건 및 이용에 관한 제반 사항과 기타 필요한 사항을 구체적으로 규정함을 목적으로 합니다.
제 2 조 (용어의 정의)
① "이용자"라 함은 당 사이트에 접속하여 이 약관에 따라 당 사이트가 제공하는 서비스를 받는 회원 및 비회원을
말합니다.
② "회원"이라 함은 서비스를 이용하기 위하여 당 사이트에 개인정보를 제공하여 아이디(ID)와 비밀번호를 부여
받은 자를 말합니다.
③ "회원 아이디(ID)"라 함은 회원의 식별 및 서비스 이용을 위하여 자신이 선정한 문자 및 숫자의 조합을
말합니다.
④ "비밀번호(패스워드)"라 함은 회원이 자신의 비밀보호를 위하여 선정한 문자 및 숫자의 조합을 말합니다.
제 3 조 (이용약관의 효력 및 변경)
① 이 약관은 당 사이트에 게시하거나 기타의 방법으로 회원에게 공지함으로써 효력이 발생합니다.
② 당 사이트는 이 약관을 개정할 경우에 적용일자 및 개정사유를 명시하여 현행 약관과 함께 당 사이트의
초기화면에 그 적용일자 7일 이전부터 적용일자 전일까지 공지합니다. 다만, 회원에게 불리하게 약관내용을
변경하는 경우에는 최소한 30일 이상의 사전 유예기간을 두고 공지합니다. 이 경우 당 사이트는 개정 전
내용과 개정 후 내용을 명확하게 비교하여 이용자가 알기 쉽도록 표시합니다.
제 4 조(약관 외 준칙)
① 이 약관은 당 사이트가 제공하는 서비스에 관한 이용안내와 함께 적용됩니다.
② 이 약관에 명시되지 아니한 사항은 관계법령의 규정이 적용됩니다.
제 2 장 이용계약의 체결
제 5 조 (이용계약의 성립 등)
① 이용계약은 이용고객이 당 사이트가 정한 약관에 「동의합니다」를 선택하고, 당 사이트가 정한
온라인신청양식을 작성하여 서비스 이용을 신청한 후, 당 사이트가 이를 승낙함으로써 성립합니다.
② 제1항의 승낙은 당 사이트가 제공하는 과학기술정보검색, 맞춤정보, 서지정보 등 다른 서비스의 이용승낙을
포함합니다.
제 6 조 (회원가입)
서비스를 이용하고자 하는 고객은 당 사이트에서 정한 회원가입양식에 개인정보를 기재하여 가입을 하여야 합니다.
제 7 조 (개인정보의 보호 및 사용)
당 사이트는 관계법령이 정하는 바에 따라 회원 등록정보를 포함한 회원의 개인정보를 보호하기 위해 노력합니다. 회원 개인정보의 보호 및 사용에 대해서는 관련법령 및 당 사이트의 개인정보 보호정책이 적용됩니다.
제 8 조 (이용 신청의 승낙과 제한)
① 당 사이트는 제6조의 규정에 의한 이용신청고객에 대하여 서비스 이용을 승낙합니다.
② 당 사이트는 아래사항에 해당하는 경우에 대해서 승낙하지 아니 합니다.
- 이용계약 신청서의 내용을 허위로 기재한 경우
- 기타 규정한 제반사항을 위반하며 신청하는 경우
제 9 조 (회원 ID 부여 및 변경 등)
① 당 사이트는 이용고객에 대하여 약관에 정하는 바에 따라 자신이 선정한 회원 ID를 부여합니다.
② 회원 ID는 원칙적으로 변경이 불가하며 부득이한 사유로 인하여 변경 하고자 하는 경우에는 해당 ID를
해지하고 재가입해야 합니다.
③ 기타 회원 개인정보 관리 및 변경 등에 관한 사항은 서비스별 안내에 정하는 바에 의합니다.
제 3 장 계약 당사자의 의무
제 10 조 (KISTI의 의무)
① 당 사이트는 이용고객이 희망한 서비스 제공 개시일에 특별한 사정이 없는 한 서비스를 이용할 수 있도록
하여야 합니다.
② 당 사이트는 개인정보 보호를 위해 보안시스템을 구축하며 개인정보 보호정책을 공시하고 준수합니다.
③ 당 사이트는 회원으로부터 제기되는 의견이나 불만이 정당하다고 객관적으로 인정될 경우에는 적절한 절차를
거쳐 즉시 처리하여야 합니다. 다만, 즉시 처리가 곤란한 경우는 회원에게 그 사유와 처리일정을 통보하여야
합니다.
제 11 조 (회원의 의무)
① 이용자는 회원가입 신청 또는 회원정보 변경 시 실명으로 모든 사항을 사실에 근거하여 작성하여야 하며,
허위 또는 타인의 정보를 등록할 경우 일체의 권리를 주장할 수 없습니다.
② 당 사이트가 관계법령 및 개인정보 보호정책에 의거하여 그 책임을 지는 경우를 제외하고 회원에게 부여된
ID의 비밀번호 관리소홀, 부정사용에 의하여 발생하는 모든 결과에 대한 책임은 회원에게 있습니다.
③ 회원은 당 사이트 및 제 3자의 지적 재산권을 침해해서는 안 됩니다.
제 4 장 서비스의 이용
제 12 조 (서비스 이용 시간)
① 서비스 이용은 당 사이트의 업무상 또는 기술상 특별한 지장이 없는 한 연중무휴, 1일 24시간 운영을
원칙으로 합니다. 단, 당 사이트는 시스템 정기점검, 증설 및 교체를 위해 당 사이트가 정한 날이나 시간에
서비스를 일시 중단할 수 있으며, 예정되어 있는 작업으로 인한 서비스 일시중단은 당 사이트 홈페이지를
통해 사전에 공지합니다.
② 당 사이트는 서비스를 특정범위로 분할하여 각 범위별로 이용가능시간을 별도로 지정할 수 있습니다. 다만
이 경우 그 내용을 공지합니다.
제 13 조 (홈페이지 저작권)
① NDSL에서 제공하는 모든 저작물의 저작권은 원저작자에게 있으며, KISTI는 복제/배포/전송권을 확보하고
있습니다.
② NDSL에서 제공하는 콘텐츠를 상업적 및 기타 영리목적으로 복제/배포/전송할 경우 사전에 KISTI의 허락을
받아야 합니다.
③ NDSL에서 제공하는 콘텐츠를 보도, 비평, 교육, 연구 등을 위하여 정당한 범위 안에서 공정한 관행에
합치되게 인용할 수 있습니다.
④ NDSL에서 제공하는 콘텐츠를 무단 복제, 전송, 배포 기타 저작권법에 위반되는 방법으로 이용할 경우
저작권법 제136조에 따라 5년 이하의 징역 또는 5천만 원 이하의 벌금에 처해질 수 있습니다.
제 14 조 (유료서비스)
① 당 사이트 및 협력기관이 정한 유료서비스(원문복사 등)는 별도로 정해진 바에 따르며, 변경사항은 시행 전에
당 사이트 홈페이지를 통하여 회원에게 공지합니다.
② 유료서비스를 이용하려는 회원은 정해진 요금체계에 따라 요금을 납부해야 합니다.
제 5 장 계약 해지 및 이용 제한
제 15 조 (계약 해지)
회원이 이용계약을 해지하고자 하는 때에는 [가입해지] 메뉴를 이용해 직접 해지해야 합니다.
제 16 조 (서비스 이용제한)
① 당 사이트는 회원이 서비스 이용내용에 있어서 본 약관 제 11조 내용을 위반하거나, 다음 각 호에 해당하는
경우 서비스 이용을 제한할 수 있습니다.
- 2년 이상 서비스를 이용한 적이 없는 경우
- 기타 정상적인 서비스 운영에 방해가 될 경우
② 상기 이용제한 규정에 따라 서비스를 이용하는 회원에게 서비스 이용에 대하여 별도 공지 없이 서비스 이용의
일시정지, 이용계약 해지 할 수 있습니다.
제 17 조 (전자우편주소 수집 금지)
회원은 전자우편주소 추출기 등을 이용하여 전자우편주소를 수집 또는 제3자에게 제공할 수 없습니다.
제 6 장 손해배상 및 기타사항
제 18 조 (손해배상)
당 사이트는 무료로 제공되는 서비스와 관련하여 회원에게 어떠한 손해가 발생하더라도 당 사이트가 고의 또는 과실로 인한 손해발생을 제외하고는 이에 대하여 책임을 부담하지 아니합니다.
제 19 조 (관할 법원)
서비스 이용으로 발생한 분쟁에 대해 소송이 제기되는 경우 민사 소송법상의 관할 법원에 제기합니다.
[부 칙]
1. (시행일) 이 약관은 2016년 9월 5일부터 적용되며, 종전 약관은 본 약관으로 대체되며, 개정된 약관의 적용일 이전 가입자도 개정된 약관의 적용을 받습니다.